The paper contains results of studies into the formation of oxide layers on 10CrMo9-10 (10H2M) steel long-term operated at an elevated temperature (T = 545°C, t = 200,000h). The oxide layer was studied on a surface and a cross-section at the inner and outer surface of the tube wall on the outlet both on the fire and counter-fire side of the tube wall surface. The obtained results of research have shown a higher degree of degradation, both of the steel itself and oxide layers, on the fire side. In addition, it has been shown that on the outside tube wall, apart from iron oxides, there are also deposits composed mainly of Al2SiO5.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00