Tytuł:: Structure and Properties of Nd-Fe-B Alloy Subjected to HDDR Process
Autorzy:: Szymański, M.
Michalski, B.
Leonowicz, M.
Miazga, Z.
Powiązania:: https://bibliotekanauki.pl/articles/352047.pdf
Data publikacji:: 2016
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: HDDR
magnets hydrogenation
Nd-Fe-B alloy
neodymium magnets
magnets recycling
Opis:: In this paper the Hydrogenation, Disproportionation, Desorption and Recombination (HDDR) route was tested, for the Nd-Fe-B master alloy, as a prospective procedure for recycling of sintered scrap neodymium magnets. The HDDR method is based on the hydrogen induced reversal phase transformation of Nd-Fe-B alloy: Nd₂Fe₁₄B + (2±x) H₂ = 2NdH_2±x + Fe₂B + 12Fe. Microstructural observations (SEM), phase constitution studies (XRD) and measurement of magnetic properties (VSM) were done to investigate the HDDR transformation progress. It was observed that disproportionation reaction starts at the grain boundaries, where the Nd-rich phase is located. Average grain size was reduced and coercive material was produced as a result of the HDDR process. Obtained results are similar to literature data.
Źródło:: Archives of Metallurgy and Materials; 2016, 61, 1; 217-220
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: High-coercivity Nd-Fe-B Powders Obtained by High-Temperature Milling
Wysokokoercyjne proszki Nd-Fe-B otrzymywane przez mielenie w wysokiej temperaturze
Autorzy:: Kaszuwara, W.
Michalski, B.
Orlowski, P.
Powiązania:: https://bibliotekanauki.pl/articles/355400.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: hard magnetic materials
Nd-Fe-B
mechanical alloying
mechanical milling
twarde materiały magnetyczne
mechaniczna synteza
obróbka mechaniczna
Opis:: The possibility of employing high temperature milling (600°C) for the production of highly coercive Nd-Fe-B powders was examined. The materials were the Nd₁₂Fe₈₂B₆, alloy which was subjected to mechanical milling and the powders of the constituent elements of this alloy which were processed by mechanical alloying. The processes were conducted in the two variants: the first variant consisted of mechanical milling performed at a high temperature which was maintained during the entire process, and the other variant included preliminary milling carried out at room temperature and then the milling temperature was increased. All the processes gave nanocrystalline powders with hard magnetic properties. The powders produced by mechanical milling had better properties than those produced by mechanical] alloying as they were more homogeneous and contained smaller amounts of the α-Fe phase.
W pracy badano możliwości zastosowania procesu mielenia w wysokiej temperaturze (600°C) do otrzymywania wyso- kokoercyjnych proszków Nd-Fe-B. Mieleniu poddano stop Nd₁₂Fe₈₂B₆,. a także zastosowano metodę mechanicznej syntezy stopów tzn. mielono proszki pierwiastków składników stopu. Procesy prowadzono w dwóch wariantach: cały proces odbywał się w podwyższonej temperaturze lub stosowano wstępne mielenie w temperaturze pokojowej, a następnie mielenie w wysokiej temperaturze. We wszystkich procesach uzyskano nanokrystalicze proszki o właściwościach magnetycznie twardych Proszki uzyskane w procesie mielenia stopu miały właściwości lepsze od proszków otrzymanych w procesie mechanicznej syntezy stopów, ponieważ były bardziej jednorodne i posiadały mniejszy udział fazy α-Fe.
Źródło:: Archives of Metallurgy and Materials; 2014, 59, 1; 47-50
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Nd-Fe-B" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język