Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "Tin (Sn)" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-3 z 3
    Tytuł:
    Verify the plasma parameters generated from the Tin material using the laser-induced plasma technique
    Autorzy:
    Ahmed, Baida M.
    Aadim, Kadhim A.
    Khalaf, Madyan A.
    Powiązania:
    https://bibliotekanauki.pl/articles/1030607.pdf
    Data publikacji:
    2020
    Wydawca:
    Przedsiębiorstwo Wydawnictw Naukowych Darwin / Scientific Publishing House DARWIN
    Tematy:
    Laser-Induced Plasma (LIP)
    Nd:YAG laser
    Optical Emission Spectroscopic (OES)
    Tin (Sn)
    Opis:
    In this work, A spectroscopic research on laser-produced tin plasma using optical emission spectroscopy (OES) technology is provided. Laser-induced Sn plasma produced at various laser energy has also been defined by visible emission spectroscopy. Plasma is created by a solid tin object radiated by a pulsed laser in a room environment. A Nd:YAG laser pulse 9 ns in duration with wavelength of 1064 nm and a focal length of 10 cm in the range of energy 500-800 mJ is used to generate plasma from a planar Sn sample. The electron temperature (Te) was calculated in ratio line intensities method, while the electron density (ne) was calculated using Saha-Boltzmann equation, also another plasma parameters was calculated such as plasma (fp), Debye length (λD) and Debye number (ND). The increase in electron temperature and density was observed as a function of laser energies. Measurement of the production of the electron temperature in the rang 0.926-0.952 eV, While the electron density is in the rang (1.9×1015-2.5×1015) cm-3.
    Źródło:
    World Scientific News; 2020, 144; 326-337
    2392-2192
    Pojawia się w:
    World Scientific News
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wpływ zawartości Sn na odporność korozyjną stopów żelaza
    Effect of Sn content on corrosion resistance of iron
    Autorzy:
    Jagielska-Wiaderek, K.
    Bala, H.
    Denis-Brewczyńska, D.
    Powiązania:
    https://bibliotekanauki.pl/articles/391373.pdf
    Data publikacji:
    2017
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Odlewnictwa
    Tematy:
    cyna
    odlewnicze stopy Fe-Sn
    szybkość korozji
    korozja atmosferyczna
    tin
    Fe-Sn casting alloys
    corrosion rate
    atmospheric corrosion
    Opis:
    W pracy scharakteryzowano odporność na korozję kwasową sześciu stopów żelaza zawierających dodatki od 0,007 do 1,03% wag. cyny. Stopy te uzyskano przez przetapianie w piecu Tammana czystego żelaza (99,98% Fe) z dodatkami spektralnie czystej cyny. Otrzymane wytopy poddano badaniom odporności na korozję kwasową, wykonując przyśpieszony test na korozję atmosferyczną, badania elektrochemiczne oraz pomiary szybkości korozji (określane z analizy roztworów korozyjnych na zawartość Fe2+). Wykonane pomiary elektrochemiczne pokazują, że zarówno w środowisku kwasu siarkowego, jak i zakwaszonego siarczanu sodu obecność 0,007−1,03% Sn w żelazie nie wykazuje istotnego wpływu na szybkość korozji badanych stopów. Uzyskane wartości ikor (wyznaczone na drodze ekstrapolacji do Ekor, jak i na podstawie Rp), w granicach ich błędu pomiarowego, można uznać za niezależne od zawartości cyny w stopie. Obserwuje się jednak wpływ obecności cyny na przebieg korozji atmosferycznej w kwaśnej mgle solnej – szybkość ta ulega zmniejszeniu w miarę wzrostu zawartości Sn w analizowanych próbkach.
    The study characterizes the acid corrosion resistance of six iron alloys containing additions from 0.007 to 1.03 wt. % of tin. The alloys were obtained by way of remelting in a Tamman furnace made of pure iron (99.98% Fe) with additions of spectrally pure tin. The obtained melts underwent studies of acid corrosion resistance by means of an atmospheric corrosion test, electrochemical tests and corrosion rate measurements (determination from the analysis of the corrosion solutions in respect of the Fe2+ content). The performed electrochemical measurements show that both in the environment of sulfuric acid and acidified sodium sulfate, the presence of 0.007−1.03% Sn in the iron does not exhibit a significant effect on the corrosion rate of the examined alloys. The obtained values of icor (determined by way of extrapolation to Ecor and based on Rp), within their measurement error, can be treated as independent of the tin content in the alloy. However, one can observe the effect of the presence of tin on the course of atmospheric corrosion in the acid salt spray – this rate is reduced with an increase of the Sn content in the analyzed samples.
    Źródło:
    Prace Instytutu Odlewnictwa; 2017, 57, 1; 3-10
    1899-2439
    Pojawia się w:
    Prace Instytutu Odlewnictwa
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Assessment of Impact of Nickel Additions on Tin Bronzes
    Autorzy:
    Kozana, J.
    Garbacz-Klempka, A.
    Piękoś, M.
    Czekaj, J.
    Perek-Nowak, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/382525.pdf
    Data publikacji:
    2018
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    wear resistant alloys
    tin bronze
    microstructure
    alloy additives
    Cu–Sn–Ni alloy
    stopy odporne na zużycie
    brąz cynowy
    mikrostruktura
    dodatki stopowe
    stop Cu-Sn-Ni
    Opis:
    High prices of tin and its limited resources, as well as several valuable properties characterising Cu-Sn alloys, cause searching for materials of similar or better properties at lower production costs. The influence of various nickel additions to CuSn10 casting bronze and to CuSn8 bronze of a decreased tin content was tested. Investigations comprised melting processes and casting of tin bronzes containing various nickel additions (up to 5%). The applied variable conditions of solidification and cooling of castings (metal and ceramic moulds) allowed to assess these alloys sensitivity in forming macro and microstructures. In order to determine the direction of changes in the analysed Cu-Sn-Ni alloys, the metallographic and strength tests were performed. In addition, the solidification character was analysed on the basis of the thermal analysis tests. The obtained results indicated the influence of nickel in the solidification and cooling ways of the analysed alloys (significantly increased temperatures of the solidification beginning along with increased nickel fractions in Cu-Sn alloys) as well as in the microstructure pattern (clearly visible grain size changes). The hardness and tensile strength values were also changed. It was found, that decreasing of the tin content in the analysed bronzes to which approximately 3% of nickel was added, was possible, while maintaining the same ultimate tensile strength (UTS) and hardness (HB) and improved plasticity (A5).
    Źródło:
    Archives of Foundry Engineering; 2018, 18, 1; 53-60
    1897-3310
    2299-2944
    Pojawia się w:
    Archives of Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies