    Tytuł:
    Permeability of Medical Gloves to Mono- and Dimethacrylate Monomers in Dental Restorative Materials
    Autorzy:
    Lonnroth, E. C.
    Ruyter, I. E.
    Powiązania:
    https://bibliotekanauki.pl/articles/90066.pdf
    Data publikacji:
    2002
    Wydawca:
    Centralny Instytut Ochrony Pracy
    Tematy:
    protection
    methacrylates
    composites
    resins
    adhesives
    metakrylany
    materiały na środki ochrony indywidualnej
    usługi stomatologiczne
    rękawice ochronne
    medycyna pracy
    materiały dentystyczne
    Opis:
    Dental personnel manually handle methacrylate-based restorative materials, which can cause skin irritation and allergies. The protection given by different types of medical gloves is not well known. Breakthrough time (BTT, min) was used as a measure of protection according to a European standard, using 2 test mixtures consisting of respectively 3 and 5 monomers. Fourteen gloves representing natural rubber latex, synthetic rubber, and synthetic polymeric material were tested. The BTT ranged from some minutes to more than 2 hrs for the 4 monomers with a molecular mass less than 300. The longest protection was recorded for Nitra Touch (nitrile rubber), Tactylon (synthetic rubber), and Metin (PVC).
    Źródło:
    International Journal of Occupational Safety and Ergonomics; 2002, 8, 4; 497-509
    1080-3548
    Pojawia się w:
    International Journal of Occupational Safety and Ergonomics
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wpływ metody fotopolimeryzacji kompozytów stomatologicznych na bazie żywic dimetakrylanowych na naprężenia skurczowe oraz wybrane właściwości utwardzonego materiału
    Effect of the method of photopolymerization of dental composites based on dimethacrylate resin on the shrinkage stresses and selected properties of the cured material
    Autorzy:
    Bociong, K.
    Krasowski, M.
    Domarecka, M.
    Sokołowski, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/947262.pdf
    Data publikacji:
    2016
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Chemii Przemysłowej
    Tematy:
    żywice dimetakrylanowe
    kompozyty stomatologiczne
    fotopolimeryzacja
    naprężenia skurczowe
    dimethacrylate resins
    dental composites
    photopolymerization
    shrinkage stresses
    Opis:
    Materiały kompozytowe na bazie żywic dimetakrylanowych, stosowane w stomatologii zachowawczej, polimeryzowano różnymi metodami za pomocą światła o różnej gęstości mocy. Analizowano wpływ sposobu naświetlania kompozytu na powstające w materiale naprężenia skurczowe oraz wybrane właściwości utwardzonego kompozytu. Próbki naświetlano z jednej strony w sposób: ciągły, przerywany, z zastosowaniem metody soft-start lub pulse delay. Oceniono efektywność polimeryzacji, średnicową wytrzymałość na rozciąganie (DTS) oraz mikrotwardość Vickersa (HV) badanych kompozytów. Stwierdzono, że najmniejsze naprężenia skurczowe są generowane podczas naświetlania kompozytu w sposób konwencjonalny (naświetlanie ciągłe) oraz metodą pulse delay, natomiast największe naprężenia skurczowe występują w materiale naświetlanym w sposób przerywany. Ponadto kompozyt naświetlany metodą pulse delay charakteryzuje się największą twardością HV1. Nie stwierdzono statystycznie istotnych różnic między DTS próbek polimeryzowanych w różny sposób. Niezależnie od czasu i warunków naświetlania kompozytów stopień konwersji jest zadowalający i wynosi nie mniej niż 65%.
    The composite materials used in conservative dentistry were obtained through polymerization of dimethacrylate resins by light with different power density. The effects of composite irradiation method on the shrinkage stresses induced in the material and selected properties of the cured product were analyzed. The polymerization was carried out for 60 s irradiating the sample from one side continuously, intermittently (after every 20 sec exposure the samples were conditioned for 5 min), by using the "soft-start” method (10s at 200 mW/cm2, 5 s at 200–1400 mW/cm2, remaining time at 1400 mW/cm2) or "pulse delay” method (2 s at 200mW/cm2, 2 min break, 58 s at 1400 mW/cm2). The efficiency of polymerization, diametral tensile strength (DTS) and Vickers microhardness (HV) of the composites were evaluated. It was found that the smallest stresses are generated during the irradiation of the composite in aconventional way (continuous exposure) and using "pulse delay” method. The largest stresses occur in the material irradiated in an intermittent way. The composite irradiated using "pulse delay” method has the highest hardness HV1. There are no statistically significant differences between DTS of the differently polymerized samples. Regardless of how long and by what method the composites were cured their degree of conversion was satisfactory and not lower than 65%.
    Źródło:
    Polimery; 2016, 61, 7-8; 499-508
    0032-2725
    Pojawia się w:
    Polimery
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Wpływ zawartości oraz rodzajów monomerów sieciujących w kopolimerach zawierających poliester nienasycony modyfikowany izobutanolem na właściwości nienasyconych żywic poliestrowych
    Effect of content and types of crosslinking monomers in copolymers containing isobutanol modified unsaturated polyester on the properties of unsaturated polyester resins
    Autorzy:
    Chabros, A.
    Gawdzik, B.
    Powiązania:
    https://bibliotekanauki.pl/articles/279039.pdf
    Data publikacji:
    2017
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Inżynierii Materiałów Polimerowych i Barwników
    Tematy:
    nienasycone żywice poliestrowe
    emisja styrenu
    dimetakrylan glikolu dietylenowego
    unsaturated polyester resin
    styrene emission
    diethylene glycol dimethacrylate
    Opis:
    W wyniku polimeryzacji rodnikowej poliestru nienasyconego uzyskano kopolimery ze zmienną zawartością styrenu i dimetakrylanu glikolu dietylenowego jako monomerów sieciujących. Poliester nienasycony syntezowany był dwuetapowo z łatwo dostępnych surowców: bezwodnika maleinowego, glikoli etylenowego i 1,2-propylenowego oraz alkoholu izobutylowego. Zbadano wpływ monomerów sieciujących na reaktywność i lepkość nienasyconych żywic poliestrowych (NŻP) oraz scharakteryzowano właściwości mechaniczne i termiczne produktów polimeryzacji.
    As a result of radical polymerization of the unsaturated polyester, copolymers with variable content of styrene and diethylene glycol dimethacrylate as crosslinking monomers were obtained. The unsaturated polyester was synthesized in two steps from readily available raw materials: maleic anhydride, ethylene glycol, propylene glycol and isobutyl alcohol. The influence of crosslinking monomers on reactivity and viscosity of unsaturated polyester resins (UPR’s) was investigated. The mechanical and thermal properties of the polymerization products were characterized.
    Źródło:
    Przetwórstwo Tworzyw; 2017, T. 23, Nr 3 (177), 3 (177); 165-171
    1429-0472
    Pojawia się w:
    Przetwórstwo Tworzyw
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies