Skocz do pozycji: 1.

Tytuł:

Electroplastic Effect of High Manganese Austenitic Steel

Autorzy:

Zimniak, Z.
Dobras, D.

Powiązania:

https://bibliotekanauki.pl/articles/353766.pdf

Data publikacji:

2019

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

electroplastic effect
high manganese steel
TWIP effect

Opis:

The article presents the results of the investigations performed on high manganese austenitic steel which underwent the test of uniaxial tension, with the application of electric current impulses. The application of low voltage impulse alternating current of high intensity during the plastic deformation of the examined steel caused the occurrence of the electroplastic effect, which changed the shape of the stress-strain curve. A drop of flow stress and elongation of the tested material was observed in the case of the application of electric current impulses, in respect of the material stretched without such impulses and stretched at an elevated temperature. The analysis of the morphology of the fractures showed differences between the samples tested under the particular conditions. An analysis of the alloy’s microstructure was also performed under different conditions. The application of electric current impulses can have a significant influence on the reduction of the forces in the plastic forming processes for this type of steel.

Źródło:

Archives of Metallurgy and Materials; 2019, 64, 1; 431-436
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 2.

Tytuł:

Attempts to Modify Austenitic Steel with Carbon Nanotubes

Autorzy:

Górka, Jacek
Kik, Tomasz
Burda, Michal

Powiązania:

https://bibliotekanauki.pl/articles/2048816.pdf

Data publikacji:

2022

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

multiwalled carbon nanotubes
carburizer
austenitic steel
TIG remelting
structure modification

Opis:

In this work, research on influence of multiwalled carbon nanotubes (MWCNTs), produced in Catalic Chemical Carbon Vapor Deposition, NANOCYLTM NC7000CNTs on a structure and properties of AISI 301 steel remelted by TIG arc. In the assessment of influence a type of carbon on properties and structure of austenitic steel, as a carbon filler was use also carburizer. In the specimens (AISI 301 plates) with dimensions 155×60×7 [mm] were drilled holes with 1.3 mm diameter and placed 0.5 mm under specimen surface. Next, to the drilled holes was implemented CNTs, carburizer and mixture of these both powders. Prepared specimens were remelted by TIG method on the CASTOTIG 2200 power source with 2.4 mm tungsten thoriated electrode with parameters sets for obtain 3.0 mm penetration depth. Remelted specimens were cut into the half of the welds distance and prepared for metallographic examinations. Cross sections of the specimens were tested on classical metallography microscopes, hardness tests, SEM analyses (on JEOL 5800 LV SEM EDX equipment) and phase identification by X-ray phase analysis on Philips APD X’Pert PW 3020 diffractometer. Hardness analysis indicates about 25% increase of hardness in the remelted area when the CTNs are used. In the specimens with carburizer there is no significant changes. SEM analyses of remelted areas on AISI 301 specimens modificated with CNTs, indicates that dark areas, initially interpret as one of the phase (based on optical microscope) is finally densely packed bladders with dimensions from 50 nm up to a few µm. These bladders are not present in the specimens with carburizer filler. High resolution scanning microscopy allow to observe in the this area protruding, longitudinal particles with 100-300 nm length. For identification of this phase, X-ray analysis was done. But very small dimensions of used CNTs (diameters about 9,5 nm), random orientation and small weight amount can make difficult or impossible to CNTs detection during XRD tests. It means that it is not possible to clearly determine nature of particles filling the cavities, it is only possible to suppose that they are CNTs beams with nanoparticles comes from their disintegration. Results of the researches indicates, that fill in the weld pool with different form of carbon (CNTs and carburizer) it is possible to achieve remelted beads with different structure and hardness distribution. It confirms validity of the research continuation with CNTs as a modifier of steels and also other metals and theirs alloys.

Źródło:

Archives of Metallurgy and Materials; 2022, 67, 1; 349-356
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 3.

Tytuł:

Influence of seawater salinity on corrosion of austenitic steel

Autorzy:

Starosta, Robert

Powiązania:

https://bibliotekanauki.pl/articles/245480.pdf

Data publikacji:

2019

Wydawca:

Instytut Techniczny Wojsk Lotniczych

Tematy:

austenitic steel
corrosion
potetiodynamic test
seawater

Opis:

Due to the paramagnetic properties and the ability to passivation, for the production of hulls of some vessels (mainly warships), corrosion-resistant (stainless) steels with austenitic structure are used. This article describes the influence of seawater salinity on selected corrosion properties of high-alloy steel X5CrNi 18-10 (304). The average salinity of the seas is taken as 3.5% content of sodium chloride. Corrosion rate of the tested material was evaluated in an aqueous solution of sodium chloride was evaluated. The NaCl concentration in corrosive solutions was 0.7%, 1.4%, 2.1%, 2.8%, 3.5%, 4.2%. Corrosion tests were performed using the potentiodynamic method. The range of electrochemical potential changes was Ecorr ±150 mV. Corrosion rate was assessed on the basis of corrosion current density measurements. Corrosion potential values against the saturated calomel electrode were also determined. Based on the obtained measurement results and non-parametric significance tests carried out, a significant influence of seawater salinity on the value of corrosion current density and corrosion potential was found. The highest value of corrosion current density (jcorr), and thus the highest corrosion rate, was recorded for 3.5% NaCl solution. In the concentration range from 0.7 to 3.5% NaCl in solution, the corrosion rate of austenitic steel increases. A further increase in salinity of electrolyte results in the inhibition of corrosion rate of steel. There is almost a full negative, linear correlation between the proportion of sodium chloride in the corrosive solution and the value of corrosion potential. Along with the rise in the salinity of seawater, increase the electrochemical activity, and thus the corrosion susceptibility, thus the corrosion susceptibility, of the austenitic steel X5CrNi 18-10 was observed.

Źródło:

Journal of KONES; 2019, 26, 3; 219-225
1231-4005
2354-0133

Pojawia się w:

Journal of KONES

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 4.

Tytuł:

Thermoelastic effect in austenitic steel referred to its hardening

Autorzy:

Pieczyska, E.

Powiązania:

https://bibliotekanauki.pl/articles/280245.pdf

Data publikacji:

1999

Wydawca:

Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej

Tematy:

thermoelastic effect
polycrystaline metal
consecutive deformation

Opis:

The effect of thermomechanical coupling occuring in metal during consecutive tensile tests, were examined. The temperature, stress and strain characteristic were found both in elastic and plastic ranges. The change of the character of the sample temperature was employed as a criterion for the limit between the elastic and plastic regimes. The thermomechanical coupling effects were interpreted in terms of the material microstructure evolution and referred to its strain hardening degree. A quite precise evaluation unloading seems to be particularly valuable.
W pracy wykazano w sposób doświadczalny, że ze wzrostem umocnienia, co wiąże się ze zwiększeniem ilości i ewolucją defektów w materiale, wzrasta efekt termosprężysty oraz efekt termosprężystego odciążania. Umocnienie realizowano drogą kolejnych cyklicznych obciążeń, jak również odpowiednią wstępną obróbką materiału. Badaniom poddano próbki takiej samej stali austenitycznej o dwóch różnych stanach wyjściowych: po wygrzewaniu ujędrniającym oraz po 50% umocnieniu w wyniku walcowania na zimno. Badania przeprowadzono na maszynie wytrzymałościowej, rejestrując jednocześnie zmiany temperatury przy wykorzystaniu zestawu termowizyjnego z komputerową rejestracją i obróbką wyników doświadczalnych. Na podstawie charakterystyk mechanicznych oraz zmiany temperatury materiału próbki zbadano termosprężyste oraz termoplastyczne efekty sprzężeń termo-mechanicznych. Wykazano, że efekty tych sprzężeń wzrastają w miarę wzrostu umocnienia materiału. W próbkach po walcowaniu przeanalizowano rozwój lokalizacji odkształcenia plastycznego. Zaobserwowano, że odkształenie plastyczne zlokalizowane podczas pierwszego cyklu, rozwija się w tym samym miejscu w kolejnych cyklach deformacji. Wyższy wzrost temperatury w próbkach po walcowaniu występuje w miejscu lokalizacji, natomiast w miarę wzrostu odległości od tego miejsca stwierdzono coraz mniejsze przyrosty temperatury.

Źródło:

Journal of Theoretical and Applied Mechanics; 1999, 2; 349-368
1429-2955

Pojawia się w:

Journal of Theoretical and Applied Mechanics

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 5.

Tytuł:

Possibility of corrosion monitoring resistance of austenitic steel for ship construction

Autorzy:

Jurczak, W.
Jurczak, K.

Powiązania:

https://bibliotekanauki.pl/articles/247396.pdf

Data publikacji:

2016

Wydawca:

Instytut Techniczny Wojsk Lotniczych

Tematy:

electrochemical corrosion
austenitic steel
monitoring

Opis:

The article presents the investigation results on possibility of electrochemical corrosion monitoring of the 1.3964 steel used for ship construction according of the patent Pl 216723. The patent’s assumption describes the method of on-line registration of electrochemical potential specifying the protective effectiveness of a thin oxide layer formed spontaneously on the steel surface. Essentials drop of the potential’s value with respect to the stationary one indicates layer cracking and initiation of pitting corrosion. Such a corrosion can be initiated by salinity and temperature of seawater and/or by a mechanical factor (strain). The carried out measurements of the potential and mechanical-electrochemical teats made it possible to determine the stress level causing the crack of oxide layer and initiation of corrosion processes in the steel. Thereby, the mechanical properties (Rm and A5) thin passive oxide layers investigated steel. Application of Electrochemical Impedance Spectroscopy (EIS) in the laboratory allows monitoring of weakness (stratification) of the film as a stage preceding to fracture [1, 2]. Stress cracking of the protective oxide layer on the 1.3964 steel takes place beyond the exploitation zone (above the tensile strength) and there is no indication to monitor the corrosion resistance on ship construction made of this stainless steel. However, in specific cases when temperature of the steel exceeds 40oC, application of the monitoring may be justified.

Źródło:

Journal of KONES; 2016, 23, 1; 131-138
1231-4005
2354-0133

Pojawia się w:

Journal of KONES

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 6.

Tytuł:

Martensite Content of Cold-Worked AISI 304L Chromium-Nickel Austenitic Steel

Autorzy:

Opiekun, Z. A.
Pająk, D.

Powiązania:

https://bibliotekanauki.pl/articles/379888.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic stainless steel
longitudinal rolling
martensitic phase
stal austenityczna
walcowanie wzdłużne
faza martenzytyczna

Opis:

The paper presents the effect of plastic strain occurring at room temperature in annealed samples of AISI 304L austenitic chromium-nickel steel on content of strain-induced &alpha′ martensite in its structure. The strain was introduced by longitudinal rolling of the samples with constant strain rate of about 300 mm/s and relative cold work ranging from 5% to 90% It has been demonstrated that the share of &alpha′ martensite in microstructure of the steel determined by means of Feritscope FMP30 depends on the degree of cold work.

Źródło:

Archives of Foundry Engineering; 2014, 14, 1 spec.; 155-158
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 7.

Tytuł:

Possibilities of Belzona adhesive joints application for austenitic steel used in ship constructions

Autorzy:

Jurczak, W.
Jurczak, K.

Powiązania:

https://bibliotekanauki.pl/articles/102361.pdf

Data publikacji:

2017

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

austenitic steel
adhesive joints
shipbuilding
Hysol
Belzona

Opis:

This paper presents the results of research on adhesive joints durability properties of ship austenitic steel done with the use of the latest adhesives – glues: a composite one from Belzona company, described as 1111 and 1212 as well as a Hysol 9466 adhesive, produced by Hysol. The 1.4301 (304) and 1.3964 (2xx) steels used for shipbuilding were single-lap adhesive joint, with varying degree of edges’ chamfering and offsetting (with a deflection). This type of alternative connections will provide protection and temporary structure’s protection in case of emergency cracking (due to corrosion or an impact) of the examined steel or welded joints of the ship’s construction and hull’s sheathings. The adhesive joints of the tested steel were made in laboratory conditions (according to the technological card) as well as outside the laboratory, hereinafter called as the emergency ones with the use of Belzon 1212. Adhesive joints of 304 and 2xx steel using Hysol 9466 adhesive made in laboratory conditions showed better durability properties than the ones made with the use of Belzona 1111 composite. However, in case of emergency connections the bonding strength as well as the bonding time (hardening) are important factors. The use of the special Belzona 1212 (for wet surfaces) gives a relatively good durability of approx. 20MPa with a much shorter (up to 20 minutes) hardening time and does not require such an accurate surface preparation as the adhesive joints made with the use of Hysol 9466.

Źródło:

Advances in Science and Technology. Research Journal; 2017, 11, 4; 134-140
2299-8624

Pojawia się w:

Advances in Science and Technology. Research Journal

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 8.

Tytuł:

Thermophysical properties of 904L austenitic steel
Właściwości cieplnofizyczne stali austenitycznej 904L

Autorzy:

Nasiłowska, B.
Bogdanowicz, Z.
Terpiłowski, J.
Pańcikiewicz, K.

Powiązania:

https://bibliotekanauki.pl/articles/264079.pdf

Data publikacji:

2018

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH

Tematy:

thermophysical properties
steel 904L
specific heat
thermal diffusivity
thermal conductivity
właściwości cieplno-fizyczne
stal 904L
ciepło właściwe
dyfuzyjność cieplna
przewodność cieplna

Opis:

This paper presents the results of the structural investigations and thermophysical properties of 904L steel parent material. Experimental studies on the structure of 904L steel proved a pure austenitic structure. Both the experimental research and analysis of the thermophysical properties of 904L steel were complemented with the results of the thermal conductivity calculations for the tested material. The paper presents a brief description of the measurements, the procedures for evaluating the data, and a set of the obtained results.
W pracy przedstawiono wyniki badań strukturalnych i właściwości cieplnofizyczne materiału rodzimego stali 904L. Badania eksperymentalne struktury stali 904L wykazały strukturę czysto austenityczną. Badania doświadczalne i analizę właściwości cieplnofizycznych stali 904L uzupełniono wynikami obliczeń przewodności cieplnej badanego materiału. W pracy przedstawiono zwięzły opis wykonywanych pomiarów, charakterystykę procedur opracowania danych oraz komplet uzyskanych wyników.

Źródło:

Metallurgy and Foundry Engineering; 2018, 44, 2; 61-71
1230-2325
2300-8377

Pojawia się w:

Metallurgy and Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 9.

Tytuł:

Mechanical Properties of High-Mn Austenitic Steel Tested under Static and Dynamic Conditions

Autorzy:

Dobrzański, L. A.
Borek, W.
Mazurkiewicz, J.

Powiązania:

https://bibliotekanauki.pl/articles/356028.pdf

Data publikacji:

2016

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

high manganese steels
TWIP mechanism
strain rate
mechanical properties
structure

Opis:

The purpose of the paper is to investigate X73MnSiAlNbTi25-1-3 high manganese austenitic steel containing 0.73% C to determine structural mechanisms decisive for increasing a reserve of cold deformation energy of such steel. The influence of a strain rate on the structure of the investigated steels and on the structural mechanisms decisive for their properties was analysed. Specialist research instrumentation was used for this purpose such as Scanning Transmission Microscopy (including EBSD examinations), conventional and high-resolution transmission electron microscopy together with diffraction examinations and metallographic examinations. It was found that the principal cause of an increased reserve of cold deformation energy of the investigated steels in dynamic conditions is the activation of mechanical twinning in the mutually intersecting systems in austenite grains and annealing twins, which are densifying when a cold deformation rate is growing, thereby confirming the basic mechanism of TWIP (TWinning Induced Plasticity).

Źródło:

Archives of Metallurgy and Materials; 2016, 61, 2A; 725-730
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 10.

Tytuł:

Analysis of residual stress in 1.4539 austenitic steel joints welded with TIG method

Powiązania:

Biuletyn Wojskowej Akademii Technicznej 2019, nr 1, s. 101-110

Współwytwórcy:

Nasiłowska, Barbara. Autor
Bogdanowicz, Zdzisław. Autor
Mońka, Grzegorz. Autor
Tomaszewski, Rafał. Autor
Zdunek, Joanna. Autor

Data publikacji:

2019

Tematy:

Złącza spawane
Naprężenia i odkształcenia
Pomiary
Badania naukowe
Artykuł z czasopisma naukowego
Artykuł z czasopisma technicznego

Opis:

Bibliografia na stronie 110.

Dostawca treści:

Bibliografia CBW

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 11.

Tytuł:

Evaluation of High Temperature Corrosion Resistance of Finned Tubes Made of Austenitic Steel And Nickel Alloys

Autorzy:

Turowska, A.
Adamiec, J.

Powiązania:

https://bibliotekanauki.pl/articles/353941.pdf

Data publikacji:

2016

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

finned tubes
laser welding
high temperature corrosion
austenitic steel
nickel alloys

Opis:

The purpose of the paper was to evaluate the resistance to high temperature corrosion of laser welded joints of finned tubes made of austenitic steel (304,304H) and nickel alloys (Inconel 600, Inconel 625). The scope of the paper covered the performance of corrosion resistance tests in the atmosphere of simulated exhaust gases of the following chemical composition: 0.2% HCl, 0.08% SO₂, 9.0% O₂ and N₂ in the temperature of 800°C for 1000 hours. One found out that both tubes made of austenitic steel and those made of nickel alloy displayed good resistance to corrosion and could be applied in the energy industry.

Źródło:

Archives of Metallurgy and Materials; 2016, 61, 2B; 1089-1093
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 12.

Tytuł:

Corrosion Resistance of Nitrogen-Doped DLC Coatings Produced in Glow Discharge Conditions on Nitrided Austenitic Steel

Autorzy:

Borowski, T.
Spychalski, M.
Rożniatowski, K.
Kulikowski, K.

Powiązania:

https://bibliotekanauki.pl/articles/354989.pdf

Data publikacji:

2020

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

DLC coating
nitrided layer
DC
pulsed glow discharge
corrosion
adhesion

Opis:

Nitrogen-doped DLC (diamond-like carbon) coatings were produced on 316L nitrided austenitic steel in direct current and pulsed glow discharge conditions. The chemical composition, surface topography, hardness and corrosion resistance of the obtained carbon coatings were examined. The coatings varied in surface morphology, roughness and hardness. Direct current glow discharge made it possible to produce a coating characterized by lower hardness, greater thickness and higher nitrogen content. The coating featured improved corrosion resistance and adhesion compared to coatings produced in the pulsed process.

Źródło:

Archives of Metallurgy and Materials; 2020, 65, 3; 1141-1146
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 13.

Tytuł:

Microstructure of 309 and 310 Austenitic Stainless Steel CMT Overlays on the 16Mo3 Pressure Vessel Steel

Autorzy:

Rozmus-Górnikowska, Magdalena
Dymek, Stanisław
Blicharski, M.
Cieniek, Łukasz
Kusiński, Jan

Powiązania:

https://bibliotekanauki.pl/articles/2049742.pdf

Data publikacji:

2021

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

309 austenitic steel
310 austenitic steel
weld overlay coating
CMT
SEM
EDS

Opis:

The aim of this work was to characterize the changes in microstructure and chemical composition of the austenitic overlays on a pressure vessel steel that occur in the vicinity of the interface between the overlay and the base material. The investigations were carried out on a 16Mo3 boiler pipes weld overlaid by 309 and 310 steels. The microstructural examinations were performed on longitudinal cross-sectioned samples. The qualitative and quantitative chemical composition analyses on metallographic samples were determined on Scanning Electron Microscopy (SEM) by means of Energy Dispersive Spectrometry (EDS). The article analyzes the influence of the solidification sequence in both types of steel on final microstructure.

Źródło:

Archives of Metallurgy and Materials; 2021, 66, 2; 645-649
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 14.

Tytuł:

Magnetic Study of Nanocrystalline TiB₂, TiC, B₄C Powders Doped to AISI 316L Austenitic Steel

Autorzy:

Bodziony, T.
Kaczmarek, S.
Biedunkiewicz, A.
Leniec, G.
Figiel, P.

Powiązania:

https://bibliotekanauki.pl/articles/1032403.pdf

Data publikacji:

2017-07

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

07.55.Jg
75.20.-g
75.50.-y
75.50.Bb
76.30.-v

Opis:

The investigations into ferromagnetic resonance and magnetic susceptibility of nanocrystalline TiB₂, TiC, and B₄C powders (Ti-B-C system) doped to AISI 316L austenitic steel with different amounts (3 vol.%, 5 vol.% and 7 vol.%) have been carried out. The ferromagnetic resonance spectra were recorded in the temperature range from helium up to room temperature. The three tested composite samples contain a number of magnetic phases in different proportions. They reveal a structure originating from several different complex magnetic centers. The composites revealed such magnetic phenomena as paramagnetism, (anti)ferromagnetism, and superparamagnetism. Magnetic susceptibility investigations supported the ferromagnetic resonance studies and their analysis. Magnetic properties of the TiB₂, TiC, B₄C powders doped to AISI steel may play important role in further possible applications of these composite systems.

Źródło:

Acta Physica Polonica A; 2017, 132, 1; 62-68
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 15.

Tytuł:

Microstructure and Mechanical Properties of Braze Welded Joints of Copper with Austenitic Steel Made by CMT Method

Autorzy:

Wojdat, T.
Kustroń, P.
Margielewska, A.
Stachowicz, M.

Powiązania:

https://bibliotekanauki.pl/articles/354652.pdf

Data publikacji:

2019

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

arc welding-brazing
CMT method
dissimilar joint

Opis:

This paper outlines issues associated with gas-shielded braze welding of CU-ETP copper with austenitic steel X5CrNi18-10(1.4301) using a consumable electrode. The possibilities for producing joints of this type using innovative low-energy welding methods are discussed. The paper provides an overview of the results of metallographic and mechanical (static shear test, microhardness) tests for braze welded joints made on an automated station using the Cold Metal Transfer (CMT) method. Significant differences in the structure and mechanical properties are indicated, resulting from the joint configuration and the type of shielding gas (argon, helium).

Źródło:

Archives of Metallurgy and Materials; 2019, 64, 4; 1411-1420
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 16.

Tytuł:

Causes of cracks of chemical apparatus made of austenitic steel
Przyczyny pęknięć aparatury chemicznej wykonanej ze stali austenitycznej

Autorzy:

Lange, A.
Białucki, P.
Małachowska, A.
Bashir, A.
Harapińska, E.

Powiązania:

https://bibliotekanauki.pl/articles/115129.pdf

Data publikacji:

2018

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

stal austenityczna
pęknięcie naprężeniowe
para wodna
austenitic steel
stress crack
steam

Opis:

The subject of the research was the installation of a water steam used in the chemical industry. Penetration tests revealed an extensive network of cracks on the surface of steel and welds. Metallographic studies, chemical composition analysis, EDX analysis were performed. Thermal treatment of steel was carried out and microhardness measurements were made. The results of the tests showed that stress corrosion was the main reason for the occurrence of cracks.
Przedmiotem badań był inżektor - element instalacji pary przegrzanej eksploatowany w przemyśle chemicznym. Badania penetracyjne ujawniły rozległą siatkę pęknięć na powierzchni stali i spoin. Wykonano badania metalograficzne, analizę składu chemicznego, analizę EDX. Przeprowadzono obróbkę cieplną stali oraz wykonano pomiary mikrotwardości. Wyniki przeprowadzonych badań wykazały, że główną przyczyną wystąpienia pęknięć była korozja naprężeniowa.

Źródło:

Welding Technology Review; 2018, 90, 12; 25-31
0033-2364
2449-7959

Pojawia się w:

Welding Technology Review

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 17.

Tytuł:

Resistance to Abrasive Wear and Volume Fraction of Carbides in Cast High-manganese Austenitic Steel with Composite Structure

Autorzy:

Tęcza, G.
Głownia, J.

Powiązania:

https://bibliotekanauki.pl/articles/381502.pdf

Data publikacji:

2015

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

resistance to abrasive wear
high-manganese steel
solution treatment
microstructure
vanadium carbide
odporność na zużycie ścierne
stal wysokomanganowa
mikrostruktura
węglik wanadu

Opis:

Cast Hadfield steel is characterised by high abrasion resistance, provided, however, that it is exposed to the effect of dynamic loads. During abrasion without loading, e.g. under the impact of loose sand jet, its wear resistance drops very drastically. To increase the abrasion resistance of this alloy under the conditions where no pressure is acting, primary vanadium carbides are formed in the metallurgical process, to obtain a composite structure after the melt solidification. The primary, very hard, carbides uniformly distributed in the austenitic matrix are reported to double the wear resistance of samples subjected to the effect of a silicon carbide-water mixture.

Źródło:

Archives of Foundry Engineering; 2015, 15, 4; 129-133
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 18.

Tytuł:

The Analysis of Deformation and Forecasting Microstructure in the Forging Process of the X6CrNiTi18-10 Austenitic Steel

Autorzy:

Kukuryk, M.

Powiązania:

https://bibliotekanauki.pl/articles/352789.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

hot forging
austenitic steel
FEM
microstructure

Opis:

The paper presents the analysis of the three-dimensional strain state for the cogging process of a forging (type: shaft) of the X6CrNiTi18-10 austenitic steel with the application of the finite element method. The results of the thermal-mechanical simulation of the hot cogging process on flat and shaped anvils, taking under consideration boundary conditions applied in industrial practice, are presented. In the research, a new method of forging, consisting in the introduction of the initial forging of the stock on anvils which have convex work surfaces, and further forging on shaped anvils, was applied. The results of the calculations make it possible to determine effective strain distribution, effective stress, mean stresses and temperature in the volume of a forging. The solution was supplemented by the addition of the model of microstructure development in the course of deformation. The conducted research constitutes the basis for determining the best possible technological process of the initial forging of a cast ingot, and provide the possibility of forecasting the deformations and parameters of the microstructure.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 1; 393-401
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 19.

Tytuł:

Mechanical Behavior of Nitrocarburised Austenitic Steel Coated with N-DLC by Means of DC and Pulsed Glow Discharge

Autorzy:

Borowski, Tomasz
Kulikowski, Krzysztof
Spychalski, Maciej
Rożniatowski, Krzysztof
Rajchel, B.
Adamczyk-Cieślak, Bogusława
Wierzchoń, Tadeusz

Powiązania:

https://bibliotekanauki.pl/articles/2048867.pdf

Data publikacji:

2022

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

DLC
nitrocarburizing
surface engineering
hardness
adhesion
wear

Opis:

AISI 316L steel was subjected to nitrocarburizing under glow discharge conditions, which was followed by DLC (diamond-like carbon) coatings deposition using the same device. The coatings were applied under conditions of direct current and pulsed glow discharge. In order to determine the influence of the produced nitrocarbon austenite layer and the type of discharge on the microstructure and mechanical properties of the coatings, the following features were analysed: surface roughness, coating thickness, structure, chemical composition, adhesion and resistance to frictional wear. For comparison purposes, DLC coatings were also deposited on steel without a nitrocarburised layer. The obtained results indicate a significant influence of the type of glow discharge on the roughness, hardness, nitrogen content and of the nitrocarburised layer on the resistance to wear by friction and adhesion of the produced coatings.

Źródło:

Archives of Metallurgy and Materials; 2022, 67, 1; 317-324
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 20.

Tytuł:

The Cracking Mechanism of Ferritic- Austenitic Cast Steel

Autorzy:

Stradomski, G.

Powiązania:

https://bibliotekanauki.pl/articles/383172.pdf

Data publikacji:

2016

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

duplex cast steel
hot cracking
solidification process
sigma phase
staliwo duplex
pękanie na gorąco
proces krzepnięcia
faza sigma

Opis:

In the high-alloy, ferritic - austenitic (duplex) stainless steels high tendency to cracking, mainly hot-is induced by micro segregation processes and change of crystallization mechanism in its final stage. The article is a continuation of the problems presented in earlier papers [1-4]. In the range of high temperature cracking appear one mechanism a decohesion - intergranular however, depending on the chemical composition of the steel, various structural factors decide of the occurrence of hot cracking. The low-carbon and low-alloy cast steel casting hot cracking cause are type II sulphide, in high carbon tool cast steel secondary cementite mesh and/or ledeburite segregated at the grain solidified grains boundaries, in the case of Hadfield steel phosphorus - carbide eutectic, which carrier is iron-manganese and low solubility of phosphorus in high manganese matrix. In duplex cast steel the additional factor increasing the risk of cracking it is very "rich" chemical composition and related with it processes of precipitation of many secondary phases.

Źródło:

Archives of Foundry Engineering; 2016, 16, 4; 153-156
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 21.

Tytuł:

Determination of Thermal Diffusivity of Austenitic Steel Using Pulsed Infrared Thermography
Wyznaczanie dyfuzyjności cieplnej stali austenitycznej przy wykorzystaniu aktywnej termografii podczerwieni

Autorzy:

Kochanowski, K.
Oliferuk, W.
Płochocki, Z.
Adamowicz, A.

Powiązania:

https://bibliotekanauki.pl/articles/354398.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

thermal diffusivity
pulsed infrared thermography
heat conduction
austenitic steel
dyfuzyjność cieplna
aktywna termografia podczerwona
przewodzenia ciepła
stal austenityczno-ferrytyczna

Opis:

The simple method of determining thermal diffusivity of solid materials at room temperature using the pulsed infrared thermography (IRT) is proposed. The theoretical basis of the method and experimental results are presented. The study was conducted on austenitic steel 316L. Theobtained results show that the thermal diffusivity value of the tested steel determined by means of pulsed infrared thermography is very approximate to the values given in the literature, obtained by using more complicated methods. The differences between these values are 0.5%.
W niniejszej pracy przedstawiono prostą metodę wyznaczania dyfuzyjności cieplnej ciał stałych w temperaturze pokojowej przy wykorzystaniu aktywnej termografii podczerwieni. Zaprezentowane zostały teoretyczne podstawy metody oraz wyniki badań doświadczalnych. Badanie przeprowadzono dla stali austenitycznej 316L. Otrzymane rezultaty pokazują, że wyznaczona wartość dyfuzyjności cieplnej badanej stali jest bardzo bliska wartościom podanym w literaturze, otrzymanym za pomocą bardziej skomplikowanych metod. Różnica między tymi wartościami sięga zaledwie 0,5%.

Źródło:

Archives of Metallurgy and Materials; 2014, 59, 3; 893-897
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 22.

Tytuł:

The effect of cavitation erosion on austenitic-ferritic steel

Autorzy:

Krawczyk, J.
Jasionowski, R.
Ura, D.
Goły, M.
Frocisz, Ł.

Powiązania:

https://bibliotekanauki.pl/articles/135269.pdf

Data publikacji:

2018

Wydawca:

Akademia Morska w Szczecinie. Wydawnictwo AMSz

Tematy:

cavitation
austenite destabilization
duplex steel
erosion wear
plastic deformation
material

Opis:

Cavitation is a one of many wear mechanisms which are related to the flow of liquid. It is one of the most destructive wear methods for stainless materials. The local changes in the pressure of the liquid stream related to the flow across the metal component cause straightening of the surface area, as well as its erosion and the formation of pits on the surface layer. The erosion value of cavitation is related to the material’s microstructure, the geometry of the element, the phase composition of the material and the surface roughness. In this paper the investigation of the cavitation process for duplex stainless steel has been performed. Samples examined in the first stages of the experiments were not significantly changed, but after a long time the hardness increase was very visible. The result of the cavitation was also cracking along the interphase boundaries, which resulted in the chipping of the material. One of the most important results was a description of the change in the wear mechanisms and its intensity during the cavitation exposure time. At first plastic micro deformation of the material’s surface occurred, then the plastic deformation increased significantly and after some time this resulted in erosion of the material and interfacial boundary decohesion; these two effects increased simultaneously. The last of the mechanisms was mechanical destabilization of the austenite, but the clear result of the mechanical destabilization of the austenite was only observed in the last sample. Martensitic transformation of the material changed the material’s mechanical properties, but for the stainless steels this resulted in electrochemical corrosion of the material, especially through the formation of an electrochemical potential between austenite and martensite.

Źródło:

Zeszyty Naukowe Akademii Morskiej w Szczecinie; 2018, 56 (128); 30-35
1733-8670
2392-0378

Pojawia się w:

Zeszyty Naukowe Akademii Morskiej w Szczecinie

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 23.

Tytuł:

High temperature corrosion of metallic materials in coal fired power plant boilers

Autorzy:

Dudziak, T.

Powiązania:

https://bibliotekanauki.pl/articles/391624.pdf

Data publikacji:

2017

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa

Tematy:

steam oxidation
high temperature
austenitic steel
Ni based alloy

Opis:

The aim of this work was to perform high temperature tests in steam conditions at 700‒800°C for 3000 hours. In this work seven alloys were studied: Cr rich austenitic steels 309S, 310S, HR3C, and two solid-solution strengthened Ni based alloys; Haynes® 230®, 617 alloy and two (γ’) gamma-prime strengthened Ni based alloys; 263 and Haynes® 282®. The obtained results suggest that the exposed materials show high corrosion resistance under steam oxidation conditions where predominantly Cr₂O₃ and MnCr₂O₄ compounds developed. The materials showed no chromia evaporation process and no exfoliation of the external oxide scale. However, two (γ’) gamma-prime strengthened Ni based alloys showed a high degree of internal oxidation that increased with temperature.

Źródło:

Prace Instytutu Odlewnictwa; 2017, 57, 4; 277-291
1899-2439

Pojawia się w:

Prace Instytutu Odlewnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 24.

Tytuł:

XRD phase investigations of steam oxidized Fe and Ni rich Cr alloys

Autorzy:

Dudziak, T.
Witkowska, M.
Ratuszek, W.
Chruściel, K.

Powiązania:

https://bibliotekanauki.pl/articles/391538.pdf

Data publikacji:

2017

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa

Tematy:

austenitic steel
Ni based alloys
high temperature
steam
XRD

Opis:

The aim of this work was to summarise XRD investigations performed after the tests carried out in steam oxidation conditions in the temperature range 700‒800°C for 3000 hours. In this work, two solid-solution strengthened alloys; Haynes® 230®, 617 alloy and two (γ’) gamma-prime strengthened alloys; 263 and Haynes® 282® and high alloyed steels rich in Cr: 309S, 310S and HR3C were exposed. The phase analyses were carried out using two techniques; Bragg-Brentano (BB) geometry and geometry of constant angle called grazing incidence α = 1° and α = 3°.

Źródło:

Prace Instytutu Odlewnictwa; 2017, 57, 4; 265-276
1899-2439

Pojawia się w:

Prace Instytutu Odlewnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 25.

Tytuł:

Investigation of Microstructures and Mechanical Properties of T92 Martensitic Steel/Super304 Austenitic Steel Weld Joints Made with Three Welding Consumables

Autorzy:

Liang, Z.
Gui, Y.
Zhao, Q.

Powiązania:

https://bibliotekanauki.pl/articles/354971.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

dissimilar welding
welding material
microstructures
mechanical properties

Opis:

The microstructures and mechanical properties of T92 martensitic steel/Super304 austenitic steel weld joints with three welding consumables were investigated. Three types of welding materials ERNiCr-3, ERNiCrCoMo-1and T-304H were utilized to obtain dissimilar welds by using gas tungsten arc weld (GTAW). The results show that heat affect zone (HAZ) of T92 steel consists of coarse-grained and fine-grained tempered martensites. The microstructures of joints produced from ERNiCrCoMo-1 consist of equiaxed dendrite and columnar dendrite grains, which are more complicated than that of ERNiCr-3. In the tensile tests, joints constructed from ERNiCrCoMo-1 and T-304H met the ASME standard. The highest fracture energy was observed in specimens with the welding material ERNiCrCoMo-1. Ni content in weld seam of ERNiCrCoMo-1 was highest, which was above 40%. In conclusion, the nickel alloy ERNiCrCoMo-1 was the most suitable welding material for joints produced from T92 martensitic steel/Super304 austenitic steel.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 3; 1249-1256
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 26.

Tytuł:

Modifying the frictional wear resistance of AISI 316L austenitic steel
Kształtowanie odporności na zużycie przez tarcie stali austenitycznej typu 316L

Autorzy:

Wierzchoń, T.
Skołek, E.
Brojanowska, A.
Burdyńska, S.
Mróz, W.

Powiązania:

https://bibliotekanauki.pl/articles/256664.pdf

Data publikacji:

2006

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Technologii Eksploatacji - Państwowy Instytut Badawczy

Tematy:

stal austenityczna 316L
azotowanie jarzeniowe
azotek boru
osadzanie laserem impulsowym
metoda hybrydowa
AISI 316L austenitic stainless steel
glow discharge nitriding
boron nitride
pulse laser deposition
hybrid process

Opis:

The rapid technical development enhances the demands on constructional materials in terms of their resistance to frictional wear, resistance to corrosion and erosion, high hardness, etc. These demands can be satisfied by, e.g. applying various surface engineering techniques that permit to modify the microstructure, the phase and chemical composition of the surface layers of the treated parts. A prospective line of the development of surface engineering is the production of composite layers by combining various surface engineering methods. This paper presents the results of examinations of the phase composition and frictional wear resistance of the layers produced by hybrid processes, i.e. such that combine glow discharge assisted nitriding performed at 450°C and 550°C with a pulsed laser deposition of boron nitride coatings (PLD method). It has been shown that the boron nitride coatings formed on nitrided 316L steel increase its frictional wear resistance.
Procesy azotowania jarzeniowego stali austenitycznych pozwalają na wytworzenie powierzchniowych warstw dyfuzyjnych zwiększających twardość i odporność na zużycie przez tarcie. Prowadzenie tych obróbek w temperaturach powyżej 460°C powoduje jednak spadek odporności korozyjnej stali. W artykule przedstawiono wyniki badań składu fazowego oraz odporności na zużycie przez tarcie warstw wytworzonych w procesach hybrydowych łączących metodę azotowania jarzeniowego w temperaturach 450°C i 550°C z procesem impulsowego laserowego osadzania powłok azotku boru (metoda PLD). Wykazano, że wytworzenie powłok azotku boru na warstwach azotowanych wytworzonych na stali 316L zwiększa ich odporność na zużycie przez tarcie.

Źródło:

Problemy Eksploatacji; 2006, 4; 205-213
1232-9312

Pojawia się w:

Problemy Eksploatacji

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 27.

Tytuł:

Struktura i właściwości mechaniczne złączy spawanych stali ferrytycznej X2CrNi12 ze stalą austenityczną X5CrNi 18-10
Structure and mechanical properties of welded joints of ferritic steel X2CrNi12 with austenitic steel X5CrNi 18-10

Autorzy:

Ciechacki, K.
Szykowny, T.

Powiązania:

https://bibliotekanauki.pl/articles/386424.pdf

Data publikacji:

2011

Wydawca:

Politechnika Białostocka. Oficyna Wydawnicza Politechniki Białostockiej

Tematy:

stal austenityczna
struktura
własności mechaniczne
austenitic steel
structure
mechanical properties

Opis:

Podstawowym celem pracy jest powiązanie charakteru mikrostruktury różnoimiennych złączy spawanych z podstawowymi właściwościami mechanicznymi. W badaniach właściwości mechanicznych określono rozkład makro i mikrotwardości w obrębie złącza, wytrzymałość na rozciąganie, udarność oraz wykonano próbę zginania. W badaniach strukturalnych posłużono się metodą mikroskopii świetlnej i mikroskopii skaningowej SEM oraz badań dyfrakcyjnych rentgenowskich. Do badań przyjęto stal o strukturze ferrytycznej X2CrNi12 i stal o strukturze austenitycznej X5CrNi 18-10 w postaci blach o grubości 5mm. Spawanie wykonano metodą GMA przy zastosowaniu trzech różnych gatunków spoiwa: 307 (G 18 8 Mn); 309LSi (G 23 12 L Si); OK. Tubrot 14.27.
The basic aim of this work is the connection of the microstructure of different joints with mechanical properties. In the range of mechanical properties the micro and macro hard- ness, impact tests, tensile and bendig strength of welded joints were measured. For microstructure investigations the light scanning electron microscopy SEM and X – ray diffraction methods were used. The ferritic X2CrNi12 and austenitic X5CrNi 18-10 steels in the form of 5 mm thick sheets were taken for investigation.

Źródło:

Acta Mechanica et Automatica; 2011, 5, 1; 17-23
1898-4088
2300-5319

Pojawia się w:

Acta Mechanica et Automatica

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 28.

Tytuł:

Modeling of damage evolution and martensitic transformation in austenitic steel at cryogenic temperature
Modelowanie rozwoju uszkodzeń i przemiany martenzytycznej w stali austenitycznej

Autorzy:

Ryś, M.

Powiązania:

https://bibliotekanauki.pl/articles/950688.pdf

Data publikacji:

2015

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

constitutive modeling
phase transformation
damage evolution
expansion joints
modelowanie konstytutywne
przemiana fazowa
rozwój uszkodzenia
połączenia dylatacyjne

Opis:

In the present work, a constitutive model of materials undergoing the plastic strain induced phase transformation and damage evolution has been developed. The model is based on the linearized transformation kinetics. Moreover, isotropic damage evolution is considered. The constitutive model has been implemented in the finite element software Abaqus/Explicit by means of the external user subroutine VUMAT. A uniaxial tension test was simulated in Abaqus/Explicit to compare experimental and numerical results. Expansion bellows was also modelled and computed as a real structural element, commonly used at cryogenic conditions.
W artykule przedstawiono konstytutywny model materiału podlegającemu przemianie fazowej wywołanej odkształceniami plastycznymi oraz rozwojowi uszkodzeń. Przemiana fazowa opisana jest modelem liniowym. Ponadto, w pracy uwzględniono izotropowy rozwój uszkodzeń. Opis konstytutywny został zaimplementowany w komercyjnym programie Abaqus/Explicit z wykorzystaniem zewnętrznej procedury użytkownika VUMAT. Dokonano symulacji testu jednoosiowego rozciągania w celu porównania wyników eksperymentalnych z numerycznymi. Jako przykład rzeczywistego elementu konstrukcyjnego, pracującego w warunkach temperatur kriogenicznych, dokonano symulacji pracy kompensatora.

Źródło:

Archive of Mechanical Engineering; 2015, LXII, 4; 523-537
0004-0738

Pojawia się w:

Archive of Mechanical Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 29.

Tytuł:

Reverse Transformation of Deformation Induced Martensite in Austenitic Stainless Steel

Autorzy:

Dryzek, E.
Sarnek, M.

Powiązania:

https://bibliotekanauki.pl/articles/1196051.pdf

Data publikacji:

2014-03

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

78.70.Bj
81.05.Bx

Opis:

Cumulative isochronal annealing of stainless steel 1.4307 samples deformed by compression was investigated using the Doppler broadening of the annihilation line measurements. Higher level of plastic deformation is accompanied not only by higher concentration of defects but also by higher amount of α' martensite. The annealing studies revealed creation of defects in the temperature range between 450C and 650C pointing out the reverse transition of α' martensite to austenite. This is confirmed by magnetic susceptibility and microhardness measurements.

Źródło:

Acta Physica Polonica A; 2014, 125, 3; 710-713
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 30.

Tytuł:

Automated Laser Welding of AISI 304 Stainless Steel by Disk Laser

Autorzy:

Lisiecki, A.
Kurc-Lisiecka, A.

Powiązania:

https://bibliotekanauki.pl/articles/354376.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

autogenous laser welding
butt joints
stainless steel
AISI 304
austenitic steel

Opis:

The automated laser welding process of 2.0 mm thick sheets of AISI 304 stainless steel was investigated. The disk laser with a beam spot diameter of 200 μm was used for bead-on-plate and next for autogenous butt joints welding. The influence of basic welding parameters such as laser power, welding speed, and focal spot position on fusion zone configuration, quality of joints, microstructure changes, and microhardness distribution across the joints were analysed and presented in this paper. The results have shown that stiffening of the 2.0 mm thick sheets is crucial for providing high quality and reproducibility of butt joint in a case of AISI 304 stainless steel due to relatively low thermal conductivity and simultaneously high thermal expansion. Relevant drop of microhardness in the weld zone was observed. The mean value of microhardness of the base metal was 230 HV0.1, while the microhardness in fusion zone of the test welds was ranged from 130 to 170 HV0.1. Additionally the microstructure changes in the weld metal and also in the heat affected zone of test joints is described.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 4; 1663-1672
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 31.

Tytuł:

Perforation test as an accuracy evaluation tool for a constitutive model of austenitic steel
Wykorzystanie próby przebijania do oceny dokładności modelu konstytutywnego stali austenitycznej

Autorzy:

Moćko, W.
Kowalewski, Z. L.

Powiązania:

https://bibliotekanauki.pl/articles/354786.pdf

Data publikacji:

2013

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

plastic behaviour
fracture properties
constitutive modeling
perforation
austenitic steel
właściwości pękania
zachowanie plastyczne
modelowanie konstytutywne
perforacja
stal austenityczna

Opis:

In this paper, a new method for assessing the accuracy of a constitutive model is proposed. The method uses perforation test done by drop weight tower. The assessment is carried out by comparison of striker velocity curve obtained using experiment and FEM simulation. In order to validate proposed method the various constitutive equations were applied i.e. Johnson-Cook, Zerilli-Armstrong and the extended Rusinek-Klepaczko to model mechanical behaviour of X4CrMnN16-12 austenitic steel. The steel was characterized at wide range of strain and strain rates using servo-hydraulic testing machine and split Hopkinson pressure bar. The relative error calculated as a difference between measured and constitutive model based stress-strain curve was applied as a reference data (classic approach). Subsequently, it was compared with relative error determined on the basis of experimental and FEM calculated striker velocity (new approach). A good correlation between classic and a new method was found. Moreover, a new method of error assessment enables to validate constitutive equation in a wide range of strain rates and temperatures on the basis of a single experiment.
W artykule zaprezentowano nową metodę oceny dokładności modelu konstytutywnego. Oparto ją na wynikach uzyskanych w próbie przebijania z użyciem młota opadowego. Wyznaczenie błędu zostało przeprowadzone na podstawie porównania prędkości penetratora zmierzonej w trakcie ekspery mentu i obliczonej na podstawie symulacji MES. W celu walidacji metody przeanalizowano wybrane równania konstytutywne: Johnsona-Cooka, Zerilli-Armstronga oraz rozszerzony model Rusinka-Klepaczko w odniesieniu do stali austenitycznej X4CrMnN 16-12. Badania właściwości mechanicznych stali zostały przeprowadzone w szerokim zakresie prędkości odkształcania z użyciem maszyny serwo-hydraulicznej oraz pręta Hopkinsona. Błąd względny wyznaczony jako różnica zmierzonej i obliczonej na podstawie równania konstytutywnego krzywej naprężenie-odkształcenie został ustalony jako wartość błędu referencyjnego (metoda klasyczna). Następnie porównano go z błędem względnym wyznaczonym na podstawie zmierzonego i obliczonego za pomocą MES chwilowego przebiegu prędkości penetratora (nowa metoda). Stwierdzono dobrą korelację pomiędzy klasyczną a nową metodą oceny dokładności modela W porównaniu do klastycznej metody możliwa jest walidacja zależności konstytutywnej w szerokim zakresie prędkości odkształcania oraz temperatury w trakcie jednego testu.

Źródło:

Archives of Metallurgy and Materials; 2013, 58, 4; 1105-1110
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 32.

Tytuł:

Polynomial interpolation of the obtained depth of nitrogen diffusion on the surface of the plasma nitrided X5CrNi18-10 austenitic steel

Autorzy:

Ogórek, M.
Biernat, G.
Frączek, T.
Knapiński, M.

Powiązania:

https://bibliotekanauki.pl/articles/122457.pdf

Data publikacji:

2015

Wydawca:

Politechnika Częstochowska. Wydawnictwo Politechniki Częstochowskiej

Tematy:

polynomial tensor interpolation
depth of nitrogen diffusion

Opis:

In the paper the polynomial tensor interpolation of the obtained results of the nitrogen diffusion depth on the surface of austenitic steel type 304 is presented.

Źródło:

Journal of Applied Mathematics and Computational Mechanics; 2015, 14, 3; 79-85
2299-9965

Pojawia się w:

Journal of Applied Mathematics and Computational Mechanics

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 33.

Tytuł:

Laboratory tests and numerical analysis of façade sub-structure made of austenitic steel
Badania laboratoryjne i analizy numeryczne dotyczące konstrukcji elewacji ze stali austenitycznych

Autorzy:

Cwyl, Maciej
Wierzbicki, Stanisław
Michalczyk, Rafał

Powiązania:

https://bibliotekanauki.pl/articles/2174093.pdf

Data publikacji:

2022

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Opis:

This article presents a study of a wall cladding system composed of stainless steel sub-frame and composite, fibre-reinforced concrete cladding panels, which was been installed on a high-rise public building. The study focused on the assessment of strength, safety and durability of design through laboratory tests and numerical analyses. The laboratory tests were conducted using a threedimensional tests stand and a full-scale mock-up of the wall cladding system built at the laboratory using the actually used materials and cladding panels. The boundary conditions and the test loads corresponded to the values of actions determined during the engineering phase of the high-rise building under analysis. Noteworthy, wind actions were verified by supplementary wind tunnel testing. In addition, the stainless steel was also tested to determine the strength properties of the material actually used in construction. These test were carried out just before commencement of the curtain wall installation. The 3D model was constructed with the application of the finite element method (FEM) to obtain adequate representation of geometry, material performance and structural behaviour of the analysed wall cladding system. Particular attention was paid to determination of the parameters defining the behaviour of the cladding system sub-frame from the angle of plastic deformations of the stainless steel and the resulting failure mechanisms of the members of the structure itself. To this end, the stainless steel was subjected to appropriate performance tests to determine material properties including the values of the proportionality limit and yield strength.
Współczesne konstrukcje metalowo - szklane notują bardzo intensywny rozwój w obszarze rozwiązań materiałowych, pełnionych funkcji w budynku oraz efektów wizualnych związanych z architekturą realizowanych obiektów. W artykule przedstawiono badania struktury elewacyjnej budynku wysokiego użyteczności publicznej, która została zaprojektowana w postaci rusztu ze stali nierdzewnej i kompozytowych paneli z betonu zbrojonego włóknami. Głównym celem niniejszej pracy była ocena nośności, bezpieczeństwa i trwałości projektowanych rozwiązań, poprzez badania laboratoryjne i analizy numeryczne. Badania laboratoryjne prowadzono na trójwymiarowym stanowisku badawczym, na fragmencie elewacji w skali rzeczywistej, który zbudowano w laboratorium z materiałów i okładzin zastosowanych na realizowanym obiekcie. Fragment elewacji badany w laboratorium został przygotowany przez wykonawców realizujących ocenianą fasadę budynku, co pozwoliło odwzorować standard wykonania taki jak na obiekcie. Warunki brzegowe oraz przyjęte obciążenia odpowiadały wartościom oddziaływań, wyznaczonym na etapie projektowania elewacji wieżowca, przy czym oddziaływania wiatru były weryfikowane uzupełniającymi badaniami w tunelu aerodynamicznym. Przeprowadzono również badania materiałowe stali nierdzewnej, mające na celu określenie rzeczywistych parametrów wytrzymałościowych zastosowanego materiału. Badania przeprowadzono bezpośrednio przed rozpoczęciem realizacji konstrukcji fasady budynku. Wyniki badań eksperymentalnych wykorzystano do walidacji modelu numerycznego odwzorowującego badany fragment elewacji Trójwymiarowy model zbudowano z wykorzystaniem metody elementów skończonych co pozwoliło na odpowiednie odwzorowanie zarówno geometrii, parametrów materiałowych jak i zachowania się analizowanego fragmentu elewacji. Szczególny nacisk położono w artykule na określenie charakterystyki pracy konstrukcji wsporczej elewacji w kontekście odkształceń plastycznych stali nierdzewnej oraz wynikające stąd mechanizmy zniszczenia elementów tej konstrukcji. W tym celu przeprowadzono badania materiałowe stali nierdzewnej w celu określenia parametrów takich jak granica proporcjonalności i granica plastyczności. W artykule wskazano na specyficzny charakter pracy wsporników konstrukcji wsporczej przy uwzględnieniu występowania odkształceń plastycznych charakterystycznych dla stali nierdzewnej. W pracy przedstawiono też mechanizm zniszczenia badanego fragmentu elewacji w przypadku jego przeciążenia.

Źródło:

Archives of Civil Engineering; 2022, 68, 4; 237--252
1230-2945

Pojawia się w:

Archives of Civil Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 34.

Tytuł:

Influence of temperature and hydrogen on fatigue fracture of 10Kh15N27T3V2MR steel

Autorzy:

Hembara, Oksana
Chepil, Olha
Hembara, Taras
Mochulskyi, Volodymyr
Sapuzhak, Yaroslav

Powiązania:

https://bibliotekanauki.pl/articles/949303.pdf

Data publikacji:

2020

Wydawca:

Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej

Tematy:

austenitic steel
hydrogen
kinetic fatigue fracture diagrams
cyclic crack resistance
durability

Opis:

A theoretical and experimental approach to prognosis of fatigue crack growth behavior and determination of the remaining resource of elements of constructions under the influence of temperature and hydrogen is discussed in the paper. Kinetic fatigue fracture diagrams of austenitic steel of 10Kh15N27T3V2MR were experimentally built and analytically described at different temperatures in a neutral environment and in hydrogen. The threshold and critical values of the stress intensity factor (SIF) were found. The durability of a turbine disk was evaluated. It is found that hydrogen reduced the remaining resource of this structural element almost by 2-3 times.

Źródło:

Journal of Theoretical and Applied Mechanics; 2020, 58, 1; 3-15
1429-2955

Pojawia się w:

Journal of Theoretical and Applied Mechanics

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 35.

Tytuł:

Corrosion resistance and microstructure of steel AISI 316L after cold plastic deformation
Odporność korozyjna oraz mikrostruktura stali AISI 316L po odkształceniu plastycznym na zimno

Autorzy:

Rutkowska-Gorczyca, M.
Podrez-Radziszewska, M.
Kajtoch, J.

Powiązania:

https://bibliotekanauki.pl/articles/264053.pdf

Data publikacji:

2009

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH

Tematy:

odporność korozyjna
stal austenityczna
zgniot
corrosion resistance
austenitic steel
cold working

Opis:

In the paper, results of microstructure and hardness examination of cold-worked alloyed steel AISI 316L are presented. In addition, determined was corrosion resistance of the steel in the Ringer solution. Corrosion tests were performed after cold working with 10, 20, 30, 40 and 50% ratio. Potentiodynamic tests included recording polarisation curves as well as determining corrosive potential and corrosive current for various cold working ratios. Cross-sections of the specimens after corrosion tests were observed and analysed using a scanning microscope.
W artykule przedstawiono wyniki badań mikrostruktury oraz twardości stali stopowej AISI 316L odkształconej plastycznie. Przeprowadzono również badania odporności korozyjnej tej stali wyznaczone w roztworze Ringera. Badania przeprowadzono w celu określenia zmian odporności korozyjnej stali, poddanej kształtowaniu plastycznemu na zimno, po uzyskaniu zgniotów 10, 20, 30, 40 oraz 50%. Zakres badań potencjodynamicznych obejmował: rejestrację krzywych polaryzacyjnych, określenie wartości potencjału korozyjnego i prądu korozyjnego przy różnych stopniach zgniotu. Po przeprowadzonych badaniach korozyjnych dokonano obserwacji powierzchni próbek za pomocą mikroskopu skaningowego w celu zarejestrowania powstałych zmian.

Źródło:

Metallurgy and Foundry Engineering; 2009, 35, 1; 35-43
1230-2325
2300-8377

Pojawia się w:

Metallurgy and Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 36.

Tytuł:

Okrętowe stale austenityczne : charakterystyka eksploatacyjna
Ship austenitic steels : operational characteristics

Autorzy:

Jurczak, W.

Powiązania:

https://bibliotekanauki.pl/articles/313756.pdf

Data publikacji:

2017

Wydawca:

Instytut Naukowo-Wydawniczy "SPATIUM"

Tematy:

stal austenityczna
konstrukcja okrętowa
diagnostyka korozyjna
austenitic steel
ship structure
corrosion diagnostics

Opis:

W artykule przedstawiono wyniki badań mechaniczno-elektrochemicznych stali 1.3964 i 1.4301 zastosowanych do konstrukcji współczesnego niszczyciela min. Eksploatacja w środowisku morskim i obciążenia eksploatacyjne, wynikające z pracy kadłuba na fali, powodują powstawanie, w określonych warunkach, korozji naprężeniowej o charakterze elektrochemicznym. Naprężenia w elementach konstrukcji okrętowych i wartość potencjału elektrochemicznego to podstawowe parametry charakteryzujące podatność tych materiałów na korozję, początkowo wżerową, a później międzykrystaliczną. Zastosowanie metody lokalnego pomiaru potencjału elektrochemicznego (Patent PL 216723) podczas eksploatacji i wyznaczenie towarzyszącego mu lokalnego odkształcenia (naprężenia) stanowi podstawę diagnostyki korozyjnej, której zainicjowanie poprzedzone jest pękaniem warstewki tlenkowej, sygnalizowanej obniżeniem wartości potencjału elektrochemicznego. Stal 1.3964 zastosowana na nośne elementy konstrukcyjne kadłuba i nadbudówki posiada wyższe właściwości mechaniczne i lepszą odporność na korozję od stali 1.4301.
The article presents the results of mechanical and electrochemical tests of steel 1.3964 and 1.4301 used for the construction of a modern mine destroyer. Exploitation in the marine environment and the operating loads resulting from the ship’s body movement on the wave cause, under certain conditions, electrochemical stress corrosion. Stresses in shipbuilding components and the value of electrochemical potential are the basic parameters characterizing the susceptibility of these materials to corrosion, initially pitting and later the intercrystalline one. The use of local electrochemical potential measurement method (Patent PL 216723) during operation as well as determination of the accompanying local deformation (stress) form the basis for corrosion diagnostics, which initiation is preceded by the oxide film’s cracking signalized by the reduction of the electrochemical potential. Steel 1.3964 used for the body’s and superstructure’s structural components has higher mechanical and corrosion resistance than steel 1.4301.

Źródło:

Autobusy : technika, eksploatacja, systemy transportowe; 2017, 18, 12; 928-932, CD
1509-5878
2450-7725

Pojawia się w:

Autobusy : technika, eksploatacja, systemy transportowe

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 37.

Tytuł:

The influence of cooling rate during welding on joint properties made of austenitic steel 1.4301
Wpływ chłodzenia podczas spawania na własności złącza stali austenitycznej 1.4301

Autorzy:

Rzeźnikiewicz, Agnieszka
Makielak, Mateusz
Dyner, Piotr

Powiązania:

https://bibliotekanauki.pl/articles/115147.pdf

Data publikacji:

2019

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

stal austenityczna
chłodzenie
spawanie
kwalifikacja technologiczna
austenitic steel
cooling
welding
technology qualification

Opis:

The aim of the research was to investigated the influence of cooling rate during welding on joint properties made of austenitic steel 1.4301. Three test panels were made: cooled in air, cooled by dipping the plate in water and cooled by spraying water from the side of the weld ridge. Non-destructive examinations (visual, penetrative and radiographic) and destructive tests (stretching, bending and impact tests) were made on the test panels. In addition, the ferrite content measurement was carried out. It has been shown that the cooling affects the ferrite content and the impact strength of the joint.
W pracy zbadano wpływ szybkości chłodzenia podczas spawania na własności złącza wykonanego ze stali austenitycznej 1.4301. Wykonano trzy płyty próbne: chłodzoną w powietrzu, chłodzoną poprzez zanurzenie płyty w wodzie oraz chłodzoną poprzez natrysk wody od strony grani. Na płytach próbnych wykonano badania nieniszczące (wizualne, penetracyjne oraz radiograficzne) oraz niszczące (rozciągania, zginania oraz badania udarności). Dodatkowo wykonano pomiar zawartości ferrytu. Wykazano, że szybkość chłodzenia ma wpływ na poziom zawartości ferrytu oraz na udarność złącza.

Źródło:

Welding Technology Review; 2019, 91, 11; 43-49
0033-2364
2449-7959

Pojawia się w:

Welding Technology Review

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 38.

Tytuł:

Analiza propagacji pęknięć półeliptycznych w stali austenitycznej z wykorzystaniem metody spadku potencjału
Analysis of semi-elliptic cracks propagation in austenitic steel using EPD method

Autorzy:

Śnieżek, L.
Mierzyński, J.
Torzewski, J.

Powiązania:

https://bibliotekanauki.pl/articles/210111.pdf

Data publikacji:

2007

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

propagacja pęknięć zmęczeniowych
metoda spadku potencjału
pęknięcia półeliptyczne
fatigue crack propagation
electric potential difference procedures
semi - elliptic cracks

Opis:

W pracy przedstawiono wyniki praktycznego zastosowania metody spadku potencjału do rejestracji zmian kształtu czoła rozwijającego się pęknięcia półeliptycznego w elementach poddanych rozciąganiu i zginaniu. Badania przeprowadzono na próbkach wykonanych ze stali austenitycznej stosowanej do konstrukcji rurociągów rzemysłowych. Warunki badań doświadczalnych ustalono na podstawie pomiarów wartości eksploatacyjnych amplitudy naprężenia w ściance rurociągu. Skalowanie układu pomiarowego, umożliwiające ciągły pomiar półosi elipsy przeprowadzono, wykorzystując metody: optyczną oraz barwienia. Dodatkowo, w celu weryfikacji długości pęknięć na powierzchni próbek, zastosowano tensometry drabinkowe. Uzyskane wyniki pozwalają na adaptację metody spadku potencjału do pomiaru rozwijających się pęknięć półeliptycznych, co w znacznym stopniu ułatwia analizę ich ropagacji.
The paper deals with practical application of the electric potential difference procedures (EPD) in order to record the changes of the front shape of an elliptic crack extending in the specimens under cyclic variable amplitude tension and bending. The material used was the austenitic steel which usually utilizes the pipeline structure construction. Load spectrum performs the transformed exploitive stress amplitudes acting on the pipeline wall. The calibration of the measure system enabling continuous recording of the elliptic semi-axes was made by means either of optical or dyeing methods. Additionally, the crack propagation patters were applied in order to measure surface rack length. The obtained results confirm the capacity of the EPD method which can be used to record the semi-elliptic crack growth. This mentioned method improves significantly the analysis of the crack propagation.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2007, 56, 1; 259-272
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 39.

Tytuł:

Study of the Weldability of Austenitic PH Steel for Power Plants

Autorzy:

Ziewiec, A.

Powiązania:

https://bibliotekanauki.pl/articles/356689.pdf

Data publikacji:

2016

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

power plants
Super 304H
DMV 304HCu steel
X10CrNiCuNb18-9-3 steel
austenitic PH stainless steels
hot cracking

Opis:

The article presents the results of Transvarestraint test of a modern precipitation hardened steel X10CrNiCuNb18-9-3 with copper. For comparison, the results of tests of conventional steel without the addition of copper X5CrNi18-10 are presented. The total length of all cracks and the maximum length of cracks were measured. The study of microstructure (LM, SEM) showed that the austenitic stainless steel X10CrNiCuNb18-9-3 is very prone to hot cracking. After performing the Transvarestraint tests three types of cracks were observed: solidification cracks occurring during crystallization, liquation cracks due to segregation in the heat affected zone (HAZ) and surface cracks. Niobium carbonitrides dispersed in the bands of segregation are the reason of high susceptibility to liquation cracking. Segregation of copper occurring during solidification causes of surface cracking. A combined effect of copper and stresses contributes to formation of hot microcracks. These microcracks propagate to a depth of 20-30 μm.

Źródło:

Archives of Metallurgy and Materials; 2016, 61, 2B; 1109-1114
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 40.

Tytuł:

Structure of 22Cr25NiWCoCu Austenitic Stainless Steel After Ageing

Autorzy:

Sroka, Marek
Zieliński, A.
Puszczało, T.
Sówka, K.
Hadzima, B.

Powiązania:

https://bibliotekanauki.pl/articles/2048810.pdf

Data publikacji:

2022

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

22Cr25NiWCoCu steel
microstructure
precipitates
ageing

Opis:

The 22Cr25NiWCoCu austenitic stainless steel was developed by AB Sandvik Material Technology in Sweden. Due to its high creep strength and good corrosion resistance, this material is well suited for use in superheaters in advanced coal-fired power boilers as well as in other types of steam boilers using various types of fuel. The examined material was subject to long-term ageing for the time of annealing up to 20 000 h at 700 and 750°C. Precipitation processes and microstructure stability as-received and after ageing were investigated. Examination of the microstructure was conducted using scanning electron microscopy. The identification of secondary phases was carried out by X-ray phase composition. Using the results of the investigations of precipitation processes in the microstructure, both within the grains and at the grain boundaries, their statistical analysis was carried out. To illustrate this impact, the following parameters were used: surface area and equivalent diameter of precipitates. Based on the surface area measurements, the percentage of the phase in the reviewed photo’s total area was calculated.

Źródło:

Archives of Metallurgy and Materials; 2022, 67, 1; 175-180
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 41.

Tytuł:

Assessment of mechanical strength and corrosion resistance at variable pH of orthodontic wires

Autorzy:

Augustyn-Nadzieja, Joanna
Szczotok, Agnieszka

Powiązania:

https://bibliotekanauki.pl/articles/1844971.pdf

Data publikacji:

2020

Wydawca:

Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów

Tematy:

tensile test
orthodontic wires
austenitic steel
nitinol (NiTi)
Tiβ
corrosion resistance

Opis:

Orthodontic wires are components of fixed appliances used to perform the necessary tooth movements in the course of the orthodontic treatment. A variety of materials e.g. metals, alloys, polymers and composites are used to produce orthodontic wires. This study examined the mechanical strength and cracks resistance of three different types of wires, i.e. made of: austenitic steel grade AISI 303, NiTi alloy and Tiβ alloy. Corrosion processes are regarded to have a harmful effect on the properties of orthodontic wires, such as their strength, biocompatibility and aesthetic appearance. In this study, we investigated the corrosive behaviour of the wires in the artificial saliva solutions with varied pH simulating the natural oral cavity environment. It was demonstrated that the orthodontic rectangular wires made of austenitic steel grade AISI 303 exhibited the highest tensile strength. The NiTi alloy wires exhibited the best plastic properties of all the examined samples. In the case of electrochemical tests (changes in corrosion potential over a period of 24 h), the wire made of austenitic steel and the NiTi alloy wire reached a stable level of the stationary potential in the acidic environment. For the wires made of Tiβ, the highest stationary potential was observed in the alkaline environment. Additionally, the Tiβ alloy wire revealed the broadest passivation area in the specified potential scope.

Źródło:

Engineering of Biomaterials; 2020, 23, 157; 2-9
1429-7248

Pojawia się w:

Engineering of Biomaterials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 42.

Tytuł:

Carbon Doped Austenitic Stainless Steel Coatings Obtained by Reactive Magnetron Sputtering

Autorzy:

Fryska, S.
Giza, P.
Jedrzejewski, R.
Baranowska, J.

Powiązania:

https://bibliotekanauki.pl/articles/1402218.pdf

Data publikacji:

2015-11

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

68.60.-p
68.60.Bs
68.55.J-
81.15.-z

Opis:

The paper presents the results of investigations of carbon doped austenitic stainless steel coatings (carbon S-phase) obtained by the reactive magnetron sputtering in the reactive atmosphere composed of argon and methane as a carbon source. Stainless steel targets were sputtered under different conditions. During the experiments the argon to methane proportion varied within a range 11/2-7/6. The other parameters such as temperature, pressure, sputtering power, etc. were kept constant. The phase composition was determined using the X-ray diffraction. Electron probe microanalysis (energy dispersive spectroscopy and wavelength dispersive spectroscopy) and glow discharge optical emission spectrometry techniques were used to study element composition of the coatings. Microstructure was investigated by scanning electron microscopy. It was found that varying the methane volume in the reactive atmosphere, it is possible to control the lattice parameter of the carbon S-phase.

Źródło:

Acta Physica Polonica A; 2015, 128, 5; 879-882
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 43.

Tytuł:

Application of the EBSD method on explosively welded joins of Al ‒ austenitic CrNi steel bimetal
Zastosowanie metody EBSD na bimetalicznych polączeniach spawanych wybuchowo Al - austenitycznej stali CrNi

Autorzy:

Lokaj, Jan
Sahul, Miroslav
Sahul, Martin
Čaplovic, Lubomir

Powiązania:

https://bibliotekanauki.pl/articles/27787810.pdf

Data publikacji:

2022

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Przemysłu Organicznego

Tematy:

EBFS method
explosive welding
aluminium
austenitic steel
metoda EBDS
zgrzewanie wybuchowe
stal austenityczna

Opis:

Electron Backscatter Diffraction (EBSD) is a scanning electron microscope (SEM) based technique, which enables a sample’s microstructure to be analysed, visualised and quantified. The EBSD method together with associated techniques provides useful information how to interpret the obtained results. Microstructure is the internal structure of a material investigated on the microscopic scale. It is of interest because a material’s internal features (i.e. structure) influences its properties and behaviour. The EBSD method has become the primary tool for characterising microstructures in most metals, alloys, composites and ceramics. The range of applications is numerous, from rapid measurement of grain size and texture in metal sheets, welded joints etc. Many of these materials are relatively simple to analyse using EBSD, but advanced tools such as high-resolution pattern correlation approaches can be applied to improve our understanding of these materials [1]. This method has been applied to investigace the structure of Al ‒ austenitic CrNi steel. Only partial results as for the EBSD method will be given here.
Detektor EBSD (dyfrakcja elektronów wstecznie rozproszonych) zainstalowany w skaningowym mikroskopie elektronowym (SEM) umożliwia analizę, wizualizację i ocenę ilościową mikrostruktury próbki. Metoda EBSD wraz z powiązanymi technikami dostarcza przydatnych informacji, umożliwiających interpretację wyników. Mikrostruktura to wewnętrzna struktura materiału badana w skali mikroskopowej. Jest ona interesująca, ponieważ wewnętrzne cechy materiału (tj. struktura) determinują jego właściwości. Metoda EBSD stała się podstawowym narzędziem do charakteryzowania mikrostruktur w większości metali, stopów, kompozytów i ceramiki. Zakres zastosowań jest szeroki, obejmujący m.in. szybki pomiaru wielkości ziarna i tekstury w blachach, złączach spawanych itp. Wiele z tych materiałów można stosunkowołatwo poddać analizie EBSD, ale zaawansowane narzędzia, takie jak metody operate o analizę obrazu, można zastosować w celu lepszego poznania struktury tych materiałów [1]. Metodę tę zastosowano do badania struktury bimetalu typu aluminium-stal austenityczna CrNi. W tym miejscu omówione jedynie częściowe wyniki analizy EBSD.

Źródło:

Materiały Wysokoenergetyczne; 2022, 14(S); 146--153
2083-0165

Pojawia się w:

Materiały Wysokoenergetyczne

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 44.

Tytuł:

Estimation of defect depth in steel plate using lock-in IR thermography

Autorzy:

Zimnoch, M.
Oliferuk, W.
Maj, M.

Powiązania:

https://bibliotekanauki.pl/articles/386540.pdf

Data publikacji:

2010

Wydawca:

Politechnika Białostocka. Oficyna Wydawnicza Politechniki Białostockiej

Tematy:

estymacja
podczerwień
fale termiczne
stal austenityczna
estimation
infrared thermography
thermal waves
austenitic steel

Opis:

The paper deals with the application of lock-in active infrared thermography as one of the non-contact and nondestructive techniques used for defect depth estimation. Preliminary research was done by testing a specimen made of austenitic steel plate with artificially created defects, i.e. flat-bottom holes. The obtained dependence between defect depth and phase shift was presented for different frequencies of “thermal waves” generated inside the sample. The experiment was carried out to determine the application of the lock-in thermography approach in testing materials with a high thermal diffusivity.

Źródło:

Acta Mechanica et Automatica; 2010, 4, 4; 106-109
1898-4088
2300-5319

Pojawia się w:

Acta Mechanica et Automatica

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 45.

Tytuł:

Effects of Cr - Ni 18/9 austenitic cast steel modification by mischmetal

Autorzy:

Gajewski, M.
Kasińska, J.

Powiązania:

https://bibliotekanauki.pl/articles/380312.pdf

Data publikacji:

2012

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

staliwo austenityczne
modyfikacja
miszmetal
właściwości mechaniczne
korozja międzykrystaliczna
austenitic cast steel
modification
mechanical properties
intergranular corrosion

Opis:

This paper presents the results of Cr - Ni 18/9 austenitic cast steel modifications by mischmetal. The study was conducted on industrial melts. Cast steel was melted in an electric induction furnace with a capacity of 2000 kg and a basic lining crucible. The mischmetal was introduced into the ladle during tapping of the cast steel from the furnace. The effectiveness of modification was examined with the carbon content of 0.1% and the presence of \delta ferrite in the structure of cast steel stabilized with titanium. The changes in the structure of cast steel and their effect on mechanical properties and intergranular corrosion were studied. It was found that rare earth metals decrease the sulfur content in cast steel and above all, they cause a distinct change in morphology of the \delta ferrite and non-metallic inclusions. These changes have improved mechanical properties. R02, Rm, and A5 and toughness increased significantly. There was a great increase of the resistance to intergranular corrosion in the Huey test. The study confirmed the high efficiency of cast steel modification by mischmetal in industrial environments. The final effect of modification depends on the form and manner of placing mischmetal into the liquid metal and the melting technology, ie the degree of deoxidation and desulfurization of the metal in the furnace.

Źródło:

Archives of Foundry Engineering; 2012, 12, 4; 47-52
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 46.

Tytuł:

Analiza wybranych właściwości materiałów stosowanych na instrumentarium chirurgiczne
Analysis of selected properties of materials used for surgical instruments

Autorzy:

Chrobak, Aleksandara
Łagan, Sylwia

Powiązania:

https://bibliotekanauki.pl/articles/2201497.pdf

Data publikacji:

2020

Wydawca:

Politechnika Śląska. Katedra Biomechatroniki

Tematy:

stal austenityczna
stal martenzytyczna
korozja
zwilżalność powierzchni
austenitic steel
martensitic steel
corrosion
surface wettability

Opis:

Celem niniejszej pracy była analiza porównawcza wybranych właściwości materiałów metalicznych wykorzystywanych na narzędzia chirurgiczne. Przeprowadzono badania określające odporność na korozję (metodą grawimetryczną), zwilżalność powierzchni (metodą kropli siedzącej) oraz analizę swobodnej energii powierzchniowej z wykorzystaniem dwóch modeli analitycznych: Owensa-Wendta oraz van Ossa-Chauhury-Gooda. W wyniku badań wskazano właściwości stali austenitycznej i martenzytycznej determinujące dobór materiału do produkcji instrumentarium chirurgicznego.
The aim of this work was comparative analysis of selected properties of metallic materials used for surgical instruments. The studies have been conducted to determine the corrosion resistance (gravimetric method), surface wettability (sitting drop method) and free surface energy analysis using two analytical models: Owens-Wendt’s and van Oss-Chauhury-Good’s. As a result, the properties of austenitic and martensitic steel determining the choice of material for the production of surgical instruments have been indicated.

Źródło:

Aktualne Problemy Biomechaniki; 2020, 19; 5--11
1898-763X

Pojawia się w:

Aktualne Problemy Biomechaniki

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 47.

Tytuł:

Environmental Degradation of Dissimilar Austenitic 316L and Duplex 2205 Stainless Steels Welded Joints

Autorzy:

Topolska, S.
Łabanowski, J.

Powiązania:

https://bibliotekanauki.pl/articles/356004.pdf

Data publikacji:

2017

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

duplex steel 2205
austenitic steel 316L
welded joints
stress corrosion cracking (SCC)
hydrogen embrittlement

Opis:

The paper describes structure and properties of dissimilar stainless steels welded joints between duplex 2205 and austenitic 316L steels. Investigations were focused on environmentally assisted cracking of welded joints. The susceptibility to stress corrosion cracking (SCC) and hydrogen embrittlement was determined in slow strain rate tests (SSRT) with the strain rate of 2.2 × 10⁻⁶ s⁻¹. Chloride-inducted SCC was determined in the 35% boiling water solution of MgCl₂ environment at 125°C. Hydrogen assisted SCC tests were performed in synthetic sea water under cathodic polarization condition. It was shown that place of the lowest resistance to chloride stress corrosion cracking is heat affected zone at duplex steel side of dissimilar joins. That phenomenon was connected with undesirable structure of HAZ comprising of large fractions of ferrite grains with acicular austenite phase. Hydrogen assisted SCC tests showed significant reduction in ductility of duplex 2205 steel while austenitic 316L steel remains almost immune to degradation processes. SSR tests of dissimilar welded joints revealed a fracture in the area of austenitic steel.

Źródło:

Archives of Metallurgy and Materials; 2017, 62, 4; 2107-2112
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 48.

Tytuł:

Analysis of residual stress in 1.4539 austenitic steel joints welded with TIG method
Analiza naprężeń własnych w połączeniach ze stali austenitycznej 1.4539 wykonanych metodą TIG

Autorzy:

Nasiłowska, Barbara
Bogdanowicz, Zdzisław
Mońka, Grzegorz
Tomaszewski, Rafał
Zdunek, Joanna

Powiązania:

https://bibliotekanauki.pl/articles/208921.pdf

Data publikacji:

2019

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

residual stress
welded joints
TIG
Knoop microhardness
shot peening
naprężenia własne
połączenia spawane
mikrotwardość Knoopa
kulowanie

Opis:

The article compares the results of tests of residual stress determined based on Knoop microhardness measurements and obtained experimentally with the use of an x-ray diffractometer. Distribution of residual stress in the weld after strengthening of the surface layer, resulting from shot peening, was specified. A method of residual stress determination proposed by Oppel, based on Knoop microhardness distribution, was applied. An analysis of residual stress of 1.4539 austenitic steel welded joints, made with the use of TIG method and additionally strengthened with shot peening of the surface, showed good agreement of the results obtained both with the sin²ψ method and based on the microhardness measurement. The highest compression stress has occurred in a so-called Belayev point, approximately of 35 ÷ 40 μm from the surface.
W artykule porównano wyniki badań naprężeń własnych wyznaczonych na podstawie pomiarów mikrotwardości Knoopa i doświadczalnie przy użyciu dyfraktometru rentgenowskiego. Określono rozkład naprężeń własnych w spoinie po umocnieniu warstwy wierzchniej w wyniku kulowania. Zastosowano metodę wyznaczania naprężeń własnych zaproponowanych przez Oppela na podstawie rozkładu mikrotwardości Knoopa. Analiza naprężeń własnych połączeń spawanych ze stali austenitycznej 1.4539 wykonanych metodą TIG dodatkowo umocnionych przez kulowanie powierzchni wykazała dobrą zgodność wyników uzyskanych za pomocą metody sin²ψ oraz na podstawie pomiaru mikrotwardości. Największe naprężenia ściskające występowały w tzw. punkcie Bielajewa ok. 35 ÷ 40 μm od powierzchni.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2019, 68, 1; 101-110
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 49.

Tytuł:

Modelling of microstructure changes during hot deformation using cellular automata
Modelowanie za pomocą automatów komórkowych zmian mikrostruktury podczas odkształcenia na gorąco

Autorzy:

Kuc, D.
Gawąd, J.

Powiązania:

https://bibliotekanauki.pl/articles/351296.pdf

Data publikacji:

2011

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

modelowanie
automaty komórkowe
stal austenityczna
mikrostruktura
modelling
cellular automata
austenitic steel
flow stress
microstructure

Opis:

The paper is focused on an application of the cellular automata (CA) method to description of microstructure changes in continuous deformation condition. The model approach consists of Cellular Automata model of microstructure development and the thermal-mechanical finite element (FE) code. Dynamic recrystallization phenomenon is taken into account in 2D CA model which takes advantage of explicit representation of microstructure, including individual grains and grain boundaries. Flow stress is the main material parameter in mechanical part of FE and is calculated on the basis of average dislocation density obtained from the CA model. The results obtained from the model were validated with the experimental data. In the present study, austenitic steel X3CrNi18-10 was investigated. The examination of microstructure for the initial and final microstructures was carried out, using light microscopy, transmission electron microscopy and EBSD technique. Compression forces were recorded during the tests and flow stresses were determined using the inverse method.
W artykule przedstawiono model, który opisuje zmiany struktury w warunkach ciągłego odkształcenia z wykorzystaniem automatów komórkowych. Opracowane rozwiązanie wykorzystuje połączenie modelu automatów komórkowych (ang. Cellular Automata, CA) zmian mikrostruktury i kodu elementów skończonych rozwiązującego problem termomechaniczny. Do opracowania modelu zmian mikrostruktury wykorzystano dwuwymiarową siatkę automatów komórkowych. Model zmian naprężenia uplastyczniającego bazuje na średniej gęstości dyslokacji wyliczonej poprzez homogenizację gęstości dyslokacji w siatce automatów komórkowych. Opracowany model zweryfikowano w oparciu o wyznaczone krzywe płynięcia dla stali austenitycznej X3CrNi18-10 i badania mikrostruktury z wykorzystaniem mikroskopii świetlnej, transmisyjnej mikroskopii elektronowej oraz techniki EBSD. Naprężenie uplastyczniające zostało wyznaczone w oparciu o metodę obliczeń odwrotnych na podstawie danych uzyskanych z prób osiowosymetrycznego ściskania.

Źródło:

Archives of Metallurgy and Materials; 2011, 56, 2; 523-532
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 50.

Tytuł:

Wpływ kulowania na strukturę, mikrotwardość i naprężenia własne stali austenitycznej 1.4539
Shot-peening effect on the structure, microhardness, and compressive stresses of the austenitic steel 1.4539

Autorzy:

Nasiłowska, B.
Bogdanowicz, Z.
Brzeziński, M.
Mońka, G.
Zasada, D.

Powiązania:

https://bibliotekanauki.pl/articles/210396.pdf

Data publikacji:

2015

Wydawca:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego

Tematy:

stal austenityczna 1.4539
naprężenia własne
metoda Waismana-Philipsa
austenitic steel 1.4539
residual stresses
Waisman-Philips’a method

Opis:

W artykule przedstawiono wpływ kulowania pneumatycznego (shot peeningu) na strukturę, mikrotwardość i naprężenia własne próbek ze stali austenitycznej 1.4539. Badania wykazały umocnienie warstwy wierzchniej i wytworzenie naprężeń własnych ściskających w warstwach podpowierzchniowych kulowanych elementów.
This article presents shot-peening effect on the structure, microhardness, and compressive stresses of the austenitic steel 1.4539. The research shows strengthening of the top layer and the formation of compressive stresses in the subsurface layers of the shot-peening elements.

Źródło:

Biuletyn Wojskowej Akademii Technicznej; 2015, 64, 2; 103-110
1234-5865

Pojawia się w:

Biuletyn Wojskowej Akademii Technicznej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 51.

Tytuł:

Prediction of Ferrite Content in Austenitic Cr-Ni Steel Castings During Production

Autorzy:

Senberger, J.
Pernica, V.
Kana, V.
Zadera, A.

Powiązania:

https://bibliotekanauki.pl/articles/380650.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

solidification
metallography
austenitic steel
austenite
ferrite
DeLong diagram
krzepnięcie
metalografia
stal austenityczna
austenit
ferryt
diagram DeLong

Opis:

Determination of the ferrite content in austenitic steels, which solidified under defined conditions. Ferrite content in austenitic matrix was determined from samples with wall thickness of 60 mm. Measured ferrite contents served to propose the regression equations for the calculation of the ferrite content in steels with Cr content of 18 up to 22 % and Ni of 9 up to 11 %. An additional regression equation was proposed for steels with a higher Ni content. The proposed regression equations have been checked up on the operating melts. In conclusion, the ferrite content in the axis of the casting of wall thickness of 500 mm has been calculated and it was compared to the ferrite determined in the usual way from the cast-on test.

Źródło:

Archives of Foundry Engineering; 2018, 18, 3; 91-94
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 52.

Tytuł:

The Mechanism of Corrosion of Steel 304L in the Presence of Copper in Industrial Installations
Mechanizm korozji stali austenitycznej 304L w obecności miedzi w instalacjach przemysłowych

Autorzy:

Lachowicz, M. M.
Lachowicz, M. B.

Powiązania:

https://bibliotekanauki.pl/articles/354474.pdf

Data publikacji:

2015

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic steel
copper
pitting corrosion
mechanism of corrosion
stal austenityczna
miedź
korozja wżerowa
mechanizm korozji

Opis:

This paper presents the mechanism of corrosion of austenitic steel in the presence of copper. It has been found that when corrosion occurs, the presence of copper in the corrosive solution in the neighbourhood of austenitic steel results in the intensification of the corrosion processes. In the macroscopic scale, austenitic steel constitutes a cathode, but since copper precipitates can deposit on it, the steel can locally pass to the active state and become an anode in the places where copper deposited, which leads to its local corrosion due to galvanic corrosion.
W pracy przedstawiono mechanizm korozji stali austenitycznej w obecności miedzi. Stwierdzono, że w przypadku wystąpienia korozji stali austenitycznej w obecności miedzi, prowadzi to do intensyfikacji zachodzących procesów korozyjnych. W skali makroskopowej stal austenityczna stanowi katodę, jednak możliwość osadzania się na niej wydzieleń miedzi powoduje, że lokalnie może ona przejść w stan aktywny i w tych miejscach stać się anodą, co prowadz do jej lokalnej korozji wskutek wystąpienia korozji galwanicznej.

Źródło:

Archives of Metallurgy and Materials; 2015, 60, 4; 2657-2662
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 53.

Tytuł:

Martensite Content and Mechanical Properties of Uniaxial Tension AlSi 304L Steel

Autorzy:

Opiekun, Z. A.

Powiązania:

https://bibliotekanauki.pl/articles/383243.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic steel
uniaxial tension
martensite phase
mechanical properties
stal austenityczna
naprężenie jednoosiowe
faza martenzytyczna
właściwości mechaniczne

Opis:

The paper presents the effect of plastic strain occurring at room temperature in annealed samples of AlSi 304L austenitic chromium-nickel steel on content of strain-induced α′ martensite in its structure. The strain was introduced by uniaxial tension with constant strain rate of about 0.083 mm/s. It has been demonstrated that the share of &alpha′ martensite in microstructure of the steel determined by means of Feritscope FMP30 in the time at uniaxial tension.

Źródło:

Archives of Foundry Engineering; 2014, 14, 1 spec.; 151-154
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 54.

Tytuł:

Laser welding of panel joints of stainless steel heat exchangers
Spawanie laserowe złączy panelowych wymienników ciepła ze stali nierdzewnej

Autorzy:

Lisiecki, Aleksander
Wójciga, Piotr
Kurc-Lisiecka, Agnieszka
Barczyk, Michał
Krawczyk, Sonia

Powiązania:

https://bibliotekanauki.pl/articles/115055.pdf

Data publikacji:

2019

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

spawanie laserowe
złącze panelowe
stal nierdzewna
stal austenityczna
laser welding
pillow plate
stainless steel
austenitic steel

Opis:

Results of study on the laser welding process of pillow plates heat exchangers are presented in the article. The influence of basic parameters of CO2 laser welding on the quality of overlap joints of AISI 304 stainless steel plates 2.0 and 4.0 mm thick was determined. The range of optimal parameters of welding, providing the highest quality and high mechanical performance of the test joints was determined. The technological conditions elaborated during the study were applied for manufacturing of the real pillow plates heat exchangers with dimensions of 1.5x1.5 m.
W artykule przedstawiono wyniki badań procesu spawania laserowego złączy panelowych wymienników ciepła. Określono wpływ podstawowych parametrów spawania laserem gazowym CO2 na jakość złączy zakładkowych blach ze stali austenitycznej AISI 304 o grubości 2,0 i 4,0 mm. Określono zakres optymalnych parametrów spawania zapewniających najwyższą jakość i wysoką wytrzymałość złączy. Opracowane warunki technologiczne spawania laserowego zastosowano do wytwarzania partii panelowych wymienników ciepła o wymiarach 1,5x1,5 m.

Źródło:

Welding Technology Review; 2019, 91, 7; 7-19
0033-2364
2449-7959

Pojawia się w:

Welding Technology Review

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 55.

Tytuł:

The Analysis of AISI A3 Type Ferritic-Austenitic Cast Steel Crystallization Mechanism

Autorzy:

Stradomski, G.

Powiązania:

https://bibliotekanauki.pl/articles/380395.pdf

Data publikacji:

2017

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

duplex cast steel
solidification
numerical methods
DTA
peritectic reaction
sigma phase
staliwo typu duplex
krzepnięcie
metoda numeryczna
reakcja perytektyczna
faza sigma

Opis:

High-alloy corrosion-resistant ferritic-austenitic steels and cast steels are a group of high potential construction materials. This is evidenced by the development of new alloys both low alloys grades such as the ASTM 2101 series or high alloy like super or hyper duplex series 2507 or 2707 [1-5]. The potential of these materials is also presented by the increasing frequency of sintered components made both from duplex steel powders as well as mixtures of austenitic and ferritic steels [6, 7]. This article is a continuation of the problems presented in earlier works [5, 8, 9] and its inspiration were technological observed problems related to the production of duplex cast steel. The analyzed AISI A3 type cast steel is widely used in both wet exhaust gas desulphurisation systems in coal fired power plants as well as in aggressive working environments. Technological problems such as hot cracking presented in works [5, 8], with are effects of the rich chemical composition and phenomena occurring during crystallization, must be known to the technologists. The presented in this work phenomena which occur during the crystallization and cooling of ferritic-austenitic cast steel were investigated using numerical methods with use of the ThermoCalc and FactSage® software, as well with use of experimental thermal-derivative analysis.

Źródło:

Archives of Foundry Engineering; 2017, 17, 3; 229-233
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 56.

Tytuł:

Determination of dynamic characteristics of austenitic steel to be utilized in FEM simulation and its verification
Wyznaczanie charakterystyki dynamicznej stali austenitycznej na potrzeby symulacji mes i jej weryfikacja

Autorzy:

Szturomski, B.
Świątek, K.
Jurczak, W.

Powiązania:

https://bibliotekanauki.pl/articles/222122.pdf

Data publikacji:

2018

Wydawca:

Akademia Marynarki Wojennej. Wydział Dowodzenia i Operacji Morskich

Tematy:

dynamic characteristics of material
drop-weight type impact hammer
rotary hammer
Johnson-Cook constitutive model
dynamiczna charakterystyka materiału
młot rotacyjny
młot opadowy
model konstytutywny Johnsona-Cooka

Opis:

This paper presents the dynamic mechanical properties of austenitic steel with improved durability, which is used in the construction of hulls of minesweepers, mine destroyers, submarines and other naval vessels. Dynamic tensile tests performed on the steel samples using a rotary hammer with a strain rate of up to 1000 s-1 allowed determination of elastic-plastic characteristics of the material in the form of a polynomial of Johnson-Cook constitutive model, taking into account the influence of strain rate and temperature. A characteristic of this type is utilized in numerical calculations in the CAE software. The obtained characteristics were experimentally verified by bending tests of flat samples with a drop-weight type impact hammer. Simultaneously numerical calculations were performed in order to compare the deformation state.
W artykule przedstawiono dynamiczne właściwości mechaniczne stali austenitycznej o podwyż-szonej wytrzymałości, która jest wykorzystywana do budowy kadłubów trałowców, niszczycieli min, okrętów podwodnych oraz innych jednostek wojennych. Na podstawie dynamicznego roz-ciągania próbek na młocie rotacyjnym w zakresie prędkości odkształcenia do 1000 s-1 opracowano sprężysto-plastyczną charakterystykę materiału w formie wielomianu w postaci modelu konstytutywnego Johnsona-Cooka uwzgledniającego prędkość odkształcenia i wpływ temperatury. Charakterystyka tego typu wykorzystywana jest w obliczeniach numerycznych w programach CAE. Otrzymaną charakterystykę zweryfikowano, wykonując eksperyment udarowego zgięcia płaskownika na młocie opadowym, dla którego równolegle wykonano obliczenia numeryczne, porównując stan deformacji.

Źródło:

Zeszyty Naukowe Akademii Marynarki Wojennej; 2018, R. 59 nr 2 (213), 2 (213); 35-42
0860-889X

Pojawia się w:

Zeszyty Naukowe Akademii Marynarki Wojennej

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 57.

Tytuł:

Laser-borided composite layer produced on austenitic 316L steel

Autorzy:

Mikołajczak, D.
Kulka, M.
Makuch, N.
Dziarski, P.

Powiązania:

https://bibliotekanauki.pl/articles/1203965.pdf

Data publikacji:

2016

Wydawca:

Politechnika Poznańska. Wydawnictwo Politechniki Poznańskiej

Tematy:

laser boriding
austenitic steel
microstructure
hardness
wear resistance
borowanie laserowe
stal austenityczna
mikrostruktura
twardość
odporność na zużycie

Opis:

Austenitic 316L steel is well-known for its good resistance to corrosion and oxidation. Therefore, this material is often used wherever corrosive media or high temperatures are to be expected. The main drawback of this material is very low hardness and low resistance to mechanical wear. In this study, the laser boriding was used in order to improve the wear behavior of this material. As a consequence, a composite surface layer was produced. The microstructure of laser-borided steel was characterized by only two zones: re-melted zone and base material. In the re-melted zone, a composite microstructure, consisting of hard ceramic phases (borides) and a soft austenitic matrix, was observed. A significant increase in hardness and wear resistance of such a layer was obtained.

Źródło:

Archives of Mechanical Technology and Materials; 2016, 36; 35-39
2450-9469

Pojawia się w:

Archives of Mechanical Technology and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 58.

Tytuł:

The Role of Carbon in the Mechanism of Ferritic-Austenitic Cast Steel Solidification

Autorzy:

Stradomski, G.

Powiązania:

https://bibliotekanauki.pl/articles/381622.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

duplex cast steel
microstructure
hot crack
primary structure
staliwo typu duplex
mikrostruktura
pękanie
struktura

Opis:

The paper presents the results of research on the microstructure of GX2CrNiMoCuN25-6-3-3 and GX2CrNiMoCuN25-6-3 cast steels with a varying carbon content. The cause for undertaking the research were technological problems with hot cracking in bulk castings of duplex cast steel with a carbon content of approx. 0.06% and with 23% Cr, 8.5% Ni, 3% Mo and 2.4% Cu. The research has shown a significant effect of increased carbon content on the ferrite and austenite microstructure morphology, while exceeding the carbon content of 0.06% results in a change of the shape of primary grains from equiaxial to columnar.

Źródło:

Archives of Foundry Engineering; 2014, 14, 3; 83-86
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 59.

Tytuł:

Comparison of corrosion resistance in physiological saline solution of two austenitic stainless steels – 316LV and REX734

Autorzy:

Romańczuk, E.
Oksiuta, Z.

Powiązania:

https://bibliotekanauki.pl/articles/387266.pdf

Data publikacji:

2017

Wydawca:

Politechnika Białostocka. Oficyna Wydawnicza Politechniki Białostockiej

Tematy:

REX734 austenitic stainless steel
316 LV austenitic stainless steel
potentiodynamic corrosion tests
XRD analysis
SEM observation

Opis:

In this work two austenitic stainless steels, REX734 and 316LV were tested in terms of their microstructure and corrosion properties. The REX734 is a newer generation stainless steel, with modified chemical composition, in comparison to the 316LV grade. Potentiodynamic study of corrosion resistance was conducted in physiological saline solution (0.9% NaCl solution). In spite of the similarities of microstructure, grain size and phase structure in both materials, the corrosion tests revealed that the REX734, with lower nickel and higher nitrogen content, had better corrosion resistance than 316LV. Repassivation potential in the REX734 was almost six times higher than for the 316LV steel. Superior corrosion resistance of the REX734 steel was also confirmed by surface observations of both materials, since bigger and more densely distributed pits were detected in 316LV alloy.

Źródło:

Acta Mechanica et Automatica; 2017, 11, 2; 91-95
1898-4088
2300-5319

Pojawia się w:

Acta Mechanica et Automatica

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 60.

Tytuł:

Trwałość eksploatacyjna i rozporządzalna trwałość resztkowa stali T321H
The life time and disposable residual life of T321H steel

Autorzy:

Purzyńska, H.
Zieliński, A.
Dobrzański, J.
Hernas, A.

Powiązania:

https://bibliotekanauki.pl/articles/182132.pdf

Data publikacji:

2015

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica

Tematy:

struktura
właściwości mechaniczne
stal austenityczna T321H
structure
mechanical properties
austenitic steel T321H

Opis:

Podstawowym celem prowadzonych badań stali T321H w stanie wyjściowym i po różnych czasach pracy było zbudowanie modelu umożliwiającego przewidywanie trwałości eksploatacyjnej materiału elementów części ciśnieniowej kotła po długotrwałej eksploatacji w warunkach pełzania wykonanych z tej stali. W pracy wykonano badania pełzania stali austenitycznej T321H przeznaczonej na elementy kotłów o parametrach nadkrytycznych. Przeprowadzono badania właściwości wytrzymałościowych oraz analizę struktury badanej stali w stanie wyjściowym oraz po długotrwałej ekspozycji w warunkach pełzania (tzn. po ok. 200000 godzin pracy). Wykonane badania umożliwiły wstępne opracowanie klasyfikacji zmian mikrostruktury i rozwoju procesów wydzieleniowych. Zastosowana metodyka oraz uzyskane wyniki badań będą w przyszłości wykorzystane w budowaniu modeli umożliwiających przewidywanie trwałości eksploatacyjnej dla innych materiałów o strukturze austenitycznej.
The main purpose of testing T321H steel in its initial state and after different service times was to build a model to allow forecasting the lifetime of the material of boiler pressure section components made from this steel after longterm service under creep conditions. In this paper, creep tests of T321H austenitic steel for the elements of boilers with supercritical parameters were carried out. The investigations of mechanical properties and structure analysis of the tested steel in initial state and after long-term exposure to creep conditions (i.e. after approx. 20 000 h service) were performed. These tests enabled the preliminary elaboration of the classification of changes in microstructure and development of precipitation processes. In the future, the applied methodology and obtained test results will be used in building models to enable forecasting lifetime for other materials with austenitic structure.

Źródło:

Prace Instytutu Metalurgii Żelaza; 2015, T. 67, nr 1, 1; 44-52
0137-9941

Pojawia się w:

Prace Instytutu Metalurgii Żelaza

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 61.

Tytuł:

X-Ray Phase Analysis of Nitrided Layers of X2CrNiMo17-12-2 Austenitic Steel
Rentgenowska analiza fazowa warstw azotowanych stali austenitycznej X2CrNiMo17-12-2

Autorzy:

Frączek, T.
Olejnik, M.
Pilarska, M.

Powiązania:

https://bibliotekanauki.pl/articles/354335.pdf

Data publikacji:

2015

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

X-ray phase analysis
nitrided layers
stal austeniczna X2CrNiMo17-12-2
rentgenowska analiza fazowa
warstwy azotowane
stal austenityczna X2CrNiMo17-12-2

Opis:

This work presents the results of diffraction analyses carried out using X-ray phase analyses (XRD and GIXRD) of nitrided layers of X2CrNiMo17-12-2 austenitic steel. Plasma nitriding process was c arried out in the temperature range of 325 ÷ 400 °C and time of 2 ÷ 4 h. Hydrogen-nitrogen plasma was used as reactive atmosphere (H2 75% + N2 25%) with pressure of 150 Pa. On the basis of the X-ray analyses it was stated that the obtained nitrided layers consisted of a subsurface layer of chromium nitrides and a zone of nitrogen saturated austenite.
W pracy zaprezentowano wyniki badań strukturalnych metodą rentgenowskiej analizy fazowej (XRD i GIXRD) warstw azotowanych na podłożu stali austenitycznej X2CrNiMo17-12-2. Proces azotowania jarzeniowego przeprowadzono w zakresie temperatur 325 ÷ 400 °C i czasu 2 ÷ 4 h. Atmosferę reaktywną stanowiła plazma wodorowo-azotowa (H2 75% + N2 25%) o ciśnieniu 150 Pa. Na podstawie badań rentgenowskich stwierdzono, że otrzymane warstwy azotowane składają się z przypowierzchniowej warstwy azotków chromu oraz strefy austenitu przesyconego azotem. Zastosowanie ekranu aktywnego spowodowało wzrost głębokości dyfuzji azotu w głąb azotowanej powierzchni oraz zwiększyło jego koncentrację w fazie austenitu przesyconego azotem.

Źródło:

Archives of Metallurgy and Materials; 2015, 60, 3A; 2005-2012
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 62.

Tytuł:

CO2 laser spot welding of thin sheets AISI 321 austenitic stainless steel

Autorzy:

Shehab, A. A.
Nawi, S. A.
Al-Rubaiy, A. AAG
Hammoudi, Z.
Hafedh, S. A.
Abass, M. H.
Alali, M. S.
Ali, S. D.

Powiązania:

https://bibliotekanauki.pl/articles/1818484.pdf

Data publikacji:

2020

Wydawca:

Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach

Tematy:

thin sheet metal
austenitic stainless steel
CO2 CW LSW
mechanical properties
welding profile
FE analysis
blachy cienkie
stal austenityczna nierdzewna
właściwości mechaniczne
profil spawalniczy
analiza elementów skończonych

Opis:

Purpose: The present work aims to investigate the influence of CO2 laser spot welding (LSW) parameters on welding profile and mechanical properties of lap joint of AISI 321 thin sheet metals, and analyze the welding profile numerically by finite element (FE) method. Design/methodology/approach: The weld carried out using 150 W CO2 continues wave laser system. The impact of exposure time and laser power on the welding profile was investigated using an optical microscope. Microhardness and tensile strength tests were used to evaluate the mechanical properties of the joint. Ansys software was utilized to simulate the welding profile numerically. Findings: The results revealed that 2 s exposure time and 50 W power have led to uniform welding profile and highest shear force (340 N), lower hardness gradient across the heat affected zone (HAZ) and fusion zone (FZ). Finite element (FE) analysis of the welding profile showed good agreement with experimental analysis. Research limitations/implications: The selection of laser spot welding parameters for thin sheet metal was critical due to the probability of metal vaporisation with extra heat input during welding. Practical implications: Laser welding of AISI 321 steel is used in multiple industrial sectors such as power plants, petroleum refinement stations, pharmaceutical industry, and households. Thus, selecting the best welding parameters ensures high-quality joint. Originality/value: The use of CO2 laser in continuous wave (CW) mode instead of pulse mode for spot welding of thin sheet metal of AISI 321 austenitic stainless steel consider a real challenge because of the difficulty of control the heat input via proper selection of the welding parameters in order to not burn the processed target. Besides, the maintenance is easier and operation cost is lower in continuous CO2 than pulse mode.

Źródło:

Archives of Materials Science and Engineering; 2020, 106, 2; 68--77
1897-2764

Pojawia się w:

Archives of Materials Science and Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 63.

Tytuł:

Numerical Modelling of Micro-Stresses in Carbonised Austenitic Cast Steel Under Rapid Cooling Conditions

Autorzy:

Tuleja, J.
Zatorski, Z.

Powiązania:

https://bibliotekanauki.pl/articles/353044.pdf

Data publikacji:

2017

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

finite element method
micro-stresses
austenitic cast steel
carbides
fracture

Opis:

The paper presents a method of the numerical modelling of micro-stresses in carbonised austenitic cast steel being developed during rapid cooling due to differences in the values of thermal expansion coefficients for this material phases – carbides and austenitic matrix. Micro-stresses are indicated as the main cause of crack initiation in the tooling elements of carburising furnaces being mainly made of austenitic cast steel. A calculation model of carbonised and thermally fatigued austenitic cast steel was developed based on the microstructure images obtained using light microscopy techniques and the phase composition evaluated with the X-ray diffraction method. The values of the stress tensor components and the reduced stress in the complex models of test material structure were determined numerically by the finite element method. The effort analysis was performed and the areas where development of cracks is to be expected were identified, which was experimentally confirmed.

Źródło:

Archives of Metallurgy and Materials; 2017, 62, 2A; 635-641
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 64.

Tytuł:

Analiza zmian mikrostruktury stali dla energetyki poddanych cyklicznym zmianom temperatury i/lub obciążenia, przy wykorzystaniu możliwości nowoczesnego dylatometru odkształceniowego
Analysis of microstructure changes of steel for power plant applications subjected to cyclical temperature and/or mechanical load variations, by means of modern deformational dilatometer

Autorzy:

Zalecki, W.
Wrożyna, A.
Zieliński, A.

Powiązania:

https://bibliotekanauki.pl/articles/181664.pdf

Data publikacji:

2017

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica

Tematy:

stop niklu
stal austenityczna
dylatometr odkształceniowy
zmęczenie
pełzanie
nickel alloy
austenitic steel
deformation dilatometer
fatigue
creep

Opis:

Celem pracy było zbadanie zmian mikrostruktury (głównie procesy wydzielania) w następstwie działania cyklicznych zmian temperatury i/lub obciążenia. W szczególności przetestowano możliwości badawcze dylatometru DIL805A-/D/T w zakresie zastosowania równoległych cyklicznych zmian temperatury i obciążenia w próbkach stali dla energetyki. W wyniku przeprowadzonych badań zaobserwowano, że w strukturze odkształcanych stali nastąpiła intensyfikacja procesów wydzielania węglików. W stosunku do stanu dostawy nastąpiło utworzenie na granicach ziaren ciągłej siatki wydzieleń. Stwierdzono, że odkształcenie i/lub cykliczne zmiany temperatury silniej oddziaływały na zmiany struktury stopu HR6W niż stali Sanicro 25.
parallel temperature and load variations in specimens made of engineering steels for power plant constructions. In the microstructure of the samples subjected to deformation the intensification of carbides precipitation processes was found out. In comparison to the steel as delivered the net of carbides was created on the grains boundaries .The process of carbides precipitation caused by deformation and/or cyclic temperature variation was more advanced in HR6W alloy then in Sanicro 25 steel grades.

Źródło:

Prace Instytutu Metalurgii Żelaza; 2017, T. 69, nr 3, 3; 45-54
0137-9941

Pojawia się w:

Prace Instytutu Metalurgii Żelaza

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 65.

Tytuł:

Microstructural Changes in a High-Manganese Austenitic Fe-Mn-Al-C Steel
Zmiany mikrostrukturalne w wysokomanganowej stali austenitycznej Fe-Mn-Al-C

Autorzy:

Witkowska, M.
Zielińska-Lipiec, A.
Kowalska, J.
Ratuszek, W.

Powiązania:

https://bibliotekanauki.pl/articles/350948.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

high-manganese austenitic steel hot-rolling
spinodal decomposition
carbides
microstructure
wysokomanganowa stal austenityczna
rozpad spinodalny
węgliki
mikrostruktura

Opis:

Microstructural changes in the age-hardenable Fe-28wt.%Mn-9wt.%Al-1wt.%C steel during ageing at 550°C for various times have been investigated by transmission electron microscopy (TEM) and X-ray diffraction (XRD). The steel was produced in an induction furnace and the ingot, after homogenization at 1150°C for 3 hours under a protective argon atmosphere, was hot-rolled and subsequently cold-rolled up to 23% reduction. The sheet was then aged at 550°C for various times in an argon atmosphere and cooled in air. XRD analysis and TEM observations revealed a modulated structure and superlattice reflections produced by spinodal decomposition, which occurred during ageing at 550°C. Theexistence of satellites suggests that either (Fe, Mn)₃AlC_x carbides were formed within the austenite matrix by spinodal decomposition during cooling or chemical fluctuactions occurred between the (Fe, Mn)₃AlC_x carbides and the austenitic matrix.
W pracy analizowano zmiany mikrostruktury w stali Fe-28%wt. Mn-9%wt. Al-1%wt.C zachodzące podczas starzenia w temperaturze 550°C w różnych czasach. Stal Fe-28Mn-9Al-1C wytopiono w próżniowym piecu indukcyjnym. Po odlaniu wlewek homogenizowano w temperaturze 1150°C przez 3 godziny w atmosferze argonu. Wlewek walcowano na gorąco a następnie na zimno do 23 % odkształcenia. Próbki po odkształceniu starzono w temperaturze 550°C dla różnych czasów w atmosferze argonu i chłodzono na powietrzu. Obserwacje elektronomikroskopowe starzonej stali Fe-28Mn-9Al-1C ujawniły modulowaną strukturę i refleksy od nadstruktury, co było efektem rozpadu spinodalnego, który miał miejsce podczas procesu starzenia. Występowanie satelitów na zapisach dyfrakcyjnych sugeruje, że węgliki (Fe, Mn)₃AlC_x powstały w osnowie austenitycznej na skutek rozpadu spinodalnego zachodzącego podczas chłodzenia czy fluktuacji chemicznych występujących pomiędzy węglikami Fe, Mn)₃AlC_x i osnową austenityczną.

Źródło:

Archives of Metallurgy and Materials; 2014, 59, 3; 971-975
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 66.

Tytuł:

Badania porównawcze odporności korozyjnej stali austenitycznej AISI 304L (EN 1.4307) stosowanej do przewozu wybranych płynów
Comparative studies of the corrosion resistance of AISI 304L austenitic stainless steel (EN 1.4307) for the carriage of selected liquids

Autorzy:

Rokosz, K.
Hryniewicz, T.
Solecki, G.
Dudek, Ł.

Powiązania:

https://bibliotekanauki.pl/articles/314516.pdf

Data publikacji:

2015

Wydawca:

Instytut Naukowo-Wydawniczy "SPATIUM"

Tematy:

korozja wżerowa
stal austenityczna 304L
stal nierdzewna
płyny
pitting corrosion
austenitic steel 304L
stainless steel
liquids

Opis:

Niniejszy artykuł przedstawia badania porównawcze odporności korozyjnej austenitycznej stali stopowej AISI 304L (EN 1.4307). Wyniki przeprowadzonych badań dają możliwość oceny odporności stali nierdzewnej na korozję wżerową w różnych środowiskach spotykanych w przemyśle spożywczym. Badania prowadzone były w sześciu różnych środowiskach: roztworze Ringera, wodnym roztworze 3% wag. NaCl, mleku, piwie, soku z cytryny, oraz w Coca-Coli. W każdym z badanych roztworów/płynów zaobserwowano zjawisko korozji wżerowej. Największą odporność na korozję wżerową wykazała próbka w roztworze Ringera.
This paper presents a comparative study of the corrosion resistance of austenitic stainless steel AISI 304L (EN 1.4307). The studies show the resistance to pitting corrosion of stainless steel in various environments encountered in the food industry. The tests were carried out in six different environments/fluids: Ringer's solution, an aqueous solution of 3 wt% NaCl, milk, beer, lemon juice, and Coca-Cola. In each case, the phenomenon of pitting corrosion has been observed. The highest resistance to pitting corrosion was noticed in the Ringer’s solution.

Źródło:

Autobusy : technika, eksploatacja, systemy transportowe; 2015, 16, 6; 195-197
1509-5878
2450-7725

Pojawia się w:

Autobusy : technika, eksploatacja, systemy transportowe

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 67.

Tytuł:

Fatigue strength improvement of the AISI 316Ti austenitic stainless steel by shot peening

Autorzy:

Novy, F.
Dundekova, S.
Bokuvka, O.
Trsko, L.

Powiązania:

https://bibliotekanauki.pl/articles/111990.pdf

Data publikacji:

2014

Wydawca:

Stowarzyszenie Menedżerów Jakości i Produkcji

Tematy:

stainless steel
AISI 316L
shot peening
fatigue strength
stal nierdzewna
śrutowanie
wytrzymałość na zmęczenie

Opis:

Stainless steels are structural materials used for a wide range of applications. One of the fields of application of these highly corrosion resistant materials is for various medical applications. Different methods of mechanical property improvement have been studied in recent years to increase the durability of components manufactured from these materials. The main goal of this study was an analysis of fatigue strength improvement of the AISI 316Ti austenitic stainless steel by shot peening. A significant improvement of surface hardness, yield strength and fatigue limit by shot peening was observed in this study. This is despite increasing the surface roughness which usually degrades material’s fatigue strength.

Źródło:

Production Engineering Archives; 2014, 4, 3; 2-6
2353-5156
2353-7779

Pojawia się w:

Production Engineering Archives

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 68.

Tytuł:

Corrosion Resistance of X5CrNi18-10 Stainless Steel

Autorzy:

Kciuk, M.
Lasok, S.

Powiązania:

https://bibliotekanauki.pl/articles/352190.pdf

Data publikacji:

2017

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic stainless steel
sensitization
corrosion resistance
potentiodynamic tests

Opis:

The paper presents the influence of heat treatment on the structure and corrosion resistance of X5CrNi18-10 steel. To determine the structure which has been obtained after heat treatment the methods of light and scanning electron microscopy with EDS microanalysis were used. The electrochemical corrosion properties of the investigated steel were studied in 3.5% NaCl solution using potentiodynamic polarization tests. Basing on the registered curves, the corrosion current, polarization resistance and corrosion potential were determined. The corrosion tests were followed by fractographic researches.

Źródło:

Archives of Metallurgy and Materials; 2017, 62, 4; 2101-2106
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 69.

Tytuł:

Qualification of brazing procedure for furnace brazing of austenitic steel according to requirements of the ASME BPVC, section IX
Kwalifikowanie technologii lutowania twardego próżniowego stali austenitycznej zgodnie z wymaganiami przepisów ASME BPVC, sekcja IX

Autorzy:

Rogalski, Grzegorz
Landowski, Michał
Świerczyńska, Aleksandra
Łabanowski, Jerzy
Tomków, Jacek

Powiązania:

https://bibliotekanauki.pl/articles/1510538.pdf

Data publikacji:

2019

Wydawca:

Stowarzyszenie Inżynierów i Techników Mechaników Polskich

Tematy:

lutowanie twarde
lutowanie próżniowe
stal nierdzewna
stal austenityczna
wymiennik ciepła
brazing
furnace brazing
austenitic steel
stainless steel
heat exchanger

Opis:

The article presents the procedure for qualifying brazing technology in a vacuum furnace on the example of stainless steel elements joined with copper filler material from the F-No group. 105, in accordance with the ASME Sec. IX, part QB (ASME Boiler and Pressure Vessel Code. Qualification Standard for Welding, Brazing and Fusing; Procedures; Welders; Brazers; and Welding, Brazing and Fusing Operators). The essential variables of the furnace brazing process are discussed in relation to the requirements of the protocol of qualified PQR (Procedure Qualification Record) and BPS (Brazing Procedure Specification) in accordance with the ASME Sec. IX. The requirements for joints by the calculation code ASME Sec. VIII div.1 (Rules of Construction of Pressure Vessels), related to the working temperature of the designed device have also been taken into account. The paper presents examples of brazed joints made and their properties (strength, fill level of the clearance) obtained on the basis of the carried out tests. Attention was paid to the technological aspects during the performance of brazed joints using vacuum furnaces.
W artykule przedstawiono procedurę kwalifikowania technologii lutowania twardego w piecu próżniowym na przykładzie elementów ze stali wysokostopowej nierdzewnej austenitycznej łączonych lutem miedzianym z grupy F-No. 105, zgodnie z przepisami ASME Sec. IX, part QB (ASME Boiler and Pressure Vessel Code. Qualification Standard for Welding, Brazing and Fusing; Procedures; Welders; Brazers; and Welding, Brazing and Fusing Operators). Omówiono zmienne zasadnicze procesu lutowania próżniowego w odniesieniu do wymagań stawianych dokumentacji tj.: protokołowi z kwalifikowanej technologii lutowania PQR (ang. Procedure Qualification Record) oraz Instrukcji technologicznej lutowania BPS (ang. Brazing Procedure Specification) zgodnie z przepisami ASME Sec. IX. Uwzględniono również wymagania stawiane połączeniom przez kod obliczeniowy ASME Sec. VIII div.1 (ang. Rules of Construction of Pressure Vessels), a związane z temperaturą pracy projektowanego urządzenia. Przedstawiono przykłady wykonanych połączeń lutowanych oraz ich właściwości (wytrzymałościowe, stopień wypełnienia szczeliny lutowniczej) uzyskane na podstawie przeprowadzonych badań. Zwrócono uwagę na aspekty technologiczne podczas wykonywania złączy lutowanych przy zastosowaniu pieców próżniowych.

Źródło:

Welding Technology Review; 2019, 91, 9; 13-24
0033-2364
2449-7959

Pojawia się w:

Welding Technology Review

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 70.

Tytuł:

Influence of temperature on corrosion resistance of austenitic stainless steel in cl¯ containing solutions

Autorzy:

Zatkalíková, Viera
Markovičová, Lenka

Powiązania:

https://bibliotekanauki.pl/articles/111992.pdf

Data publikacji:

2019

Wydawca:

Stowarzyszenie Menedżerów Jakości i Produkcji

Tematy:

pitting corrosion
temperature
cyclic potentiodynamic test
immersion test
pitting potential
korozja wżerowa
temperatura
test potencjodynamiczny

Opis:

Temperature is considered a complicated external factor of the susceptibility of stainless steels to the pitting. This paper deals with the corrosion behaviour of AISI 316Ti stainless steel in temperature range 22 - 80°C in aggressive chloride environments (3 and 5% FeCl₃ solutions). The corrosion resistance of tested steel is evaluated on the base of results of exposure immersion tests and cyclic potentiodynamic tests. According to the obtained results the resistance of AISI 316Ti to the pitting is markedly affected by temperature changes in the range 22 - 80°C. Intensity of corrosion attack increases with the rise of Cl¯ concentration. Gentle changes of temperature and Cl¯ concentration cause significant differences in character of local damage. The appearance of pitted surfaces changes with the rise of the temperature (a density of pitting increases, a size of pits decreases). The strongest change in appearance is observed between 40 and 50ºC.

Źródło:

Production Engineering Archives; 2019, 25; 43-46
2353-5156
2353-7779

Pojawia się w:

Production Engineering Archives

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 71.

Tytuł:

Influence of ageing on microstructure and mechanical properties of TP347HFG austenitic stainless steel

Autorzy:

Golański, Grzegorz
Purzyńska, Hanna

Powiązania:

https://bibliotekanauki.pl/articles/2204539.pdf

Data publikacji:

2023

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic stainless steel
precipitates
microstructure
mechanical properties
mikrostruktura
właściwości mechaniczne
stal austenityczna nierdzewna
wytrącanie

Opis:

The paper presents the results of microstructural and mechanical investigation of long-term aged TP347HFG austenitic stainless steel. Ageing was performed at a time of up to 30 000 hours and the temperature of 600 and 650◦C. Ageing was proved to lead to the precipitation of secondary phase particles not only inside grains but also on the boundaries of grains and twins. The MX precipitates were observed inside the grains. However, M23C6 carbides and sigma phase precipitates were observed on grain boundaries. The changes in the microstructure of the examined steel translated into the mechanical properties, i.e. initially observed growth and then the decrease of yield strength and a gradual decrease in impact energy. The overageing process – a decrease in strength properties – was associated with the growth of the size of M23C6 carbides and the precipitation of the sigma phase. The reduction of impact energy in TP347HFG austenitic stainless steel was found to be associated with the precipitation of M23C6 carbides in the case of the 600◦C temperature, and the M23C6 carbides and sigma phase in the case of the 650◦C temperature. The rate of changes in the microstructure and mechanical properties depended on the ageing temperature.

Źródło:

Bulletin of the Polish Academy of Sciences. Technical Sciences; 2023, 71, 2; art. no. e144607
0239-7528

Pojawia się w:

Bulletin of the Polish Academy of Sciences. Technical Sciences

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 72.

Tytuł:

Wpływ temperatury starzenia na mikrostrukturę i właściwości mechaniczne stali TP347HFG
Influence of Aging on Microstructure and Mechanical Properties of TP347HFG Steel

Autorzy:

Andrzejewski, Michał
Golański, Grzegorz
Lipiński, Tomasz
Nowacki, Krzysztof

Powiązania:

https://bibliotekanauki.pl/chapters/28394707.pdf

Data publikacji:

2023-12-14

Wydawca:

Politechnika Częstochowska. Wydawnictwo Politechniki Częstochowskiej

Tematy:

austenityczna stal TP347HFG
mikrostruktura
starzenie
właściwości mechaniczne
austenitic steel TP347HFG
aging
microstructure
mechanical properties

Opis:

W rozdziale przedstawiono wyniki badań żarowytrzymałej stali austenitycznej TP347HFG po starzeniu w temperaturze 600 i 700℃ w czasie do 30 000 godzin. Zakres przeprowadzonych badań obejmował analizę mikrostruktury za pomocą mikroskopu optycznego i skaningowego mikroskopu elektronowego oraz badania własności mechanicznych. W stanie dostawy badana stal posiadała mikrostrukturę austenitu z licznymi bliźniakami oraz wydzieleniami pierwotnymi i wtórnymi. Starzenie przyczyniło się do procesów wydzieleniowych zachodzących na granicach ziaren, granicach bliźniaków oraz wewnątrz ziaren. Procesy wydzieleniowe po granicach ziaren skutkowały tworzeniem miejscami tzw. ciągłej siatki wydzieleń. Ponadto po 5000 h starzenia w temperaturze 700℃ na styku trzech granic ziaren ujawniono występowanie charakterystycznych wydzieleń fazy σ. Wydzielanie się faz wtórnych w mikrostrukturze badanej stali wpływało na zmiany właściwości mechanicznych, które uzależnione były od temperatury starzenia. W temperaturze 600℃ widoczny był zarówno wzrost twardości, jak i właściwości wytrzymałościowych oraz względnie łagodne obniżanie wartości energii łamania. Z kolei dla temperatury 700℃ widoczny był efekt przestarzenia oraz istotne obniżenie ciągliwości.
The chapter presents the results of research on the heat-resistant austen- itic steel TP347HFG after aging at temperatures of 600 and 700℃ for up to 30,000 hours. The scope of the study included analysis of the microstructure using an op- tical microscope and a scanning electron microscope, as well as mechanical prop- erties tests. In the as-delivered state, the studied steel had an austenitic microstruc- ture with numerous twins and primary and secondary precipitates. Aging contributed to precipitate processes occurring at grain boundaries, twin boundaries, and within grains. Precipitation processes at grain boundaries resulted in the for- mation of continuous precipitate networks in some areas. Furthermore, after 5,000 hours of aging at a temperature of 700℃, the characteristic σ-phase precipitates were observed at the junction of three grain boundaries. The precipitation of sec- ondary phases in the microstructure of the studied steel affected changes in mechan- ical properties, which were dependent on the aging temperature. At a temperature of 600℃, both an increase in hardness and strength properties as well as a relatively mild decrease in fracture energy values were observed. On the other hand, at a tem- perature of 700℃, the overaging effect was visible, resulting in a significant de- crease in ductility.

Źródło:

Potencjał innowacyjny w inżynierii materiałowej i zarządzaniu produkcją; 47-55
9788371939457

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 73.

Tytuł:

Corrosion of AlSi 304L Austenitic Stainless Steel in Non-Stationary Aqueous HCl + NaCl Solution

Autorzy:

Opiekun, Z. A.
Orłowicz, A. W.
Kupiec, B.

Powiązania:

https://bibliotekanauki.pl/articles/383327.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic stainless steel
structures
hardness
microhardness
stress
corrosion
stal austenityczna
struktury
twardość
mikrotwardość
naprężenie
korozja

Opis:

The paper describes the process of stress corrosion in a Ø50 mm rod made of AISI 304L austenitic chromium-nickel steel. Discs cut off from the steel rod were moved at a speed of 1.25 m/s for a test period of 408 h in a corrosive environment of aqueous solution containing 3% HCl and 8.6 g NaCl at room temperature. It was found that deepest cracks and irregular pitting occurred locally in areas of microstructure containing grains of hard lamellar &alpha' martensite and along boundaries between filamentary delta ferrite (Feδ) precipitates and &alpha′ phase. The corrosion developed in a trans-crystalline manner with branches propagating along boundaries of lamellar &alpha′ phase grains.

Źródło:

Archives of Foundry Engineering; 2014, 14, 1 spec.; 165-168
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 74.

Tytuł:

Effect of Delta Ferrite on the Mechanical Properties of Dissimilar Ferritic-Austenitic Stainless Steel Welds

Autorzy:

Ghasemi, R.
Beidokhti, B.
Fazel-Najafabadi, M.

Powiązania:

https://bibliotekanauki.pl/articles/353040.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

stainless steel
welding
delta ferrite
electron microscopy
austenite

Opis:

The dissimilar welds of AISI 304 to AISI 430 stainless steel was investigated by using gas tungsten arc welding. Three filler metals including ER309L, ER316L and ER2594 were applied. The weakest region of the welds was the heat affected zone of 430 stainless steel due to the formation of martensite. Also, the wide grain growth zone was observed in this side. The ferrite number for type 309L, 316L and 2594 weld metals was about 15, 32 and 57, respectively. The hardness and tensile strength values of the weld metals were higher than that of the heat affected zones and the base metals. The ferrite presented higher hardness values than the austenite in type 316L and 309L joints; while the hardness of austenite and ferrite was comparable in type 2594 weld metal.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 1; 437-443
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 75.

Tytuł:

Stored energy of plastic deformation in tube bending processes

Autorzy:

Śloderbach, Z.
Pająk, J.

Powiązania:

https://bibliotekanauki.pl/articles/264871.pdf

Data publikacji:

2013

Wydawca:

Uniwersytet Zielonogórski. Oficyna Wydawnicza

Tematy:

odkształcenia plastyczne
gięcie rur
energia zmagazynowana
stal austenityczna
kocioł stalowy
plastic deformation
tube bending
stored energy
austenitic steel
boiler steel

Opis:

The paper presents an aproximate analytic method for determination of the stored energy of plastic deformation during cold bending of metal tubes at bending machines. Calculations were performed for outer points of the tube layers subjected to tension and compression (the points of maximum strains). The percentage of stored energy related to the plastic strain work was determined and the results were presented in graphs. The influence and importance of the stored energy of plastic deformation on the service life of pipeline bends are discussed.

Źródło:

International Journal of Applied Mechanics and Engineering; 2013, 18, 1; 235-248
1734-4492
2353-9003

Pojawia się w:

International Journal of Applied Mechanics and Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 76.

Tytuł:

Irradiation of austenitic steel 10Cr12Mn14Ni4AlMo and titanium alloy Ti-Al-V by pulsed streams of fast nitrogen ions and plasma in a dense plasma focus

Autorzy:

Gribkov, V. A.
Pimenov, V. N.
Roschupkin, V. V.
Maslyaev, S. A.
Demina, E. V.
Lyakhovitsky, M. M.
Dubrovsky, A. V.
Sasinovskaya, I. P.

Powiązania:

https://bibliotekanauki.pl/articles/971548.pdf

Data publikacji:

2012

Wydawca:

Instytut Chemii i Techniki Jądrowej

Tematy:

radiation
damage
phase transition
nanohardness
dense plasma focus (DPF)

Opis:

Austenitic steel 10Cr12Mn14Ni4AlMo and Ti-4Al-3V alloy were irradiated with nanosecond pulsed nitrogen ion and plasma streams in plasma focus devices. The two different modes of the treatment were applied: high power density (greater-than or equal to 10 8 W/cm2) irradiation with melting of the surface layer and irradiation with power density similar to 10 7 W/cm2 below the melting threshold. Structure and phase changes as well as the mechanisms of modification and hardening of the surface layers of the steel and titanium alloy upon applied irradiation are discussed.

Źródło:

Nukleonika; 2012, 57, 2; 291-295
0029-5922
1508-5791

Pojawia się w:

Nukleonika

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 77.

Tytuł:

Contribution of Different Hardening Mechanisms during Cold Working of AISI 304L Austenitic Stainless Steel

Autorzy:

Mirzaie, T.
Mirzadeh, H.
Naghizadeh, M.

Powiązania:

https://bibliotekanauki.pl/articles/356145.pdf

Data publikacji:

2018

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

stainless steels
deformation-induced martensite
work hardening

Opis:

The contributions of work-hardening of austenite and the presence of martensite on the hardening of an AISI 304L stainless steel were evaluated based on plastic deformation under different reductions in thickness at two rolling temperatures. The cold deformation temperatures of 300 K and 373 K were chosen to induce strain-hardening plus strain-induced martensitic transformation in the former and strain-hardening in the latter. This made it possible to elucidate the real effects of strengthening mechanisms of metastable austenitic stainless steels during mechanical working.

Źródło:

Archives of Metallurgy and Materials; 2018, 63, 3; 1317-1320
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 78.

Tytuł:

Microstructure and texture evolution in the welded semi-austenitic PH steel after the heat treatment

Autorzy:

Ziewiec, A.
Witkowska, M.
Zielińska-Lipiec, A.

Powiązania:

https://bibliotekanauki.pl/articles/1153207.pdf

Data publikacji:

2016-10

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

81.20.Vj
81.40.Gh
81.40.Ef
68.37.Lp

Opis:

The aim of this study was to reveal the influence of the heat treatment after welding of 17-7PH (X7CrNiAl17-7) steel on the microstructure evolution and the texture of the welds. Microstructure investigation carried out by light microscopy and transmission electron microscopy showed that the austenite and δ ferrite coexist in as-welded condition. Annealing at the temperature range between 400°C and 620°C after welding causes small changes in the microstructure and the hardness of the welds increases. Heat treatment at 760°C for 1 h resulted in the partial destabilization of the austenite. Aging after destabilization leads to tempering of the martensite: first the hardness increases and then decreases. The maximum hardness is observed when the ageing temperature reaches 510°C. XRD studies confirmed the presence of the two phases: δ ferrite and austenite. Annealing at 400°C/1 h and 550°C/1 h results in changes of the intensities for individual peaks derived from austenite and ferrite. The calculated ratios of peak intensity were compared with the intensities of the reference sample. The differences in intensities suggested strong texture of the material.

Źródło:

Acta Physica Polonica A; 2016, 130, 4; 956-959
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 79.

Tytuł:

Comparison of Vacuum Sintered and Selective Laser Melted Steel AISI 316L

Autorzy:

Brytan, Z.

Powiązania:

https://bibliotekanauki.pl/articles/351485.pdf

Data publikacji:

2017

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic stainless steel
316L
selective laser melting
SLM

Opis:

The paper presents the results of the basic mechanical properties determined in the static tensile test, impact un-notched Charpy test and hardness of austenitic stainless steel type 316L produced by two techniques: classical pressing and sintering in a vacuum with rapid cooling and selective laser melting (SLM). In this work fracture surface of Charpy test, samples were studied. The results indicate that application of selective laser melting (SLM) makes it possible to double increase the strength properties of components manufactured from austenitic stainless steel type 316L compared to sintering in a vacuum. Resulted in mechanical properties strongly depend on porosity characteristic and the presence of superficial oxides in the case of sintered steel and the character of observed microstructural defects deriving from non-fully melted powder particles and the formation of voids between subsequently melted pool tracks during the SLM.

Źródło:

Archives of Metallurgy and Materials; 2017, 62, 4; 2125-2131
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 80.

Tytuł:

Korozja stali i żeliwa sferoidalnego ferrytycznego w ciekłej cynie
Corrosion of steel and spheroidal ferritic cast iron in liquid tin

Autorzy:

Opiekun, Z. A.
Orłowicz, W. A.

Powiązania:

https://bibliotekanauki.pl/articles/391725.pdf

Data publikacji:

2013

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa

Tematy:

korozja
stal austenityczna
stal konstrukcyjna
żeliwo sferoidalne ferrytyczne
ciekła cyna
corrosion
austenitic steel
construction steel
spheroidal ferritic cast iron
liquid tin

Opis:

W artykule przedstawiono przebieg korozji w ciekłej cynie próbek z żeliwa sferoidalnego ferrytycznego, próbek ze stali austenitycznej chromowo-niklowej X2CrNi 19-12 (00H18N10) i próbek ze stali konstrukcyjnej niskostopowej 12CrMo 4-5 (15HM). Próby oddziaływania wykonano przy stałej temperaturze ciekłej cyny 600°C w czasie 170 h. Przeprowadzone badania metalograficzne wykazały, że najszybciej korozji w ciekłej cynie (z szybkością 0,12 mm/h) ulegały próbki ze stali X2CrNi 19-12, wolniej próbki ze stali 12CrMo 4-5 (szybkość korozji około 0,004 mm/h), a najwolniej korodowały próbki z żeliwa sferoidalnego ferrytycznego (szybkość korozji około 0,003 mm/h).
The article presents a course of static corrosion of spheroidal ferritic cast iron, austenite stainless steel X2CrNi19-12 (00H18N10) and samples of low-alloy construction steel 12CrMo4-5 (15HM) in liquid tin. The tests were performed at temperature of 600°C in liquid tin for 170 hours. It has been found, that the fastest corrosion was observed in austenite steel (average rate ca. 0.12 mm/h). Slower corrosion was observed in steel 12CrMo4-5 (average rate ca. 0.004 mm/h) and the slowest corrosion was observed in spheroidal ferritic iron cast specimen (average rate ca. 0.003 mm/h) in liquid tin.

Źródło:

Prace Instytutu Odlewnictwa; 2013, 53, 3; 19-26
1899-2439

Pojawia się w:

Prace Instytutu Odlewnictwa

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 81.

Tytuł:

Comparison of Energy Absorption Properties of High Nitrogen Austenitic Steel and Cast Alloy Determined Using Low Velocity Perforation Test
Porównanie wyznaczonych w trakcie próby przebijania energochłonnych właściwości stali austenitycznej oraz staliwa o wysokiej zawartości azotu

Autorzy:

Moćko, W.

Powiązania:

https://bibliotekanauki.pl/articles/352019.pdf

Data publikacji:

2014

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

energy absorption
austenitic steel
cast alloy
constitutive modeling
damage initiation criterion
absorpcja energii
stal austenityczna
staliwo
modelowanie konstytutywne
kryterium inicjalizacji uszkodzenia

Opis:

The results of energy absorbing analysis of VP159 austenitic steel and LH556 cast alloy were presented in this article. The assessment was carried out on the basis of drop-weight tower perforation test at impact energy equal to 500J and striker velocity equal to 12,5 m/s. Moreover, the basic mechanical properties of both tested materials were estimated in order to calibrate coefficients of the Johnson-Cook visco-plasticity model and Johnson-Cook damage initialization criterion as well. Subsequently, both models were applied for the finite element method simulation of perforation process. The reasonable agreement between measured and calculated shape of energy absorption curves were obtained for steel and cast alloy as well.
W pracy przedstawiono wyniki analizy zdolności do pochłaniania energii blach wykonanych ze stali austenitycznej typu VP159 oraz staliwa LH556. Ocenę przeprowadzono wykorzystując test przebijania wykonany z użyciem młota opadowego przy energii uderzenia 500J i prędkości iglicy równej 12,5 m/s. Dodatkowo wyznaczono także charakterystyki mechaniczne obu materiałów. Na tej podstawie dokonano kalibracji modelu lepko-plastyczności Johnsona-Cooka oraz oszacowano kryterium inicjalizacji uszkodzenia Johnsona-Cooka. Następnie modele zostały wykorzystane do symulacji procesu przebijania z użyciem MES. Zarówno dla stali jak i staliwa uzyskano dobrą zgodność pomiędzy zmierzonymi i obliczonymi krzywymi pochłaniania energii.

Źródło:

Archives of Metallurgy and Materials; 2014, 59, 1; 65-69
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 82.

Tytuł:

Contribution to Deoxidation of Austenitic Steels in a Vacuum Induction Furnace with Carbon

Autorzy:

Šenberger, J.
Pernica, V.

Powiązania:

https://bibliotekanauki.pl/articles/379906.pdf

Data publikacji:

2015

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

vacuum induction furnace
deoxidation
carbon
austenitic steel
petrochemistry
oxygen activity
total oxygen
próżniowy piec indukcyjny
odtlenianie
węgiel
staliwo austenityczne
petrochemia
aktywność tlenu

Opis:

Deoxidation of steel with carbon under reduced pressure is often used for increasing the steel purity. Suitable units for this purpose in foundries are vacuum induction furnaces. Possibilities of increasing the steel purity by deoxidation with carbon in the vacuum induction furnace were studied for the steel for the petrochemistry of specific composition 25Cr/35Ni. The charge composed of the return material only was melted in the air. During melting the charge oxidized and the oxidizing slag formed. Chemical composition of steel, morphology, chemical composition of inclusions in the steel and chemical composition of slag after vacuuming were studied on the basis of samples taken before and after vacuuming. Temperature and oxygen activity were measured before and after vacuuming. Globular inclusions with dominant content of silicon and manganese were observed in steel before and after vacuuming. Contents of total oxygen in steel didn’t change significantly during vacuuming. On the basis of composition of inclusions and measured oxygen activity the activity of Cr₂O₃ in inclusions was calculated. A slag sample was taken after vacuuming and equilibrium oxygen activity in steel with regard to the Cr₂O₃ content in the slag was estimated from the slag composition. Equilibrium oxygen activity in relation to the Cr₂O₃ content in the slag was higher than equilibrium activity measured in the steel. For this reason it is not possible, under the studied conditions, to decrease oxygen content in steel during vacuuming.

Źródło:

Archives of Foundry Engineering; 2015, 15, 2; 105-109
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 83.

Tytuł:

Badania wstępne obróbki elektroerozyjnej w gazie z zastosowaniem dodatkowego chłodzenia przedmiotu obrabianego
Preliminary tests of electrodischarge machining in gaseous dielectric with additional workpiece cooling

Autorzy:

Żyra, Agnieszka
Skoczypiec, Sebastian

Powiązania:

https://bibliotekanauki.pl/articles/339791.pdf

Data publikacji:

2019

Wydawca:

Polskie Towarzystwo Zarządzania Produkcją

Tematy:

electrodischarge machining
EDM
dry EDM
austenitic steel X5CrNi 1810
obróbka elektroerozyjna
sucha obróbka elektroerozyjna
stal austenityczna X5CrNi 1810

Opis:

Electrodischarge machining (EDM) in the gas can be an alternative to traditional electrodischarge machining in dielectric liquids. Dry EDM has many advantages comparing with traditional EDM, what is more with optimal machining parameters it is possible to gain very good accuracy and quality of machined surface. Moreover, EDM in the gas is environmental friendly, even that it is still not used in industry because of the problems with proper heat dissipation from the machining gap which results in problems with achieving satisfying repetitiveness. In the paper the results of austenitic steel X5CrNi 1810 electrodischarge drilling in the air and in the air in deionised water environment were presented. The aim of the research was to determinate the influence of current intensity, current voltage, pulse on time, pulse off time and a type of electrodes’ polarization on the material removal rate, working electrode wear and the machined material surface structure.

Źródło:

Zarządzanie Przedsiębiorstwem; 2019, 22, 1; 25-32
1643-4773

Pojawia się w:

Zarządzanie Przedsiębiorstwem

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 84.

Tytuł:

Ewolucja mikrostruktury i właściwości użytkowych austenitycznej stali X8CrNiTi18-10 (T321H) podczas długotrwałej eksploatacji w warunkach pełzania
Evolution of microstructure and essential characteristics of austenitic steel X8CrNiTi18-10 (T321H) after long-term creep service

Autorzy:

Purzyńska, H.
Dobrzański, J.

Powiązania:

https://bibliotekanauki.pl/articles/182066.pdf

Data publikacji:

2017

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica

Tematy:

stal austenityczna
pełzanie
długotrwała eksploatacja
trwałość resztkowa
stopień wyczerpania
procesy wydzieleniowe
austenitic steel
creep
long-term service
residual strength
exhaustion degree
precipitation processes

Opis:

Zmiany mikrostruktury, podstawowych właściwości wytrzymałościowych oraz odporności na pełzanie austenitycznej stali X8CrNiTi18-10 (T321H) po długotrwałej eksploatacji w warunkach pełzania. Opis procesu degradacji tej stali podczas długotrwałego pełzania. Ocena wpływu rodzaju i ilości występujących wydzieleń oraz struktury dyslokacyjnej na odporność na pełzanie (resztkowa wytrzymałość na pełzanie, szybkość pełzania) i stopień wyczerpania. Model degradacji mikrostruktury w wyniku eksploatacji w warunkach pełzania w odniesieniu do stopnia wyczerpania. Sekwencja kolejnych stadiów rozwoju procesu wydzieleniowego stali X8CrNiTi18-10 eksploatowanej w warunkach pełzania w zależności od stopnia wyczerpania. Klasy struktury w zależności od stopnia rozwoju procesów wydzieleniowych i struktury dyslokacyjnej w powiązaniu ze stopniem wyczerpania. Sposób klasyfikowania stanu materiału na podstawie zmian w strukturze w oparciu o procesy składowe w odniesieniu do stopnia wyczerpania. Metodologia oceny austenitycznej stali X8CrNiTi18-10 po eksploatacji w warunkach pełzania na podstawie oceny stanu mikrostruktury. Stan mikrostruktury i poziom właściwości użytkowych po eksploatacji w warunkach pełzania a stopień wyczerpania.
Changes in microstructure of basic strength properties and creep resistance of austenitic steel X8CrNiTi18-10 (T321H) after long-term service under creep conditions. Description of degradation process for this steel during long term creep. Evaluation of the effect of the type and quantity of the occurring precipitation and the form of dislocation structure on creep resistance (residual creep resistance, creep rate) and exhaustion degree. Microstructure degradation model as a result of use under creep conditions in relation to exhaustion degree. Sequence of subsequent development stages of precipitation process for the X8CrNiTi18-10 steel service under creep conditions depending on exhaustion degree. Structure class depending on the development stage of precipitation processes and dislocation structure In relation to exhaustion degree. Classification of the state of material pertaining to changes in structure based on constituent processes in relation to exhaustion degree. Evaluation methodology for austenitic steel X8CrNiTi18-10 after service under creep conditions based on the assessment of the state of microstructure. State of microstructure and level of essential characteristics after use under creep conditions vs exhaustion degree.

Źródło:

Prace Instytutu Metalurgii Żelaza; 2017, T. 69, nr 3, 3; 11-38
0137-9941

Pojawia się w:

Prace Instytutu Metalurgii Żelaza

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 85.

Tytuł:

Biozgodność stopów protetycznych w funkcji czasu
Biocompatibility of prosthetic alloys as a function of time

Autorzy:

Hajduga, M.
Kalukin, B.
Kalukin, A.

Powiązania:

https://bibliotekanauki.pl/articles/99348.pdf

Data publikacji:

2009

Wydawca:

Politechnika Śląska. Katedra Biomechatroniki

Tematy:

protetyka stomatologiczna
proteza dentystyczna
uzupełnienie protetyczne
stop protetyczny
implantacyjna stal austenityczna
biozgodność
prosthodontics
dental prosthesis
prosthetic restoration
prosthetic alloy
implantation austenitic steel
biocompatibility

Opis:

Od przeszło 3000 lat główną grupą materiałów, przeznaczonych do implantacji w organizmie ludzkim są metale i ich stopy. W ostatnim stuleciu najczęściej używana była i jest do dzisiaj implantacyjna stal austenityczna. W ostatnich 30 latach częściowo wyparły ją stopy niklu, kobaltu czy tytanu. Jedną z funkcji, mających wpływ na biozgodność materiału jest czas przebywania konstrukcji w agresywnym środowisku płynów ustrojowych. Autorzy podjęli próbę określenia zakresu zmian w materiałach metalicznych, po długotrwałej implantacji w jamie ustnej. Celem pracy jest określenie wpływu czasu użytkowania na zmianę właściwości materiałowych stopów stomatologicznych. W jej zakresie mieszczą się mikroskopowe badania metalograficzne, mikroanaliza rentgenowska oraz badania mikrotwardości. Wstępna analiza wyników potwierdza tak szerokie rozpowszechnienie implantacyjnej stali austenitycznej.
From 3000 years the majority of materials made for implantation in the human body are metals and alloys. In the last century the most commonly used was steel austenitic implantation. In the past 30 years, it was partly replaced by nickel alloys, cobalt alloys and titanium. One of the functions having the effect on biocompatibility of material is time of construction in aggressive environment, body fluids. The authors undertook an attempt to determine the extent of changes in the metallic materials after long-term implantation in the oral cavity. The aim of this work is to determine the effect of time for a change of using the material used in dental alloys. In this field there are metallographic microscopic examinations, X-ray microanalysis and micro hardness. Preliminary analysis of the results confirms such a wide spread of implantation austenitic steel.

Źródło:

Aktualne Problemy Biomechaniki; 2009, 3; 53-58
1898-763X

Pojawia się w:

Aktualne Problemy Biomechaniki

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 86.

Tytuł:

Sensitizing Effects of Ti Alloying Contents on Damage Behavior of Austenitic Stainless Steel Exposed to Ultrasonic Vibratory Cavitation

Autorzy:

Lee, J.
Kim, S.

Powiązania:

https://bibliotekanauki.pl/articles/1186947.pdf

Data publikacji:

2016-04

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

47.55.dp

Opis:

The cavitation damage characteristics of austenitic stainless steel with different concentrations of Ti were investigated. The microstructure of the alloys was observed with optical microscope to identify its correlation with cavitation resistance. Hardness of the alloys was measured to examine its contribution to cavitation damage. It was found that the microstructure played a more significant role in cavitation damage behavior of austenitic stainless steel with Ti than the hardness. The findings in this study revealed that Ti addition in austenitic stainless steel may present either a beneficial or detrimental effect on cavitation damage behavior, depending on the microstructural characteristics. In particular, Ti content of 1.0% represented the most deteriorated cavitation characteristics due to the formation of relatively coarse precipitates. Therefore, control of Ti concentration is essential for marine application of austenitic stainless steel.

Źródło:

Acta Physica Polonica A; 2016, 129, 4; 578-583
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 87.

Tytuł:

Effect of Element Addition, Microstructure Characteristics, Mechanical Properties, Machining and Welding Processes of the Hadfield Austenitic Manganese Steel

Autorzy:

Zellagui, Rihab
Hemmouche, Larbi
Ait-Sadi, Hassiba
Chelli, Amel

Powiązania:

https://bibliotekanauki.pl/articles/2125536.pdf

Data publikacji:

2022

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

Hadfield steel
austenite
carbides
element addition effect
machinability
welding

Opis:

High manganese steel, also called Hadfield steel, is an alloy essentially made up of iron, carbon, and manganese. This type of steel occupies an important place in the industry. It possesses high impact toughness and high resistance against abrasive wear and hardens considerably during work hardening. The problem with this kind of steel is the generation of carbides at the grain boundaries after the casting. However, heat treatment at the high-temperature range between 950°C and 1150°C followed by rapid quenching in water is proposed as a solution to remove carbides and obtain a fully austenitic structure. Under the work hardening effects, the hardness of Hadfield steel increases greatly due to the transformation of the austenite γ to martensite ε or α and mechanical twinning, which acts as an obstacle for sliding dislocations. Hot machining is the only solution to machine Hadfield steel adequately without damage of tools or changing the mechanical characteristics of the steel. The choice of welding parameters is important to prevent the formation of carbides and obtain welded steel with great characteristics. This paper aims to give an overview about Hadfield steel, element addition effect, microstructure, heat treatments, work hardening, machinability and welding processes.

Źródło:

Archives of Metallurgy and Materials; 2022, 67, 3; 863--868
1733-3490

Pojawia się w:

Archives of Metallurgy and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 88.

Tytuł:

The Influence of the type of coating on the cutting tool wear during turning of 316L austenitic stainless steel

Autorzy:

Maruda, R. W.
Szczotkarz, N.

Powiązania:

https://bibliotekanauki.pl/articles/94100.pdf

Data publikacji:

2018

Wydawca:

Politechnika Poznańska. Wydawnictwo Politechniki Poznańskiej

Tematy:

dry cutting
tool wear
316L austenitic steel
SEM
TiN and TiAlN coatings
cięcie na sucho
zużycie narzędzi
stal austenityczna 316L
powłoki TiN i TiAlN

Opis:

The paper presents the influence of coatings applied with the use of PVD method on cutting tools on the wear of the tool and compares it with an uncoated P25 cemented carbide plate. During the experiment, two types of TiAlN coatings were used, applied in various proportions, as well as TiN coating. During the tests, the average width of the wear band on the flank face in B VBBzone and the width of KBcrater were monitored. Moreover, the scanning analysis of the tool was conducted in order to determine the intensity of adhesive wear. The lowest values of selected tool wear indicators were found out with the use of TiAlN coating applied in eight layers in the proportions 33/67% -TiN/TiAlN. The scanning analysis proved the highest adhesive wear of the uncoated P25 cemented carbide plate, as well as increased abrasive wear of the flank face and the formation of a crater in comparison with coated plates.

Źródło:

Archives of Mechanical Technology and Materials; 2018, 38; 45-49
2450-9469

Pojawia się w:

Archives of Mechanical Technology and Materials

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 89.

Tytuł:

Intermittency and Deformation Band Propagation in an Austenitic FeMnC TWIP Steel

Autorzy:

Lebyodkin, M.
Lebedkina, T.
Roth, A.
Allain, S.

Powiązania:

https://bibliotekanauki.pl/articles/1418489.pdf

Data publikacji:

2012-09

Wydawca:

Polska Akademia Nauk. Instytut Fizyki PAN

Tematy:

62.20.F-
81.70.-q
05.65.+b
62.65.+k

Opis:

Plastic deformation of austenitic FeMnC TWIP steels exhibits complex spatiotemporal patterns associated with the occurrence of deformation bands and the concomitant fluctuations of the deforming stress. Although the plastic instability is a generic property of these steels and is usually attributed to interaction of dislocations with solutes (the Portevin-Le Chatelier effect), both the kinematics of the deformation bands and the characteristic shape of stress serrations observed in the carbon-containing TWIP steel at room temperature manifest unusual features. The nature of these peculiarities and the mechanism of jerky flow in such steels are unclear. In the present work, an attempt is made to get an insight into the jerky flow in the Fe22Mn0.6C steel by studying the time series characterizing the evolution of plastic deformation at various scales: stress-time curves, local strain field, and acoustic emission accompanying the deformation processes. Stress and strain fluctuations related to two distinct scale ranges are detected and characterized.

Źródło:

Acta Physica Polonica A; 2012, 122, 3; 478-481
0587-4246
1898-794X

Pojawia się w:

Acta Physica Polonica A

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 90.

Tytuł:

Effect of porosity on the properties of nickel-free stainless steel obtained by powder metallurgy route

Autorzy:

Romańczuk-Ruszuk, Eliza
Lipowicz, Paweł
Sztorch, Bogna
Przekop, Robert

Powiązania:

https://bibliotekanauki.pl/chapters/2196290.pdf

Data publikacji:

2022

Wydawca:

Politechnika Białostocka. Oficyna Wydawnicza Politechniki Białostockiej

Tematy:

nickel-free austenitic stainless steel
powder metallurgy
porosity
mechanical alloying
corrosion resistance

Opis:

This paper presents the results of research on nickel-free austenitic stain- less steel with the composition Fe-18% Cr-12% Mn, obtained by powder metallurgy, with the use of mechanical alloying of elementary powders, manganese nitride and various process atmospheres. The influence of different protective atmosphere of the process (nitrogen and argon) and the addition of manganese nitride on poros- ity, microstructure, hardness and corrosion resistance of the sinters was described. Steel samples after pressing and sintering at 1200°C (1473 K) in nitrogen were char- acterized by a relative density above 80% and a porosity among 12–19%. In tested materials the pores on the surface are visible in each of the tested materials, which is confirmed by SEM images. The material obtained from powders with manganese nitride after mechanical alloying in nitrogen is characterized by the highest hard- ness and corrosion resistance. The addition of manganese nitride can be another way of introducing nitrogen into nickel-free steel.

Źródło:

Advances in biomedical engineering; 181–190
9788367185400

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 91.

Tytuł:

Composite space armous with the bainitic-austenitic and maraging steel layers

Autorzy:

Wiśniewski, Adam (1947- ).
Garbarz, Bogdan.
Burian, Wojciech.
Marcisz, Jarosław.

Powiązania:

Problemy Techniki Uzbrojenia 2013, nr 4, s. 33-41

Data publikacji:

2013

Tematy:

Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
Pancerze (powłoki) badanie
Pancerze przestrzenne badanie
Nanotechnologia
Metody badawcze
Naprężenia i odkształcenia
Pociski

Opis:

Rys., tab.
Bibliogr.

Dostawca treści:

Bibliografia CBW

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 92.

Tytuł:

Wearing quality of austenitic, duplex cast steel, gray and spheroidal graphite iron

Autorzy:

Pietrowski, S.

Powiązania:

https://bibliotekanauki.pl/articles/382903.pdf

Data publikacji:

2012

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

nowe technologie materiałowe
staliwo austenityczne
żeliwo typu duplex
zużycie ścierne
zużycie adhezyjne
new materials technologies
austenitic cast steel
duplex cast iron
abrasion wear
adhesive wear

Opis:

The current work presents the research results of abrasion wear and adhesive wear at rubbing and liquid friction of new austenitic, austenitic-ferritic ('duplex') cast steel and gray cast iron EN-GJL-250, spheroidal graphite iron EN-GJS-600-3, pearlitic with ledeburitic carbides and spheroidal graphite iron with ledeburitic carbides with a microstructure of the metal matrix: pearlitic, upper bainite, mixture of upper and lower bainite, martensitic with austenite, pearlitic-martensitic-bainitic-ausferritic obtained in the raw state. The wearing quality test was carried out on a specially designed and made bench. Resistance to abrasion wear was tested using sand paper P40. Resistance to adhesive wear was tested in interaction with steel C55 normalized, hardened and sulfonitrided. The liquid friction was obtained using CASTROL oil. It was stated that austenitic cast steel and 'duplex' are characterized by a similar value of abrasion wear and adhesive wear at rubbing friction. The smallest decrease in mass was shown by the cast steel in interaction with the sulfonitrided steel C55. Austenitic cast steel and 'duplex' in different combinations of friction pairs have a higher wear quality than gray cast iron EN-GJL-250 and spheroidal graphite iron EN-GJS-600-3. Austenitic cast steel and 'duplex' are characterized by a lower wearing quality than the spheroidal graphite iron with bainitic-martensitic microstructure. In the adhesive wear test using CASTROL oil the tested cast steels and cast irons showed a small mass decrease within the range of 1-2 mg.

Źródło:

Archives of Foundry Engineering; 2012, 12, 2; 235-244
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 93.

Tytuł:

MIG welding of austenitic 316L steel used in means of transport

Autorzy:

Szczucka-Lasota, Bożena
Węgrzyn, Tomasz

Powiązania:

https://bibliotekanauki.pl/articles/2203054.pdf

Data publikacji:

2022

Wydawca:

Politechnika Śląska. Wydawnictwo Politechniki Śląskiej

Tematy:

civil engineering
transport
mobile platforms
MIG welding
316L steel
inżynieria lądowa
platforma ruchoma
spawanie MIG
stal 316L

Opis:

The austenitic 316L steel (1.4401) is an important stainless material used to build various means of transport. Austenitic steel has high resistance to atmospheric corrosion. The austenitic steel is treated as a good weldable material, although cracks are possible. This paper analyses the influence of various MIG welding parameters on the creation of correct joints used in the stainless steel structures of mobile platforms elements, as an example of welding structures, in various means of transport. Various tests verifying the mechanical properties of MIG welds, including non-destructive tests, tensile strength and hardness tests, were carried out. This article aims to show how important and complex the task is to select the correct welding parameters for elements of means of transport made of austenitic steel on the example of elements of mobile platforms.

Źródło:

Zeszyty Naukowe. Transport / Politechnika Śląska; 2022, 116; 247--256
0209-3324
2450-1549

Pojawia się w:

Zeszyty Naukowe. Transport / Politechnika Śląska

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 94.

Tytuł:

Mechanical properties of phase constituents in selected grades of cast steel

Autorzy:

Garbiak, M.
Zubko, P.

Powiązania:

https://bibliotekanauki.pl/articles/382574.pdf

Data publikacji:

2011

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

nanoindentation measurement
Young modulus
austenitic cast steel
pomiar nanoindentacji
moduł Younga
staliwo austenityczne

Opis:

The nanoindentation measurements performed on three cast steels of 0.3C-30Ni-18Cr type with various content of niobium and titanium were carried out. Mechanical properties of the main phase constituents of the alloys, such as austenite, MC and M23C6 type carbides, were determined and analysed. The values of hardness (H) and Young modulus (E) for the austenite matrix were similar within the tested alloys. Essential differences (H=12÷24 GPa; E = 250÷400 GPa) were found between the carbide p hases p resent in tested alloys. The nanoindentation measurement on small particles is affected by different effects. One of these effects was excluded using numerical simulation of impressing the phase constituent into the matrix during indentation. The values of H and E obtained from simulation were: 30/450 GPa for NbC; 50/580 GPa for TiC; and 19/320 GPa for Cr₂₃C₆ respectively.

Źródło:

Archives of Foundry Engineering; 2011, 11, 3 spec.; 57-60
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 95.

Tytuł:

Cast steels for creep-resistant parts used in heat treatment plants

Autorzy:

Drotlew, A.
Garbiak, M.
Piekarski, B.

Powiązania:

https://bibliotekanauki.pl/articles/380318.pdf

Data publikacji:

2012

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

innowacyjne technologie odlewnicze
innowacyjne materiały odlewnicze
staliwo austenityczne Ni-Cr
obróbka cieplna
innovative foundry technologies
innovative foundry materials
cast Ni-Cr austenitic steel
castings for heat treatment plants

Opis:

Creep-resistant parts of heat treatment furnaces are in most cases made from high-alloyed chromium-nickel and nickel-chromium iron alloys, both cast and wrought. This paper presents the types of casting alloys used for this particular purpose, since the majority of furnace components are made by the casting process. Standards were cited which give symbols of alloy grades used in technical specifications by the domestic industry. It has been indicated that castings made currently are based on a wider spectrum of the creep-resistant alloy grades than the number of alloys covered by the standards. Alloy grades recommended by the technical literature for individual parts of the furnace equipment were given. The recommendations reflect both the type of the technological process used and the technical tasks performed by individual parts of the furnace equipment. Comments were also made on the role of individual alloying elements in shaping the performance properties of castings.

Źródło:

Archives of Foundry Engineering; 2012, 12, 4; 31-38
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 96.

Tytuł:

Wpływ parametrów technologicznych operacji powierzchniowej obróbki plastycznej na strukturę geometryczną powierzchni czopów wału wykonanego ze stali austenitycznej
The effect of technological parameters of surface plastic working on the geometric structure of the surface of a neck of a shaft made from austenitic steel

Autorzy:

Starosta, R.
Labuda, W.

Powiązania:

https://bibliotekanauki.pl/articles/211456.pdf

Data publikacji:

2011

Wydawca:

Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej

Tematy:

obróbka plastyczna
nagniatanie
stal odporna na korozję
warstwa wierzchnia
pompy krętne
plastic working
burnishing
corrosion resistant steel
surface layer
torque pumps

Opis:

Na statkach, w instalacjach wody zaburtowej (np. instalacji chłodzenia silników), często wykorzystuje się pompy krętne. Ze względu na trudne warunki ich pracy do budowy tego rodzaju pomp stosuje się materiały odporne na zużycie kawitacyjne oraz korozję elektrochemiczną wywoływaną przez wodę morską. W przypadku wałów pomp najczęstszą niesprawnością jest zużycie czopów (korozyjne, cierne i zmęczenie stykowe) w miejscu montażu uszczelnień (dławnic). Zwiększenie trwałości eksploatacyjnej pomp krętnych można osiągnąć dzięki zastosowaniu obróbki nagniataniem jako technologii, która umożliwia uzyskanie stosunkowo małej chropowatości powierzchni przy jednoczesnym jej umocnieniu zgniotem. Celem badań było wyznaczenie optymalnych parametrów procesu nagniatania i zmniejszenie chropowatości powierzchni czopów wałów okrętowych pomp krętnych wykonanych ze stali odpornej na korozję X5CrNi18-10. Proces nagniatania przeprowadzono nagniatakiem jednorolkowym SRMD firmy Yamato. Podczas nagniatania zastosowano zróżnicowane następujące parametry procesu technologicznego: siła nagniatania, prędkość nagniatania, posuw oraz liczba przejść. Istotny wpływ na zmniejszenie chropowatości powierzchni nagniatanych czopów ma posuw i siła nagniatania. Prędkość nagniatania oraz liczba kolejnych przejść nagniataka wpływają w niewielkim stopniu na gładkość obrabianych powierzchni. Stosując mały posuw fn = 0,13 mm/obr oraz siłę Fn 1,1 kN uzyskano chropowatość powierzchni o Ra= 0,07 m. Następne przejścia narzędzia powodują nieduże zmniejszenie chropowatości. Przyczyniają się one do uzyskania geometrii powierzchni o kształcie krzywej udziału materiałowego zapewniającej hipotetycznie zwiększenie odporności na zużycie cierne jak i polepszenie szczelności wału we współpracy z dławnicą okrętowej pompy krętnej.
Torque pumps are frequently used in the outside water installations of ships (e.g. engine cooling installations). Due to the difficult conditions of their operation, materials resistant to cavitation wear and electrochemical corrosion caused by sea water are used in their construction. In the case of pump shafts, the most frequently occu-ring malfunction is shaft neck wear (corrosion, friction, and contact fatigue) in the vicinity of the seals (pac-king). An increase in the exploitation durability of torque pumps can be achieved thanks to the process of burnishing technology, which makes it possible to achieve a relatively small surface roughness with simultaneous strengthening of the surface through deformation hardening. The purpose of studies was to determine optimal process parameters of the burnishing process and to decrease surface roughness of shaft necks of ship torque pumps made from corrosion resistant steel X5CrNi18-10. The burnishing process was carried out using a SRMD one-roller burnishing tool of the Yamato company. During burnishing the following varied technological process parameters were applied: burnishing force, burnishing speed, advance, and the number of passes. Advance and burnishing force has a significant effect on the decrease of surface roughness of burnished shaft necks. Burnishing speed and the amount of subsequent passes of the burnishing tool have an insignificant effect on the smoothness of worked surfaces. For a small advance of fn = 0.13 mm/rot and a force of Fn 1.1 kN, a surface roughness of Ra= 0.07 m was obtained. Further tool passes cause a slight decreases in roughness. These passes contribute to the achievement of a surface geometry with the shape of the Abbott-Firestone curve hypothetically ensuring an increase in abrasive wear resistance as well as improvement of shaft tightness in cooperation with the packing of the ship torque pump.

Źródło:

Obróbka Plastyczna Metali; 2011, 22, 2; 121-139
0867-2628

Pojawia się w:

Obróbka Plastyczna Metali

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 97.

Tytuł:

A novel deep penetrating eddy current probe based on phase shifted fields and its application to inspection of defects

Autorzy:

Wu, Meixian
Zhang, Dongli
Wang, Chuanglong

Powiązania:

https://bibliotekanauki.pl/articles/221582.pdf

Data publikacji:

2020

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

skin effect
penetration depth
austenitic stainless steel
eddy current probe
phase shifted fields

Opis:

Due to the skin effect of eddy currents, the depth of cracks which can be detected by the traditional eddy current probe is very limited. In order to improve the ability of eddy current probes to inspect deep cracks in metal thick-walled structures, a new eddy current probe using an excitation system with phase shifted fields was proposed. Its feasibility for detecting deep cracks was verified by simulation and experiments. The results showed that the penetration depth of eddy currents in austenitic stainless steel is effectively enhanced by using the new probe.

Źródło:

Metrology and Measurement Systems; 2020, 27, 2; 275-287
0860-8229

Pojawia się w:

Metrology and Measurement Systems

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 98.

Tytuł:

Oxide Layer Evolution of Cast Fe24Cr12NiXNb Heat-Resistant Cast Steels at 900°C in Atmospheric Air

Autorzy:

Ramos, P. A.
Coelho, R. S.
Pinto, H. C.
Soldera, F.
Mücklich, F.
Brito, P. P.

Powiązania:

https://bibliotekanauki.pl/articles/1837826.pdf

Data publikacji:

2021

Wydawca:

Polska Akademia Nauk. Czytelnia Czasopism PAN

Tematy:

austenitic cast steel
microstructure
Nb-alloyed steels
oxidation
staliwo austenityczne
mikrostruktura
stal stopowa
utlenianie

Opis:

The austenitic stainless steels are a group of alloys normally used under high mechanical and thermal requests, in which high temperature oxidation is normally present due to oxygen presence. This study examines the oxide layer evolution for Fe24Cr12NiXNb modified austenitic stainless steel A297 HH with 0,09%Nb and 0,77%Nb content at 900°C under atmospheric air and isothermal oxidation. The modifiers elements such as Mo, Co and Ti, added to provide high mechanical strength, varied due to the casting procedure, however main elements such as Cr, Ni, Mn and Si were kept at balanced levels to avoid microstructure changing. The oxide layer analysis was performed by confocal laser scanning microscopy (CLS) and scanning electron microscopy (SEM). The elemental analysis of the different phases was measured with energy dispersive X-ray spectroscopy (EDX). The Nb-alloyed steel generated a thicker Cr oxide layer. Generally elemental Nb did not provide any noticeable difference in oxide scale growth, for the specific range of Nb amount and temperature studied. High temperature oxidation up to 120h was characterized by protective Cr oxidation, after this period a non-protective Fe-based oxidation took place. Cr, Fe and Ni oxides were observed in the multilayer oxide scale.

Źródło:

Archives of Foundry Engineering; 2021, 21, 1; 125-131
1897-3310
2299-2944

Pojawia się w:

Archives of Foundry Engineering

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 99.

Tytuł:

Badania porównawcze odporności korozyjnej stali austenitycznej AISI 304L (EN 1.4307) po walcowaniu na zimno oraz po pasywowaniu w kwasie cytrynowym oraz EDTA
Comparative studies of corrosion resistance of AISI 304L (EN 1.4307) austenitic stainless steel after cold rolling and passivation in the citric acid and edetic acid

Autorzy:

Rokosz, K.
Hryniewicz, T.
Solecki, G.
Dudek, Ł.

Powiązania:

https://bibliotekanauki.pl/articles/314431.pdf

Data publikacji:

2015

Wydawca:

Instytut Naukowo-Wydawniczy "SPATIUM"

Tematy:

korozja wżerowa
stal austenityczna 304L
stal nierdzewna
pasywacja
walcowanie na zimno
kwas wersenowy
kwas cytrynowy
EDTA
pitting corrosion
AISI 304L austenitic steel
stainless steel
passivation
cold rolling
edetic acid
citric acid

Opis:

Niniejszy artykuł prezentuje badania porównawcze odporności korozyjnej austenitycznej stali stopowej AISI 304L (EN 1.4307) w roztworze Ringera. Wyniki badań przedstawiają odporność stali na korozję wżerową stali po walcowaniu na zimno oraz pasywowaniu w różnych warunkach. Badania elektrochemiczne przeprowadzono dla trzech grup próbek: po walcowaniu na zimno, po walcowaniu na zimno oraz pasywowaniu w kwasie cytrynowym i kwasie wersenowym w temperaturach 20°C i 60°C. W każdym z wymienionych przypadków zaobserwowano zjawisko korozji wżerowej. Największą odporność na korozję wżerową wykazała próbka walcowana na zimno poddana pasywowaniu w temperaturze 60°C.
This paper presents a comparative study of the corrosion resistance of austenitic steel AISI 304L (EN 1.4307) in the Ringer’s solution. The studies describe the resistance to pitting corrosion of the stainless steel after the cold rolling and passivation under different conditions. Electrochemical studies were carried out on three groups of samples: after cold rolling, after cold rolling and passivation in the citric acid and edetic acid at temperatures of 20°C and 60°C. In each of these cases, the phenomenon of pitting corrosion has been noted. The highest resistance to pitting corrosion was observed in the samples subjected to the cold rolling and passivation at 60°C.

Źródło:

Autobusy : technika, eksploatacja, systemy transportowe; 2015, 16, 6; 198-201
1509-5878
2450-7725

Pojawia się w:

Autobusy : technika, eksploatacja, systemy transportowe

Dostawca treści:

Biblioteka Nauki

/5

Artykuł

Zmień widok

• na półce

Skocz do pozycji: 100.

Tytuł:

Zbrojenie ze stali nierdzewnej jako sposób na wydłużenie trwałości konstrukcji żelbetowych
Stainless steel reinforcement as a method of extending the durability of reinforced concrete structures

Autorzy:

Jaśniok, M.

Powiązania:

https://bibliotekanauki.pl/articles/161938.pdf

Data publikacji:

2018

Wydawca:

Polski Związek Inżynierów i Techników Budownictwa

Tematy:

konstrukcja żelbetowa
trwałość
ochrona przed korozją
stal zbrojeniowa
stal nierdzewna
stal austenityczna
stal ferrytyczna
stal duplex
porównanie właściwości
reinforced concrete structure
durability
corrosion protection
reinforcing steel
stainless steel
austenitic steel
ferritic steel
duplex steel
properties comparison

Opis:

Artykuł opisuje sposób wydłużenia trwałości konstrukcji żelbetowej przez zastosowanie stali nierdzewnej zamiast tradycyjnej stali węglowej. Na wstępie wyjaśniono termin „stal nierdzewna” oraz opisano trzy rodzaje struktury stali stosowanej jako zbrojenie do betonu: austenityczną, ferrytyczną i duplex. Omówiono właściwości mechaniczne i fizyczne tych stali, a następnie porównawczo opisano przebieg i skutki ich degradacji korozyjnej wywołanej przez różne poziomy stężeń chlorków w betonie. W podsumowaniu przedstawiono przykład ciekawego zastosowania zbrojenia ze stali austenitycznej w odpowiedzialnej konstrukcji betonowej.
This article describes the way of extending the durability of reinforced concrete structure by using stainless steel instead of traditional carbon steel. The term „stainless steel” was first explained and three types of steel structure used as reinforcement for concrete were described: austenitic, ferritic and duplex. Mechanical and physical properties of these steels were discussed, and then the course and effects of their corrosion degradation caused by different levels of chloride concentrations in concrete were compared. The summary presents an interesting example of the use of austenitic steel reinforcement in a responsible concrete structure.

Źródło:

Przegląd Budowlany; 2018, 89, 11; 24-27
0033-2038

Pojawia się w:

Przegląd Budowlany