Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "Dercz, J." wg kryterium: Autor

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-9 z 9
    Tytuł:
    Effect of high energy ball milling on the structure and phase decomposition of the multiferroic Bi₅Ti₃FeO₁₅ ceramics
    Autorzy:
    Dercz, J.
    Zubko, M.
    Dercz, G.
    Matuła, I.
    Powiązania:
    https://bibliotekanauki.pl/articles/1075760.pdf
    Data publikacji:
    2016-10
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    75.85.+t
    61.05.cp
    68.37.Lp
    81.20.Wk
    Opis:
    The paper presents the results of the Bi₅Ti₃FeO₁₅ multiferroic phase stability analysis during high-energy ball milling aimed at obtaining fine dispersion ceramic powder. The X-ray diffraction and transmission electron microscopy methods were used to analyse the structure and verify the degree of crystallite dispersion. Structural data analysis was carried out using the Rietveld method. To carry out the analysis of the morphology, the scanning electron microscopy was used. The results that were obtained showed that the high energy ball milling process results in the decomposition of the initial ceramics, where finally Bi₅Ti₃FeO₁₅ and Bi are obtained. An increase in the proportion of the amorphous phase and an increase in the dispersion of the grains and crystallites of the powder that occurs with an increase in the milling time were observed.
    Źródło:
    Acta Physica Polonica A; 2016, 130, 4; 852-855
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Processing, Microstructure and Dielectric Properties of the $Bi_5Ti_3FeO_{15}$ Ceramic
    Autorzy:
    Rymarczyk, J.
    Dercz, G.
    Ilczuk, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811567.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    77.84.-s
    81.20.Ev
    81.05.Je
    61.05.cp
    68.37.Ef
    Opis:
    The aim of the present work is the analysis of microstructure, dielectric permittivity and thermal properties analysis of $Bi_5Ti_3FeO_{15}$ ceramics obtained by two methods. The studied $Bi_5Ti_3FeO_{15}$ ceramics were prepared by conventional synthesis and hot uniaxial pressing reaction from the conventional mixture of oxides, viz. $TiO_2$, $Fe_2O_3$, $Bi_2O_3$. The studied material has layered perovskite like structures, first described by Aurivillius in 1949 and Subbaro in 1969. The ceramic $Bi_5Ti_3FeO_{15}$ is known to contain a series of compounds with the general formula: $Bi_{m+1}Fe_{m-3}Ti_3O_{3m+3}$. The X-ray diffraction methods were used for qualitative phase analysis of studied samples. The morphology was analyzed by scanning electron microscopy method. The thermal properties of the studied materials were measured using the differential thermal analysis at a constant heating rate of 15 K/min under an argon protective atmosphere. Thermal dependence of dielectric permittivity was studied between room temperature and 1137 K.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6A; A-191-A-197
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Mössbauer Spectroscopy, X-Ray Diffraction and SEM Studies on Multiferroic $Bi_5Ti_3FeO_{15}$ Ceramics
    Autorzy:
    Rymarczyk, J.
    Hanc, A.
    Dercz, G.
    Ilczuk, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811595.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    61.05.Qr
    81.05.Je
    68.37.Hk
    61.05.cp
    77.84.-s
    Opis:
    Magnetoelectric multiferroics are materials which exhibit both magnetic order and ferroelectricity in the same phase. Multiferroic materials, where ferroelectricity and magnetism coexist, were extensively studied. This class of materials offers a large application potential for new devices due to the two coupled degrees of freedom based on the local off-centered distortion and the electron spin. The studied $Bi_5Ti_3FeO_{15}$ ceramics was prepared by conventional synthesis and hot uniaxial pressing reaction applying the conventional mixture of $TiO_2$, $Fe_2O_3$ and $Bi_2O_3$ oxides as precursor materials. The present work focuses on the structure analysis of multiferroic $Bi_5Ti_3FeO_{15}$ ceramics performed by X-ray diffraction method, scanning electron microscopy and the Mössbauer spectroscopy methods.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6; 1579-1584
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    A Study of Point Defects in the B2-Phase Region of the Fe-Al System by Mössbauer Spectroscopy
    Autorzy:
    Hanc, A.
    Kansy, J.
    Dercz, G.
    Pająk, L.
    Oleszak, D.
    Mrzigod, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811589.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    75.50.Bb
    61.72.J-
    76.80.+y
    Opis:
    In this work, we employed the Mössbauer spectroscopy and X-ray powder diffraction in a study of point defect formation in intermetallic phases of the B2 structure of the Fe-Al system as a function of Al concentration. The results are compared with the concentrations of point defect determined from positron annihilation data. In the Mössbauer effect, two types of samples are investigated: Fe-Al alloys with few additives obtained by induction melting and Al-rich metallic powders produced by the self-decomposition method and intensive grinding of high energy in the electro-magneto-mechanical mill. We present the values of the $\text{}^{57}Fe$ isomer shift and quadrupole splitting for the components describing the point defect in the local environment of a Mössbauer nuclide. The concentration of the Fe vacancies and Fe atoms substituting Al (Fe-AS) are determined. The results showed that an increase in Al content causes an increase in vacancy and Fe-AS concentration.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6; 1555-1562
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Semi-conducting properties of titanium dioxide layer on surface of Ti-15Mo implant alloy in biological milieu
    Autorzy:
    Szklarska, M.
    Dercz, G.
    Kubisztal, J.
    Balin, K.
    Łosiewicz, B.
    Powiązania:
    https://bibliotekanauki.pl/articles/1152668.pdf
    Data publikacji:
    2016-10
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    87.85.jj
    82.45.Bb
    72.20.-i
    Opis:
    The object of this work was to investigate structure, electrochemical behavior and semiconducting properties of the TiO₂ oxide layer on the Ti-15Mo implant alloy surface in normal and inflammatory conditions of physiological saline solution. X-ray photoelectron spectroscopy measurements confirm the presence of the oxide layer on the Ti-15Mo alloy surface. Electrochemical studies indicate excellent corrosion resistance of Ti-15Mo alloy in physiological saline solution. It was found that the investigated material under normal and inflammatory conditions behave like an insulator and n-type semiconductor, respectively.
    Źródło:
    Acta Physica Polonica A; 2016, 130, 4; 1085-1087
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Influence of Passivation Type on Corrosion Resistance of Ti15Mo Alloy in Simulated Body Fluids
    Wpływ rodzaju pasywacji powierzchni stopu Ti15Mo na jego odporność korozyjną w środowisku płynów ustrojowych
    Autorzy:
    Szklarska, M.
    Dercz, G.
    Rak, J.
    Łosiewicz, B.
    Simka, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/353709.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    biomaterial
    electrochemical impedance spectroscopy
    corrosion resistance
    passivation
    titanium alloys
    biomateriały
    elektrochemiczna spektroskopia impedancyjna
    odporność na korozję
    pasywacja
    stopy tytanu
    Opis:
    This work reports on determination of the influence of passivation type of Ti15wt.%Mo implant alloy surface on its corrosion resistance in simulated body fluids. The alloy under investigation was subjected to natural self-passivation in air, and forced passivation by autoclaving in steam, boiling in 30 % solution of H2O2, and electrochemical passivation in 0.9 % NaCl solution. Resistance of the passivated Ti15Mo alloy to pitting corrosion was studied at 37ºC in 0.9 % NaCl solution using open circuit potential method, anodic polarization curves, and electrochemical impedance spectroscopy (EIS). Comparative estimation of the determined parameters of corrosion resistance revealed that the obtained passive layers improve anticorrosive properties of the tested alloy. Surface of the alloy subjected to passivation in steam autoclave reveals the highest protection against pitting corrosion. Anodic potentiodynamic curves showed that the Ti15Mo alloy after different passivation types of the surface is characterized by a lack of susceptibility to pitting corrosion up to potential of 9 V. Based on the EIS investigations, the thickness of the formed oxide layers (TiO2, anatase) was determined to be in the range from 2.0 to 7.8 nm in dependence on the applied type of passivation. It was ascertained that electrochemical properties of the Ti15Mo alloy and possibility of its surface passivation using simple methods, make it an attractive material for use in biomedicine for long-term implants.
    Praca dotyczy określenia wpływu rodzaju pasywacji powierzchni stopu Ti15%wag.Mo na jego odporność korozyjną w środowisku płynów ustrojowych. Badany stop poddano naturalnej samopasywacji w powietrzu oraz wymuszonej pasywacji w autoklawie parowym, w gotującym się 30 % roztworze H2O2 oraz elektrochemicznej pasywacji w 0,9 % roztworze NaCl. Odporność pasywowanego stopu Ti15Mo na korozję wżerową badano w temperaturze 37°C w roztworze 0,9 % NaCl metodą potencjału obwodu otwartego, krzywych polaryzacji anodowej oraz elektrochemicznej spektroskopii impedancyjnej (ESI). Ocena porównawcza wyznaczonych parametrów odporności korozyjnej wykazała, że wytworzone warstwy pasywne poprawiają właściwości antykorozyjne badanego stopu. Powierzchnia stopu poddana pasywacji w autoklawie parowym wykazuje najwyższą ochronę przed korozją wżerową. Anodowe krzywe potencjodynamiczne ujawniły, że stop Ti15Mo poddany różnym sposobom pasywacji powierzchni wykazuje brak podatności na korozję wżerową aż do potencjału wynoszącego 9 V. W oparciu o badania ESI wyznaczona została grubość otrzymanych warstw tlenkowych (TiO2, anataz), która w zależności od zastosowanego sposobu pasywacji mieściła się w zakresie od 2,0 do 7,8 nm. Stwierdzono, że właściwości elektrochemiczne stopu Ti15Mo oraz możliwość pasywowania jego powierzchni prostymi metodami, czynią go atrakcyjnym materiałem do zastosowań w biomedycynie na implanty długoterminowe.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 4; 2687-2694
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Modification of Ti-6Al-4V Alloy Surface by EPD-PEO Process in ZrSiO4 Suspension
    Modyfikacja powierzchni stopu Ti-6Al-4V metodą PEO-EPDw zawiesinie ZrSiO4
    Autorzy:
    Krząkała, A.
    Młyński, J.
    Dercz, G.
    Michalska, J.
    Maciej, A.
    Niużyła, Ł.
    Simka, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/356201.pdf
    Data publikacji:
    2014
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Ti-6Al-4V alloy
    suspension
    anodic oxidation
    zirconium silicate
    stop Ti6Al4V
    zawiesina
    utlenianie anodowe
    krzemian cyrkonu
    Opis:
    Investigations on the surface modification of the Ti-6Al-4V alloy by plasma electrolytic oxidation are reported here. The oxidation process was carried out in a solution containing a zirconium silicate (ZrSiO4) suspension and sodium hydroxide (NaOH). Anodising was realised at voltages in a range from 100 V to 250 V. It was found that the morphology of the sample surface did not change during the oxidation of the alloy at 100 V. Application of voltages higher than 100 V led to the incorporation of zirconium silicate into the formed oxide layer and to significant changes of the surface morphology.
    W pracy przedstawiono wyniki badań nad modyfikacją powierzchni stopu Ti-6A1-4V metodą plazmowego utleniania elek- trochemicznego. Proces ten prowadzono w roztworze zawierającym zawiesinę krzemianu cyrkonu (ZrSiO4 oraz wodorotlenek sodu (NaOH). Anodowanie prowadzono w zakresie napięcia od 100 do 250 V. Stwierdzono, że zastosowanie napięcia 100 V nie powoduje zmian w morfologii powierzchni stopu. Natomiast zastosowanie napięcia wyższego od 100 V powoduje wbudowanie krzemianu cyrkonu w tworzącą się warstewką tlenową oraz znaczne zmiany w morfologii powierzchni stopu Ti-6A1-4V.
    Źródło:
    Archives of Metallurgy and Materials; 2014, 59, 1; 199-204
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Structural Studies with the Use of XRD and Mössbauer Spectroscopy οf $Bi_5Ti_3FeO_{15}$ Ceramic Powders Obtained by Mechanical Synthesis
    Autorzy:
    Dercz, G.
    Rymarczyk, J.
    Hanc, A.
    Prusik, K.
    Babilas, R.
    Pająk, L.
    Ilczuk, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/1811608.pdf
    Data publikacji:
    2008-12
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    61.05.Qr
    61.05.C-
    61.05.J-
    81.07.Bc
    81.20.Wk
    Opis:
    In this paper the structural and Mössbauer spectral properties of multiferroic ceramic $Bi_5Ti_3FeO_{15}$ powders prepared by high-energy ball milling of polycrystalline precursor material (mixture of $Bi_2O_3$, $TiO_2$ and $Fe_2O_3$ powders) are presented. Mechanical synthesis was performed by high-energy vibratory mill. The X-ray diffraction methods were applied for the structure characterization of the studied samples. The parameters of diffraction line profiles were determined by PRO-FIT Toraya procedure. The crystallite sizes and lattice distortions were analyzed using the Williamson-Hall method. Investigations of hyperfine interactions in the studied materials were carried out by the Mössbauer spectroscopy. The powder morphology was analyzed by scanning electron microscopy and transmission electron microscopy techniques. It was found that during high-energy milling phase transitions, a decrease in crystallite size and amorphization process are observed.
    Źródło:
    Acta Physica Polonica A; 2008, 114, 6; 1623-1629
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Microstructure and Properties of YSZ Coatings Prepared by Plasma Spray Physical Vapor Deposition for Biomedical Application
    Autorzy:
    Barczyk, J.
    Dercz, G.
    Matuła, I.
    Góral, M.
    Maszybrocka, J.
    Bochenek, D.
    Gurdziel, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/356455.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    PS-PVD method
    bioactive coatings
    cp-Ti
    YSZ
    osseointegration
    Opis:
    This paper presents the study of microstructure and properties of 8 mol% yttrium stabilized zirconia coating fabricated by Plasma Spray Physical Vapor Deposition technique on commercial pure titanium. The coating was characterized by X-ray diffraction, high resolution scanning electron microscope, profilometer, nanoindentation and nanomachining tests. The X-ray phase analysis exhibit the tetragonal Zr0.935 Y0.065O1.968, TiO and α-Ti phases. The Rietveld refinement technique were indicated the changes of crystal structure of the produced coatings. The characteristic structure of columns were observed in High Resolutions Scanning Electron Microscopy. Moreover, the obtained coating had various development of surfaces, thickness was equal to 3.1(1) μm and roughness 0.40(7) μm. Furthermore, the production coatings did not show microcracks, delamination and crumbing. The performed experiment encourages carried out us to tests for osseointegration.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 2; 779-783
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-9 z 9

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies