Evaluation of the compliance of aircraft wing flap with use of the fracture mechanics
Autorzy:
Kłysz, S.
Baran, M.
Powiązania:
https://bibliotekanauki.pl/articles/243350.pdf
Data publikacji:
2018
Wydawca:
Instytut Techniczny Wojsk Lotniczych
Tematy:
airplane wing flap
crack growth
stress intensity factor
Irwin-Kies theory
Opis:
Research in the field of fracture mechanics and determination of material characteristics are used for practical purposes, such as the assessment of static and dynamic strength of structural components, analysis of their fatigue life or extending the life span of their operation. A structural component, considered to be safe from fatigue cracking point of view, was investigated and results were presented in this article. In particular, an analysis was made to determine the stress intensity factor for the cracked wing flap construction, based on static and fatigue tests, using the Irwin-Kies theory. The flap with a service crack was subjected to fatigue tests with a load similar to the one registered during flight measurements. The flap without a service crack was subjected to static tests, after cutting the cracks of specified lengths and shapes (similar to the service crack) in the skin of the flap. The article presents changing the length of the flap crack in subsequent load cycles, change in the maximum values of force and the crack opening displacement in subsequent load cycles, dependence of P-COD in the first and second stage of fatigue testing of the wing flap, dependence of the wing flap compliance on the length of the crack and experimentally determined dependence for wing flap. The occurrence of a flap crack up to approximately 230 mm does not cause a significant growth of the stress intensity factor.
Źródło:
Journal of KONES; 2018, 25, 4; 547-554
1231-4005
2354-0133
Pojawia się w:
Journal of KONES
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies