Nondestructive Radioactive Tracer Technique in Characterization of Anion Exchange Resins Purolite NRW-8000 and Duolite A-368
Autorzy:
Singare, P.U.
Powiązania:
https://bibliotekanauki.pl/articles/411749.pdf
Data publikacji:
2013
Wydawca:
Przedsiębiorstwo Wydawnictw Naukowych Darwin / Scientific Publishing House DARWIN
Tematy:
ion-exchange resin
anion exchange
Purolite NRW-8000
Duolite A-368
radio tracer isotopes
131I
82Br
characterization
isotopic Exchange
Opis:
Radioactive tracer isotopes 131I and 82Br were used to characterize anion exchange resins Purolite NRW-8000 and Duolite A-368 by application of nondestructive technique. The resin characterization was based on their performance during iodide and bromide ion-isotopic exchange reactions. It was observed that during the iodide ion-isotopic exchange reaction at a constant temperature of 40.0 °C, as the concentration of labeled iodide ion solution increases from 0.001 mol/L to 0.004 mol/L, the percentage of iodide ions exchanged increases from 62.10 % to 68.10 % using Purolite NRW-8000 resins and from 44.20 % to 46.80 % using Duolite A-368 resins. Also at a constant temperature of 40.0 °C, 1.000 g of ion exchange resins and 0.003 mol/L labeled iodide ion solution, the values of specific reaction rate (min-1), amount of iodide ion exchanged (mmol), initial rate of iodide ion exchange (mmol/min) and log Kd were calculated as 0.260, 0.500, 0.130 and 11.8 respectively for Purolite NRW-8000 resin, which was higher than the respective values of 0.130, 0.345, 0.045 and 6.7 as that obtained for Duolite A-368 resins. The similar trend was observed for the two resins during bromide ion-isotopic exchange reaction. From the overall results it appears that under identical experimental conditions, Purolite NRW-8000 resins show superior performance over Duolite A-368 resins. It is expected here that the present nondestructive technique can be extended further for characterization of different industrial grade ion exchange resins, which will help in their selection for specific industrial application.
Źródło:
International Letters of Chemistry, Physics and Astronomy; 2013, 12; 14-27
2299-3843
Pojawia się w:
International Letters of Chemistry, Physics and Astronomy
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies