    Tytuł:
    Leaching behaviour of zinc from a smithsonite ore in sodium hydroxide solutions
    Autorzy:
    Ehsani, Ilhan
    Ucyildiz, Ayse
    Obut, Abdullah
    Powiązania:
    https://bibliotekanauki.pl/articles/110552.pdf
    Data publikacji:
    2019
    Wydawca:
    Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
    Tematy:
    alkaline leaching
    calcium zincate
    nonsulfide zinc ore
    smithsonite
    zinc carbonate
    Opis:
    In this study, the leaching behaviour of zinc from a smithsonite ore sample (23.43% Zn) having goethite and calcite as main gangue minerals was investigated in sodium hydroxide solutions using Xray diffraction and chemical analyses. Within the studied NaOH concentration range (1-4 mole/dm3), higher leaching ratio values for Zn were obtained by leaching at 298 K because of the decreased stability of soluble zincate species in solution at higher temperatures. When the concentration of NaOH solution was increased from 1 to 3 mole/dm3 at 298 K, leaching ratio value of Zn increased from 3.8 to 70.1%. At 4 mole/dm3 NaOH concentration, Zn leaching ratio value (70.9%) levelled off due to the formation of solid hydrated calcium zincate phase in leaching solution. On the other hand, very low leaching ratio values of Zn were obtained by leaching in 1 mole/dm3 NaOH solution at 298 K (3.8%) and 363 K (1.4%) due to the formation of solid zinc hydroxide and solid zinc oxide phases, respectively. It was observed that increasing leaching time from 1800 to 14400 s at 3 mole/dm3 NaOH concentration, favoured the formation of hydrated calcium zincate phase and so decreased the leaching ratio of Zn to a lower value (60.6%). The effect of solid/liquid ratio was also investigated and it was found that when solid/liquid ratio was decreased, Zn leaching ratio values decreased at constant OH/Zn mole ratio and increased at constant NaOH concentration conditions. Besides, for some of the experiments, leaching ratio values of lead were also given.
    Źródło:
    Physicochemical Problems of Mineral Processing; 2019, 55, 2; 407-416
    1643-1049
    2084-4735
    Pojawia się w:
    Physicochemical Problems of Mineral Processing
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of heating on structure and leaching characteristics of a zinc carbonate ore
    Autorzy:
    Kumas, Cavit
    Obut, Abdullah
    Powiązania:
    https://bibliotekanauki.pl/articles/1446908.pdf
    Data publikacji:
    2021
    Wydawca:
    Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
    Tematy:
    calcium zincate
    smithsonite
    sodium hydroxide leaching
    zinc carbonate ore
    zinc oxide
    Opis:
    In this work, the structural changes occurred in a zinc carbonate (smithsonite) ore sample following heating at temperatures between 523 K and 1173 K were investigated in detail using X-ray diffraction (XRD), thermal (TG/DTA) and Fourier-transform infrared (FT-IR) spectroscopy analyses. Afterwards, the leaching characteristics of zinc from the ore sample and the heated ore samples in sodium hydroxide solutions were determined. While heating at 523 K did not cause any structural change in the ore sample, heating at 723 K completely converted smithsonite $(ZnCO_3)$ in the ore sample to zinc oxide $(ZnO)$, which resulted lower zinc leaching efficiencies of 40.6% and 62.0% for 3 and 4 mol/dm3 NaOH concentrations, respectively, in comparison to zinc leaching efficiencies (67.2% and 70.7%) obtained for the unheated ore sample. On the other hand, due to neoformation of dissolution resistant $ZnFe_2O_4$, $Ca_2ZnSi2O_7$ and $Zn_2SiO_4$ phases during heating and formation of $CaZn_2(OH)_6∙2H_2O$ phase during leaching, the leaching efficiency of zinc further decreased to 22.2% and 31.3%, respectively, in 3 and 4 $mol$ / $dm^3$ NaOH solutions for the ore sample heated at 1173 K. The formation of zinc-containing dissolution resistant phases by high-temperature heating was observed to be the only reason for the reduction in the zinc leaching efficiency (49.4% at 1173 K) at the highest NaOH concentration (8 mol/dm3) studied. In this work, the comparative precipitation studies were also conducted and crystalline zinc oxides with different morphologies could be precipitated at considerably high efficiencies from the selected pregnant solutions obtained following leaching.
    Źródło:
    Physicochemical Problems of Mineral Processing; 2021, 57, 5; 23-32
    1643-1049
    2084-4735
    Pojawia się w:
    Physicochemical Problems of Mineral Processing
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wpływ cynku na właściwości cementów powszechnego użytku
    The influence of zinc on properties of common cements
    Autorzy:
    Tkocz, A.
    Duszak, B.
    Kalarus, D.
    Powiązania:
    https://bibliotekanauki.pl/articles/392318.pdf
    Data publikacji:
    2017
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
    Tematy:
    cynk
    metal ciężki
    cement
    czas wiązania
    opóźnienie
    cynkano-glinian wapnia
    zinc
    heavy metal
    setting time
    retardation
    calcium zincate-aluminate
    Opis:
    W pracy omówiono wyniki badań dotyczących wpływu cynku na właściwości cementów. Celem artykułu było wyjaśnienie niektórych ważnych problemów związanych ze zwiększonym dodatkiem cynku, a także różnic wynikających z dodawania związków cynku bezpośrednio do cementu oraz do zestawu surowcowego do produkcji klinkieru portlandzkiego. Omówiono także wpływ cynkano-glinianów wapnia, które powstają w klinkierze ze zwiększoną zawartością cynku w składzie surowcowym, na właściwości cementów. Przedstawiono również opis ostatnich badań dotyczących granicznej zawartości cynku (dodawanego wraz z surowcami), po przekroczeniu której następuje gwałtowne pogorszenie właściwości cementu.
    In the paper the results of recent studies of the zinc influence on cement properties are presented. The aim of this work was clarification of some important issues associated with higher zinc content, and also the explanation of the differences, which result from the way of zinc introduction i.e. addition of zinc compounds directly to cement and to the raw mix to Portland clinker production. The influence of zinc phases, which form in clinker with higher zinc content in raw mix, on cement properties was also discussed. Description of recent studies concerning the limit zinc content (added with raw materials), which exceeding causes rapid deterioration of cement properties.
    Źródło:
    Prace Instytutu Ceramiki i Materiałów Budowlanych; 2017, R. 10, nr 28, 28; 76-87
    1899-3230
    Pojawia się w:
    Prace Instytutu Ceramiki i Materiałów Budowlanych
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies