- Influence of Solid Solution and Aging Treatment Conditions on the Formation of Ultrafine-Grained Structure of CuCr0.6 Alloy Processed by Compression with Oscillatory Torsion
- Autorzy:
-
Urbańczyk-Gucwa, A.
Brzezińska, A.
Rodak, K. - Powiązania:
- https://bibliotekanauki.pl/articles/947582.pdf
- Data publikacji:
- 2018
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Tematy:
-
CuCr0.6 alloy
severe plastic deformation
ultrafine-grains
STEM - Opis:
- The samples of the CuCr0.6 alloy in the solution treated and additionally in aging states were severely plastically deformed by compression with oscillatory torsion (COT) method to produce ultrafine – grained structure. The samples were processed by using process parameters as: frequency of torsion (f = 1.6 Hz), compression speed (v = 0.04 mm/s), angle torsion (α = ±6°), height reduction (Δh = 7 mm). The total effective strain was εft = 40. The microstructure has been analyzed by scanning transmission electron microscope (STEM) Hitachi HD-2300A equipped with a cold field emission gun at an accelerating voltage of 200 kV. The quantitative microstructure investigations as disorientation angles were performed using a FEI INSPECT F scanning electron microscope (SEM) equipped with a cold field emission gun and a electron backscattering diffraction (EBSD) detector. The mechanical properties were determined using MST QTest/10 machine equipped with digital image correlation (DIC). The COT processed alloy previously aged at 500°C per 2h shows high mechanical strength, ultimate tensile strength UTS: 521 MPa and yield tensile strength YS: 488 MP attributed to the high density of coherent precipitates and ultrafine grained structure. Keywords: CuCr0.6 alloy, severe plastic deformation, ultrafine-grains, STEM
- Źródło:
-
Archives of Metallurgy and Materials; 2018, 63, 4; 2061-2066
1733-3490 - Pojawia się w:
- Archives of Metallurgy and Materials
- Dostawca treści:
- Biblioteka Nauki
Artykuł