- Tytuł:
- Coda wave interferometry for monitoring the fracture process of concrete beams under bending test
- Autorzy:
-
Knak, Magdalena
Wojtczak, Erwin
Rucka, Magdalena - Powiązania:
- https://bibliotekanauki.pl/articles/27311414.pdf
- Data publikacji:
- 2023
- Wydawca:
- Polska Akademia Nauk. Czasopisma i Monografie PAN
- Tematy:
-
non-destructive testing
concrete beams
crack detection
fracture process
ultrasonic waves
coda wave interferometry
digital image correlation
badania nieniszczące
wykrywanie pęknięć
proces pękania
fale ultradźwiękowe
interferometria fal koda
cyfrowa korelacja obrazów
belka betonowa - Opis:
- Early detection of damage is necessary for the safe and reliable use of civil engineering structures made of concrete. Recently, the identification of micro-cracks in concrete has become an area of growing interest, especially when it comes to using wave-based techniques. In this paper, a non-destructive testing approach for the characterization of the fracture process was presented. Experimental tests were performed on concrete beams subjected to mechanical degradation in a 3-point bending test. Ultrasonic waves were registered on a specimen surface by piezoelectric transducers located at several points. Then, the signals were processed taking advantage of wave scattering due to micro-crack disturbances. For early-stage damage detection, coda wave interferometry was used. The novelty of the work concerns the application of the complex decorrelation matrix and the moving reference trace approach for better distinguishment of sensors located in different parts of a crack zone. To enhance coda wave-based damage identification results, optical imaging of crack development was performed by means of digital image correlation measurement. The results obtained showed that the coda wave interferometry technique can be successfully used as a quantitative measure of changes in the structure of concrete. The results also indicated that the course of decorrelation coefficient curves enabled the identification of three stages during degradation, and it depended on the location of acquisition points versus the crack zone.
- Źródło:
-
Bulletin of the Polish Academy of Sciences. Technical Sciences; 2023, 71, 3; art. no. e144118
0239-7528 - Pojawia się w:
- Bulletin of the Polish Academy of Sciences. Technical Sciences
- Dostawca treści:
- Biblioteka Nauki
Artykuł