Influence of notch (TIP) radius on fatigue crack growth rate
Wpływ promienia (wierzchołka) karbu na prędkość wzrostu pęknięć zmęczeniowych - Autorzy:
-
Rozumek, D.
Macha, A.
Lazzarin, P.
Meneghetti, G. - Powiązania:
- https://bibliotekanauki.pl/articles/280366.pdf
- Data publikacji:
- 2006
- Wydawca:
- Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
- Tematy:
-
zakres integralny
stosunek ładunku
karby
fatigue crack growth
J-integral range
load ratio
notch - Opis:
-
The paper deals with the problem of fatigue crack propagation from notches in plates made of FeP04 steel and AA356-T6 aluminium alloy. The tests were performed under different stress ranges by keeping the nominal load ratio (R=0.1) constant. The specimens were weakened by nearly sharp and blunt two sided notches. The results of the fatigue tests were then reanalysed in terms of the J-integral range including influence of the notch. It was observed that the blunter notches are, the higher fatigue crack growth rate is.
W pracy przedstawiono propagację pęknięć zmęczeniowych, w próbkach płaskich z karbami, wykonanych ze stali FeP04 i stopu aluminium AA356- T6. Badania wykonywano przy różnych zakresach naprężeń i stałym współczynniku asymetrii cyklu (R = 0.1). Próbki były osłabione przez dwustronne ostre i łagodne karby. Wyniki badail zmęczeniowych opisano za pomocą zakresu całki J z uwzględnieniem wpływu karbu. Stwierdzono, że im łagodniejszy karb, tym większa prędkość wzrostu pęknięć zmęczeniowych. - Źródło:
-