Tytuł:: The Effect of Annealing Temperature on the Phase Constitution and Magnetic Properties of the Pr₈Dy₁Fe₆₀Co₇Mn₆B₁₄Zr₁Ti₃ Alloy Ribbons
Autorzy:: Przybył, A.
Pawlik, K.
Pawlik, P.
Gębara, P.
Kaszuwara, W.
Wysłocki, J.
Filipecka, K.
Powiązania:: https://bibliotekanauki.pl/articles/1402331.pdf
Data publikacji:: 2015-07
Wydawca:: Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:: 75.20.En
91.60.Pn
Opis:: Melt-spun ribbons were produced from the Pr₈Dy₁Fe₆₀Co₇Mn₆B₁₄Zr₁Ti₃ base alloy at the surface velocity of the cooper wheel of 30 m/s. The studies showed amorphous structure of ribbons and their soft magnetic properties. X-ray diffraction was used to determine phase constitution of all obtained samples. Annealing of ribbons caused formation of nanocomposite structure, which was a result of coexistence of hard magnetic RE₂(Fe,Co)₁₄B and soft magnetic α-Fe phases. Basic magnetic properties such as: coercivity $\text{}_{J}H_{c}$, remanence $J_{r}$ and maximum energy product $(BH)_\text{max}$ were determined from the measured hysteresis loops. The microstructure of selected specimens was observed by transmission electron microscopy technique.
Źródło:: Acta Physica Polonica A; 2015, 128, 1; 94-97
0587-4246
1898-794X
Pojawia się w:: Acta Physica Polonica A
Dostawca treści:: Biblioteka Nauki

Artykuł

Skocz do pozycji: 2.

Tytuł:: Magnetic Properties and Phase Constitution of the Nanocrystalline $(Nd_{10}Fe_{67}B_{23})_{100-x}Nb_{x}$ (where x=1, 2, 3, 4) Alloy Ribbons
Autorzy:: Kaźmierczak, M.
Pawlik, K.
Pawlik, P.
Gębara, P.
Przybył, A.
Wysłocki, J.
Powiązania:: https://bibliotekanauki.pl/articles/1402329.pdf
Data publikacji:: 2015-07
Wydawca:: Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:: 75.20.En
91.60.Pn
Opis:: In the present work the magnetic properties and phase constitution of $(Nd_{10}Fe_{67}B_{23})_{100-x}Nb_{x}$ (where x=1, 2, 3, 4) alloys in a form of ribbons were investigated. The ribbon samples were obtained by controlled atmosphere melt-spinning technique. In order to generate the nanocrystalline microstructure, ribbons were annealed at various temperatures (from 923 K to 1023 K) for 5 min. Subsequent annealing resulted in an evolution of the phase constitution accompanied by a change of their magnetic properties. The X-ray diffraction studies show presence of hard magnetic $Nd_{2}Fe_{14}B$, paramagnetic $Nd_{1+\epsilon}Fe_{4}B_{4}$ and ferromagnetic metastable $Nd_{2}Fe_{23}B_{3}$ phases. The best hard magnetic parameters were measure for annealed ribbons of the $(Nd_{10}Fe_{67}B_{23})_{96}Nb_{4}$ alloy.
Źródło:: Acta Physica Polonica A; 2015, 128, 1; 91-93