- Influence of printing direction on 3D printed ABS specimens
- Autorzy:
-
Markiz, Nassim
Horváth, Eszter
Ficzere, Péter - Powiązania:
- https://bibliotekanauki.pl/articles/1839511.pdf
- Data publikacji:
- 2020
- Wydawca:
- Stowarzyszenie Menedżerów Jakości i Produkcji
- Tematy:
-
additive manufacturing
ABS
tensile test
FDM
printing direction
produkcja dodatkowa
próba rozciągania
kierunek druku - Opis:
- In the recent years, additive manufacturing became an interesting topic in many fields due to the ease of manufacturing complex objects. However, it is impossible to determine the mechanical properties of any additive manufacturing parts without testing them. In this work, the mechanical properties with focus on ultimate tensile strength and modulus of elasticity of 3D printed acrylonitrile butadiene styrene (ABS) specimens were investigated. The tensile tests were carried using Zwick Z005 loading machine with a capacity of 5KN according to the American Society for Testing and Materials (ASTM) D638 standard test methods for tensile properties of plastics. The aim of this study is to investigate the influence of printing direction on the mechanical properties of the printed specimens. Thus, for each printing direction ( and ), five specimens were printed. Tensile testing of the 3D printed ABS specimens showed that the printing direction made the strongest specimen at an ultimate tensile strength of 22 MPa while at printing direction it showed 12 MPa. No influence on the modulus of elasticity was noticed. The experimental results are presented in the manuscript.
- Źródło:
-
Production Engineering Archives; 2020, 26, 3; 127-130
2353-5156
2353-7779 - Pojawia się w:
- Production Engineering Archives
- Dostawca treści:
- Biblioteka Nauki