Basic theory and optimization of gold containing antimony concentrate leaching by alkaline sulfide
Autorzy:
Wu, Hao
Feng, Yali
Li, Haoran
Liao, Shengde
Wang, Hongjun
Powiązania:
https://bibliotekanauki.pl/articles/109524.pdf
Data publikacji:
2019
Wydawca:
Politechnika Wrocławska. Oficyna Wydawnicza Politechniki Wrocławskiej
Tematy:
antimony concentrate
leaching process
alkaline leaching
kinetics
Opis:
As sodium sulfide is easily oxidized to polysulfide and thiosulfate which have a gold leaching effect, gold would dissolve in leaching solution when extracting stibium from gold containing antimony concentrate by alkaline sulfide. Through leaching test and kinetics analysis, the decomposition regularity of sodium sulfide and leaching rate were studied under different leaching conditions. The results indicated that the gold content in antimony concentrate was 28.41g/Mg, and the content of antimony and sulfur was 36.01% and 14.04%, respectively. The main metallic minerals were native gold, arsenopyrite, stibnite, and the gangue minerals were mainly quartz. Anodic polarization curve shows reduced iron powder can increase the peak potential of the oxidation of the leaching solution and it can effectively prevent the decomposition of sodium sulfide and the dissolution of gold. Optimized stibium-extraction efficiency was achieved under the following conditions: a concentration of sodium sulfide and sodium hydroxide at 110g/dm³ and 20g/dm³, respectively; a ratio of iron powder to concentrate of 1:30; a ratio of liquid to solid of 5:1; agitation speed of 600rad/min; reaction temperature of 353.15K; and a reaction time of 3 h. Under the optimized conditions, high antimony recovery (97.35%) and low gold dissolution (1.32%) were achieved.
Źródło:
Physicochemical Problems of Mineral Processing; 2019, 55, 1; 248-257
1643-1049
2084-4735
Pojawia się w:
Physicochemical Problems of Mineral Processing
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies