Degradation of welded joint made of T91 steel with different additional materials
Degradacja złącza stali T91 spawanego różnymi materiałami dodatkowymi - Autorzy:
-
Wojsyk, Kwiryn
Klimaszewska, Klaudia
Golański, Grzegorz - Powiązania:
- https://bibliotekanauki.pl/articles/115157.pdf
- Data publikacji:
- 2019
- Wydawca:
- Stowarzyszenie Inżynierów i Techników Mechaników Polskich
- Tematy:
-
materiał niskostopowy
materiał wypełniający
złącze jednorodne
starzenie
stal T91
low alloy material
filler material
heterogeneous joint
ageing
T91 steel - Opis:
-
The aim of the research was to analyse the processes of degradation observed in a similar welded joint of T91 steel. The analysis was performed for welded joints after long-term annealing for up to 8000 hours at the temperature of 600 °C. Microstructural analysis and hardness testing were performed. The purpose of the tests was to evaluate the effect of annealing time at the temperature of ageing on formation and properties of the decarburized zone in the inter-bead area of the welded joint. The study presents the results of physical examinations of the joint welded using two different filler materials (similar welded joint) after long-term effect of high temperature.
Celem badań była analiza procesów degradacji obserwowanych w złączu spawanym ze stali T91. Analizę wykonano dla połączeń spawanych po długotrwałym wyżarzaniu do 8000 godzin w temperaturze 600°C. Przeprowadzono analizę mikrostrukturalną i badania twardości. Celem badań była ocena wpływu czasu wyżarzania w temperaturze starzenia na powstawanie i właściwości strefy odwęglonej w obszarze międzyściegowym złącza spawanego. - Źródło:
-