Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "adhesive process" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-4 z 4
    Tytuł:
    Surface free energy of extruded polymer compositions
    Autorzy:
    Garbacz, Tomasz
    Powiązania:
    https://bibliotekanauki.pl/articles/110140.pdf
    Data publikacji:
    2019
    Wydawca:
    Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
    Tematy:
    extrusion process
    blowing agent
    antistatic agent
    wettability
    surface free energy
    adhesive properties
    Opis:
    Suitable adhesive properties of the polymer compositions provide largely outer surface of the product. The aim of the studies was evaluation of the efficiency of the extrusion process and physical properties of PVC modified by selected auxiliary. In the studies PVC was used. PVC was modified by blowing agent (0-1.5% by mass) and antistatic agent (0-0.8% by mass) in the form of polyvinyl chloride concentrates. Efficiency of extrusion process is determined also by selected proprieties of surface layer of a mill cake of polyvinyl chloride. Surface free energy has been calculated in Owens-Wendt method. Antistatic agent causes diminishing of wettability and adsorption of surface layer and eventually increase of surface free energy of surface layer. For ensuring appropriate adhesion properties of a surface layer it would be advisable to use, for polyvinyl chloride modification, the antistatic agent in the amount not smaller than 0.4% by mass in relation to polyvinyl chloride mass. Taking into account research results, which can be useful during the development of processing technology of the polyvinyl chloride used for polymers composites, it can be stated that the content of the blowing agent used, noticeably decreasing polymer mass and simultaneously not worsening the properties of a surface layer, should not exceed 0.5÷1.0% by mass in relation to polyvinyl chloride mass.
    Źródło:
    Physicochemical Problems of Mineral Processing; 2019, 55, 6; 1509-1516
    1643-1049
    2084-4735
    Pojawia się w:
    Physicochemical Problems of Mineral Processing
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Ocena wybranych kompozycji klejowych do klejów strukturalnych metodą różnicowej kalorymetrii skaningowej
    Study of the chosen adhesive compositions of structural adhesives using differential scanning calorimetry (DSC)
    Autorzy:
    Butwin, A.
    Czech, Z.
    Powiązania:
    https://bibliotekanauki.pl/articles/270556.pdf
    Data publikacji:
    2010
    Wydawca:
    Centralny Ośrodek Badawczo-Rozwojowy Aparatury Badawczej i Dydaktycznej, COBRABiD
    Tematy:
    kleje strukturalne
    proces sieciowania kompozycji klejowych
    metoda różnicowej kalorymetrii skaningowej
    structural adhesives
    crosslinking process of adhesive composition
    differential scanning calorimetry (DSC)
    Opis:
    Przeprowadzono badania procesu sieciowania kompozycji klejowych do klejów strukturalnych o właściwościach samoprzylepnych metodą różnicowej kalorymetrii skaningowej (DSC). W tym celu opracowano skład jakościowy i ilościowy prekursora samoprzylepnego kleju strukturalnego (S-PSA), a w następnym etapie utworzono kompozycje klejowe z prekursora, żywicy epoksydowej oraz wybranych utwardzaczy utajonych.
    Research of crosslinking process of adhesive composition to structural adhesives of pressure-sensitive properties was conducted using differential scanning calorimetry (DSC). For that purpose there was obtained a precursor of pressure-sensitive structural adhesive (S-PSA) and in the next steps this adhesive was modified using epoxy resin and crosslinking agent.
    Źródło:
    Aparatura Badawcza i Dydaktyczna; 2010, 15, 3; 71-77
    2392-1765
    Pojawia się w:
    Aparatura Badawcza i Dydaktyczna
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Mechanical mixing and deaeration station for adhesive compositions
    Stanowisko do mechanicznego mieszania i odpowietrzania kompozycji klejowych
    Autorzy:
    Miturska-Barańska, Izabela
    Powiązania:
    https://bibliotekanauki.pl/articles/31232946.pdf
    Data publikacji:
    2023
    Wydawca:
    Politechnika Rzeszowska im. Ignacego Łukasiewicza. Oficyna Wydawnicza
    Tematy:
    mixing
    adhesive process
    adhesive composition
    SEM
    mieszanie
    proces klejenia
    kompozycja klejowa
    Opis:
    This paper presents the design of a specialised mixing and deaeration station for adhesive compositions. The aim of the work was to present a device for simultaneous mixing and gas bubble removal, as well as to verify the correctness of the practical application of the station by conducting experimental tests. In the experimental research, the subject of the study was an adhesive composition of the Epidian 5 epoxy resin with the PAC curing agent, which was prepared using four mixing methods carried out with the use of the station for simultaneous mixing and deaeration. The first mixing variant (V1) consisted of mixing the adhesive composition with a paddle mixer at 1170 rpm for 3 minutes, while in the second variant (V2) mixing was carried out with a dispersing disc mixer at 1170 rpm for 3 minutes. The third variant (V3) of mixing was carried out as variant 2, except that the adhesive composition was subjected to deaeration during mixing, while variant 4 (V4) additionally used deaeration of the composition after the mixing process for 2 minutes. The tested adhesive composition was physically modified by adding particles of calcium carbonate CaCO3 to verify the correct mixing of the composition components. The prepared samples were subjected to tensile and compressive strength tests. The structure of the prepared samples was also analysed using scanning electron microscopy (SEM). The tests carried out showed that the stand for simultaneous mixing and deaeration of adhesive compositions meets the expectations set for it. Mixing variant 4, in which mixing was realised using a dispersing disc mixer, proved to be the most favourable mixing method. Mixing was carried out at a speed of 1170 rpm for 3 minutes. In addition, during the mixing process, a deaeration process of the mixed composition was carried out, as well as deaeration was realised after the mixing process in a time of 2 minutes. Changing the mixing parameters contributed to an increase in both the tensile strength and compressive strength of the tested compositions. SEM analysis of the observed samples showed that changing the mixing parameters reduced the amount of air bubbles in the adhesive structure and, in the case of modified compositions, resulted in a better distribution of the filler in the structure of the mixed compositions.
    W niniejszej pracy przedstawiono projekt specjalizowanego stanowiska do mieszania i odpowietrzania kompozycji klejowych. Celem pracy była prezentacja urządzenia do jednoczesnego mieszania i usuwania pęcherzy gazowych, a także sprawdzenie prawidłowości praktycznego zastosowania stanowiska przez przeprowadzenie badań doświadczalnych. W badaniach doświadczalnych przedmiotem badań była kompozycja klejowa żywicy epoksydowej Epidian 5 z utwardzaczem PAC, którą przygotowano z zastosowaniem 4 sposobów mieszania realizowanych z użyciem stanowiska do jednoczesnego mieszania i odpowietrzania. Pierwszy wariant mieszania (V1) polegał na mieszaniu kompozycji klejowej mieszadłem łopatkowym z prędkością 1170 obr/min w czasie 3 minut, w drugim wariancie (V2) mieszanie realizowano z zastosowaniem mieszadła tarczowego dyspergującego z prędkością 1170 obr/min w czasie 3 minut. Trzeci wariant (V3) mieszania był realizowany tak jak wariant 2, z tym że kompozycję klejową poddano odpowietrzaniu w trakcie mieszania, natomiast w wariancie 4 (V4) zastosowano dodatkowo odpowietrzanie kompozycji po procesie mieszania w czasie 2 minut. Badaną kompozycję klejową poddano fizycznej modyfikacji poprzez dodanie cząsteczek węglanu wapnia CaCO3 celem weryfikacji poprawności zmieszania składników kompozycji. Wykonane próbki poddano badaniom wytrzymałości na rozciąganie i ściskanie. Analizowano również strukturę wykonanych próbek z zastosowaniem skaningowej mikroskopii elektronowej. Przeprowadzone badania wykazały, że stanowisko do jednoczesnego mieszania i odpowietrzania kompozycji klejowych spełnia stawiane mu oczekiwania. Najkorzystniejszym sposobem mieszania okazał się 4 wariant mieszania, w którym mieszanie zrealizowano z użyciem mieszadła tarczowego dyspergującego. Mieszanie realizowano z prędkością 1170 obr/min w czasie 3 minut. Dodatkowo w trakcie mieszania przeprowadzano process odpowietrzania mieszanej kompozycji, jak również odpowietrzanie realizowano po procesie mieszania w czasie 2 minut. Zmiana parametrów mieszania przyczyniła się do wzrostu wytrzymałości zarówno na rozciąganie, jak i wytrzymałości na ściskanie badanych kompozycji. Analiza SEM obserwowanych próbek wykazała, że zmiana parametrów mieszania pozwala zmniejszyć ilość pęcherzy powietrza w strukturze kleju, a w przypadku kompozycji modyfikowanych spowodowała lepsze rozprowadzenie napełniacza w strukturze mieszanych kompozycji.
    Źródło:
    Technologia i Automatyzacja Montażu; 2023, 4; 38-47
    2450-8217
    Pojawia się w:
    Technologia i Automatyzacja Montażu
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Foaming of polyvinylacetate adhesives - improved technologic parameters for a solid wood gluing process
    Spienianie klejów polioctanowinylowych - poprawa parametrów technologicznych do klejenia drewna litego
    Autorzy:
    Sedliacik, J.
    Schmidtova, J.
    Smidriakova, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/7852.pdf
    Data publikacji:
    2014
    Wydawca:
    Szkoła Główna Gospodarstwa Wiejskiego w Warszawie. Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
    Tematy:
    foaming
    polyvinylacetate adhesive
    technological parameter
    wood
    gluing process
    wooden panel
    shear strength
    Źródło:
    Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology; 2014, 87
    1898-5912
    Pojawia się w:
    Annals of Warsaw University of Life Sciences - SGGW. Forestry and Wood Technology
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-4 z 4

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies