Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "10CrMo9-10 steel" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-7 z 7
    Tytuł:
    The Defects of Oxide Layers Formed on 10CrMo9-10 Steel Operated for 200,000 Hours at an Elevated Temperature
    Autorzy:
    Gwoździk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/353504.pdf
    Data publikacji:
    2016
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    oxide layer
    10CrMo9-10 steel
    LM
    SEM
    AFM
    XRD
    Opis:
    The paper contains results of studies into the formation of oxide layers on 10CrMo9-10 (10H2M) steel long-term operated at an elevated temperature (T = 545°C, t = 200,000h). The oxide layer was studied on a surface and a cross-section at the inner and outer surface of the tube wall on the outlet both on the fire and counter-fire side of the tube wall surface. The obtained results of research have shown a higher degree of degradation, both of the steel itself and oxide layers, on the fire side. In addition, it has been shown that on the outside tube wall, apart from iron oxides, there are also deposits composed mainly of Al2SiO5.
    Źródło:
    Archives of Metallurgy and Materials; 2016, 61, 2B; 987-992
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Analysis of crystallite size changes in a hematite and magnetite formed on steel used in the power idustry
    Autorzy:
    Gwoździk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/297993.pdf
    Data publikacji:
    2018
    Wydawca:
    Uniwersytet Warmińsko-Mazurski w Olsztynie
    Tematy:
    10CrMo9-10 steel
    hematite
    magnetite
    X-ray diffraction
    crystallite sizes
    Opis:
    The paper presents results of studies on the crystallite sizes of oxide layer formed during a long-term operation on 10CrMo9-10 steel at an elevated temperature (T = 545° C, t = 200,000 h). This value was determined by a method based on analysis of the diffraction line profile, according to a Scherrer formula. The oxide layer was studied on a surface and a cross-section at the outer and inner site on the pipe outlet, at the fire and counter-fire wall of the tube. X-ray studies were carried out on the surface of a tube, then the layer’s surface was polished and the diffraction measurements repeated to reveal differences in the originated oxides layer.
    Źródło:
    Technical Sciences / University of Warmia and Mazury in Olsztyn; 2018, 21(1); 65-73
    1505-4675
    2083-4527
    Pojawia się w:
    Technical Sciences / University of Warmia and Mazury in Olsztyn
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Changes of crystallite sizes in the oxide layer forming during long-term operation of 10CrMo9-10 steel
    Autorzy:
    Gwoździk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/298126.pdf
    Data publikacji:
    2017
    Wydawca:
    Uniwersytet Warmińsko-Mazurski w Olsztynie
    Tematy:
    10CrMo9-10 steel
    oxide layer
    X-ray diffraction
    crystallite sizes
    Opis:
    The paper contains results of the studies on X-ray diffraction analysis XRD (studying the phase composition, crystallite sizes) of oxide layers on 10CrMo9-10 steel, operated for a long time at an elevated temperature (T = 525°C, t = 200,000 h). The oxide layer was studied on a surface and a cross-section at the outer on the inlet both on the fire and counter-fire side of the tube wall surface. X-ray studies were carried out on the outer surface of a tube, and then the layer surface was polished down and the diffraction measurements were performed again to determine crystallite size in oxide layers. Based on the width and the position of the main coat and substrate reflections, the size of the crystallites was determined using the Scherrer formula.
    Źródło:
    Technical Sciences / University of Warmia and Mazury in Olsztyn; 2017, 20(3); 289-296
    1505-4675
    2083-4527
    Pojawia się w:
    Technical Sciences / University of Warmia and Mazury in Olsztyn
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Characterization of oxide layers formed on 10CrMo9-10 steel operated for a long time in the power industry
    Autorzy:
    Gwoździk, Monika
    Ullrich, Christiane
    Schimpf, Christian
    Rafaja, David
    Kulesza, Sławomir
    Bramowicz, Mirosław
    Powiązania:
    https://bibliotekanauki.pl/articles/2086836.pdf
    Data publikacji:
    2021
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    power industry
    10CrMo9-10 steel
    oxide layers
    energetyka
    stal 10CrMo9-10
    warstwy tlenkowe
    Opis:
    This paper presents the results of diagnostic examinations conducted on the coils of super-heaters made of 10CrMo9‒10 steel that were operated in industrial conditions at 480°C for 130 thousand hours. The tube was exposed in a coal-fired boiler. The chemical and phase composition of the oxide/deposit layers formed on both sides of the tube walls (outside – flue-gas side and inside – steam side) and their sequence was examined using optical microscopy, scanning electron microscopy with electron backscatter diffraction and energy-dispersive X-ray spectroscopy, and X-ray diffraction. The changes in the mechanical properties caused by corrosion and aging processes were concluded from the hardness measurements. In addition, the nature of cracks in the oxide layers caused by pressing a Vickers indenter was determined. The results of these examinations have shown a high degradation of steel on the flue-gas inflow side and identified the main corrosion products and mechanisms.
    Źródło:
    Bulletin of the Polish Academy of Sciences. Technical Sciences; 2021, 69, 4; e137730, 1--10
    0239-7528
    Pojawia się w:
    Bulletin of the Polish Academy of Sciences. Technical Sciences
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The influence of the parameters of heat treatment on the mechanical properties of welded joints
    Autorzy:
    Łuczak, K.
    Wolany, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/378914.pdf
    Data publikacji:
    2019
    Wydawca:
    Stowarzyszenie Komputerowej Nauki o Materiałach i Inżynierii Powierzchni w Gliwicach
    Tematy:
    heat treatment
    welded joints
    10CrMo9-10 steel
    obróbka cieplna
    złącze spawane
    stal 10CrMo9-10
    Opis:
    Purpose: The main goal of the work is to determine the influence of the parameters of stress relief annealing on the mechanical and structural properties of welded joints made of chromium-molybdenum type 10CrMo9-10 steel. Design/methodology/approach: In the study, commercial 10CRMO9-10 steel was used, the Polish equivalent of 10H2M. This is a chromium-molybdenum toughened steel, i.e. after normalization (910-960°C) and high tempering (650-780°C). The materials were subjected to heat treatment, tests of mechanical properties, Charpy impact test, hardness of individual material zones, as well as macro and microscopic observations. Findings: The hardness tests indicated, that materials subjected to a single heat treatment possess the greatest hardness. Materials undergoing several heat treatments, possess hardness on a similar level to materials that have been annealed once, however they are characterized by low reproducibility of results. The most important parameter of heat treatment of the tested steel is heating up to a temperature of 690°C. Due to such heating, optimal mechanical properties are achieved, which results in long and safe exploitation of the produced elements. Research limitations/implications: The processes of heat treatment are very important to achieve optimal strength properties of welded joints. Practical implications: The development of energy worldwide has caused the creation of machines working in higher pressure and temperature ranges. The influence of temperatures decreases the service life of a given element. The adaptation and completion of the appropriate process of heat treatment extends the exploitation time of elements. Originality/value: Determining the mechanical properties of 10H2M steel, dependent on the temperature of heat treatment and heating time. It was concluded that the optimal parameter of heat treatment for the tested materials – is heating at a temperature of 690°C.
    Źródło:
    Archives of Materials Science and Engineering; 2019, 95, 2; 55-66
    1897-2764
    Pojawia się w:
    Archives of Materials Science and Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Effect of Heat Treatment Parameters on Mechanical Characteristics of 10CrMo9-10 Steel Tube Bends
    Wpływ parametrów obróbki cieplnej na charakterystyki mechaniczne łuków rurowych ze stali 10CrMo9-10
    Autorzy:
    Cieśla, M.
    Findziński, R.
    Junak, G.
    Kawała, T.
    Powiązania:
    https://bibliotekanauki.pl/articles/351031.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    heat treatment
    10CrMo9-10 steel
    tube bending
    obróbka cieplna
    stal 10CrMo9-10
    łuki rurowe
    Opis:
    The purpose of the paper was to analyse the effect of diverse heat treatment parameters (normalising and tempering) on mechanical characteristics of the material used to develop ϕ508x20 tube bends made of the 10CrMo9-10 steel by application of induction heating. The research conducted included tests of basic mechanical properties as well as low cycle fatigue and creep at the temperature of 500°C. With reference to the results thus obtained, it has been established that there is a relationship between mechanical properties of bends and individual features of their microstructure conditional to the heat treatment parameters. Among other conclusions drawn in the research, it has been found that the main structural factor conditioning the mechanical properties of bends was the grain size. Heat treatment parameters characterised by lower temperature and shorter tempering time triggered changes in the material microstructure, such as increased grain comminution. The effects of the said changes included improvement of strength characteristics (Rm, Rp0,2) as well as increased material durability under conditions of fatigue and creep. Main criterion-specific mechanical properties and geometric features of the bends developed conformed with the relevant requirements of reference standards (PN-EN 10216-2, PN-EN 12952).
    W pracy analizowano wpływ zróżnicowanych parametrów obróbki cieplnej (normalizowanie i odpuszczanie) na charakterystyki mechaniczne materiału łuków rurowych ϕ508x20 ze stali 10CrMo9-10 wykonanych z zastosowaniem nagrzewania indukcyjnego. Przeprowadzono badania podstawowych własności mechanicznych oraz zmęczenia niskocyklowego i pełzania w temperaturze 500°C. Na podstawie uzyskanych wyników stwierdzono, że istnieje związek pomiędzy właściwościami mechanicznymi łuków, a cechami ich mikrostruktury determinowanymi parametrami obróbki cieplnej. Stwierdzono między innymi, że głównym czynnikiem strukturalnym warunkującym właściwości mechaniczne łuku była wielkość ziarna. Parametry obróbki cieplnej charakteryzujące się niższą temperaturą i krótszym czasem odpuszczania, skutkowały zmianami mikrostruktury materiału w tym większym rozdrobnieniem ziarna. Efektem tych zmian był wzrost właściwości wytrzymałościowych (Rm, Rp0,2) jak również zwiększenie trwałości materiału w warunkach zmęczenia i pełzania. Podstawowe, kryterialne właściwości mechaniczne i cechy geometryczne wykonanych łuków spełniały wymogi przedmiotowych norm (PN-EN 10216-2, PN-EN 12952).
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 4; 2971-2976
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Evaluation of microstructure of steel for the power industry by means of triafole replica method
    Ocena mikrostruktury stali dla energetyki metodą replik triafolowych
    Autorzy:
    Gwoździk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/264090.pdf
    Data publikacji:
    2013
    Wydawca:
    Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
    Tematy:
    badania nieniszczące
    repliki triafolowe
    stal 10CrMo9-10
    enegetyka
    non-destructive testing
    triafole replica
    10CrMo9-10 steel
    power industry
    Opis:
    W pracy przedstawiono zagadnienie mikrostruktury stali przeznaczonych dla energetyki do pracy w podwyższonej temperaturze. Badano materiał zarówno w stanie wyjściowym, jak i po eksploatacji. Badania mikrostruktury wykonano metodą replik triafolowych w celu określenia stopnia wyeksploatowania materiału. Sprawdzono jakość odwzorowania struktury na replikach triafolowych, porównując je z obrazami ze zgładów metalograficznych. Podjęto próby poprawy jakości obrazu struktury na replikach przez stosowanie różnego stopnia wytrawienia zgładów oraz obserwacje replik niecieniowanych i cieniowanych. W artykule omówiono także najczęściej spotykane wady technologiczne powstające podczas wykonywania replik.
    The paper presents microstructures of steel designated for the operation at elevated temperatures in the power industry. Materials were examined both in the initial state as well as after the operation. The microstructure was examined using triafol replicas to determine the degree of materials wearing out. The quality of the structure representation on triafol replicas was checked, comparing them with the images from microsections. Attempts were made to improve the structure image quality on replicas through application of various degrees of microsection etching, and observation of unshaded and shaded replicas. The paper presents also most frequently encountered technological defects originating during replica preparation.
    Źródło:
    Metallurgy and Foundry Engineering; 2013, 39, 1; 7-14
    1230-2325
    2300-8377
    Pojawia się w:
    Metallurgy and Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-7 z 7

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies