Wyszukujesz frazę "Al-Si-Mg alloy" wg kryterium: Temat


Wyświetlanie 1-8 z 8
Tytuł:
Influence of Cooling Rate on Intergranular Corrosion in Al-Si7-Mg Alloy
Autorzy:
Bernat, L.
Powiązania:
https://bibliotekanauki.pl/articles/381720.pdf
Data publikacji:
2015
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
Al-Si-Mg alloy
intergranular corrosion
cooling rate
stop Al-Si-Mg
korozja międzykrystaliczna
szybkość chłodzenia
Opis:
The use of aluminium cast alloys in automotive industry results from a tendency to considerably lower vehicle mass. Subject to working conditions, silumin casts may show occurrence of intergranular corrosion that reduces mechanical properties of the parts produced. The paper presents the influence of cooling rate – R of a plate cast of aluminium alloy EN AC-AlSi7Mg0,3 on the depth of appearance of intergranular corrosion. Samples were exposed to corrosive medium by immersion for 2,5; 12; 24 and 48 hours in an aqueous solution of NaCl+HCl+H2O. The study demonstrated that cooling rate – R and subsurface porosity significantly influence on distribution and depth of intergranular corrosion in casts of subeutectic silumin.
Źródło:
Archives of Foundry Engineering; 2015, 15, 3 spec.; 107-111
1897-3310
2299-2944
Pojawia się w:
Archives of Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Computer-aided analysis of a new process for flanging hollow parts
Autorzy:
Winiarski, G.
Powiązania:
https://bibliotekanauki.pl/articles/118231.pdf
Data publikacji:
2014
Wydawca:
Polskie Towarzystwo Promocji Wiedzy
Tematy:
flanging
hollow parts
Al-Mg-Si alloy
FEM
Opis:
The paper presents a new process for flanging hollow parts. This process is performed using a specially designed set of tools with movable sleeves. The principle of operation of the tool set is described and examples of the numerical analysis results are given. The FEM simulation was performed on the assumption that the hot-formed hollow workpiece (tube) is made of AlMgSi aluminum alloy. The obtained FEM results show changes in the workpiece shape during flanging, variations in the forming force and the damage function distribution computed according to the C-L failure criterion. The theoretical results of the new flanging method provided basis for experimental tests.
Źródło:
Applied Computer Science; 2014, 10, 1; 19-29
1895-3735
Pojawia się w:
Applied Computer Science
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
The Role of Microstructure on the Corrosion Behaviour of as cast AlCu4MgSi and MgAl2Si Alloys
Autorzy:
Lachowicz, M. M.
Jasionowski, R.
Powiązania:
https://bibliotekanauki.pl/articles/381379.pdf
Data publikacji:
2018
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
metallography
corrosion resistance
aluminum alloy
magnesium alloy
Al-Cu-Mg-Si alloy
Mg-Al-Si alloy
metalografia
odporność korozyjna
stop aluminium
stop magnezu
stop Al-Cu-Mg-Si
stop Mg-Al-Si
Opis:
In this work, the effect of the microstructure on corrosion behavior of selected Mg- and Al-based as cast alloys, was evaluated. The electrochemical examinations were carried out, and then a morphology of corrosion products formed due to local polarization on materials surface, was analyzed. It was documented that the presence of Mg2Si phase plays an important role in the corrosion course of Mg-based alloy. A selective etching was observed in sites of Mg2Si precipitates having “Chinese script”- like morphology. Analogous situation was found for Al-based alloy, where the key role was played by cathodic θ-CuAl2 phase.
Źródło:
Archives of Foundry Engineering; 2018, 18, 2; 125-130
1897-3310
2299-2944
Pojawia się w:
Archives of Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Effect of additional alloying and heat treatment on phase composition and morphology in Al-Mg-Si-type casting alloy
Wpływ dodatków stopowych i obróbki cieplnej na skład fazowy i morfologię stopu odlewniczego typu Al-Mg-Si
Autorzy:
Boyko, V.
Czekaj, E.
Warmuzek, M.
Mykhalenkov, K.
Powiązania:
https://bibliotekanauki.pl/articles/263779.pdf
Data publikacji:
2017
Wydawca:
Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
Tematy:
Al-Mg-Si casting alloy
casting
alloying
heat treatment
aging
precipitation
stop odlewniczy Al-Mg-Si
odlewanie
stopowanie
obróbka cieplna
starzenie
wydzielenie
Opis:
The structure of permanent mold and high pressure die castings of the AlMg5Si2Mn alloy after alloying with Li and Sc has been investigated by scanning and transmission electron microscopy, hardness and microhardness measurements, energy dispersive X-ray analysis. Three conditions, as cast, solution treated and aged, were investigated. It was shown that in as-cast state, the structure of an alloy having the nominal composition AlMg5Si2Mn consists of four phases: first – the Al based solid solution, second – the (Al) + (Mg2Si) eutectic, third – the primary Mg2Si crystals and fourth – the α-Al(Mn, Fe)Si phase. Similar phases were observed in the alloys containing Sc or Li. After two days of storing in an as-cast condition, the solid solution in all tested alloys decomposes and forms zebra-crossing shaped precipitates. TEM examinations revealed that these precipitates nucleate heterogeneously on dislocations. The solution treatment at 575.0°C results in spheroidization of the Mg2Si lamellas, dissolution of the precipitates and formation of α-Al(Mn, Fe)Si dispersoids, nucleating on the surfaces of Mg2Si lamellas. In the Sc containing alloys, the formation of Al3Sc was detected after 120 min soaking. Further heating resulted in the growth of these precipitates. Aging of the Al-Mg-Si alloys leads to an increase of hardness in all studied alloys. This effect is mainly related to precipitation strengthening, via solid solution decomposition and formation of β’’-phase. In Li-alloyed specimens, plates of β Mg2Si phase were observed together with small cubic-shaped δ’ Al3Li precipitates.
Strukturę odlewów wykonywanych w formach stałych i odlewów wysokociśnieniowych ze stopu AlMg5Si2Mn po stopowaniu Li i Sc badano za pomocą skaningowej i transmisyjnej mikroskopii elektronowej, a także wykonując pomiary twardości i mikrotwardości oraz prowadząc analizę rentgenowską z dyspersją energii. Badano trzy warianty: stan po odlaniu, odlew przesycony i starzony. Wykazano, że w stanie po odlaniu struktura stopu o nominalnym składzie AlMg5Si2Mn składa się z czterech faz: pierwsza – roztwór stały na bazie Al, druga – (Al) + (Mg2Si) eutektyczna, trzecia – pierwotne kryształy Mg2Si i czwarta – α-Al(Mn, Fe)Si. Podobne fazy zaobserwowano w stopach zawierających Sc lub Li. Po dwóch dniach przechowywania w stanie po odlaniu roztwór stały we wszystkich testowanych stopach rozkłada się i tworzy wydzielenia w kształcie przejściowym. Badania TEM ujawniły, że wytrącają one heterogenicznie jądro podczas dyslokacji. Obróbka roztworu przy 575,0°C powoduje sferoidyzację płytek Mg2Si, rozkład wydzieleń i tworzenie dyspersoidów oraz zarodkowanie na powierzchniach płytek Mg2Si. W stopie zawierającym Sc fazę Al3Sc wykryto po 120 min wygrzewania. Dalsze ogrzewanie spowodowało wzrost tych wydzieleń. Starzenie stopów Al-Mg-Si prowadzi do wzrostu twardości wszystkich badanych stopów. Efekt ten jest głównie związany z utwardzaniem wydzieleniowym na skutek rozkładu w stanie stałym i tworzenia fazy β’’. W próbkach ze stopu z litem obserwowano płytki fazy β-Mg2Si wraz z małymi sześciennymi wydzieleniami δ’-Al3Li.
Źródło:
Metallurgy and Foundry Engineering; 2017, 43, 3; 219-239
1230-2325
2300-8377
Pojawia się w:
Metallurgy and Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Design of new casting alloys of Al-Mg-Si-Mn system with alloying additions, its structure, and mechanical properties
Projektowanie nowych stopów odlewniczych układu Al-Mg-Si-Mn z dodatkami stopowymi wraz z ich strukturą i właściwościami mechanicznymi
Autorzy:
Boyko, V.
Czekaj, E.
Warmuzek, M.
Mykhalenkov, K.
Powiązania:
https://bibliotekanauki.pl/articles/263781.pdf
Data publikacji:
2017
Wydawca:
Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
Tematy:
Al-Mg-Si-Mn alloy
casting
Lithium
heat treatment
mechanical properties
stop Al-Mg-Si-Mn
odlewanie
lit
obróbka cieplna
właściwości mechaniczne
Opis:
The strength of Al-Mg-Si-Mn casting alloy strongly depends on Mg content in solid solution and precipitation of strengthening phases. Alloys with the nominal composition AlMg5Si2Mn with addition of Li and Ti+Zr were studied by means of differential scanning calorimetry (DSC), transmission electron microscopy (TEM) and energy dispersive X-Ray analysis (EDX). DSC measurements show that the eutectic melting temperature was about 595°C and it is higher than that of commercial A356 casting alloy. The macro- and microhardness tests show that in as-cast state hardness were higher than for A356 and continuously growth during artificial aging. TEM investigations reveal that during artificial aging three different precipitation types are forms in the alloy matrix. Two of them belong to the different structures of Mg2Si precipitates. Appearance of the third one identified as δ’-Al3Li phase represent that Al-Mg-Si system can be successfully used for designing of Li-containing casting alloy which is not developed yet.
Wytrzymałość stopu Al-Mg-Si-Mn w dużym stopniu zależy od zawartości Mg w roztworze stałym i wydzieleń faz wzmacniających. Stopy o nominalnym składzie AlMg5Si2Mn z dodatkiem Li i Ti + Zr badano za pomocą różnicowej kalorymetrii skaningowej (DSC), transmisyjnej mikroskopii elektronowej (TEM) i dyspersyjnej analizy promieniowania rentgenowskiego (EDX). Pomiary DSC pokazują, że eutektyczna temperatura topnienia wynosiła około 595°C i była wyższa niż w przypadku komercyjnego stopu odlewniczego A356. Testy makro- i mikrotwardości pokazują, że w stanie po odlaniu twardość była wyższa niż w przypadku A356 i stale rosła podczas sztucznego starzenia. Badania TEM wykazały, że podczas sztucznego starzenia w osnowie stopu występują trzy różne rodzaje wydzieleń. Dwa z nich należą do wydzieleń Mg2Si o różnej strukturze. Pojawienie się trzeciej, zidentyfikowanej jako faza δ’-Al3Li, oznacza, że układ Al-Mg-Si może być z powodzeniem stosowany do projektowania stopu odlewniczego zawierającego Li, który jeszcze nie został opracowany.
Źródło:
Metallurgy and Foundry Engineering; 2017, 43, 3; 141-152
1230-2325
2300-8377
Pojawia się w:
Metallurgy and Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
HRTEM observation of the precipitates in Cu and Ag added Al-Mg-Si alloys
Obserwacja wydzieleń w stopach Al-Mg-Si z dodatkiem Cu i Ag techniką wysokorozdzielczej transmisyjnej mikroskopii elektronowej
Autorzy:
Tokuda, M.
Matsuda, K.
Nagai, T.
Kawabata, T.
Nakamura, J.
Ikeno, S.
Powiązania:
https://bibliotekanauki.pl/articles/353776.pdf
Data publikacji:
2013
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
Al-Mg-Si alloy
precipitation
effect of Ag/Cu
TEM
stop AlMgSi
wydzielenia
wpływ Cu i Ag
Opis:
It has been known that Cu- and Ag-added Al-1.0mass%Mg2Si alloys (Al-Mg-Si-Cu alloy and Al-Mg-Si-Ag alloy) have higher hardness and elongation than those of Al-1.0mass%Mg2Si alloy. In this study, the aging behaviour of Al-Mg-Si-Cu alloy, Al-Mg-Si-Ag alloy and (Cu+Ag)-addition Al -1.0 mass% Mg2Si alloy has been investigated by hardness test and TEM observation. The Al-Mg-Si-Cu-Ag alloy has the fastest age-hardening rate in the early aging period and the finest microstructure at the peak hardness among three alloys. Therefore the microstructure of the precipitate in Al-Mg-Si-Cu-Ag alloy has been investigated by HRTEM observation to understand the effect of Cu and Ag addition on aging precipitation.
Znanym jest, że stopy Al-1.0 %wag. Mg2Si z dodatkiem Cu i Ag (stopy Al-Mg-Si-Cu i Al-Mg-Si-Ag) charakteryzują się wyższą twardością i większym wydłużeniem niż stopy Al-1.0 %wag. Mg2Si. W pracy badano proces starzenia stopów Al-Mg-Si-Cu, Al-Mg-Si-Ag oraz Al-1.0 %wag. Mg2Si z dodatkiem (Cu+Ag) przy użyciu pomiarów twardości i transmisyjnej mikroskopii elektronowej. Stop Al-Mg-Si-Cu-Ag charakteryzuje się najszybszym wzrostem twardości w początkowym etapie starzenia i najbardziej rozdrobniona mikrostruktura dla maksimum twardości sposród trzech badanych stopów.Wzwiązku z tym, mikrostruktura wydzieleń w stopach Al-Mg-Si-Cu-Ag zbadana została technika wysokorozdzielczej mikroskopii elektronowej w celu zrozumienia wpływu Cu i Ag na proces wydzielenia podczas starzenia.
Źródło:
Archives of Metallurgy and Materials; 2013, 58, 2; 363-364
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Reducing the Negative of the Iron in the Alloy Based on Al-Si-Mg by Manganese
Autorzy:
Podprocka, R.
Bolibruchova, D.
Chalupova, M.
Powiązania:
https://bibliotekanauki.pl/articles/381839.pdf
Data publikacji:
2017
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
alloy Al-Si-Mg
manganese
intermetallic phases
reducing of iron
stop Al-Si-Mg
mangan
fazy międzymetaliczne
redukcja żelaza
Opis:
In Al-Si alloy the iron is the most common impurity and with presence of other elements in alloy creates the intermetallic compounds, which decreases mechanical properties and increases of porosity. The cause of the negative effect of intermetallic particles on the mechanical properties is that it is more easily break off the tension load as the aluminium matrix or small particles of silicon. By adding suitable alloying elements, also known as iron correctors, is possible to reduce this harmful effect. In the article is evaluated influence of manganese on microstructure with performed EDX analysis selected intermetallic phases and tensile test and measurement of length of Al5FeSi phase. For realization experiments was used AlSi7Mg0.3 alloy with increased iron content. Manganese was added in the amount 0.3 wt. %, 0.6 wt. %, 0.8 wt.% and 1,2 wt. %. From performed measurements it has been concluded, that increased amount of manganese, i.e. Mn/Fe ratio, does not have significant influence on mechanical properties AlSi7Mg0.3 alloy in the melted state.
Źródło:
Archives of Foundry Engineering; 2017, 17, 2; 212-216
1897-3310
2299-2944
Pojawia się w:
Archives of Foundry Engineering
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Zastosowanie prasowania obwiedniowego do wytwarzania tarczy sprzęgła kłowego wykonanego ze stopu AlMgSi
The application of orbital forging to the production of AlMgSi alloy claw clutch rin
Autorzy:
Samołyk, G.
Powiązania:
https://bibliotekanauki.pl/articles/211438.pdf
Data publikacji:
2010
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Obróbki Plastycznej
Tematy:
prasowanie obwiedniowe
tarcza sprzęgła kłowego
MES (metoda elementów skończonych)
stop AlMgSi
orbital forging
claw clutch ring
FEM
Al-Mg-Si alloy
Opis:
W artykule przedstawiono wybrane wyniki analizy numerycznej prasowania obwiedniowego tarczy posiadającej trzy występy kłowe. Założono, że narzędzia wykonują ruch złożony, a tarcza (element składowy sprzęgła sprężystego kłowego) wykonana ze stopu AlMgSi jest kształtowana na zimno. Analiza termo-mechaniczna została wykonana za pomocą programu Deform-3D, który bazuje na metodzie elementów skończonych. Uzyskane wyniki obliczeń przedstawiają przede wszystkim znaczenie prędkości liniowej matrycy dolnej na wielkość siły prasowania oraz na zdolność wypełnienia wykroju roboczego przez materiał. Ponadto, autor porównał wyniki symulacji procesu prasowania obwiedniowego z tradycyjnym procesem wyciskania przeciwbieżnego tarczy sprzęgła kłowego.
The article presents selected results obtained from a numerical analysis of orbital forging of a ring with three claws. It has been assumed that the dies make a resultant motion and that the AlMgSi alloy ring, which forms part of the flexible elastomeric couplings, is cold formed. The thermo-mechanical analysis has been conducted with the Deform-3D software which is based on the finite element method. The obtained results primarily show how the lower die linear velocity affects the forging force and die cavity filling. Furthermore, the author compares the results of the conducted orbital forging simulation with a conventional method of producing claw clutch rings in backward extrusion.
Źródło:
Obróbka Plastyczna Metali; 2010, 21, 4; 229-238
0867-2628
Pojawia się w:
Obróbka Plastyczna Metali
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-8 z 8

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies