- Tytuł:
- Influence of Borosilicate Addition on Mechanical Properties and Sinterability of 8YSZ
- Autorzy:
- Aktas, B.
- Powiązania:
- https://bibliotekanauki.pl/articles/1186987.pdf
- Data publikacji:
- 2016-04
- Wydawca:
- Polska Akademia Nauk. Instytut Fizyki PAN
- Tematy:
-
81.05.Je
81.40.Np
82.47.Ed - Opis:
- The influence of borosilicate (BS) addition on the mechanical properties and sinterability of yttria-stabilized zirconia (8YSZ) was investigated using scanning electron microscopy (SEM) and Vickers-hardness test. Undoped and 0.5-10 wt.% BS-doped 8YSZ powders were prepared using a colloidal process. The powders were then pelletized under a pressure of 200 MPa. The BS-doped 8YSZ specimens were sintered at 1200-1400°C for 1 h. SEM results showed that intergranular glass phases were formed at the grain boundaries of 8YSZ, particularly in the 5 and 10 wt.% BS-doped 8YSZ specimens. These intergranular glass phases caused a decrease in grain size of 8YSZ. The grain sizes of the undoped and 0.5 wt% BS-doped 8YSZ specimens were 2.68 μm and 1.83 μm, respectively. The addition of BS to 8YSZ caused a decrease in the relative density. In addition, the relative density was found to be increased with higher sintering temperature. The hardness of 8YSZ decreased with the increase in BS dopant amount, due to presence at the grain boundaries of a BS glassy phase that has a lower hardness than 8YSZ.
- Źródło:
-
Acta Physica Polonica A; 2016, 129, 4; 677-679
0587-4246
1898-794X - Pojawia się w:
- Acta Physica Polonica A
- Dostawca treści:
- Biblioteka Nauki
Artykuł