    Strength Properties of Ceramic Moulds Containing Spent Moulding Sand After Initial Reclamation
    Autorzy:
    Angrecki, M.
    Kamińska, J.
    Jakubski, J.
    Wieliczko, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/379908.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    ceramic shell moulds
    spending moulding sand
    reclaimed sand
    lost wax process
    strength properties
    formy ceramiczne
    piasek formierski
    właściwości wytrzymałościowe
    Opis:
    The results of testing the strength properties of experimental ceramic materials containing spending moulding sand after initial mechanical reclamation as a material for subsequent layers of the stucco composition were presented. Tests were carried out on spent moulding sands from various foundry technologies, i.e. sand with furfuryl resin and sand with hydrated sodium silicate. The spent, agglomerated moulding sand has undergone a crushing process. Next, the required granular fractions used for individual layers of the stucco material were separated. Ceramic samples, in which the spent moulding sand was a substitute for fresh silica sand in successive layers of the stucco composition, were prepared. As a reference material, identical ceramic samples were used but with all layers made from the fresh silica sand. Samples prepared in this way were used to determine the bending strength of ceramic materials in the temperature range from 20 to 900ºC. The obtained values of the bending strength have demonstrated that spent moulding sand can be used in investment casting with no adverse effect on the strength of ceramic materials.
    Źródło:
    Archives of Foundry Engineering; 2019, 3; 5-10
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Technologiczne właściwości mas formierskich z SiC z przeznaczeniem dla ceramicznych form odlewniczych dla przemysłu lotniczego
    The technological properties of SiC based slurries for manufacturing of ceramic shell moulds for aerospace industry
    Autorzy:
    Wiśniewski, P.
    Małek, M.
    Sitek, R.
    Matysiak, H.
    Kurzydłowski, K. J.
    Powiązania:
    https://bibliotekanauki.pl/articles/168709.pdf
    Data publikacji:
    2014
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
    Tematy:
    spoiwo
    odlewanie precyzyjne
    poli(alkohol winylowy)
    SiC
    masa formierska
    forma odlewnicza
    binder
    investment casting
    poly(vinyl alcohol)
    slurry
    shell moulds
    Opis:
    W artykule przedstawiono wyniki badań technologicznych właściwości mas formierskich z węglika krzemu przeznaczonych do otrzymywania elementów silników lotniczych metodą odlewania precyzyjnego. Całkowite stężenie fazy stałej w ceramicznych masach lejnych z SiC wynosiło 65% wag. Spoiwem konstrukcyjnym był nanokompozyt polimerowo-ceramiczny zawierający nanocząstki Al2O3 (IE). Jako spoiwo modyfikujące zastosowano wodny roztwór poli(alkoholu winylowego) (PVAL) 47-88 o ciężarze cząsteczkowym 47000 g/mol i stopniu hydrolizy 88%, który dodawano w ilościach 6, 10 i 15% w stosunku do proszku. Proszek SiC charakteryzowano z użyciem: wielkości cząstek metodą dyfrakcji laserowej, skaningowego mikroskopu elektronowego (SEM) oraz składu fazowego w dyfraktometrze rentgenowskim. Masy formierskie charakteryzowano pod względem: lepkości dynamicznej i względnej, gęstości, pH oraz adhezji do płyty (tzw. test płyty) oraz modelu woskowego. Pomiary te przeprowadzano przez 96 h w warunkach laboratoryjnych w temperaturze 21ºC. Otrzymane wyniki pokazały, że masy lejne w układzie SiC, nanokompozyt oraz (PVAL) charakteryzują się obiecującymi właściwościami i mają szansę zostać zastosowane do otrzymywania części silników lotniczych.
    In the present paper technological properties of silicon carbide slurries in manufacturing shell moulds for investment casting of aircraft turbine elements were studied. Ceramic SiC slurries with a solid concentration of 65 wt. % were applied. As a structural binder polymer nanocomposite containing nano Al2O3 was used. The poly(vinyl alcohol) (PVAL) 47-88 with molecular weight 47000 g/mol and hydrolysis degree 88%, used as a modification binder was added at different amount: 6, 10, 15 wt. %. Characterization of SiC powder was made by: grain size by laser diffraction, Scanning Electron Microscopy (SEM) and X-Ray diffraction (XRD) methods. The properties of ceramic slurries such as: relative and dynamic viscosity, density, pH, plate (plate weight test) and wax adhesion were studied by a range of techniques. These measurements were taken in laboratory conditions by 96 hours at temperature 21ºC.The results shows that slurries based on SiC, nanocomposite binder and PVAL meet the investment casting requirements of aircraft turbine parts and had promising properties.
    Źródło:
    Szkło i Ceramika; 2014, R. 65, nr 3, 3; 11-15
    0039-8144
    Pojawia się w:
    Szkło i Ceramika
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Ocena czasu suszenia pierwszej i drugiej warstwy ceramicznej formy odlewniczej z wykorzystaniem kamery termowizyjnej
    Thermovisual estimation of the time necessary for drying the two outer layers of a ceramic casting die
    Autorzy:
    Koralnik, M. K.
    Wiśniewski, P.
    Moszczyńska, D.
    Sitek, R.
    Mizera, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/168814.pdf
    Data publikacji:
    2017
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
    Tematy:
    ceramiczne formy odlewnicze
    masy formierskie
    nano SiO2
    suszenie
    termowizja
    odlewanie metodą traconego wosku
    shell moulds
    slurries
    drying
    thermovision
    investment casting
    Opis:
    W artykule przedstawiono wyniki badań dotyczące oceny czasu suszenia przymodelowej oraz konstrukcyjnej warstwy ceramicznej formy odlewniczej. W celu wykonania pomiarów wytworzono dwie testowe masy lejne, które posłużyły do wytworzenia odpowiednio pierwszej oraz konstrukcyjnej warstwy formy ceramicznej. Do wykonania mas formierskich zastosowano proszki tlenku glinu i wodne spoiwo na bazie krzemionki koloidalnej. Mikrostrukturę proszków badano przy użyciu elektronowego mikroskopu skaningowego, natomiast rozmiar cząstek określono przy pomocy analizatora laserowego. Gęstwy, które wykorzystano do budowy badanych warstw ceramicznej formy odlewniczej, przygotowano w mieszadle mechanicznym. Ich parametry, takie jak: temperatura, pH, lepkość względna i dynamiczna, były odczytywane przez pięć dni z rzędu. Pomiary termowizyjne przeprowadzono w pomieszczeniu o kontrolowanej temperaturze i znanej wilgotności. Wykazano, że formy ulegają całkowitej dehydratacji w momencie osiągnięcia temperatury otoczenia.
    The paper evaluates the drying time of two layers (model and constructional) of ceramic casting dies. The slurries were prepared using the aluminum oxide and a colloidal silica-based water binder. The constituents were examined in a scanning electron microscope (SEM), their particle size was determined in a LA-950 analyzer. Then, they were mixed in a mechanical mixer and the properties of the mixtures, such as the temperature, pH, as well as relative and dynamic viscosity were monitored using a thermo-visual camera during five consecutive days. After reaching the ambient temperature, the dies appeared to be fully dehydrated.
    Źródło:
    Szkło i Ceramika; 2017, R. 68, nr 1, 1; 6-10
    0039-8144
    Pojawia się w:
    Szkło i Ceramika
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies