Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "SEM/EBSD" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-6 z 6
    Tytuł:
    Crystal Lattice Rotations Induced by Shear Banding in fcc Metals Deformed at High Strain Rates
    Autorzy:
    Mania, Izabela
    Paul, Henryk
    Chulist, Robert
    Petrzak, Paweł
    Miszczyk, Magdalena
    Prażmowski, Mariusz
    Powiązania:
    https://bibliotekanauki.pl/articles/2203719.pdf
    Data publikacji:
    2023
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    shear bands
    high strain rates
    texture
    SEM/EBSD
    Opis:
    In this paper, the microstructural and texture changes in polycrystalline CuZn30 alloy, copper, and AA1050 aluminium alloy have been studied to describe the crystal lattice rotation during shear bands formation. The hat-shaped specimens were deformed using a drop-hammer at the strain rate of 560 s-1. Microstructure evolution was investigated using optical microscopy, whereas texture changes were examined with the use of a scanning electron microscope equipped with the EBSD facility. The microstructural observations were correlated with nanohardness measurements to evaluate the mechanical properties of the sheared regions. The analyses demonstrate the gradual nature of the shear banding process, which can be described as a mechanism of the bands nucleation and then successive growth rather than as an abrupt instability. It was found that regardless of the initial orientation of the grains inside the sheared region, a well-defined tendency of the crystal lattice rotation is observed. This rotation mechanism leads to the formation of specific texture components of the sheared region, different from the one observed in a weakly or non-deformed matrix. During the process of rotation, one of the {111} planes in each grain of the sheared region ‘tends’ to overlap with the plane of maximum shear stresses and one of the <110> or <112> directions align with the shear direction. This allows slip propagation through the boundaries between adjacent grains without apparent change in the shear direction. Finally, in order to trace the rotation path, transforming the matrix texture components into shear band, rotation axis and angles were identified.
    Źródło:
    Archives of Metallurgy and Materials; 2023, 68, 1; 319--329
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Microstructural Features and Mechanical Properties after Applying Rolling with Cyclic Movement of Rolls of an Al-Li Alloys
    Autorzy:
    Brzezińska, A.
    Urbańczyk-Gucwa, A.
    Molak, R.
    Rodak, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/352162.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Al-Li alloy
    severe plastic deformation
    ultrafine-grains
    STEM
    SEM/EBSD
    Opis:
    Two strength-age hardening aluminum-lithium alloys: Al-2.3wt%Li and Al-2.2wt%Li-0.1wt%Zr in two different heat treatment conditions: solution state (S) and additionally in aging state (A) were severely plastically deformed by rolling with cyclic movement of rolls (RCMR) method to produce ultrafine - grained structure. Two thermo-mechanical treatments were used: (S+A+RCMR) and (S+RCMR+A+RCMR). To investigate the combined effect of plastic deformation and heat treatment, tensile tests were performed. Microstructural observations were undertaken using scanning transmission electron microscopy (STEM), and scanning transmission electron microscopy (SEM) equipped with electron backscattering diffraction detector (EBSD). Based on the obtained results, it can be deduced that maximum mechanical properties as: yield strength (YS) and ultimate tensile strength (UTS) couldbe achieved when the microstructure of alloys is in (S+A+RCMR) state. For samples in (S+RCMR+A+RCMR) state, ductility is higher than for (S+A+RCMR) state. The microstructural results shows that the favourable conditions for decreasing grain size of alloys is (S+A+RCMR) state. Additionally, in this state is much greater dislocation density than for (S+RCMR+A+RCMR) state. The microstructure of alloys in (S+RCMR+A+RCMR) state is characterized by grains/subgrains with higher average diameter and with higher misorientation angles compared with (S+A+RCMR) state.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 4; 1533-1540
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Characterization of Explosive Weld Joints by TEM and SEM/EBSD
    Charakterystyka strefy połączenia uzyskanego metodą zgrzewania wybuchowego z wykorzystaniem TEM oraz SEM/EBSD
    Autorzy:
    Paul, H.
    Morgiel, J
    Baudin, T.
    Brisset, F.
    Prażmowski, M.
    Miszczyk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/352611.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    explosive welding
    TEM
    SEM/EBSD
    interface
    phase transformations
    microstructure
    zgrzewanie wybuchowe
    przemiany fazowe
    mikrostruktura
    Opis:
    The layers near the interface of explosively welded plates were investigated by means of microscopic observations with the use of transmission electron microscopy (TEM) equipped with energy dispersive spectrometry and scanning electron microscopy equipped with electron backscattered diffraction facility (SEM/EBSD). The metal compositions based on carbon or stainless steels (base plate) and Ti, Zr and Ta (flyer plate) were analyzed. The study was focused on the possible interdiffusion across the interface and the changes in the dislocation structure of bonded plates in the layers near-the-interface. It was found that the extremely rapid temperature increase followed by high cooling rates in the areas near the interface favour the formation of metastable phases. The crystalline or glassy nature of the phases formed inside melted zones strongly depends on the chemical composition of bonded metals. The amorphous phases dominates the melted zone of the (carbon or stainless steel)/Zr whereas the mixture of amorphous phases and nano- grains were identified in (carbon steel)/Ti and (stainless steel)/Ta clads. The elongated shape of the (sub)grains and the randomly distributed dislocations inside them as well as the shear bands and twins observed in the layers near-the-interface of all investigated clads, clearly indicated that during explosive welding, the deformation processes were prevailing over the softening ones.
    W pracy analizowano zmiany strukturalne oraz składu chemicznego, jakie zachodzą w pobliżu powierzchni połączenia płyt metalowych spajanych z wykorzystaniem energii wybuchu. Badano kompozycje materiałów bazujące na stali węglowej lub stopowej (płyta bazowa) w połączeniu z Ti, Zr lub Ta (płyta lotna). W prowadzonej analizie wykorzystano transmisyjny mikroskop elektronowy (TEM) wyposażony w spektrometr promieniowania X (EDX) a także skaningowy mikroskop elektronowy wyposażony w system pomiaru orientacji lokalnych (SEM/EBSD). Zaobserwowano, że ekstremalnie szybki wzrost temperatury a następnie szybkie chłodzenie prowadzi do uformowania się w strefie przetopień faz niestabilnych o silnie zróżnicowanym składzie chemicznym. Krystaliczna lub amorficzna natura formujących się faz uzależniona jest od składu chemicznego łączonych metali. Faza amorficzna dominuje w strefach przetopień formujących się w układzie płyt (stal austenityczna lub węglowa)/Zr podczas, gdy mieszanina faz amorficznych i ultra drobnokrystalicznych dominuje w układach płyt (stal węglowa)/Ti oraz (stal astenityczna)/Ta. Analizy strukturalne pokazują, że w warstwach łączonych płyt położonych przy powierzchni połączenia, obserwuje się podstrukturę komórkową z duża ilością dyslokacji zgromadzonych w ich wnętrzu a także bliźniaki odkształcenia (Zr, Ti) oraz pasma ścinania (stal, Zr). Fakty te pozwalają na stwierdzenie, że procesy odkształcenia dominują nad procesami zmiękczenia. Udokumentowano także, że pomimo trudności w preparatyce próbek wynikających z silnie odmiennych własności elektrochemicznych łączonych metali, połączenie technik opartych o TEM oraz SEM/EBSD pozwala w pełni opisać zjawiska zachodzące w meso- i nano- skali w pobliżu powierzchni połączenia.
    Źródło:
    Archives of Metallurgy and Materials; 2014, 59, 3; 1129-1136
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Deformation Microstructure And Texture Transformations In FCC Metals Of Medium-To-High Stacking Fault Energy: Critical Role Of Micro- And Macro-Scale Shear Bands
    Zmiany mikrostrukturalne i teksturowe w odkształconych metalach o sieci RSC o średniej i wysokiej energii błędu ułożenia: krytyczna rola mikro- i makro-pasm ścinania
    Autorzy:
    Paul, H.
    Miszczyk, M. M.
    Powiązania:
    https://bibliotekanauki.pl/articles/353921.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    shear bands
    texture
    SEM/EBSD
    copper
    AA1050 alloy
    plane strain compression
    pasma ścinania
    tekstura
    miedź
    stop AA1050
    Opis:
    Microstructure and texture development in medium-to-high stacking fault energy face centred cubic metals were investigated in order to examine the role of lattice re-orientation on slip propagation across grain boundaries and to characterize the influence of micro- and macro-scale copper-type shear bands on textural changes at large deformations. Polycrystalline pure copper (fine - and coarse - grained) and fine-grained AA1050 alloy were deformed in plane strain compression at room temperature to form two sets of well-defined macroscopic shear bands. The deformation-induced sub-structures and local changes in crystallographic orientations were investigated mostly by scanning electron microscopy equipped with high resolution electron backscattered facility. In all the deformed grains within macro- shear bands a strong tendency to strain-induced re-orientation was observed. The flat, strongly deformed grains exhibited a deflection within narrow areas. The latter increased the layers’ inclination with respect to ED and led to kink-type bands, which are the precursors of MSBs. The mechanism of macro- / micro-shear bands formation is strictly crystallographic since in all the areas of the sheared zone, the crystal lattice rotated such that one of the {111} slip planes became nearly parallel to the shear plane and the <011> direction became parallel to the direction of maximum shear. This strain-induced crystal lattice rotation led to the formation of specific macro- / micro-shear bands components that facilitated slip propagation across the grain boundaries without any visible variation in the slip direction.
    W pracy badano zmiany strukturalne i teksturowe w metalach o sieci regularnej ściennie centrowanej związane z lokalną re-orientacją sieci krystalicznej wynikającą z formowania się mikro- i makro- pasm ścinania. Analizowano polikrystaliczne próbki miedzi oraz aluminium o czystości technicznej (stop AA1050) odkształcane w temperaturze otoczenia w próbie nieswobodnego ściskania do zakresu odkształceń, w których następuje wyraźne uformowanie się dwóch rodzin makroskopowych pasm ścinania. W badaniach wykorzystano skaningowy mikroskop elektronowy wyposażony w system automatycznego pomiaru orientacji lokalnych. Zaobserwowano, że w ziarnach umiejscowionych w obszarze makroskopowych pasm ścinania występuje ściśle zdefiniowana tendencja rotacji sieci krystalicznej, w wyniku której jedna z płaszczyzn typu {111} przyjmuje położenie zbliżone do położenia płaszczyzny ścinania, a jeden z kierunków typu <110> (lub <112>) wykazuje tendencję do sytuowania się równolegle do kierunku ścinania. Obserwowana w obszarze wnętrza pasm ścinania rotacja prowadzi do uformowania się specyficznej (mikro)tekstury, która umożliwia propagację poślizgów poprzez granice ziaren bez ‘istotnej’ zmiany kierunku ścinania.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 3; 2235-2246
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Zastosowanie metod FEG SEM i EBSD do badań struktury stali AHSS na różnych etapach procesu ciągłego wyżarzania
    Application of FEG-SEM and EBSD methods in examinations of AHSS steel structure at various stages of continuous annealing process
    Autorzy:
    Radwański, K.
    Kuziak, R.
    Zalecki, W.
    Wrożyna, A.
    Molenda, R.
    Opara, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/181928.pdf
    Data publikacji:
    2015
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Metalurgii Żelaza im. Stanisława Staszica
    Tematy:
    stal DP
    obróbka cieplna
    wyżarzanie
    FEG SEM
    EBSD
    DP steel
    heat treatment
    annealing
    FEG-SEM
    Opis:
    Celem pracy było wykorzystanie metod FEG SEM i EBSD w celu określenia wpływu parametrów procesu ciągłego wyżarzania na zmiany struktury taśm w stanie po walcowaniu na zimno. Obróbkę cieplną wykonano w zakresie temperatur 600÷820°C. W tym celu przeprowadzono również symulacje fizyczne cykli cieplnych ciągłego wyżarzania na próbkach taśm, które poddano następnie badaniom właściwości mechanicznych w statycznej próbie rozciągania. Badania struktury wykonano za pomocą elektronowego mikroskopu skaningowego FEG SEM z szerokim zastosowaniem metody EBSD. Scharakteryzowano możliwości badawcze metody EBSD oraz zastosowano je w badaniach procesów zdrowienia i rekrystalizacji statycznej oraz struktur powstałych po przemianach fazowych w oparciu o analizę parametrów takich jak: Kernel Average Misorientation (KAM), Grain Average Misorientation (GAM), Image Quality (IQ) i kąty dezorientacji. W wyniku przeprowadzonych badań stwierdzono, że w zakresie temperatur 600÷720°C zachodzą procesy zdrowienia i rekrystalizacji statycznej taśm, które ulegają przyspieszeniu ze wzrostem temperatury. Procesy te zachodzą odmiennie w obszarach, w których po walcowaniu na zimno występował ferryt i perlit. W przypadku perlitu procesowi powstawania nowych ziarn towarzyszy dyfuzja węgla i koagulacja cząstek cementytu na granicach ziarn. Począwszy od temperatury 730°C w strukturze obserwuje się martenzyt oraz bainit, których udział powierzchniowy rośnie wraz ze zwiększaniem temperatury wyżarzania. Po przeprowadzonych cyklach obróbki cieplnej taśmy charakteryzują się następującymi właściwościami mechanicznymi: Rp0.2 = 300÷450 MPa, Rm = 630÷720 MPa, A50 = 11÷17%.
    The study was aimed at use of FEG SEM and EBSD methods in order to determine the impact of continuous annealing process parameters on changes in strips structure following cold rolling. Heat treatment was conducted in the temperature range 600÷820°C. Moreover, for this purpose, physical simulations were conducted of continuous annealing thermal cycles on samples of strips which, subsequently were subject to static tensile test. Examinations of the structure were conducted by means of scanning electron microscope FEG SEM with broad application of EBSD method. Research capacities of EBSD method were characterized and applied in examinations of recovery and static recrystallization as well as structures formed as a result of phase transitions based on analysis of parameters such as: Kernel Average Misorientation (KAM), Grain Average Misorientation (GAM), Image Quality (IQ) and misorientation angles. As a result of the conducted examinations, it was found that in the temperature range 600÷720°C recovery and static recrystallization of strips occur, which are accelerated along with increase in temperature. These processes differ in the areas with presence of ferrite and pearlite following cold rolling. In case of pearlite, the process of new grain formation is accompanied by carbon diffusion and coagulation of cementite particles on grain boundaries. Starting from the temperature of 730°C, martensite and bainite are observed in the structure, the surface share of which increases along with increase in the temperature of annealing. Following the conducted cycles of heat treatment, the strips are characterized with the following mechanical properties: Rp0.2 = 300÷450 MPa, Rm = 630÷720 MPa, A50 = 11÷17%.
    Źródło:
    Prace Instytutu Metalurgii Żelaza; 2015, T. 67, nr 2, 2; 136-147
    0137-9941
    Pojawia się w:
    Prace Instytutu Metalurgii Żelaza
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Niskotemperaturowe starzenie cyrkonowych materiałów ceramicznych Y-tzp. Cz. 2. Wstępne badania procesu z wykorzystaniem techniki EBSD
    Low-temperature degradation of Y-TZP zirconia ceramics. Part 2: Preliminary EBSD study
    Autorzy:
    Tymowicz-Grzyb, P.
    Jaegermann, Z.
    Powiązania:
    https://bibliotekanauki.pl/articles/168873.pdf
    Data publikacji:
    2017
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Ceramiki i Materiałów Budowlanych
    Tematy:
    protetyka stomatologiczna
    ceramika cyrkonowa
    starzenie niskotemperaturowe
    XRD
    SEM
    EBSD
    dental prosthetics
    zirconia ceramics
    low-temperature degradation
    Opis:
    W publikacji przedstawiono wyniki badania zjawiska starzenia niskotemperaturowego materiałów cyrkonowych metodą opartą na dyfrakcji elektronów wstecznie rozproszonych EBSD (ang. Elektron Backscattered Diffraction). Celem pracy była próba odpowiedzi na pytanie czy metoda EBSD może służyć do zidentyfikowania początkowych etapów procesu niskotemperaturowego starzenia materiałów cyrkonowych Y-TZP. Do celów porównawczych wykorzystano wcześniejsze wyniki badań procesu starzenia prowadzone metodami XRD i obserwacji SEM, opublikowane w części 1 artykułu. Analiza wyników przeprowadzonych badań pokazała, że czułość metody EBSD w wykrywaniu wczesnych zmian transformacji t→m jest znacznie wyższa niż metod XRD i SEM. Analiza obrazów dyfrakcyjnych uzyskanych metodą EBSD wykazała obecność fazy jednoskośnej w powierzchniowych warstwach materiałów pomimo tego, że nie wykazały jej badania dyfrakcyjne XRD.
    The results of EBSD (Elektron Backscattered Diffraction) study on the low-temperature degradation (LTD) phenomenon of zirconia materials were presented. The aim of the study was to answer the question whether the EBSD method can be used to identify the initial LTD stages of Y-TZP zirconia. For comparative purposes, previous results on XRD study and SEM observation, published in part 1 of the article, was used. The results of the studies have shown that the sensitivity of EBSD method for detecting early stages of t→m transformation is significantly higher than that of XRD and SEM. Analysis of EBSD diffraction patterns revealed the presence of monoclinic phase in the superficial layers of materials despite the fact that the diffraction patterns did not show it.
    Źródło:
    Szkło i Ceramika; 2017, R. 68, nr 5, 5; 14-18
    0039-8144
    Pojawia się w:
    Szkło i Ceramika
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-6 z 6

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies