Leaching behaviour of zinc from a smithsonite ore in sodium hydroxide solutions
Autorzy:
Ehsani, Ilhan
Ucyildiz, Ayse
Obut, Abdullah
Powiązania:
https://bibliotekanauki.pl/articles/110552.pdf
Data publikacji:
2019
Wydawca:
Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
Tematy:
alkaline leaching
calcium zincate
nonsulfide zinc ore
smithsonite
zinc carbonate
Opis:
In this study, the leaching behaviour of zinc from a smithsonite ore sample (23.43% Zn) having goethite and calcite as main gangue minerals was investigated in sodium hydroxide solutions using Xray diffraction and chemical analyses. Within the studied NaOH concentration range (1-4 mole/dm3), higher leaching ratio values for Zn were obtained by leaching at 298 K because of the decreased stability of soluble zincate species in solution at higher temperatures. When the concentration of NaOH solution was increased from 1 to 3 mole/dm3 at 298 K, leaching ratio value of Zn increased from 3.8 to 70.1%. At 4 mole/dm3 NaOH concentration, Zn leaching ratio value (70.9%) levelled off due to the formation of solid hydrated calcium zincate phase in leaching solution. On the other hand, very low leaching ratio values of Zn were obtained by leaching in 1 mole/dm3 NaOH solution at 298 K (3.8%) and 363 K (1.4%) due to the formation of solid zinc hydroxide and solid zinc oxide phases, respectively. It was observed that increasing leaching time from 1800 to 14400 s at 3 mole/dm3 NaOH concentration, favoured the formation of hydrated calcium zincate phase and so decreased the leaching ratio of Zn to a lower value (60.6%). The effect of solid/liquid ratio was also investigated and it was found that when solid/liquid ratio was decreased, Zn leaching ratio values decreased at constant OH/Zn mole ratio and increased at constant NaOH concentration conditions. Besides, for some of the experiments, leaching ratio values of lead were also given.
Źródło:
Physicochemical Problems of Mineral Processing; 2019, 55, 2; 407-416
1643-1049
2084-4735
Pojawia się w:
Physicochemical Problems of Mineral Processing
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies