- Characterization of CoTi Intermetallic Materials Produced by Electric Current Activated Sintering
- Autorzy:
-
Ergin, N.
Ozdemir, O. - Powiązania:
- https://bibliotekanauki.pl/articles/1219351.pdf
- Data publikacji:
- 2014-02
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.20.Ev
81.40.Pq - Opis:
- In the present work, the characterization and production of CoTi intermetallic materials produced by electric current activated sintering under 300 MPa uniaxial pressure in open air at 2000 A for 6 min was investigated. Cobalt powder with 10 μm size and titanium powder < 40 μm size having 99.9% and 99.5% purity, respectively, were used. The elemental powders were mixed in the stoichiometric ratio corresponding to the CoTi intermetallic, in a molar proportion of 1:1. Scanning electron microscopy and X-ray diffraction analysis were used to characterize produced samples. In microstructural examinations it was found that the sample has multi-phase microstructure. X-ray diffraction studies revealed that the phases are CoTi, $CoTi_2$, $TiCo_2$, and $CoTiO_3$. The relative density of test materials measured according to Archimedes' principle was 87.6%, and the microhardness of materials was about 646.74 $HV_{0.1}$.
- Źródło:
-
Acta Physica Polonica A; 2014, 125, 2; 399-401
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł