Tytuł:: Impact of Zirconium on the Structural and Mechanical Properties of Commercial AlSi10MgCu Alloys
Autorzy:: Hajduch, P.
Djurdjevic, M. B.
Bolibruchová, D.
Simicevic, Z.
Powiązania:: https://bibliotekanauki.pl/articles/356527.pdf
Data publikacji:: 2019
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: zirconium
AlSi10MgCu alloy
hardness
solid solution treatment
Opis:: The impact of small addition of zirconium in hypoeutectic commercial AlSi10MgCu alloys on their mechanical properties (hardness) in as cast and thermally treated conditions was investigated. Small addition of zirconium does not change significantly the as cast and heat-treated microstructure of investigated alloys except to reduce the SDAS and grain size of primary α-aluminium phases. Addition of zirconium up to 0.14 wt. percentage increases the hardness of investigated alloys in as cast conditions. The increase in the hardness of samples after various solid solution times can correlate very well with the formation of small needle like coherent Al₃Zr particles.
Źródło:: Archives of Metallurgy and Materials; 2019, 64, 3; 1107-1110
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Skocz do pozycji: 2.

Tytuł:: Effect of Zirconium on the Solidification Path and Structural Properties of Commercial AlSi10MgCu Alloys
Autorzy:: Hajduch, P.
Djurdjevic, M. B.
Bolibruchová, D.
Simicevic, Z.
Powiązania:: https://bibliotekanauki.pl/articles/351378.pdf
Data publikacji:: 2020
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: zirconium
AlSi10MgCu alloy
grain size
SDAS
porosity
Opis:: Comprehensive understanding of the melt quality is of vital importance for foundry man. The effect of each particular element need to be properly analysed. Therefore, the aim of this paper was to analyse the impact of various content of zirconium on the solidification path and structural characteristics (SDAS, grain size, porosity) of as cast commercial AlSi10MgCu alloys. It has been found that addition of zirconium up to 0.24 wt.% reduce significantly the grains size (from 3.5 mm to 1.2 mm), SDAS (from 57.3 μm to 50.4 μm) and porosity (from 19% to 5%), leading to production of sound cast parts.