Impact testing of carbon fiber-epoxy resin composite with graphene

The article presents the state of knowledge in the field of dynamic tests with the use of Drop Tower devices of the impact energy of a spherical pivot 18 J. Developed structures of composite samples were presented, with dimensions of 150x100 mm, consist of unidirectional prepreg MTM46/HTS (12K)-150-35% RW and adhesive film with and without addition of graphene plane. The impact strength of these composites panels were investigated according to ASTM D7136/7136M-15 method. Relationship between impact force versus time during impact test was presented. Relationship between deformation and impact energy in the time of the test was also consulted. The type and degree of samples destruction were observed by the microscope. The effect of graphene addition on the properties of carbon fiber-epoxy resin composites were determined.

W artykule przedstawiono stan wiedzy w zakresie badań dynamicznych z zastosowaniem urządzenia Drop Tower o energii uderzenia trzpienia kulistego 18 J. Przedstawiono opracowane konstrukcje wykonanych płyt kompozytowych z użyciem preimpregnatu jednokierunkowego MTM46/HTS(12K)-150-35% RW o wymiarach 150x100 mm z klejem błonkowym i płyt kompozytowych z grafenem na nośniku z kleju błonkowego. Wykonano badania wytrzymałości tych płyt na uderzenie według normy ASTM D7136/7136M-15. Przedstawiono wykresy zależności siły od czasu podczas uderzenia próbek oraz zależności głębokości deformacji i energii uderzenia od czasu w próbie uderzenia. Oceniono sposób i stopień zniszczenia próbek z zastosowaniem mikroskopu. Określono wpływ grafenu na właściwości kompozytu węglowo-epoksydowego.