- Mechanical Properties of HTPE/Bu-NENA Binder and the Kinetics of Bu-NENA Evaporation
- Autorzy:
-
Yuan, Shen
Luo, Yunjun - Powiązania:
- https://bibliotekanauki.pl/articles/358657.pdf
- Data publikacji:
- 2020
- Wydawca:
- Sieć Badawcza Łukasiewicz - Instytut Przemysłu Organicznego
- Tematy:
-
hydroxyl-terminated polyether
HTPE
N-butyl-N-(2-nitroxyethyl)nitramine
BuNENA
mechanical properties
cross-linking network structure
evaporation - Opis:
- The correlation between the mechanical properties of hydroxyl-terminated polyether (HTPE)/N-butyl-N-(2-nitroxyethyl)nitramine (Bu-NENA) binders with different plasticization ratios (pl/po), varied from 0.9 to 1.5, have been studied. The very early stage of evaporation of Bu-NENA from the HTPE/Bu-NENA binder, with a pl/po ratio of 1.2, has been investigated. The results revealed that the pl/po ratio has strong influences on the mechanical properties. When the pl/po ratio was 1.2, the mechanical properties of the HTPE/Bu-NENA binder were satisfactory, the maximum tensile strength and the elongation at break being 2.39 MPa and 93.27%, respectively. The evaporation rate constant of Bu-NENA from HTPE/Bu-NENA binder with a pl/po ratio of 1.2 increased from 0.31·10–5 to 2.32·10–5 s–1 as the temperature was increased from 50 to 90 °C. The value of the activation energy of evaporation was 51.47 kJ/mol and its pre-exponential factor was 6.14·102 s–1.
- Źródło:
-
Central European Journal of Energetic Materials; 2020, 17, 1; 119-141
1733-7178 - Pojawia się w:
- Central European Journal of Energetic Materials
- Dostawca treści:
- Biblioteka Nauki