Kinetics of transformation during supersaturation and ageing of the Al-4.7%Cu alloy
Kinetyka przemian podczas przesycania i starzenia stopu Al-4,7%Cu
Autorzy:
Wierszyłłowski, I.
Wieczorek, S.
Stankowiak, S.
Samolczyk, J.
Powiązania:
https://bibliotekanauki.pl/articles/211598.pdf
Data publikacji:
2005
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej
Tematy:
kinetyka przemiany
przesycanie
stop Al-4,7%Cu
transformation kinetics
supersaturation
Al-4,7% Cu alloy
Opis:
The processes taking place during supersaturation of the Al-4.7% Cu alloy have been studied by the methods of quantitative metallography and dilatometry. The grain growth activation energy was about 95 kJ/mol, the exponent of time, n, was close to 0.4. Dissolution of precipitates has caused two - stage shrinkage of the sample which had activation energies of 90 kJ/mole (first stage, n = 0.8) and 63 kJ/mole (second stage, n = 0.4). The kinetics of the phase transformation during ageing of the Al-4.7% Cu alloy has been studied by the dilatometry and DTA (Differential Thermal Analysis). The activation energy of the precipitation processes within the range of 50-320 oC varied between 50 and 100 kJ/mole and confirmed the results obtained previously. For the precipitation processes within the range of 320-462 oC, the activation energy varied from 226-300 kJ/mole. The results obtained have been compared to literature data with good agreement.
Badano przemiany zachodzące podczas przesycania stopu Al-4,7% Cu metodami metalografii ilościowej i metodą dylatometryczną. Energia aktywacji rozrostu ziarna wynosiła ok. 95 kJ/mol, a wykładnik potęgowy n ok. 0,4. Rozpuszczanie wydzieleń i rozrostu ziarna spowodowało skurcz próbek. Przebiegał on szybciej na początku procesu (energia aktywacji ok. 95 kJ/mol, n = 0,8) a potem wolniej (energia aktywacji ok. 63 kJ/mol, n = 0,4). Kinetykę przemian fazowych podczas starzenia stopu badano metodą dylatometryczną i analizy termoróżnicowej (DTA). Energie aktywacji procesów wydzielania w zakresie temperatur 50-320 oC wynosiły od 50-100 kJ/mol i były zbliżone do uzyskiwanych wcześniej. Energie aktywacji procesów wydzieleniowych w zakresie temperatur 320-462 oC wynosiły ok. 226-300 kJ/mol i były zbliżone do wartości podawanych w literaturze.
Źródło:
Obróbka Plastyczna Metali; 2005, 16, 5; 31-37
0867-2628
Pojawia się w:
Obróbka Plastyczna Metali
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Kinetyka przemian podczas przesycania i starzenia stopu Al-4,7%Cu
Kinetics of transformation during supersaturation and ageing of the Al-4.7%Cu alloy
Autorzy:
Wierszyłłowski, I.
Wieczorek, S.
Stankowiak, S.
Samolczyk, J.
Powiązania:
https://bibliotekanauki.pl/articles/211582.pdf
Data publikacji:
2005
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej
Tematy:
kinetyka przemiany
przesycanie
stop Al-4,7%Cu
transformation kinetics
supersaturation
Al-4,7% Cu alloy
Opis:
Badano przemiany zachodzące podczas przesycania stopu Al-4,7% Cu metodami metalografii ilościowej i metodą dylatometryczną. Energia aktywacji rozrostu ziarna wynosiła ok. 95 kJ/mol, a wykładnik potęgowy n ok. 0,4. Rozpuszczanie wydzieleń i rozrostu ziarna spowodowało skurcz próbek. Przebiegał on szybciej na początku procesu (energia aktywacji ok. 95 kJ/mol, n = 0,8) a potem wolniej (energia aktywacji ok. 63 kJ/mol, n = 0,4). Kinetykę przemian fazowych podczas starzenia stopu badano metodą dylatometryczną i analizy termoróżnicowej (DTA). Energie aktywacji procesów wydzielania w zakresie temperatur 50-320 oC wynosiły od 50-100 kJ/mol i były zbliżone do uzyskiwanych wcześniej. Energie aktywacji procesów wydzieleniowych w zakresie temperatur 320-462 oC wynosiły ok. 226-300 kJ/mol i były zbliżone do wartości podawanych w literaturze.
The processes taking place during supersaturation of the Al-4.7% Cu alloy have been studied by the methods of quantitative metallography and dilatometry. The grain growth activation energy was about 95 kJ/mol, the exponent of time, n, was close to 0.4. Dissolution of precipitates has caused two - stage shrinkage of the sample which had activation energies of 90 kJ/mole (first stage, n = 0.8) and 63 kJ/mole (second stage, n = 0.4). The kinetics of the phase transformation during ageing of the Al-4.7% Cu alloy has been studied by the dilatometry and DTA (Differential Thermal Analysis). The activation energy of the precipitation processes within the range of 50-320 oC varied between 50 and 100 kJ/mole and confirmed the results obtained previously. For the precipitation processes within the range of 320-462 oC, the activation energy varied from 226-300 kJ/mole. The results obtained have been compared to literature data with good agreement.
Źródło:
Obróbka Plastyczna Metali; 2005, 16, 5; 23-30
0867-2628
Pojawia się w:
Obróbka Plastyczna Metali
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Relacje pomiędzy procesami starzenia i odkształcenia stopu Al-4,7%Cu. Badania twardości i DTA
Relationship between ageing and deformation processes of Al-4.7 Mass % Cu alloy. Hardness and DTA studies
Autorzy:
Wierszyłłowski, I.
Powiązania:
https://bibliotekanauki.pl/articles/212236.pdf
Data publikacji:
2006
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej
Tematy:
stop Al-4,7%Cu
przesycanie
starzenie
odkształcenie plastyczne
twardość
Al-4.7 Mass % Cu alloy
supersaturation
ageing
deformation
hardness
Opis:
Przeprowadzono badania twardości i DTA stopu Al-4,7%Cu poddanego przesycaniu, starzeniu i odkształceniu w rożnych warunkach i starzeniu izotermicznym w 175 oC. Deformacja po przesycaniu zwiększa liczbę dyslokacji w stopie i proporcjonalnie obniża temperatury początku wydzielania się ?", ?' i ? (Al2Cu) oraz temperatury rozpuszczania się ?" i ?'. Zgniot po przesycaniu i starzeniu, w badanym zakresie, proporcjonalnie zwiększa twardość stopu Al-4,7%Cu. Zgniot po przesycaniu podwyższa początkową twardość stopu, nie wpływa jednak na maksymalną twardość uzyskiwaną po starzeniu w badanej temperaturze. Naturalne starzenie po przesycaniu podwyższa początkową twardość stopu starzonego w 175 oC i obniża nieco jego maksymalną twardość.
Hardness studies were executed of four groups made of Al-4.7 Mass % Cu alloy: 1 the samples after supersaturation and isothermal ageing at 175 oC; 2 supersaturation, natural ageing and isothermal ageing; 3 and 4 supersaturation, isothermal ageing and plastic deformation; 5 plastic deformation after supersaturation and isothermal ageing. Isochronal DTA studies of samples the alloy were performed of two groups of samples: 1 supersaturated and 2 supersaturated and deformed after supersaturation. The DTA results show that number of dislocation introduced by plastic deformation into supersaturated alloy causes decrease the temperatures of endothermic picks of ?", ?'and ? (Al2Cu) precipitation. The exothermic picks temperatures for dissolution of ?" and ?'precipitation are also decreased. The decrease of temperatures is proportional to degree of deformation. Plastic deformation followed of supersaturation and ageing increases hardness of samples proportional to deformation degree. Deformation followed of supersaturation increase hardness at the beginning of ageing, but do not influence the maximum hardness value, natural ageing followed supersaturation acts similar as deformation.
Źródło:
Obróbka Plastyczna Metali; 2006, 17, 1; 51-56
0867-2628
Pojawia się w:
Obróbka Plastyczna Metali
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-3 z 3

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies