- Tytuł:
-
Nitrogen And Oxygen Amount In Weld After Welding With Micro-Jet Cooling
Zawartość azotu i tlenu w stalowym spoinie po spawaniu z chłodzeniem mikro-jetowym - Autorzy:
-
Węgrzyn, T.
Piwnik, J. - Powiązania:
- https://bibliotekanauki.pl/articles/353105.pdf
- Data publikacji:
- 2015
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
welding
micro-jet cooling gases
weld
metallographic structure
nitrogen and oxygen in weld
spawanie
gaz chłodzący mikro-jetowy
spaw
struktury metalograficzne
azot i tlen w spoinie - Opis:
-
Micro-jet cooling after welding was tested only for MIG welding process with argon, helium and nitrogen as a shielded gases. A paper presents a piece of information about nitrogen and oxygen in weld after micro-jet cooling. There are put down information about gases that could be chosen both for MIG/MAG welding and for micro-jet process. There were given main information about influence of various micro-jet gases on metallographic structure of steel welds. Mechanical properties of weld was presented in terms of nitrogen and oxygen amount in WMD (weld metal deposit).
Chłodzenie mikro-jetowe było stosowane tylko w spawalniczym procesie MIG, gdzie gazem osłonowym były argon, hel i azot. W artykule przedstawiono informacje na temat zawartości azotu i tlenu w spoinie po chłodzeniu mikro-jetowym. Podano informacje zarówno dla gazów, które mogą być wybrane dla spawania MIG/MAG i dla mikro-jetowego procesu. Uzyskano informacje o wpływie doboru gazu mikro-jetowego na strukturę metalograficzną stalowych spoin. Własności mechaniczne złącza podano w funkcji zawartości azotu i tlenu w stopiwie. - Źródło:
-
Archives of Metallurgy and Materials; 2015, 60, 2A; 657-660