Polymer Blended (Epoxy/Vinylester) Nanocomposites Resistance against Pulling & Sliding Wear Loads
Autorzy:
Harisankar, P.
Reddy, Y. V. M.
Reddy, K. H.
Powiązania:
https://bibliotekanauki.pl/articles/971334.pdf
Data publikacji:
2014
Wydawca:
Przedsiębiorstwo Wydawnictw Naukowych Darwin / Scientific Publishing House DARWIN
Tematy:
blended polymer composite
vinylester
epoxy
mechanical properties
sliding wear
Taguchi Method
SEM
Opis:
This paper discloses the development and synthesis of polymer blended nanocomposites filled with nanoclay. The hybridization of epoxy is mixed with vinylester resin (VER) to prepare polymer blend filled with organoclay was studied to enhance mechanical properties of epoxy/VER. Clay loading was done in such a way that with different wt. proportions viz.1, 1.5, 2.0, 2.5, 3.0, 4.0, 5.0, & 7.5 w % ratios. Appropriately cured samples gave excellent mechanical and tribological properties. Results showed that the tensile strength of the composites increased with increase in filler content for the range of filler contents (2.5-4 % vol.). The results indicated that at 4 % wt. of filler concentration the tensile strength obtained is good i.e. 47.79 MPa with density 1.37 gm/cm3 and hardness 45.5. Dry Sliding wear tests were also conducted by following a well-planned experimental schedule based on Taguchi’s design of experiments, considering parameters like Filler content, Normal load, Sliding Velocity and Sliding distance, on a Pin-On-Disc set-up (ASTM G-99 standard, Make: DUCOM Engineers, Bangalore, India). In the experimentation composite pins were worn against a rotating steel disc (Europe Norm) EN-31, (Rockwell C Hardness) HRC 60 and (Roughness Average) Ra 0.02 microns. Control factors like Filler Content, Normal Load were found to be significant factors affecting the Wear rate i.e. the inclusion of nanoclay as filler found to be contributed in improving the wear resistance of the composite. SEM observations are made to probe the wear mechanisms involved.
Źródło:
International Letters of Chemistry, Physics and Astronomy; 2014, 18; 75-90
2299-3843
Pojawia się w:
International Letters of Chemistry, Physics and Astronomy
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-1 z 1

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies