Melt-spun ribbons were produced from the Pr₈Dy₁Fe₆₀Co₇Mn₆B₁₄Zr₁Ti₃ base alloy at the surface velocity of the cooper wheel of 30 m/s. The studies showed amorphous structure of ribbons and their soft magnetic properties. X-ray diffraction was used to determine phase constitution of all obtained samples. Annealing of ribbons caused formation of nanocomposite structure, which was a result of coexistence of hard magnetic RE₂(Fe,Co)₁₄B and soft magnetic α-Fe phases. Basic magnetic properties such as: coercivity $\text{}_{J}H_{c}$, remanence $J_{r}$ and maximum energy product $(BH)_\text{max}$ were determined from the measured hysteresis loops. The microstructure of selected specimens was observed by transmission electron microscopy technique.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00