Skocz do pozycji: 1.

Tytuł:

Morphology and properties of the graphene layer on the copper substrate

Autorzy:

Pietrzak, K.
Olesińska, W.
Strąk, C.
Siedlec, R.
Gładki, A.

Powiązania:

https://bibliotekanauki.pl/articles/778091.pdf

Data publikacji:

2015

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

copper
graphene
graphene oxide
reduced graphene oxide

Opis:

The aim of the work presented in the article was to clarify controversial comments about anti-corrosion and mechanical properties of graphene coatings, deposited on copper substrates. It was designed special experimental cycle comprising: preparation of graphene forms and copper, the observation of layers Cu / GO (rGO) after the thermal reduction processes and oxidative test in air at 150°C temperature and 350 h in time. The resulting coatings and graphene layers were subjected to tribological test for hardness. The observed differences in the continuity of the coverage copper surface by graphene forms, allowed to understand the macroscopic effect of increased hardness and wear resistance layers rGO/Cu.

Źródło:

Polish Journal of Chemical Technology; 2015, 17, 4; 104-108
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 2.

Tytuł:

Graphene-Based Composite Membrane for Water Desalination

Autorzy:

Dybowski, K.
Kowalczyk, P.
Kula, P.
Jeziorna, A.
Atraszkiewicz, R.
Kołodziejczyk, Ł.
Zawadzki, P.
Nowak, D.
Kazimierczak, T.
Kucińska, M.

Powiązania:

https://bibliotekanauki.pl/articles/354170.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

graphene
desalination
water filtration
polycrystalline graphene
graphene composite

Opis:

The article presents the results of studies on the efficacy of water desalination (i.e. Elimination of NaCl ions from the solution) using graphene-polyamide composite membranes. The membranę used for filtration consists of a monolayer of polycrystalline graphene on a porous polyamide carrier support (nylon 66). The degree of desalination for an aqueous NaCl solution percolated through the membrane was 18%. In the future this type of membrane may replace the currently used reverse osmosis membranes.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 3; 1379-1383
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 3.

Tytuł:

Manufacturing of composites samples with graphene
Wytwarzanie kompozytowych próbek z grafenem

Autorzy:

Wiśniewski, A.
Sałacińska, A.
Szymański, R.
Kunikowska, A.

Powiązania:

https://bibliotekanauki.pl/articles/213647.pdf

Data publikacji:

2016

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Lotnictwa

Tematy:

composite
graphene
composites with graphene

Opis:

The article presents the state of knowledge within the scope of graphene production used in polymer matrices composites, as well as methods of obtaining graphene for these composites, including chemical method. The way of obtaining graphene in form of planes with dimensions of90 x 100 mm and the method of manufacturing multilayer composite with graphene were presented. Composites were produced from carbon fiber-epoxy resin prepregs in out of autoclave process. The adhesive film were used as an additional component which allows to transfer of graphene plane on carbon-epoxy resin prepregs and facilitate the consolidation process. In terms of the quality analysis of prepared composite samples results of ultrasonic tests of composites plate without the graphene and with graphene as an A-scan, B-scan, C-scan, S-scan were shown. The use of ultrasonic methods of registration: C-scan type amplitude of the echo and bottom echo signal amplitude, that allows to detect manufacturing defects caused by the mismatch of parallel edges of carbon prepregs, were engaged. The analysis of C-scan images allows to determine the accuracy of the angular orientation of the carbon layers.
W artykule przedstawiono stan wiedzy w zakresie wytwarzania grafenu do zastosowań w kompozytach o osnowach polimerowych, a także metody pozyskiwania grafenu dla tych kompozytów, w tym metodę chemiczną. Przedstawiono sposób pozyskiwania grafenu w formie płaszczyzn o wymiarach 90x100 mm, a także metodę wytwarzania wielowarstwowego kompozytu z grafenem. Kompozyty wytwarzano z preimpregantów węglowo-epoksydowych w procesie bezautoklawowym. Zastosowano klej błonkowy, jako dodatkowy składnik kompozytu pozwalający na przeniesienie płaszczyzn grafenowych na preimpregnat węglowo-epoksydowy oraz ułatwiający proces konsolidacji kompozytu. W zakresie wykonanych analiz jakości przygotowanych próbek kompozytowych przedstawiono wyniki badań ultradźwiękowych płyt kompozytowych bez grafenu i z grafenem w postaci: A-scan, B-scan, C-scan i S-scan. Przedstawiono użycie metody ultradźwiękowej z rejestracją typu C-scan amplitudy echa oraz amplitudy echa dna, która pozwala na wykrycie wad produkcyjnych powstałych w wyniku niedopasowania równoległego krawędzi preimpregnatu węglowego. Z analizy obrazów typu C-scan określono dokładność kątową ułożenia warstw węglowych.

Źródło:

Prace Instytutu Lotnictwa; 2016, 4 (245); 262-270
0509-6669
2300-5408

Pojawia się w:

Prace Instytutu Lotnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 4.

Tytuł:

Applications of chitosan–graphene oxide nanocomposites in medical science: a review

Autorzy:

Pieklarz, Katarzyna
Tylman, Michał
Modrzejewska, Zofia

Powiązania:

https://bibliotekanauki.pl/articles/1034405.pdf

Data publikacji:

2018

Wydawca:

Sieć Badawcza Łukasiewicz - Polskie Towarzystwo Chitynowe

Tematy:

biopolymers
chitosan
graphene
graphene oxide
nanomedicine

Opis:

Combinations of biopolymers with nanostructured carbon materials have been the subject of interest of many scientists in recent years. Particularly significant are nanocomposites made of chitosan, which is a linear aminopolysaccharide obtained in the process of deacetylation of chitin, and graphene oxide (GO). These systems, due to the atypical properties of both components such as non-toxicity, biocompatibility with human tissues and organs as well as bacteriostaticity, are characterised by a wide range of biomedical applications. They may be used in emergency medicine as dressing materials which accelerate wound healing, as well as carriers of drugs/genes and biological macromolecules, for example proteins, peptides and nucleic acids. In addition, CS-GO systems can potentially be used in regenerative medicine as scaffolds for cell culture. For this reason, the current publication presents the possibilities of the application of chitosan–graphene oxide nanocomposites in medicine considering the characteristics of the system components.

Źródło:

Progress on Chemistry and Application of Chitin and its Derivatives; 2018, 23; 5-24
1896-5644

Pojawia się w:

Progress on Chemistry and Application of Chitin and its Derivatives

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 5.

Tytuł:

Impact of the Method of Separating Graphene from the Growth Substrate on the Quality of the 2D Material Obtained

Autorzy:

Dybowski, K.
Romaniak, G.
Kula, P.
Jeziorna, A.
Kowalczyk, P.
Atraszkiewicz, R.
Kołodziejczyk, Ł.
Nowak, D.
Zawadzki, P.
Kucińska, M.

Powiązania:

https://bibliotekanauki.pl/articles/351974.pdf

Data publikacji:

2019

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

graphene
polycrystalline graphene
electrochemical delamination
chemical etching
graphene transfer

Opis:

This article presents the research results on impact of the method of polycrystalline graphene layers separation from the growth substrate on the obtained carbon material quality. The studies were carried out on graphene sheets obtained by metallurgical method on a liquid metal substrate (HSMG® graphene). The graphene was separated using chemical etching method or the electrochemical delamination method, by separating by means of electrolysis. During electrolysis, hydrogen is emitted on a graphene-covered of cathode (metal growth substrate) as a result of the voltage applied. The graphene layer breaks away from metallic substrate by gas accumulation between them. The results from these separation processes were evaluated by means of different tools, such as SEM, TEM and AFM microscopy as well as Raman Spectroscopy. In summary, the majority of analyses indicate that the graphene obtained as a result of hydrogen delamination possesses higher purity, smaller size and number of defects, its surface is smooth and less developed after the transfer process to the target substrate.

Źródło:

Archives of Metallurgy and Materials; 2019, 64, 4; 1321-1326
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 6.

Tytuł:

Graphene and graphene oxide in the oil and gas industry

Autorzy:

Jamrozik, A.

Powiązania:

https://bibliotekanauki.pl/articles/299253.pdf

Data publikacji:

2017

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH

Tematy:

drilling
nanotechnologies
graphene
graphene oxide

Opis:

Presently, nanotechnology and nanomaterials have found a number of applications in drilling, exploration and production (E&P) works, as well as in the area of refinery and distribution of crude oil and natural gas. Nanomaterials enjoy considerable popularity owing to their new and unique features which differentiate them from classical materials. Graphene is a relatively new material. Currently it occupies the seventh position among the most commonly used nanomaterials in oil and gas industry. This paper presents the properties graphene and graphene oxide and gives an insight into the applicability of graphene and graphene oxide in the oil and gas industry.

Źródło:

AGH Drilling, Oil, Gas; 2017, 34, 3; 731-744
2299-4157
2300-7052

Pojawia się w:

AGH Drilling, Oil, Gas

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 7.

Tytuł:

Graphene oxide and green-synthesized reduced graphene oxide in chitosanbased nanocomposites

Autorzy:

Kosowska, K.
Domalik-Pyzik, P.
Chłopek, J.

Powiązania:

https://bibliotekanauki.pl/articles/284287.pdf

Data publikacji:

2017

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

graphene oxide
reduced graphene oxide
chitosan
hydroxyapatite
biomaterial

Opis:

The first part of the paper concerns synthesis and characterization of two types of nanomaterials: graphene oxide (GO) prepared by modified Marcano method and reduced graphene oxide (rGO) synthesized using green reductant, L-ascorbic acid. Their structural properties were investigated by attenuated total reflection Fourier-transform infrared spectroscopy (ATR-FTIR) and X-ray diffraction (XRD). Results confirmed that L-ascorbic acid is an effective reducing agent. Intensity of the oxygen-groups decreased dramatically what resulted in reduction of the GO interlayer spacing from 0.8 nm to 0.4 nm. The second part of the research was concentrated on the properties of chitosan nanocomposites modified with GO and rGO. Films were prepared by mixing of the chitosan solution with the nanoparticles dispersion. Scanning electron microscopy (SEM) was used to investigate the microstructure of the composites surface. In addition, wettability and pore size of the freeze-dried scaffolds were evaluated. Results of the mechanical tests (increase in Young’s modulus) and structural characterization confirmed that chitosan solution and GO dispersion can be mixed homogeneously. Reduction of GO during composite synthesis resulted in better dispersion of the nanosheets what increased surface roughness, wettability and stability in distilled water, PBS and Ringer’s solution compared to composite with GO. After detailed biological examination, rGO-modified nanocomposites can be potentially applied in tissue engineering.

Źródło:

Engineering of Biomaterials; 2017, 20, 142; 11-16
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 8.

Tytuł:

Preparation and properties of nanocrystalline Ni/graphene composite coatings deposited by electrochemical method

Autorzy:

Cieślak, G.
Trzaska, M.

Powiązania:

https://bibliotekanauki.pl/articles/949445.pdf

Data publikacji:

2018

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

Graphene
electrodeposition
composite coatings
Ni/graphene coatings

Opis:

The paper presents results of studies of composite nickel/graphene coatings produced by electrodeposition method on a steel substrate. The method of producing composite coatings with nanocrystalline nickel matrix and dispersion phase in the form of graphene is presented. For comparative purposes, the study also includes nano-crystalline Ni coatings produced by electrochemical reduction without built-in graphene flakes. Graphene was characterized by Raman spectroscopy, transmission and scanning electron microscopes. Results of studies on the structure and morphology of Ni and Ni/graphene layers produced in a bath containing different amounts of graphene are presented. Material of the coatings was characterized by SEM, light microscopy, X-ray diffraction. The microhardness of the coatings was examined by Knoop measurements. The adhesion of the coatings with the substrate was tested using a scratchtester. The influence of graphene on the structure and properties of composite coatings deposited from a bath with different graphene contents was determined.

Źródło:

Polish Journal of Chemical Technology; 2018, 20, 1; 29-34
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 9.

Tytuł:

The sensitivity of sensor structures with oxide graphene exposed to selected gaseous atmospheres

Autorzy:

Pustelny, T.
Drewniak, S.
Setkiewicz, M.
Maciak, E.
Urbańczyk, M.
Procek, M.
Gut, K.
Opilski, Z.
Jagiello, J.
Lipinska, L.

Powiązania:

https://bibliotekanauki.pl/articles/200229.pdf

Data publikacji:

2013

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

graphene
graphene oxide
gas sensors
resistive sensors

Opis:

The paper presents the results of investigations on the resistive structure with a graphene oxide (GO) sensing layer. The effects of dangerous gases (hydrogen and nitrogen dioxide) on the structure were studied; the resistance changes were examined during the flow of the selected gas in the atmosphere of synthetic air. Measurements were performed with a special emphasis on the detection of low concentrations of the analyzed gases. The reactions of the sensing structure to the effect of nitrogen and synthetic air at different humidity were also tested. Much attention was also paid to the fast response of the sensor to the changes in the gas atmosphere. The thin palladium layer (~2 nm) has been applied in order to improve the sensing properties of the structure. The investigations were performed in the temperature range from RT to 120°C and the analyzed gases in synthetic air were batched alternately with pure synthetic air.

Źródło:

Bulletin of the Polish Academy of Sciences. Technical Sciences; 2013, 61, 3; 705-710
0239-7528

Pojawia się w:

Bulletin of the Polish Academy of Sciences. Technical Sciences

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 10.

Tytuł:

Adhesion of bacterial films on polymer food films covered by graphene oxide emulsion and graphene nanoparticles

Autorzy:

Kopczyńska, E.
Czerwińska, E.
Mitura, K. A.

Powiązania:

https://bibliotekanauki.pl/articles/283876.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

nanoparticles
graphene
emulsion

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 100
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 11.

Tytuł:

Thermoplastic elastomers containing 2D nanofillers: montmorillonite, graphene nanoplatelets and oxidized graphene platelets

Autorzy:

Paszkiewicz, S.
Pawelec, I.
Szymczyk, A.
Rosłaniec, Z.

Powiązania:

https://bibliotekanauki.pl/articles/779218.pdf

Data publikacji:

2015

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

montmorillonite
graphene oxide
graphene nanoplatelets
thermoplastic elastomers
in situ polymerization

Opis:

This paper presents a comparative study on which type of platelets nanofiller, organic or inorganic, will affect the properties of thermoplastic elastomer matrix in the stronger manner. Therefore, poly(trimethylene terephthalate-block-poly(tetramethylene oxide) copolymer (PTT-PTMO) based nanocomposites with 0.5 wt.% of clay (MMT), graphene nanoplatelets (GNP) and graphene oxide (GO) have been prepared by in situ polymerization. The structure of the nanocomposites was characterized by transmission electron microscopy (TEM) in order to present good dispersion without large aggregates. It was indicated that PTT-PTMO/GNP composite shows the highest crystallization temperature. Unlike the addition of GNP and GO, the introduction of MMT does not have great effect on the glass transition temperature of PTMO-rich soft phase. An addition of all three types of nanoplatelets in the nanocomposites caused the enhancement in tensile modulus and yield stress. Additionally, the cyclic tensile tests showed that prepared nanocomposites have values of permanent set slightly higher than neat PTT-PTMO.

Źródło:

Polish Journal of Chemical Technology; 2015, 17, 4; 74-81
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 12.

Tytuł:

Characterization of graphene oxide-loaded chitosan hydrogels and their application for 3D printing

Autorzy:

Domalik-Pyzik, P.
Chłopek, J.

Powiązania:

https://bibliotekanauki.pl/articles/286115.pdf

Data publikacji:

2017

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

hydrogels
graphene
chitosan

Źródło:

Engineering of Biomaterials; 2017, 20, no. 143 spec. iss.; 83
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 13.

Tytuł:

Bacteria adhesion to graphenic surfaces

Autorzy:

Duch, J.
Golda-Cepa, M.
Kotarba, A.

Powiązania:

https://bibliotekanauki.pl/articles/283807.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

graphene
surfaces
bacteria

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 68
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 14.

Tytuł:

Modification of graphene oxide and reduced graphene oxide with inorganic nanoparticles

Autorzy:

Jagiełło, J.
Baran, M.
Lipińska, L.

Powiązania:

https://bibliotekanauki.pl/articles/284372.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

graphene
oxide
nanoparticles

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 50
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 15.

Tytuł:

The impact of unmodified graphene - based substrates on basic properties of human umbilical cord-derived mesenchymal stem cells in vitro

Autorzy:

Noga, S.
Moździerz, A.
Sekuła, M.
Karnas, E.
Jagiełło, J.
Madeja, Z.
Lipińska, L.
Zuba-Surma, E.

Powiązania:

https://bibliotekanauki.pl/articles/285808.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

stem cells
graphene
substrates

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 83
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 16.

Tytuł:

Application of polymer- and graphene- based materials in biomedical research

Autorzy:

Sekuła, M.
Domalik-Pyzik, P.
Noga, S.
Karnas, E.
Kosowska, K.
Hunger, M.
Złocista-Szewczyk, N.
Jagiełło, J.
Lipińska, L.
Pielichowska, K.
Chłopek, J.
Zuba-Surma, E.

Powiązania:

https://bibliotekanauki.pl/articles/283753.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

polymers
graphene
regenerative medicine

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 66
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 17.

Tytuł:

Composite coatings of polylactide with graphene oxide and hydroxyapatite on titanium

Autorzy:

Torcuato, M. S.
Szaraniec, B.
Kąc, S.
Chłopek, J.

Powiązania:

https://bibliotekanauki.pl/articles/284150.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

coatings
graphene oxide
hydroxyapatite

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 116
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 18.

Tytuł:

Nanokompozyty z grafenem: wytwarzanie, właściwości i znaczenie w budownictwie
Nanocomposites with graphene: preparation, properties and role in construction engineering

Autorzy:

Trzaska, Zdzisław
Trzaska, Maria

Powiązania:

https://bibliotekanauki.pl/articles/460804.pdf

Data publikacji:

2016-09

Wydawca:

Mazowieckie Biuro Planowania Regionalnego w Warszawie

Tematy:

nanokompozyty
grafen
Nanocomposites
graphene

Opis:

Znaczący postęp w rozwoju nowych technologii, w tym inżynierii materiałowej, jaki się dokonał w ubiegłym dwudziestoleciu stawia obecnie projektowanie nowych konstrukcji i urządzeń w świetle wymagań dotąd niemożliwych do spełnienia.. Konstrukcje i urządzenia wykonane z użyciem nanotechnologii całkowicie spełniają wysokie wymagania wytrzymałościowe i kreują postęp techniczny. Nanokompozyty są materiałami wyjątkowo korzystnymi, pod wieloma względami, i efektywnie stosowanymi w praktycznej realizacji złożonych konstrukcji oraz w inżynierii powierzchni. Spełnienie wciąż rosnących wymagań w stosunku do bardzo obciążonych konstrukcji, szczególnie w budownictwie, przemyśle samochodowym i lotniczym, coraz intensywniej wymuszają stosowanie materiałów jednocześnie lekkich, wytrzymałych, niezawodnych i odpornych na działanie środowiska naturalnego. Na przeciw takim wymaganiom wychodzą nanokompozyty o różnych osnowach i z grafenem jako fazą rozproszoną. Właściwości wybranych nanokompozytów z grafenem, metody ich wytwarzania i potencjalne obszary zastosowania stanowią przedmiot rozważań przedstawionych w referacie. Szczególna uwaga jest poświęcona nakompozytom metal/grafen, polimery/grafen, beton/grafen i nanokrystalicznej celulozie.
Significant progress in the development of new technologies, including materials science that has been made in the past two decades puts the current design of new structures and facilities in the light of the requirements are impossible to meet the ever. Structures and devices made using nanotechnology fully meet high strength requirements and create technical progress. Nanocomposites are materials extremely favorable, in many respects, and effectively used in the practical implementation of complex structures and surface engineering. Meeting growing requirements for a heavily loaded structures, particularly in construction, automotive and aerospace industries, increasingly necessitate the use of materials simultaneously light, strong, reliable and resistant to the environment. For such demands go against nanocomposites with different matrices and graphene as the dispersed phase. The properties selected from graphene nanocomposites, methods for their preparation and potential areas of application are the subject of the considerations set out in the paper. Particular attention is devoted to nanocomposites: metal/graphene, polymers/graphene, concrete/graphene and nanocrystalline cellulose.

Źródło:

MAZOWSZE Studia Regionalne; 2016, 19; 223-245
1689-4774

Pojawia się w:

MAZOWSZE Studia Regionalne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 19.

Tytuł:

Graphene-based Current Mode Logic Circuits : a Simulation Study for an Emerging Technology

Autorzy:

Abdollahi, Hassan
Hooshmand, Reza
Owlia, Hadi

Powiązania:

https://bibliotekanauki.pl/articles/226818.pdf

Data publikacji:

2019

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

current mode logic (CML)
graphene
graphene FET
low-power design

Opis:

In this paper, the usage of graphene transistors is introduced to be a suitable solution for extending low power designs. Static and current mode logic (CML) styles on both nanoscale graphene and silicon FINFET technologies are compared. Results show that power in CML styles approximately are independent of frequency and the graphene-based CML (G-CML) designs are more power-efficient as the frequency and complexity increase. Compared to silicon-based CML (Si-CML) standard cells, there is 94% reduction in power consumption for G-CML counterparts. Furthermore, a G-CML 4-bit adder respectively offers 8.9 and 1.7 times less power and delay than the Si-CML adder.

Źródło:

International Journal of Electronics and Telecommunications; 2019, 65, 3; 381-388
2300-1933

Pojawia się w:

International Journal of Electronics and Telecommunications

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 20.

Tytuł:

Use of carbon and aluminosilicate nanofillers in XNBR composites designed for protective materials against oils

Autorzy:

Krzemińska, S. M.
Smejda-Krzewicka, A. A.
Leniart, A.

Powiązania:

https://bibliotekanauki.pl/articles/778545.pdf

Data publikacji:

2018

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

carboxylated nitrile butadiene rubber
XNBR composites
graphene
graphene oxide
bentonite

Opis:

The objective of the work was to investigate the possibility of application of carbon and bentonite nanoparticles in carboxylated acrylonitrile-butadiene rubber (XNBR) and the related effects of the nanofi llers on the structure, as well as mechanical and barrier properties, of the resulting composites. The composites were designed for use in protective clothing and gloves. XNBR compounds were modifi ed with 2 phr of graphene fl akes, graphene oxide, or modifi ed bentonite, and crosslinked with sulfur-accelerator system. Rubber compounds were prepared using a conventional method with a laboratory rolling mill. The composites were studied in terms of structure (WAXS), surface morphology (AFM), the presence of functional groups (ATR-FTIR) barrier properties against chemical substances (mineral oil) and swelling properties, as well as mechanical properties (abrasion resistance and tensile strength). The composites were characterized by very high resistance to oil permeation (breakthrough time >480 min). The type of nanofi ller added to the XNBR blend in the amount of 2 phr did not signifi cantly affect mechanical parameters.

Źródło:

Polish Journal of Chemical Technology; 2018, 20, 2; 15-23
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 21.

Tytuł:

Structure and Properties of Nanocomposite Nickel/Graphene Oxide Coatings Produced by Electrochemical Reduction Method

Autorzy:

Cieślak, G.
Trzaska, M.

Powiązania:

https://bibliotekanauki.pl/articles/354431.pdf

Data publikacji:

2019

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

graphene oxide
nanocomposites
electrodeposition
nickel/graphene oxide coatings
corrosion tests

Opis:

The paper presents the results of research on nanocomposite nickel/graphene oxide (Ni/GO) coatings produced by electrochemical reduction method on a steel substrate. Discussed is the method of manufacturing composite coatings with nickel matrix and embedded graphene oxide flakes. For comparative purposes, the studies also included a nanocrystalline Ni coating without embedded graphene oxide flakes. Graphene oxide was characterized by Raman spectroscopy, infrared spectroscopy (FTIR) and transmission (TEM) and scanning (SEM) electron microscopy. Results of studies on the structure of nickel and composite Ni/GO coatings deposited in a bath containing different amount of graphene oxide are presented. The coatings were characterized by scanning electron microscopy, light microscopy, Raman spectroscopy and X-ray diffraction. The adhesion of the prepared coatings to the substrate was examined by the scratch method. The microhardness of the coatings was measured using the Vickers method on perpendicular cross-sections to the surface. Corrosion tests of the coatings were investigated using the potentiodynamic method. The influence of graphene oxide on the structure and properties of composite coatings deposited from baths with different content of graphene oxide was determined.

Źródło:

Archives of Metallurgy and Materials; 2019, 64, 4; 1479-1486
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 22.

Tytuł:

Zastosowanie materiałów grafenowych w tribologii : analiza stanu zagadnienia i badania wstępne
Application of graphene materials in tribology : analysis of state of the problem and the preliminary research

Autorzy:

Dąbrowski, Igor Jakub
Nogas, Patrycja Magdalena
Kałdoński, Tadeusz
Nasiłowska, Barbara
Djas, Małgorzata

Powiązania:

https://bibliotekanauki.pl/articles/211119.pdf

Data publikacji:

2019

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

tribologia
substancje smarne
grafen
tlenek grafenu
tribology
lubricants
graphene
graphene oxide

Opis:

Publikacja ma na celu przybliżenie podstawowych informacji na temat jednego z najbardziej interesujących materiałów ostatnich lat, jakim jest grafen. Zamieszczono w niej informacje dotyczące struktury grafenu oraz niezwykłych właściwości, jakie z niej wynikają. Przedstawione zostały również metody wytwarzania grafenu oraz obszary techniki, w jakich opisywana substancja znajduje zastosowanie, oraz to, jak może zostać wykorzystana w przyszłości. Szczególną uwagę poświęcono formom zastosowania grafenu w tribologii, obejmującym wykorzystanie wspomnianej substancji w materiałach kompozytowych, powłokach ochronnych oraz jako dodatku do substancji smarnych. Publikacja została opracowana w oparciu o informacje i wyniki badań, zamieszczone w krajowych oraz zagranicznych artykułach, a także wyniki wstępnych badań własnych. Wyniki tych badań dotyczą zmian podstawowych parametrów smarnościowych substancji (oleju i smaru plastycznego) zawierających różną ilość tlenku grafenu (lub porównawczo heksagonalnego azotku boru). Rezultaty potwierdziły korzystny wpływ obecności tlenku grafenu w substancji smarującej na jej właściwości smarnościowe.
Present publication describes one of the most interesting materials discovered in recent years, which is graphene. This paperwork contains information about graphene’s structure, properties, applications and methods of synthesis. The special attention has been given to tribological applications of graphene structures, including the usage of the graphene itself in the composite materials, protective integuments, and additives to lubricants (oils, greases). This publication was based on the information and research results published in the international articles and preliminary researches realized at the Military University of Technology as well. The research results concern the changes of basic lubricants’ parameters, which contain different amount of graphene oxide (or comparatively of hexagonal boron nitride). The results obtained during the tests indicate that graphene oxide could improve lubricating abilities of oils and greases.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2019, 68, 2; 81-108
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 23.

Tytuł:

Development of Graphene Based Flow Sensor

Autorzy:

Kowalski, A.
Safinowski, M.
Szewczyk, R.
Winiarski, W.

Powiązania:

https://bibliotekanauki.pl/articles/385013.pdf

Data publikacji:

2015

Wydawca:

Sieć Badawcza Łukasiewicz - Przemysłowy Instytut Automatyki i Pomiarów

Tematy:

graphene
flow
sensor
voltage

Opis:

This paper shows the research on a flow sensor based on graphene. Presented Results show the linear relation between voltage induced on graphene layer and flow velocity. The measurement shows that signal level is relatively low, and it is highly correlated with the time of the sample being submerged in water. A significant temperature dependency has been shown which indicates on necessity to develop a compensation system for the sensor. On the other hand, induced voltage is related to ion concentration of the liquid, so the sensor must be recalibrated for every working environment. The most important thing that turned out during research is that although the voltage signal itself is highly inconsistent, the difference between its value in steady state and for flowing liquid is always visible and correlated to the flow value – this property can be used in further deployment. Huge advantage of the sensor is also its scalability which opens so far unknown possibilities of applications.

Źródło:

Journal of Automation Mobile Robotics and Intelligent Systems; 2015, 9, 4; 55-57
1897-8649
2080-2145

Pojawia się w:

Journal of Automation Mobile Robotics and Intelligent Systems

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 24.

Tytuł:

Effect of Sample Thickness on Carbon Ejection from Ultrathin Graphite Bombarded by keV C_{60}

Autorzy:

Golunski, M.
Postawa, Z.

Powiązania:

https://bibliotekanauki.pl/articles/1030136.pdf

Data publikacji:

2017-08

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

Computer simulations
sputtering
graphene

Opis:

Molecular dynamics computer simulations are employed to investigate the effect of a sample thickness on the ejection process from ultrathin graphite. The thickness of graphite varies from 2 to 16 graphene layers and the system is bombarded by 10 keV C₆₀ projectiles at normal incidence. The ejection yield and the kinetic energy of emitted atoms are monitored. The implications of the results to a novel analytical approach in secondary ion mass spectrometry based on the ultrathin free-standing graphene substrates and transmission geometry are discussed.

Źródło:

Acta Physica Polonica A; 2017, 132, 2; 222-224
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 25.

Tytuł:

Preparation of functionalized graphene oxide coatings on gold

Autorzy:

Trzaskowski, M.
Ciach, T.

Powiązania:

https://bibliotekanauki.pl/articles/285667.pdf

Data publikacji:

2016

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

gold
coatings
graphene oxide

Źródło:

Engineering of Biomaterials; 2016, 19, 138; 88
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 26.

Tytuł:

Applications of flake graphene in tissue engineering

Autorzy:

Lipińska, L.
Jagiełło, J.
Baran, M.
Kurp, K.

Powiązania:

https://bibliotekanauki.pl/articles/285746.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

graphene
tissue engineering
oxide

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 51
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 27.

Tytuł:

Alginate-based hydrogels modified with graphene oxide and hydroxyapatite for cartilage tissue regeneration

Autorzy:

Lach, A.
Skoczeń, M.
Ordon, K.
Pielichowska, K.

Powiązania:

https://bibliotekanauki.pl/articles/283907.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

graphene
hydroxyapatite
tissue regeneration

Źródło:

Engineering of Biomaterials; 2018, 21, 148; 52
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 28.

Tytuł:

Graphene Polymer Composites: Art of Review on Fabrication Method, Properties, and Future Perspectives

Autorzy:

Niyobuhungiro, Daniel
Hong, Liu

Powiązania:

https://bibliotekanauki.pl/articles/2024186.pdf

Data publikacji:

2021

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

graphene
graphene polymer composites
fabrication
properties
grafen
kompozyty polimerowe z grafenem
wytwarzanie
właściwości

Opis:

Graphene has shown unique properties and introduced new challenges to light materials applicable in different areas. In addition to the polymer, it has brought materials with marvelous properties: mechanical, electrical, thermal, and related to conductivity. Different methods were discovered to produce good nanocomposites. This review summarized those methods, as well as discussed the properties of graphene combined with different kinds of polymers. Furthermore, the different factors affecting graphene reinforced polymer nanocomposites were studied. In the end, the challenges and future prospects for graphene polymer nanocomposites were considered.

Źródło:

Advances in Science and Technology. Research Journal; 2021, 15, 1; 37-49
2299-8624

Pojawia się w:

Advances in Science and Technology. Research Journal

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 29.

Tytuł:

Design and analysis of a graphene-based Tera-Hertz antenna with lower complexities

Autorzy:

Islam, Md. Mashrur
Ahmed, Saleh
Mahmud, Nadim

Powiązania:

https://bibliotekanauki.pl/articles/1075613.pdf

Data publikacji:

2019

Wydawca:

Przedsiębiorstwo Wydawnictw Naukowych Darwin / Scientific Publishing House DARWIN

Tematy:

Graphene
PEC
THz
brain imaging

Opis:

A graphene based rectangular patch antenna is designed at .979 THz with a return loss of -20 & VSWR of 2.1. A comparison of patch between graphene & its counterparts is investigated & found the superiority of graphene over PEC & Copper. This type of patch antenna can be used for future THz brain imaging.

Źródło:

World Scientific News; 2019, 125; 18-31
2392-2192

Pojawia się w:

World Scientific News

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 30.

Tytuł:

Chitosan-based nanocomposites modified with reduced graphene oxide prepared via green synthesis

Autorzy:

Kosowska, K.
Domalik-Pyzik, P.
Jagiełło, J.
Lipińska, L.
Chłopek, J.

Powiązania:

https://bibliotekanauki.pl/articles/284680.pdf

Data publikacji:

2017

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

nanocomposites
graphene oxide
green synthesis

Źródło:

Engineering of Biomaterials; 2017, 20, no. 143 spec. iss.; 59
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 31.

Tytuł:

Composite coatings with nickel matrix and graphene as dispersed phase

Autorzy:

Gajewska-Midziałek, A.

Powiązania:

https://bibliotekanauki.pl/articles/778669.pdf

Data publikacji:

2018

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

nickel
graphene
electrodeposition
composite coatings

Opis:

The paper presents the results of the studies of nickel-graphene composite coatings deposited by the electrochemical reduction method. A bath with low concentration of nickel ions, graphene as dispersed particles and organic compounds were used for deposition of the composite coatings nickel-graphene. The results of investigations of coatings deposited from the electrolyte containing 0.33, 0.5 and 1 g/dm³  graphene and two surface-active compounds were shown. The particles content in the coatings, the surface morphology, the cross-sectional structures of the coated samples, thickness and internal stresses were measured. Voltammetric method was used for examination of the corrosion resistance of samples of composite coatings in 0.5 M NaCl solution. The obtained results suggest that the content of incorporated graphene particles increases with an increasing amount of graphene in plating bath. The applications of organic addition agents was advantageous because it caused compressive stresses in the coatings. All of the nickel-graphene composite coatings had better corrosion resistance than the nickel coatings.

Źródło:

Polish Journal of Chemical Technology; 2018, 20, 1; 54-59
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 32.

Tytuł:

Compression after impact testing ofcarbon-epoxy resin composites samples with graphene
Badania wytrzymałości resztkowej po uderzeniu węglowo-epoksydowych próbek kompozytowych z grafenem

Autorzy:

Wiśniewski, A.
Sałacińska, A.

Powiązania:

https://bibliotekanauki.pl/articles/213342.pdf

Data publikacji:

2016

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Lotnictwa

Tematy:

composite
graphene
composite with graphene
CAI test
kompozyt
grafen
kompozyt z grafenem

Opis:

The article presents compression after impact test of composite samples with graphene. In the presented research, graphene (in the form of a planes of (dimensions) 90x 100 mm on adhesive film as a media agent were applied. Fabricated composite structures made of unidirectional prepreg MTM46/HTS(12K)-150-35%RW with dimensions of 150*100 mm with adhesive films and composite panels with graphene on adhesive films were presented. For samples with and without grapheme, the results of a Compression After Impact (CAI) test with compression speed of 0.005 mm/s were shown. The relationship of force versus displacement for samples with an adhesive film and graphene on an adhesive film were investigated. Studies on residual compressive strength show large differences in compressive strength for samples with graphene and without graphene. It was determined that the obtained differences are due to various locations of destruction. The destruction of the sample was not concentrated at the place of impact, but in the place where the border of the adhesive film flashed. It was found that at the upper edge of the sample partial propagation of destruction caused by the impactor occurred.
W artykule przedstawiono badania wytrzymałości resztkowej kompozytów węglowo-epoksydowych z grafenem. W pracy zastosowano płaszczyzny grafenu o wymiarach 90x 100 mm na kleju błonkowym jako na nośniku. Przedstawiono opracowane konstrukcje wykonanych płyt kompozytowych z użyciem preimpregnatu jednokierunkowego MTM46/HTS(12K)-150-35%RW o wymiarach 150x100 mm z klejem błonkowym i płyt kompozytowych z grafenem na nośniku z kleju błonkowego. Dla próbek z grafenem i bez grafenu pokazano wyniki badań statycznych wytrzymałości resztkowej próbek po uderzeniu CAI (Compression After Impact) o prędkości ściskania próbki 0,005 mm/s. Przedstawiono wykresy zależności siły od przemieszczenia dla próbek z klejem błonkowym i z grafenem na nośniku z kleju błonkowego. Badania resztkowej wytrzymałości na ściskanie wykazały duże rozbieżności wytrzymałości na ściskanie dla próbek z grafenem i bez grafenu. Określono, że otrzymane rozbieżności wynikają z miejsca zniszczenia próbek, a zniszczenie koncentrowało się nie w miejscu uderzenia próbki, ale w miejscu, gdzie przebiegała granica kleju błonkowego. Stwierdzono, że przy górnej krawędzi próbki wystąpiła częściowa propagacja zniszczenia powstałego po uderzeniu bijaka.

Źródło:

Prace Instytutu Lotnictwa; 2016, 4 (245); 280-286
0509-6669
2300-5408

Pojawia się w:

Prace Instytutu Lotnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 33.

Tytuł:

Antybakteryjne właściwości grafenu i jego pochodnych
Antibacterial properties of graphene and its derivatives

Autorzy:

Romiszewska, Anna
Bombalska, Aneta

Powiązania:

https://bibliotekanauki.pl/articles/208449.pdf

Data publikacji:

2019

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

biomedycyna
grafen
efekt antybakteryjny
tlenek grafenu
biofilm
biomedicine
graphene
graphene oxide
antibacterial effect

Opis:

Praca prezentuje przegląd literatury w zakresie zastosowania grafenu i jego pochodnych do potencjalnej ochrony przed mikroflorą bakteryjną. Poruszono zagadnienia związane z próbą wyjaśnienia mechanizmów oddziaływania grafenu i jego pochodnych: tlenku grafenu (GO) oraz zredukowanego tlenku grafenu (rGO) na komórki bakteryjne. Porównano działanie poszczególnych form węgla na komórki Gram(+) i Gram(-), uwzględniając stężenie preparatów, rodzaj pożywki hodowlanej, a także podłoże, na którym osadzono grafen. Omówiono zagadnienia związane z powstawaniem wolnych form tlenowych (ROS), efekt ostrej krawędzi, tworzenie biofilmu oraz potencjalne zastosowania grafenu jako powłoki antybakteryjnej.
The work presents a literature review on the use of graphene and its derivatives as the potential protection against bacterial microflora. Addressed issues relate to an attempt to explain the mechanisms of impact of graphene and its derivatives: graphene oxide (GO) and reduced graphene oxide (rGO) on the bacterial cells. Interaction of graphene materials (G, GO, rGO) with Gram(+) and Gram(-) were compared with regard to the concentration of the preparations, the nature of the culture medium and surface of graphene deposition. Issues related to the development of reactive oxygen species (ROS) were discussed, the effect of sharp edges of GM’s (nano-knife), biofilm formation and the potential application of graphene in nanomedicine.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2019, 68, 4; 69-84
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 34.

Tytuł:

Investigation on Mechanical Properties and Microstructures of Aluminum Hybrid Composites Reinforced with Al2O3/GNPs Binary Particles

Autorzy:

Şenel, M. Can
Gürbüz, M.

Powiązania:

https://bibliotekanauki.pl/articles/2049630.pdf

Data publikacji:

2021

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

composite
aluminum
graphene
alumina
hybrid

Opis:

Nowadays, aluminum-based composites have been produced by pure alumina (Al2O3) or pure graphene nanoplatelets (GNPs) in aluminum matrix because of the high compressive strength of alumina and the solid lubricant properties of graphene. However, there are no studies on the influence of both alumina and graphene reinforced aluminum composites. In this study, Al-Al2O3 and Al-Al2O3-GNPs composites were reinforced with pure alumina (between 0 and 30 wt.%), pure graphene (0, 0.1, 0.3, 0.5 wt.%), and their hybrid forms (Al2O3-GNPs) by the powder metallurgy method. This method involved ultrasonic dispensing, mixing, filtering, drying, pressing, and sintering processes. From the test results, the micro Vickers hardness of pure aluminum (28.2±1 HV) improved to 51.5±0.8 HV (Al-30Al2O3) and 63.1±1 HV (Al-30Al2O3-0.1GNPs). Similarly, the ultimate compressive strength (UCS) enhanced from 92.4±4 MPa (pure aluminum) to 165±4.5 MPa (Al-30Al2O3) and 188±5 MPa (Al-30Al2O3-0.1GNPs), respectively. In conclusion, the Vickers hardness and ultimate compressive strength of aluminum hybrid composites improved up to 0.1 wt.% graphene content. After 0.1 wt.% graphene content, these mechanical properties decreased because of the clumping of graphene nanoparticles.

Źródło:

Archives of Metallurgy and Materials; 2021, 66, 1; 97-106
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 35.

Tytuł:

Charakteryzacja struktur grafenowych na podłożach stałych metodami spektroskopowymi

Autorzy:

Szybowicz, M.
Dychalska, A.

Powiązania:

https://bibliotekanauki.pl/articles/274088.pdf

Data publikacji:

2016

Wydawca:

Roble

Tematy:

grafen
spektroskopia Ramana
graphene
Raman spectroscopy

Opis:

W pracy przedstawiono wykorzystanie spektroskopii ramanowskiej (mikroskopii ramanowskiej) jako użytecznego narzędzia badawczo-diagnostycznego wykorzystywanego do oceny jakości warstw grafenowych osadzanych na różnego rodzaju podłożach takich jak: SiC, SiO2, szkło, miedź oraz PET. Spektroskopia Ramana jest podstawową metodą eksperymentalną wykorzystywaną do oceny jakości grafenu, jego ciągłości, czy też zdefektowania. W prezentowanej pracy opisano wykorzystanie zmodyfikowanej techniki pomiarów ramanowskich z użyciem pomiarów konfokalnych. Zmodyfikowana technika pozwala na precyzyjny pomiar i uzyskanie dobrej jakości widma ramanowskiego (wysoki stosunek sygnału do szumu) pozwalającego na dokładne i jednoznaczne określenie jaką ilość warstw grafenowych posiada analizowana struktura. Dodatkowo przedstawiono technikę mapowania ramanowskiego wykorzystaną w celu charakteryzacji powierzchni grafenu. Tego typu metoda badawcza pozwala na analizę powierzchni struktury grafenowej w celu zbadania jej jednorodności, określenie potencjalnych defektów, badanie lokalnych zmian związanych z przekrywaniem się struktur mono lub dwuwarstwowych, czy też analizę naprężeń powstających w wyniku oddziaływania grafenu z podłożem, czy też, jak w przypadku elastycznego podłoża PET jego odkształceniom mechanicznym. Zobrazowano również zmiany parametrów warstw grafenowych pod wpływem temperatury w zależności od rodzaju zastosowanego podłoża, na którym osadzono grafen. Badania zostały przeprowadzone na komercyjnych strukturach grafenowych o deklarowanych przez producenta grafenu parametrach określających je jako monowarstwy.

Źródło:

LAB Laboratoria, Aparatura, Badania; 2016, 21, 4; 20-27
1427-5619

Pojawia się w:

LAB Laboratoria, Aparatura, Badania

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 36.

Tytuł:

Morphology and the physical and thermal properties of thermoplastic polyurethane reinforced with thermally reduced graphene oxide

Autorzy:

Strankowski, M.
Piszczyk, Ł.
Kosmela, P.
Korzeniewski, P.

Powiązania:

https://bibliotekanauki.pl/articles/779423.pdf

Data publikacji:

2015

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

nanocomposites
graphene
polyurethane
carbon nanofillers
TRG

Opis:

In this study, thermally reduced graphene oxide (TRG)-containing polyurethane nanocomposites were obtained by the extrusion method. The content of TRG incorporated into polyurethane elastomer systems equaled 0.5, 1.0, 2.0 and 3.0 wt%. The morphology, static and dynamic mechanical properties, and thermal stability of the modified materials were investigated. The application of TRG resulted in a visible increase in material stiffness as confirmed by the measurements of complex compression modulus (E′) and glass transition temperature (Tg). The Tg increased with increasing content of nanofiller in the thermoplastic system. The addition of thermally reduced graphene oxide had a slight effect on thermal stability of the obtained materials. The incorporation of 0.5, 1.0, 2.0 and 3.0 wt% of TRG into a system resulted in increased char residues compared to unmodified PU elastomer. Also, this study demonstrated that after exceeding a specific amount of TRG, the physicomechanical properties of modified materials start to deteriorate.

Źródło:

Polish Journal of Chemical Technology; 2015, 17, 4; 88-94
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 37.

Tytuł:

Metody syntez i badania właściwości grafenu
Methods of synthesis and testing properties of graphene

Autorzy:

Jonik, J.
Purchała, M.
Grajek, H.

Powiązania:

https://bibliotekanauki.pl/articles/270836.pdf

Data publikacji:

2016

Wydawca:

Centralny Ośrodek Badawczo-Rozwojowy Aparatury Badawczej i Dydaktycznej, COBRABiD

Tematy:

tlenek grafitu
tlenek grafenu
zredukowany tlenek grafenu
graphite oxide
graphene oxide
reduced graphene oxide

Opis:

Grafen i jego pochodne są materiałami o unikalnych właściwościach biochemicznych, elektrycznych, optycznych i mechanicznych, co wzbudza zainteresowanie w wielu ośrodkach badawczych. Z tego powodu, na podstawie dostępnej literatury, podjęliśmy próbę zestawienia i interpretacji wyników badań uprzednio wymienionych materiałów otrzymanych różnymi metodami. Analizując wyniki badań różnych materiałów grafenopodobnych, można przypuszczać, że najbardziej ekonomiczną metodą otrzymywania grafenu jest zmodyfikowana metoda Hummersa. Najlepszymi technikami pomiarowymi są spektroskopia Ramana i rentgenowska spektroskopia fotoelektronów. Obydwie techniki umożliwiają ocenę składu chemicznego badanych próbek oraz stopnia ich zdefektowania. W pracy przedstawiono również niektóre z licznych zastosowań tych materiałów oraz wnioski.
Graphene and its derivatives are the materials with unique biochemical, electric, optical and mechanical properties, which has aroused interest in many research centres. Therefore, on the basis of the accessible literature, we attempt to collate and interpret the results of the aforesaid materials obtained by different methods. Analysing the results for the different graphene-like materials one can suppose, that the most economical method of the graphene synthesis is the modified Hummers’ method. The most useful testing techniques are the Raman spectroscopy and the X-ray photoelectron spectroscopy. Both techniques enable the estimation of the chemical composition and the presence of defect structure in the materials. Some of the many applications of the materials and conclusions are also presented in our review.

Źródło:

Aparatura Badawcza i Dydaktyczna; 2016, 21, 2; 110-117
2392-1765

Pojawia się w:

Aparatura Badawcza i Dydaktyczna

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 38.

Tytuł:

Badania właściwości tribologicznych oleju zawierającego tlenek grafenu lub heksagonalny azotek boru
Research on tribological properties of oil containing graphene oxide or hexagonal boron nitride

Autorzy:

Nogas, Patrycja Magdalena
Gocman, Krzysztof
Kałdoński, Tadeusz

Powiązania:

https://bibliotekanauki.pl/articles/209546.pdf

Data publikacji:

2019

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

grafen
heksagonalny azotek boru
tlenek grafenu
baza olejowa
graphene
hexagonal boron nitride
graphene oxide
oil base

Opis:

Celem tej publikacji jest przedstawienie wyników badań bazy olejowej SN-650 z różnymi stężeniami tlenku grafenu (GO), zredukowanego tlenku grafenu (rGO) wyprodukowanych przez Instytut Technologii Materiałów Elektronicznych w Warszawie oraz heksagonalnego azotku boru (h-BN) wytwarzanego według technologii opracowanej w Wojskowej Akademii Technicznej. W pierwszej części pracy przedstawiono podstawowe wiadomości na temat grafenu i tlenku grafenu oraz możliwości ich zastosowania, w szczególności w dziedzinie tribologii. W drugiej części publikacji zaprezentowano wyniki badań właściwości smarnościowych próbek z dodatkiem 0,05%, 0,1%, 0,5%, 1% i 2% masy tlenku grafenu, zredukowanego tlenku grafenu oraz heksagonalnego azotku boru. Pomiary zrealizowano przy wykorzystaniu uniwersalnego nanomikrotestera UNMT oraz aparatu czterokulowego T-02, w Zakładzie Tribologii, Inżynierii Powierzchni i Logistyki Płynów Eksploatacyjnych (od 1.10.2019 r. Zakład Materiałów Pędnych i Smarów) Wydziału Mechanicznego (od 1.10.2019 r. Wydział Inżynierii Mechanicznej) Wojskowej Akademii Technicznej. Otrzymane wyniki wykazały korzystny wpływ wprowadzania do bazy olejowej SN-650 dodatków w postaci tlenku grafenu lub heksagonalnego azotku boru na właściwości tribologiczne oleju.
The aim of this publication is to present the results of studies on the SN-650 oil base with various concentrations of graphene oxide (GO), reduced graphene oxide (rGO) produced by the Institute of Electronic Materials Technology in Warsaw and hexagonal boron nitride (h-BN) produced according to the technology developed at the Military University of Technology. The first part of the publication presents basic information about graphene oxide and the possibilities of its use, in particular in the field of tribology. The second part of the publication presents the results of tests of lubricity properties of the samples with the addition of 0.05%, 0.1%, 0.5%, 1% and 2% of graphene oxide, reduced graphene oxide or hexagonal boron nitride. The measurements were carried out using the UNMT universal nano/microtester tester and the T-02 four-ball device, at the Department of Tribology, Surface Engineering and Logistics of Service Fluids, which is a part of the Institute of Mechanical Vehicles and Transport of the Mechanical Faculty of the Military University of Technology. The obtained results have demonstrated the beneficial effect of introducing additions in the form of graphene oxide or hexagonal boron nitride onto the tribological properties of the oil base.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2019, 68, 4; 29-55
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 39.

Tytuł:

Scanning electron microscope at low voltage operation – a unique characterization tool for graphene layers
Skaningowy mikroskop elektronowy pracujący w zakresie niskich wartości napięcia przyspieszającego jako unikatowe narzędzie do charakteryzacji warstw grafenu

Autorzy:

Jóźwik, I.

Powiązania:

https://bibliotekanauki.pl/articles/192086.pdf

Data publikacji:

2016

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Technologii Materiałów Elektronicznych

Tematy:

graphene
graphene characterization
low-kV scanning electron microscopy
grafen
charakteryzacja grafenu
niskoenergetyczna skaningowa mikroskopia elektronowa

Opis:

Graphene grown on Cu foils by chemical vapor deposition (CVD) technique has been investigated using commercially available scanning electron microscope at low voltage operation. The optimized conditions of SEM imaging carried out in a double-channel mode (registering secondary electrons type 1 (SE1) and backscattered electrons (BSE) images in a single scan) allowed for the visualization of typical features of graphene on Cu, such as folds, cracks and add-layers. The mechanism of thickness contrast observed in the BSE images was described in terms of low loss-BSE detection. Antioxidant qualities of graphene sheets on metallic substrate were confirmed by the ability of observation of the channeling contrast in Cu substrates at primary electrons energy of 0.5 keV.
Próbki grafenu otrzymywanego metodą chemicznego osadzania z fazy gazowej na podłożach Cu poddano badaniom przy użyciu komercyjnego skaningowego mikroskopu elektronowego (SEM) pracującego w zakresie niskich wartości napięcia przyspieszającego. Optymalizacja warunków obrazowania SEM prowadzona w trybie dwukanałowym (rejestracja obrazów SE1 i BSE podczas tego samego skanu) pozwoliła na wizualizację typowych cech grafenu na Cu takich jak fałdy, pęknięcia i dodatkowe warstwy. Mechanizm kontrastu związanego ze zmianami liczby warstw grafenu obserwowanego w obrazach BSE został przedstawiony w oparciu o detekcję elektronów BSE o niskich stratach energii. Przeciwutleniające właściwości grafenu na metalicznych podłożach zostały potwierdzone poprzez możliwość obserwacji kontrastu kanałowania elektronów w podłożach Cu przy energii elektronów pierwotnych rzędu 0,5 keV.

Źródło:

Materiały Elektroniczne; 2016, T. 44, nr 2, 2; 11-16
0209-0058

Pojawia się w:

Materiały Elektroniczne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 40.

Tytuł:

Właściwości tribologiczne smarów plastycznych zawierających tlenek grafenu lub heksagonalny azotek boru
Tribological properties of grease containing graphene oxide or hexagonal boron nitride

Autorzy:

Dąbrowski, Igor Jakub
Gocman, Krzysztof
Kałdoński, Tadeusz

Powiązania:

https://bibliotekanauki.pl/articles/210233.pdf

Data publikacji:

2019

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

grafen
smar plastyczny
tlenek grafenu
heksagonalny azotek boru
graphene
grease
graphene oxide
hexagonal boron nitride

Opis:

Celem publikacji jest przedstawienie wyników badań bazy smaru plastycznego o klasie konsystencji 2 według klasyfikacji NLGI uszlachetnionej różnymi stężeniami tlenku grafenu GO, wyprodukowanego przez Instytut Technologii Materiałów Elektronicznych w Warszawie, lub heksagonalnego azotku boru h-BN, wytworzonego w Wojskowej Akademii Technicznej. W pierwszej części publikacji przedstawiono podstawowe wiadomości na temat grafenu oraz jego zastosowań, w szczególności w zakresie tribologii. W drugiej części artykułu zaprezentowano wyniki badań właściwości tribologicznych próbek uszlachetnionych tlenkiem grafenu lub heksagonalnym azotkiem boru w ilościach: 0,05%, 0,1%, 0,5%, 1% i 2% masy. Ponadto oceniono właściwości tribologiczne tzw. „pasty grafenowej”, wykonanej z płatkowego tlenku grafenu rozpuszczonego w wodzie. Pomiary zrealizowano przy wykorzystaniu aparatu czterokulowego T-02 i uniwersalnego mikronanotestera UNMT w Zakładzie Tribologii, Inżynierii Powierzchni i Logistyki Płynów Eksploatacyjnych Wydziału Mechanicznego Wojskowej Akademii Technicznej. Otrzymane wyniki wykazały korzystny wpływ wprowadzania do bazowego smaru plastycznego dodatków w postaci tlenku grafenu lub heksagonalnego azotku boru na jego właściwości tribologiczne. Tzw. „wodna pasta” z tlenku grafenu GO okazała się tak samo skuteczna jak smar plastyczny zawierający znaczną koncentrację GO (1% lub 2% m/m).
The purpose of this paper is to present the results of research of tribological behavior of basic greases (of 2. NLGI class) including different mass concentration concentration (0.05%, 0.1%, 0.2%, 0.5%, 1%, 2%) of additives: graphene oxide (produced by the Institute of Electronic Materials Technology, Warsaw) and hexagonal boron nitride (produced by the Military University of Technology, Warsaw). In the first part of this publication there is elementary information about graphene and its applications, especially in tribological field. The next part of the paper contains the results of research on the mentioned above samples, which were investigated with four-ball apparatus T-02 and Universal Micro/Nano Tester UNMT (CETR, CA, USA), at the Department of Tribology and Service Fluids Logistics at the Faculty of Mechanical Engineering, Military University of Technology. The results proved a positive effect of adding graphene oxide or hexagonal boron nitride to basic grease on its tribological properties. In case of “water dispersion of graphene oxide”, its tribological properties were similar to the samples including significant concentration of GO.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2019, 68, 3; 65-93
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 41.

Tytuł:

Tlenek grafenu jako pasywny modulator dobroci w laserze na ceramice Nd:YAG
Graphene oxide as passively Q - switched modulator for ceramic Nd:YAG laser

Autorzy:

Podniesiński, D.
Librant, K.
Kozłowska, A.
Nakielska, M.
Lipińska, L.

Powiązania:

https://bibliotekanauki.pl/articles/192371.pdf

Data publikacji:

2013

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Technologii Materiałów Elektronicznych

Tematy:

grafen
tlenek grafenu
laser na ciele stałym
nasycalny absorber
graphene
graphene oxide
solid state laser
saturable absorber

Opis:

W artykule przedstawione zostały wyniki eksperymentów generacyjnych, w układzie lasera na ceramice Nd:YAG z pasywnym modulatorem dobroci zbudowanym na bazie tlenku grafenu. Opisano sposób przygotowania próbek tlenku grafenu na podłożu płytek szkła SiO₂, zbudowane stanowisko lasera oraz sposób przeprowadzenia pomiarów. Badany tlenek grafenu, wytworzony w Instytucie Technologii Materiałów Elektronicznych, wykazał właściwości nasycalnego absorbera. Zastosowanie tlenku grafenu o transmitancji w zakresie 80 ÷ 86 % pozwoliło uzyskać na wyjściu lasera generację impulsową o częstotliwości w zakresie 54 ÷ 250 kHz. Zarejestrowana maksymalna średnia moc wyjściowa lasera wynosiła P_śr = 330 mW.
This paper presents the results of generation experiments in the setup of a ceramic Nd: YAG laser with grapheme oxide as a passive Q - switched modulator. The preparation method of graphene oxide samples on the surface of SiO₂ glass, the arrangement of the laser setup and the measurement method are also described. The studied graphene oxide produced at the Institute of Electronic Materials Technology showed the properties of a saturable absorber. The application of grapheme oxide with transmittance in the range of (80 - 86) % allowed the pulse laser operation in the frequency range of (54 - 250) kHz. The maximum recorded average output power of the laser was P_av = 330 mW.

Źródło:

Materiały Elektroniczne; 2013, T. 41, nr 3, 3; 19-26
0209-0058

Pojawia się w:

Materiały Elektroniczne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 42.

Tytuł:

Impact testing of carbon fiber-epoxy resin composite with graphene
Testy uderzeniowe kompozytów węglowo-epoksydowych z grafenem

Autorzy:

Wiśniewski, A.
Sałacińska, A.
Wilk, J.

Powiązania:

https://bibliotekanauki.pl/articles/212850.pdf

Data publikacji:

2016

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Lotnictwa

Tematy:

composite
graphene
composite with graphene
drop tower impact test
kompozyt
grafen
kompozyty z grafenem
drop tower test

Opis:

The article presents the state of knowledge in the field of dynamic tests with the use of Drop Tower devices of the impact energy of a spherical pivot 18 J. Developed structures of composite samples were presented, with dimensions of 150x100 mm, consist of unidirectional prepreg MTM46/HTS (12K)-150-35% RW and adhesive film with and without addition of graphene plane. The impact strength of these composites panels were investigated according to ASTM D7136/7136M-15 method. Relationship between impact force versus time during impact test was presented. Relationship between deformation and impact energy in the time of the test was also consulted. The type and degree of samples destruction were observed by the microscope. The effect of graphene addition on the properties of carbon fiber-epoxy resin composites were determined.
W artykule przedstawiono stan wiedzy w zakresie badań dynamicznych z zastosowaniem urządzenia Drop Tower o energii uderzenia trzpienia kulistego 18 J. Przedstawiono opracowane konstrukcje wykonanych płyt kompozytowych z użyciem preimpregnatu jednokierunkowego MTM46/HTS(12K)-150-35% RW o wymiarach 150x100 mm z klejem błonkowym i płyt kompozytowych z grafenem na nośniku z kleju błonkowego. Wykonano badania wytrzymałości tych płyt na uderzenie według normy ASTM D7136/7136M-15. Przedstawiono wykresy zależności siły od czasu podczas uderzenia próbek oraz zależności głębokości deformacji i energii uderzenia od czasu w próbie uderzenia. Oceniono sposób i stopień zniszczenia próbek z zastosowaniem mikroskopu. Określono wpływ grafenu na właściwości kompozytu węglowo-epoksydowego.

Źródło:

Prace Instytutu Lotnictwa; 2016, 4 (245); 271-279
0509-6669
2300-5408

Pojawia się w:

Prace Instytutu Lotnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 43.

Tytuł:

Grafen otrzymywany metodą elektrolityczną na podłożach z węglika krzemu
Graphene obtained by electrolytic method on silicon carbide substrates

Autorzy:

Stańczyk, B.
Dobrzański, L.
Jagoda, A.
Możdżonek, M.
Natarajan, S.

Powiązania:

https://bibliotekanauki.pl/articles/192048.pdf

Data publikacji:

2014

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Technologii Materiałów Elektronicznych

Tematy:

grafen
metoda elektrolityczna
graphene
electrochemical metod

Opis:

W artykule przedstawiono nową technikę osadzania warstw grafenu na podłożach z węglika krzemu metodą elektrolityczną. Polega ona na zastosowaniu jako materiału elektrod grafitu i SiC oraz elektrolitu organicznego poli–styrenosulfonianu sodu (PSS). Widma Ramana osadzanych warstw wskazują na to, że otrzymano grafen. Istnienie wiązań typu C=C potwierdza spektroskopia FTIR. Prowadzono także proces z roztworów na bazie tlenku grafenu. Ponadto w procesie z rozcieńczonym elektrolitem uzyskano rzadką odmianę alotropową węglika krzemu - moissanit, który syntetycznie jest produkowany przede wszystkim na potrzeby przemysłu elektronicznego.
We present a new electrochemical deposition method of graphene layers on silicon carbide substrates. The technological arrangement was comprised of graphite, SiC electrodes and organic electrolyte, i.e. poly(sodium-4-styrenesulphonate), and in the case of an alternative technique suspension with graphene oxide was applied. Graphene layers consisting of flakes were obtained on SiC electrodes, which was concluded based on a Raman Spectroscopy analysis. Moreover, during the process with diluted electrolyte solution we achieved a rare allotropic form of silicon carbide called moissanit, which is commonly used in electronic applications.

Źródło:

Materiały Elektroniczne; 2014, T. 42, nr 3, 3; 20-25
0209-0058

Pojawia się w:

Materiały Elektroniczne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 44.

Tytuł:

Spektroskopia ramanowska grafenu
Raman spectroscopy of graphene

Autorzy:

Grodecki, K.

Powiązania:

https://bibliotekanauki.pl/articles/192289.pdf

Data publikacji:

2013

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Technologii Materiałów Elektronicznych

Tematy:

grafen
spektroskopia ramanowska
graphene
Raman spectroscopy

Opis:

Grafen jest obecnie materiałem niezwykle popularnym zarówno w środowisku naukowym, jak i w mediach. Jego unikatowe właściwości pozwalają myśleć o nim jako o następcy krzemu w elektronice. Polska ma swój wkład w badaniach tego materiału, między innymi poprzez opracowanie nowatorskiej techniki wzrostu grafenu na SiC- polegającej na osadzaniu warstw węglowych z propanu. Spektroskopia ramanowska jest uznaną i nieniszczącą techniką badań struktur węglowych, w tym grafenu. W sierpniu 2012 r. w ITME został zakupiony spektrometr ramanowski optymalizowany do badań grafenu. W artykule zostaną przedstawione podstawy spektroskopii ramanowskiej i omówione pokrótce podstawowe techniki wytwarzania grafenu. Główny nacisk został położony na przedstawienie możliwości badawczych przy użyciu spektroskopii ramanowskiej.
Graphene is a material that has recently become very popular with both the representatives of the scientific world and the media. The unique properties of graphene make it a successor to silicon in a new generation of electronics. Poland has contributed to the study of this material, among others by developing an innovative technique of graphene growth on SiC layers by chemical vapor deposition. Raman spectroscopy is a fast and non-destructive technique to analyze and characterize graphene. In August 2012 a new Raman spectrometer dedicated to the study of graphene was bought. In this article the basics of Raman spectroscopy and the graphene production technique are presented. However, the main goal is to show the capabilities and basic techniques of Raman spectroscopy in relation to graphene characterization and analysis.

Źródło:

Materiały Elektroniczne; 2013, T. 41, nr 1, 1; 47-53
0209-0058

Pojawia się w:

Materiały Elektroniczne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 45.

Tytuł:

Equilibrium and kinetics studies for the adsorption of Ni2+ and Fe3+ ions from aqueous solution by graphene oxide

Autorzy:

Konicki, W.
Aleksandrzak, M.
Mijowska, E.

Powiązania:

https://bibliotekanauki.pl/articles/778711.pdf

Data publikacji:

2017

Wydawca:

Zachodniopomorski Uniwersytet Technologiczny w Szczecinie. Wydawnictwo Uczelniane ZUT w Szczecinie

Tematy:

nickel
iron
graphene oxide
adsorption
kinetics

Opis:

In this study, the adsorption of Ni²⁺  and Fe³⁺  metal ions from aqueous solutions onto graphene oxide (GO) have been explored. The effects of various experimental factors such as pH of the solution, initial metal ion concentration and temperature were evaluated. The kinetic, equilibrium and thermodynamic studies were also investigated. The adsorption rate data were analyzed using the pseudo-first-order kinetic model, the pseudo-second-order kinetic model and the intraparticle diffusion model. Kinetic studies indicate that the adsorption of both ions follows the pseudo-second-order kinetics. The isotherms of adsorption data were analyzed by adsorption isotherm models such as Langmuir and Freundlich. Equilibrium data fitted well with the Langmuir model. The maximum adsorption capacities of Ni²⁺  and Fe³⁺  onto GO were 35.6 and 27.3 mg g^-1 , respectively. In addition, various thermodynamic parameters, such as enthalpy (ΔHO), entropy (ΔSO) and Gibbs free energy (ΔGO), were calculated.

Źródło:

Polish Journal of Chemical Technology; 2017, 19, 3; 120-129
1509-8117
1899-4741

Pojawia się w:

Polish Journal of Chemical Technology

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 46.

Tytuł:

Obtaining and Application of New Cellulose- and Graphene Oxide-Based Adsorbents for Treatment of Industrial Waste Containing Heavy Metals

Autorzy:

Fryczkowska, B.
Wyszomirski, M.
Puzoń, M.

Powiązania:

https://bibliotekanauki.pl/articles/125232.pdf

Data publikacji:

2017

Wydawca:

Polskie Towarzystwo Inżynierii Ekologicznej

Tematy:

cellulose
graphene oxide
sorption
galvanizing wastewater

Opis:

The paper presents the results of studies on the preparation and properties of composite granules produced by phase inversion from cellulose (CEL) solutions in 1-ethyl-3-methylimidazole acetate (EMIMAc), containing nano-addition in the form of graphene oxide (GO) in N,N-dimethylformamide (DMF). Water absorption and sorption of such compounds as FeCl₃, methylene blue (MB) and bovine serum albumin (BSA) were studied. In addition, attempts were made to investigate the sorption properties of the obtained cellulose granules in terms of metals removal from galvanizing wastewater. Among the many components, iron and lead were found to have the highest concentration (~ 1 mg Fe/dm³; ~2 mg Pb/dm³) in the tested wastewater sample. The qualitative and quantitative composition of the wastewater was examined by UV-Vis spectrophotometry. The studies show that doping of cellulose with Graphene oxide clearly affects the physical properties of this biopolymer. GO improves the water absorption of CEL/GO composite cellulose granules only in the concentration above 0.05% w/w. For a concentration of 0.1% w/w of GO in cellulose, water absorption is increased by ~108% compared to pure cellulose granules. In addition, the use of dry and wet granules in the study changes their sorption properties with respect to all tested substances. Studies on test solutions have shown that the sorption of cellulose granules decreases with increasing molar mass of test compounds, in the following order: FeCl₃, methylene blue (MB) and bovine albumin (BSA). This means that the cellulose granules obtained in the experiment are made up of small micropores, which makes the diffusion of compounds of high molecular weight difficult. The best sorption results were obtained for ferric ions and amounted to 66–72% for FeCl₃ solution, and ~92% for the wastewater that was sorbed on pure cellulose granules.

Źródło:

Journal of Ecological Engineering; 2017, 18, 6; 43-52
2299-8993

Pojawia się w:

Journal of Ecological Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 47.

Tytuł:

Investigating Sintering Behavior of the Graphene Nanoplatelets (GNPs) Reinforced Aluminum Nanocomposites Via Low Energy Solution Ball Milling

Autorzy:

Baig, Zeeshan
Mamat, Othman
Mustapha, Mazli
Ali, Sadaqat

Powiązania:

https://bibliotekanauki.pl/articles/355724.pdf

Data publikacji:

2020

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

graphene
aluminum
milling
dispersion
hardness
wear

Opis:

Owing to the excellent properties, graphene nanoplatelets (GNPs) show great reinforcing ability to improve the mechanical and tribological properties of Al nanocomposites for many automotive applications. In this work, the GNPs dispersion and reinforcing effect in Al nanocomposite was tested. Solvent dispersion via tip sonication and facile low energy ball milling (tumbling milling) using two milling speeds 200 and 300 rpm were employed to develop GNPs/Al powders. Sintering response of the GNPs/Al sintered samples wasgauged at two temperatures (550°C and 620°C). The effects of GNPs content, milling rotation speed and sintering temperature on the density, hardness and wear properties of the nanocomposite were examined. The results indicate that relative density % decreases with increasing GNPs content due to possible reagglomeration. The highest hardness of 35.6% and wear rate of 76.68% is achieved in 0.3 wt.% GNPs/Al nanocomposite processed at 300 rpm and 620°C as compared to pure Al due to uniform dispersion, higher diffusion rate at a higher temperature and effective lubrication effect.

Źródło:

Archives of Metallurgy and Materials; 2020, 65, 2; 755-759
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 48.

Tytuł:

Predictive modeling and machining performance optimization during drilling of polymer nanocomposites reinforced by graphene oxide/carbon fiber

Autorzy:

Kumar, Jogendra
Verma, Rajesh Kumar
Mondal, Arpan Kumar

Powiązania:

https://bibliotekanauki.pl/articles/139771.pdf

Data publikacji:

2020

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

surface roughness
RSM
thrust force
optimization
graphene

Opis:

This paper explores the parametric appraisal and machining performance optimization during drilling of polymer nanocomposites reinforced by graphene oxide/-carbon fiber. The consequences of drilling parameters like cutting velocity, feed, and weight % of graphene oxide on machining responses, namely surface roughness, thrust force, torque, delamination (In/Out) has been investigated. An integrated approach of a Combined Quality Loss concept, Weighted Principal Component Analysis (WPCA), and Taguchi theory is proposed for the evaluation of drilling efficiency. Response surface methodology was employed for drilling of samples using the titanium aluminum nitride tool. WPCA is used for aggregation of multi-response into a single objective function. Analysis of variance reveals that cutting velocity is the most influential factor trailed by feed and weight % of graphene oxide. The proposed approach predicts the outcomes of the developed model for an optimal set of parameters. It has been validated by a confirmatory test, which shows a satisfactory agreement with the actual data. The lower feed plays a vital role in surface finishing. At lower feed, the development of the defect and cracks are found less with an improved surface finish. The proposed module demonstrates the feasibility of controlling quality and productivity factors.

Źródło:

Archive of Mechanical Engineering; 2020, LXVII, 2; 229-258
0004-0738

Pojawia się w:

Archive of Mechanical Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 49.

Tytuł:

Recent advances in graphene application for electronic sensing
Najnowsze osiągnięcia w zastosowaniu grafenu w czujnikach elektronicznych

Autorzy:

Łuszczek, M.
Świsulski, D.

Powiązania:

https://bibliotekanauki.pl/articles/266875.pdf

Data publikacji:

2015

Wydawca:

Politechnika Gdańska. Wydział Elektrotechniki i Automatyki

Tematy:

graphene
sensors
GFET
metrology
grafen
sensor
metrologia

Opis:

The great interest in graphene is caused by its potential for constructing various sensors exhibiting excellent parameters. The high carrier mobility and the unique band structure of graphene makes it promising especially in the field-effect transistors (GFET) applications. In this article, recent advances of the selected graphene-based sensor applications were presented and the possible directions for further investigations were pointed out.
Ogromne zainteresowanie grafenem w dużej mierze związane jest z możliwością zastosowania tego materiału do budowy różnego typu sensorów charakteryzujących się doskonałymi parametrami. Bardzo duża ruchliwość nośników ładunku oraz specyficzna pasmowa struktura elektronowa grafenu sprawiają, iż wydaje się on być bardzo obiecującym materiałem, szczególnie do zastosowań w układach pomiarowych wykorzystujących czujniki o architekturze tranzystorów polowych z kanałem grafenowym (GFET). W artykule omówione zostały najnowsze osiągnięcia w dziedzinie badań nad zastosowaniem grafenu w wybranych typach czujników. Wskazano także możliwe kierunki dalszych badań, które mogłyby być realizowane w najbliższej przyszłości w Katedrze Metrologii i Systemów Informacyjnych na Wydziale Elektrotechniki i Automatyki Politechniki Gdańskiej.

Źródło:

Zeszyty Naukowe Wydziału Elektrotechniki i Automatyki Politechniki Gdańskiej; 2015, 47; 115-118
1425-5766
2353-1290

Pojawia się w:

Zeszyty Naukowe Wydziału Elektrotechniki i Automatyki Politechniki Gdańskiej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 50.

Tytuł:

Characteristics of pure Love mode SAW sensor with graphene interdigital transducer for biosensing applications

Autorzy:

Chen, Chen
Wang, Xinyu
Wang, Yuting

Powiązania:

https://bibliotekanauki.pl/articles/2233256.pdf

Data publikacji:

2022

Wydawca:

Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej

Tematy:

SAW biosensor
Love mode
graphene
mass sensitivity

Opis:

The characteristics of Love wave biosensors are systematically investigated. The results show that sensors with combination of a ZnO guiding layer and 90ST or 90AT Quartz substrates exhibit purer Love modes than those with the SiO2 guiding layer. The corresponding maxi- mum sensitivities are −10.9069 and −11.641m2/kg, respectively, which are nearly two times higher than those of SiO2 layer. The ZnO/90ST Quartz Love wave sensor exhibits the largest K2 of 0.3022 and achieves 0 ppm/oC of TCF at hZnO/λ = 0.0216. The sensor employing the Graphene IDT further improves the sensitivity by nearly one order of magnitude.

Źródło:

Journal of Theoretical and Applied Mechanics; 2022, 60, 4; 551--559
1429-2955

Pojawia się w:

Journal of Theoretical and Applied Mechanics

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce