Tytuł:
Investigations of corrosion behaviour of SnSb12Cu6Pb alloy in 0.1M H2SO4 and 0.5M NaCl solution
Autorzy:
Hrabia-Wiśnios, J.
Leszczyńska-Madej, B.
Kowalik, R.
Powiązania:
https://bibliotekanauki.pl/articles/368272.pdf
Data publikacji:
2020
Wydawca:
Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
Tematy:
Tin-based bearing alloys
corrosion behaviour
passivation film
selective corrosion
microstructure
stopy łożyskowe
zachowanie korozyjne
korozja selektywna
mikrostruktura
Opis:
Purpose: The results presented the microstructure and corrosive behavior of SnSb12Cu6Pb alloy (B82) in H2SO4 aqueous solution and NaCl aqueous solution. Design/methodology/approach: The electrochemical corrosion has been investigated in two different aqueous solutions: 0.1M sulfuric acid (H2SO4) and 0.5M sodium chloride (NaCl) solution measuring of potential changes relative to immersion time and conducting mass loss test. Microscopic investigations before and after corrosion tests were made using scanning electron microscopy. Findings: The obtained results indicate very good corrosion resistance of the alloy tested in NaCl solution. Corrosion progresses faster in a sulfuric acid aqueous solution compared to sodium chloride aqueous solution. Also, it was found that the dominant mechanism of corrosion degradation in both solutions is selective corrosion which is a particularly undesirable type of corrosion because it involves the loss of one alloying component and the formation of porous structure on the alloy surface. Research limitations/implications: The aqueous solutions used in this study are not a natural working environment of the bearing. However, a comparison of acidic and neutral solutions allows explaining the corrosion behavior of tin babbitts due to contaminants of oil lubricants. Further research should be conducted in more aggressive environments characteristic of industrial conditions. Practical implications: One of the important properties of bearing alloys are corrosion resistance. Corrosion properties are extremely important for the transport and storage of metallic components before they are used. Also, the working environment can have a destructive effect on the properties of the materials used. Industry environment, aging stagnant oil, and some acids may lead to selective corrosion of the tin, copper, lead, or antimony components and leaving a rough and weakened the babbitt surface. Electrochemical corrosion can contribute to the acceleration of bearing wear and consequent to bearing damage. Originality/value: Studies of the corrosion of tin-babbitt bearings are not extensive in the literature due to rare tin corrosion. This study could be an important complement to knowledge about the corrosion behavior of tin-based bearing alloys.
Źródło:
Journal of Achievements in Materials and Manufacturing Engineering; 2020, 101, 1; 5-14
1734-8412
Pojawia się w:
Journal of Achievements in Materials and Manufacturing Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies