    Tytuł:
    Fractography analysis of Inconel 718 fatigued at 700°C
    Autorzy:
    Jambor, M.
    Belan, J.
    Bokuvka, O.
    Novy, F.
    Powiązania:
    https://bibliotekanauki.pl/articles/111594.pdf
    Data publikacji:
    2016
    Wydawca:
    Stowarzyszenie Menedżerów Jakości i Produkcji
    Tematy:
    Inconel 718
    high temperature fatigue
    fractography analysis
    zmęczenie cieplne
    nadstop na bazie niklu
    analiza fraktograficzna
    odkształcenia plastyczne
    Opis:
    This work deals with the fractography analysis of nickel-base superalloy Inconel 718 fatigued at 700°C in air atmosphere in the high cycle region. During cyclic loading of this alloy at high temperatures some different mechanisms compared to cyclic loading at ambient temperature take place. Cyclic plastic deformation at high temperatures causes some structural changes, which could have some influence.
    Źródło:
    Production Engineering Archives; 2016, 13, 4; 20-25
    2353-5156
    2353-7779
    Pojawia się w:
    Production Engineering Archives
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Badania fraktograficzne zawiasu notebooka
    Fractographic examinations of the laptop hinge
    Autorzy:
    Stasiak, Z.
    Łukasik, D.
    Szala, M.
    Beer-Lech, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/101842.pdf
    Data publikacji:
    2015
    Wydawca:
    Politechnika Lubelska. Polskie Towarzystwo Promocji Wiedzy
    Tematy:
    fraktografia
    struktura
    analiza
    przełom
    fractography
    structure
    analysis
    fracture
    Opis:
    W pracy podjęto problem identyfikacji przyczyny uszkodzenia zawiasu pokrywy matrycy laptopa. Biorąc pod uwagę mechaniczne i materiałowe przyczyny wystąpienia awarii podjęto badania mające na celu określenie czy do uszkodzenia doszło z przyczyn powstałych w procesie produkcji czy niewłaściwego użytkowania. Przeprowadzono badania fraktograficzne umożliwiają identyfikację mechanizmów utraty spójności materiału na podstawie charakterystycznych cech przełomu, które wiążą się z mechanizmem pękania, z torem pęknięcia i zachowaniem się materiału (odpowiedzią materiału) w procesie odkształcania i pękania. Ponadto wykorzystano spektralną analizę chemiczną służącą do jakościowej i ilościowej oceny składu chemicznego uszkodzonego elementu. Obserwacja przy użyciu mikroskopów stereoskopowego i elektronowego dały możliwość identyfikacji struktury materiału oraz bardzo dokładną ocenę występującej wady. Ustalono, że przedmiot został wykonany metodą odlewania stopów metali lekkich, w tym przypadku stopu cynku z aluminium, co potwierdzają dane producentów oraz analiza składu chemicznego uszkodzonego elementu. Przeprowadzone badania wykazały, iż przełom został zapoczątkowany obecnością karbu. Wada ta powstała na etapie wytwarzania elementu doprowadzając do trwałego uszkodzenia przedmiotu. Ponadto, podczas demontażu uszkodzonej części zaobserwowano duży luz w elemencie łączenia uszkodzonego elementu do pozostałych, tj. śruby. Mogło to prowadzić do przyspieszonego ujawnienia powstałej wady na skutek eksploatacji, niekoniecznie niewłaściwej. Sposób mocowania mógł też świadczyć o niewłaściwym montażu elementów.
    This paper discusses the problem of identifying the cause of damage to the laptop’s cover hinge. Considering defects of the material or mechanical background, a sequence of examinations was conducted to determine whether damage happened for reasons arising in the manufacturing process, the assembling process or the improper handling. Fractographic examinations enable the identification of mechanisms of the material cohesion losing based on characteristic features of the fracture which are connected with the mechanism of cracking, with the path of the crack and behaving of material (with reply of material) in the deforming and cracking process. Moreover a spectral chemical analysis, for a qualitative and quantitative evaluation of the chemical composition of the damaged element was used. Observation using stereoscopic microscopes and electron made it possible to identify the structure of the material and a very accurate assessment of defects occurring. It was established that the item was made by casting, and the fracture was initiated by the presence of the notch. This defect arose at the manufacturing process of the element which led to the permanent damage of the item. Moreover, during disassembly of the damaged part, large loose in the join of the damaged element to screws, was observed. This could lead for accelerated reveal of the defect, arising as a result of the usage, not necessarily wrong. The way of attachment could also suggest improper assembly of the elements.
    Źródło:
    Journal of Technology and Exploitation in Mechanical Engineering; 2015, 1, 1-2; 166-177
    2451-148X
    Pojawia się w:
    Journal of Technology and Exploitation in Mechanical Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Fractographic Analysis Of Selected Boron Steels Subjected To Impact Testing
    Analiza fraktograficzna wybranych stali z borem w badaniach udarnościowych
    Autorzy:
    Dudziński, W.
    Konat, Ł.
    Białobrzeska, B.
    Powiązania:
    https://bibliotekanauki.pl/articles/355898.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    low-alloy steels with boron
    microstructural analysis
    impact strength
    fractography
    niskostopowa stal z borem
    analiza mikrostruktury
    udarność
    faktografia
    Opis:
    In this paper dynamic properties of low-alloy boron steels – Hardox 500, B27 and HTK 900H in delivered state (after hardening and tempering) are considered. Charpy V-notch (CVN) test results in connection with fractography in the ductile-to-brittle transition temperature region were analyzed. Obtained from CVN test the impact transition curve, not always predicts properly a behavior of materials in conditions of dynamic loading. So an analyze of character of fracture helps to evaluate the real behavior of materials. Tested samples were cut out longitudinally in relation to cold work direction. The results of CVN test for selected steels, in temperatures: −40°C, −20°C, 0°C and +20°C are presented. Regarding ductile-to-brittle transition temperature, there is a significant difference taking into account values of Charpy V energy absorbed and a character of fracture.
    W artykule przeprowadzono rozważania na temat dynamicznych właściwości niskostopowych stali z borem – Hardox 500, B27 oraz HTK 900H w stanie dostarczenia (po hartowaniu i odpuszczaniu). Przeprowadzono próbę udarności Charpy’ego w zakresie temperaturowego przejścia plastyczno-kruchego w powiązaniu z analizą fraktograficzną. Wyznaczona na podstawie wyników próby Charpy’ego udarnościowa krzywa przejścia, nie zawsze prawidłowo charakteryzuje zachowanie się materiału w warunkach obciążeń dynamicznych. Dlatego też fraktografia może uściślić rzeczywiste zachowanie się materiału. Próby przeprowadzono na próbkach wzdłużnych do kierunku przeróbki plastycznej w temperaturach: −40°C, −20°C, 0°C i +20°C. Stwierdzono występowanie znaczącej różnicy w określeniu temperatury przejścia w przypadku, gdy jest ona wyznaczona w oparciu o wynik próby udarności, a także gdy wyznaczono ją opierając się na charakterze przełomu.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 3; 2373-2378
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies