Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

Wyszukujesz frazę "cyclic elements" wg kryterium: Temat


Wyświetlanie 1-2 z 2
Tytuł:
Size levels for arcs
Autorzy:
Nadler, Sam
West, T.
Powiązania:
https://bibliotekanauki.pl/articles/1214951.pdf
Data publikacji:
1992
Wydawca:
Polska Akademia Nauk. Instytut Matematyczny PAN
Tematy:
hyperspace
cyclic elements
absolute retract
Opis:
We determine the size levels for any function on the hyperspace of an arc as follows. Assume Z is a continuum and consider the following three conditions: 1) Z is a planar AR; 2) cut points of Z have component number two; 3) any true cyclic element of Z contains at most two cut points of Z. Then any size level for an arc satisfies 1)-3) and conversely, if Z satisfies 1)-3), then Z is a diameter level for some arc.
Źródło:
Fundamenta Mathematicae; 1992, 141, 3; 243-255
0016-2736
Pojawia się w:
Fundamenta Mathematicae
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Effect of Rare Earth Cerium Addition on Oxidation Behavior of Co-Al-W Alloys at 800°C
Autorzy:
Migas, Damian
Liptáková, Tatiana
Moskal, Grzegorz
Powiązania:
https://bibliotekanauki.pl/articles/2048827.pdf
Data publikacji:
2022
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
rare earth elements
REE
cyclic oxidation
γ-γ′ cobalt-based superalloys
Co-Ce
Opis:
The γ/γ′ Co-based alloys are a new class of cobalt superalloys, which are characterized by remarkable high temperature strength owing to strengthening by γ′-Co3(Al, X) phases. In this investigation, the effect of cerium addition on oxidation behavior of model Co-Al-W alloys was studied. The introduction of Ce aimed at improvement of the oxidation resistance of γ′-forming Co-based superalloys. The minor additions of cerium (0.1, 0.5 at.%) were added to the base alloy Co-9Al-9W. The alloys were prepared via induction vacuum melting (VIM). Further, a primary microstructure of the alloys was analyzed with particular regard to a segregation of Ce. The thermogravimetric analysis (TG) under non-isothermal conditions was used to preliminary estimate the oxidation behavior of alloys at different temperatures. During experiment, differential thermal analysis (DTA) was performed simultaneously. After this test, cyclic oxidation expermients was carried out at 800°C for 500 h. In as-cast state, Ce segregates to interdendritic areas and forms intermetallic phases. The effect connected with melting of interdendritic precipitates was observed at 1160°C. Ce-containing alloys were less prone of oxide spallation. Moreover, oxidation rate of these alloys substantially decreased after 100h of oxidation, whereas mass of the sample corresponding to base alloy continued to increase.
Źródło:
Archives of Metallurgy and Materials; 2022, 67, 1; 203-208
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-2 z 2

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies