Tytuł:: A Study of Susceptibility and Evaluation of Causes of Cracks Formation in Braze-Weld Filler Metal in Lap Joints Aluminum – Carbon Steel Made with Use of CMT Method and High Power Diode Laser
Autorzy:: Adamiak, M.
Wyględacz, B.
Czupryński, A.
Górka, J.
Powiązania:: https://bibliotekanauki.pl/articles/958197.pdf
Data publikacji:: 2017
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: braze-welding
intermetallic compound phase
high power diode laser
brazing
Opis:: In this article results of studies on cracks formation susceptibility in braze-welded joints of thin aluminum sheets and double-sided zinc galvanized steel sheets for car body parts made by laser brazing with high power diode laser ROFIN DL 020 and CMT MIG-brazing, with filler material in form of powder and wire accordingly, were presented. Optimal welding parameters were determined by visual acceptance criteria. On joints made with optimal parameters further examinations were carried. Results of macro- and microscopic metallographic examinations, structural roentgenography, EDS microanalysis and hardness tests were presented. Causes of brittle intermetallic Fe-Al phases formation in Al-matrix filler metal in dissimilar aluminum – zinc plated carbon steel joints were pointed.
Źródło:: Archives of Metallurgy and Materials; 2017, 62, 4; 2113-2123
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Laser welding of stainless steel
Autorzy:: Kurc-Lisiecka, A.
Lisiecki, A.
Powiązania:: https://bibliotekanauki.pl/articles/368297.pdf
Data publikacji:: 2020
Wydawca:: Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
Tematy:: laser welding
AISI 304 steel
high power diode laser
HPDL
spawanie laserowe
stal AISI 304
laser diodowy dużej mocy
Opis:: Purpose: of this paper was to analyze the influence of the basic parameters of laser welding (i.e. laser beam power and welding speed, as well as energy input) of butt joints of the 2.0 mm thick stainless steel AISI 304 sheets on the weld shape and joint quality. Design/methodology/approach: The preliminary trials of simulated laser welding by melting the austenitic stainless steel sheets (the so called bead-on-plate welding), as well as the welding of the test butt joints, were carried out using the high-power diode laser (HPDL) ROFIN DL 020, without the additional material (the technique of autogenous welding). A crucial parameter that determines both the mechanical properties and the corrosive resistance of a joint (the region of a weld and HAZ - heat affected zone) in the case of stainless steels with austenitic structure is energy input, which should be kept at a minimum, and at the same time full penetration and a proper shape of the fusion zone should be ensured. The investigations included the macrostructure and microstructure observations by light microscopy, researches of mechanical properties in a static tensile test and also microhardness measurements made by Vickers method. Findings: The results have shown that it is possible to provide a proper shape of the weld of fine-grained structure and narrow heat affected zone, but it requires careful selection of the welding parameters, especially a low energy input. The microhardness measurements showed that the in case of welding the butt joints using the high-power diode laser in HAZ area a slight increase in microhardness to approx. 185HV0.2 compared to base material (160-169HV0.2) and a decrease in microhardness in the fusion zone (FZ) to approx. 140- 150HV0.2 have been observed. All welded sample broke from the joint during the testing at tensile stress between 585 MPa and 605 MPa with corresponding percentage elongation in the range of 45-57%. It can be found that the joints strength is not less than the strength of the base metal of 2.0 mm thick AISI 304 austenitic stainless steel sheet. Research limitations/implications: Studies of the weldability of stainless steels indicate that the basic influence on the quality of welded joints and reduction of thermal distortions has the heat input of welding, moreover the highest quality of welded joints of austenitic stainless steel sheets are ensured only by laser welding. Practical implications: The laser welding technology can be directly applied for welding of austenitic steel AISI 304 sheets 2.0 mm thick. Originality/value: Application of high power diode laser for welding of austenitic stainless steel AISI 304.
Źródło:: Journal of Achievements in Materials and Manufacturing Engineering; 2020, 98, 1; 32-40
1734-8412
Pojawia się w:: Journal of Achievements in Materials and Manufacturing Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "high power diode laser" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język