Tytuł:
Functional properties of aluminide layer deposited on Inconel 713 LC Ni-based superalloy in the CVD process
Właściwości użytkowe warstwy aluminidkowej wytworzonej w procesie CVD na stopie niklu Inconel 713 LC
Autorzy:
Yavorska, M.
Sieniawski, J.
Zielińska, M.
Powiązania:
https://bibliotekanauki.pl/articles/354066.pdf
Data publikacji:
2011
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
aluminide layer
low-activity CVD process
Inconel 713LC superalloy
oxidation resistance
Opis:
In the paper there was established the influence of temperature and process time on the functional properties of aluminide layer deposited on nickel based - Inconel 713 LC superalloy. The low-activity CVD processes were done at the temperature 760 and 1050°C during 4 and 8h. The effects of aluminizing were verified by the use of optical microscope (microstructure and depth layer); scanning electron microscope and energy dispersive spectroscope (chemical composition on the surface and cross-section of aluminide layer). The high temperature oxidation resistance of superalloy was a main criterion of aluminizing process effectiveness. Therefore, the isothermal oxidation tests were performed at the temperature 1150°C during 100h in air atmosphere. Surface topography of the aluminide layer was carried out after isothermal oxidation test. Hardness measurements on the cross-section of aluminide layer were performed before and after oxidation tests. On the grounds of obtained results it was found that aluminizing process temperature of 1050°C let to get a diffusion layer with a proper structure and properties. The temperature increase from 760°C to 1050°C and the time prolongation from 4 to 8 h improves the oxidation resistance of superalloy. The XRD analysis from the surface of aluminide layer has confirmed the presence of thermodynamically stable oxide layer Al(Cr)2O3 with good protective properties.
W pracy określono wpływ parametrów procesu CVD (temperatura, czas) na właściwości użytkowe warstwy aluminidkowej wytworzonej na podłożu z stopu niklu Inconel 713 LC. Proces niskoaktywny prowadzono CVD w temperaturze 760 i 1050°C oraz w czasie 4 i 8h. Efekty procesu aluminiowania weryfikowano w badaniach mikroskopowych (mikrostruktura i głębokość warstwy) oraz w badaniach składu chemicznego na powierzchni i przekroju warstwy. Jako kryterium efektywności procesu chemicznego osadzania z fazy gazowej przyjęto odporność na utlenianie w wysokiej temperaturze. Wykonano próbę utleniania izotermicznego w temperaturze 1150°C i w czasie 100h w atmosferze powietrza. Prowadzono badania topografii powierzchni warstwy aluminidkowej po procesie utleniania izotermicznego. Określono rozkład twardości na przekroju warstwy przed i po procesie utleniania. Na podstawie uzyskanych wyników badań stwierdzono, że temperatura procesu 1050°C pozwala uzyskać warstwę dyfuzyjną o prawidłowej budowie i właściwościach. Podwyższenie temperatury do 1050°C oraz zwiększenie czasu procesu aluminiowania do 8h powoduje znaczny wzrost żaroodporności. Analiza składu fazowego na powierzchni warstwy wykazała obecność zgorzeliny składającej się z termodynamicznie stabilnego tlenku Al(Cr)2O3 o dobrych właściwościach ochronnych.
Źródło:
Archives of Metallurgy and Materials; 2011, 56, 1; 187-192
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Some properties of platinum and palladium modified aluminide coatings deposited by CVD method on nickel-base superalloys
Właściwości warstw aluminidkowych modyfikowanych platyna i palladem wytworzonych metodą CVD na podłożu nadstopów niklu
Autorzy:
Zagula-Yavorska, M.
Sieniawski, J.
Gancarczyk, T.
Powiązania:
https://bibliotekanauki.pl/articles/355003.pdf
Data publikacji:
2012
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
stopy niklu
CVD
aluminiowanie
platinum and palladium modified aluminide coating
low-activity CVD process
Ni-base superalloy
oxidation resistance
Opis:
In the paper some functional properties (hardness and oxidation resistance) of platinum and palladium modified aluminide coatings deposited by the CVD method on a nickel-based superalloy were determined. The platinum and palladium microlayers, 3 μm thick were deposited by electroplating process. The heat treatment of electroplating microlayers was performed for 2h at the temperature 1050 degree Celsjus in an argon atmosphere as to increase adhesion between the coating and the substrate. The low activity CVD aluminizing process of platinum heat treated coatings 3 μm thick at the 1050degree Celsjus for 8h using IonBond equipment was performed. The effects of aluminizing process were verified by the use of an optical microscope (microstructure and coating thickness); a scanning electron microscope and an energy dispersive spectroscope (chemical composition of the surface and cross-section of the modified aluminide coating). The hardness measurements on the cross-section of nonmodified and platinum or palladium modified aluminide coatings were performed. Oxidation tests of modified aluminide coatings at the 1100 degree Celsjus for 1000 h in the air atmosphere were carried out. On the grounds of the obtained results it was found that the main phase of the platinum modified aluminide coating is β-(Ni,Pt)Al. Consequently, the palladium modification of aluminide coating causes the formation of β-(Ni,Pd)Al phase. The platinum modified aluminide coating has better oxidation resistance than nonmodified and palladium modified aluminide coating. The XRD analysis of the surface of oxidized platinum modified aluminide coating confirmed the presence of the thermodynamically stable oxide layer Al2O3, that has good protective properties. The oxides of NiAl2O4, Al1:98Cr0:02O3 and TiO2 were found on the surface of the palladium modified aluminide coating after 1000 h oxidation at the 1100 degree Celsjus the in the air atmosphere.
W pracy określono niektóre właściwości użytkowe (twardość oraz żaroodporność) warstwy aluminidkowej modyfikowanej platyną i palladem wytworzonej metodą CVD na podłożu nadstopów niklu, polikrystalicznym Inconel 713 LC i monokrystalicznym - CMSX 4. Powlokę platyny i palladu (grubość - 3μm) wytworzono metodą galwaniczną. Poprawę przyczepności powłoki galwanicznej do podłoża uzyskano przez wygrzewanie w temperaturze 1050 stopni Celsjusza w czasie 2 h w atmosferze argonu. Warstwę aluminidkowa wytworzono w procesie niskoaktywnym CVD (temperatura - 1050 stopni Celsjusza, czas - 8h). Efekty procesu aluminiowania weryfikowano w badaniach mikroskopowych (mikrostruktura i głębokość warstwy) oraz w analizie składu chemicznego na powierzchni i przekroju warstwy modyfikowanej. Pomiary twardości prowadzono na przekroju niemodyfikowanej warstwy aluminidkowej oraz warstwie modyfikowanej platyna i palladem. Próbę zmęczenia cieplnego wykonano w temperaturze 1100 stopni Celsjusza i w czasie 1000 h w atmosferze powietrza. Analiza uzyskanych wyników badan pozwała stwierdzić, ze głównym składnikiem fazowym mikrostruktury modyfikowanej platyną warstwy aluminidkowej są kryształy fazy &beta ;-(Ni,Pt)Al. Modyfikowanie palladem warstwy aluminidkowej prowadzi do tworzenia się kryształów fazy &beta ;-( -(Ni,Pd)Al jako głównego składnika fazowego mikrostruktury warstwy. Warstwę aluminidkowa modyfikowaną platyną charakteryzuje większa żaroodporność w porównaniu do warstwy aluminidkowej modyfikowanej palladem lub niemodyfikowanej. Analiza składu fazowego na powierzchni warstwy aluminidkowej modyfikowanej platyna po próbie zmęczenia cieplnego wykazała obecność zgorzeliny składającej sie z termodynamicznie stabilnego tlenku Al.2O3: Tlenek NiAl2O4; Al1:98Cr0:02O3 oraz rutyl TiO2 zaobserwowano na powierzchni warstwy aluminidkowej modyfikowanej palladem po 1000 h utleniania w temperaturze 1100 stopni Celsjusza w atmosferze powietrza.
Źródło:
Archives of Metallurgy and Materials; 2012, 57, 2; 503-509
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies