    Tytuł:
    The impact of joints’ quality on their strength in ST 3150 conveyor belts
    Autorzy:
    Kozłowski, T.
    Powiązania:
    https://bibliotekanauki.pl/articles/89144.pdf
    Data publikacji:
    2015
    Wydawca:
    Politechnika Wrocławska. Wydział Geoinżynierii, Górnictwa i Geologii. Instytut Górnictwa
    Tematy:
    conveyor belt
    joint strength
    joint defects
    Opis:
    Article discusses issues related to the weakened strength of the joints in conveyor belts. Joints are the weakest element of the belt and should be taken aimed at eliminating the errors made that may be caused by multiple factors. Every breakdown generates additional costs in the company so this is important to decrease their number. All analyzed joints were made using belts with steel cords. The results were obtained from the Conveyor Transport Laboratory at the Wroclaw University of Technology. The assessment showed a significant impact of the working defects on joint strength. Also the trend analysis performed on the samples of regenerated belts showed a linear decrease in strength along with the degree of regeneration.
    Źródło:
    Mining Science; 2015, 22, Special Issue 2; 47-55
    2300-9586
    2353-5423
    Pojawia się w:
    Mining Science
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Causes of the cracks in the pipeline made of the 15HM steel
    Autorzy:
    Słania, J.
    Krawczyk, R.
    Gątarek, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/354316.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    pipeline
    cracks
    welding process
    welded joint
    welding defects
    Opis:
    Issues referring to cracks in the pipelines made of the 15HM steel are described. Metallographic specimen of welded joints are provided. The results of impact strength tests, hardness tests and static tensile tests are given. Tests results as well as direct and indirect causes of the pipeline cracks are shown.
    Źródło:
    Archives of Metallurgy and Materials; 2017, 62, 1; 99-104
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Identification of Lack of Fusion and Incomplete Penetration in Butt Weld Joint by Ultrasonic Phased Array Method and X-Ray Method
    Autorzy:
    Koňár, R.
    Mičian, M.
    Boháčik, M.
    Gucwa, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/357016.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    internal defects
    butt weld joint
    nondestructive testing
    lack of fusion
    incomplete penetration
    Opis:
    The main goal of the article is to identify artificially created defects like lack of fusion and incomplete penetration in buttweld joint using non-destructive volumetric methods. These defects are the most serious defects in welds of steel constructionsfrom the safety point of view. For identification, an ultrasonic phased array technique and a conventional X-ray using digital imaging were used. The theoretical part of the article describes the current state of the given issue and provides basic theoretical knowledge about ultrasonic and X-ray welding tests. In the experimental part, the procedure and results of testing butt weld joint are described by both non-destructive methods. The butt weld joint was made from steel S420MC. Each indication obtained by the ultrasonic and x-ray technique is supplemented by the macrostructure of the weld taken from the indication position. The results of the experimental work mentioned in the article point to the possibility and reliability of the identification of melting defects by selected nondestructive methods in terms of their character and orientation.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 3; 1117-1124
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The influence of welded joint quality on safety and reliability in operation
    Autorzy:
    Bokuvka, O.
    Liptakova, T.
    Palcek, P.
    Chalupova, M.
    Trsko, L.
    Powiązania:
    https://bibliotekanauki.pl/articles/111736.pdf
    Data publikacji:
    2013
    Wydawca:
    Stowarzyszenie Menedżerów Jakości i Produkcji
    Tematy:
    rails
    pipes
    welded joint
    defects
    fractures
    causes
    szyny
    rury
    złącza spawane
    wady
    pęknięcia
    przyczyny
    Opis:
    The quality of welded joint is an assumption of long-term reliability in operation. On the contrary, defective work of bad quality welded joint leads to fracture and crashes of plants. In this paper the authors state that experimentally obtained causes of rails and pipes fractures were the result of bad realization of welded joint. Pores, blowholes, slags, lack of fusion, non-plastic non-metallic particles, cracks, shrink holes were the defects observed in the welded joint area. These defects substantially decreased the load-bearing cross section and the final result was fracture. The railway and high-pressure gas lines out of operation are undesirable and accompanied by considerable financial losses.
    Źródło:
    Production Engineering Archives; 2013, 1, 1; 6-9
    2353-5156
    2353-7779
    Pojawia się w:
    Production Engineering Archives
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-4 z 4

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies