High-coercivity Nd-Fe-B Powders Obtained by High-Temperature Milling

The possibility of employing high temperature milling (600°C) for the production of highly coercive Nd-Fe-B powders was examined. The materials were the Nd₁₂Fe₈₂B₆, alloy which was subjected to mechanical milling and the powders of the constituent elements of this alloy which were processed by mechanical alloying. The processes were conducted in the two variants: the first variant consisted of mechanical milling performed at a high temperature which was maintained during the entire process, and the other variant included preliminary milling carried out at room temperature and then the milling temperature was increased. All the processes gave nanocrystalline powders with hard magnetic properties. The powders produced by mechanical milling had better properties than those produced by mechanical] alloying as they were more homogeneous and contained smaller amounts of the α-Fe phase.

W pracy badano możliwości zastosowania procesu mielenia w wysokiej temperaturze (600°C) do otrzymywania wyso- kokoercyjnych proszków Nd-Fe-B. Mieleniu poddano stop Nd₁₂Fe₈₂B₆,. a także zastosowano metodę mechanicznej syntezy stopów tzn. mielono proszki pierwiastków składników stopu. Procesy prowadzono w dwóch wariantach: cały proces odbywał się w podwyższonej temperaturze lub stosowano wstępne mielenie w temperaturze pokojowej, a następnie mielenie w wysokiej temperaturze. We wszystkich procesach uzyskano nanokrystalicze proszki o właściwościach magnetycznie twardych Proszki uzyskane w procesie mielenia stopu miały właściwości lepsze od proszków otrzymanych w procesie mechanicznej syntezy stopów, ponieważ były bardziej jednorodne i posiadały mniejszy udział fazy α-Fe.