Tytuł:
Characterization of as-spun and annealed Al-Mn-Fe ribbons
Charakterystyka szybko chłodzonych taśm stopu Al-Mn-Fe w stanie wyjściowym oraz po wygrzewaniu
Autorzy:
Stan, K.
Lityńska-Dobrzyńska, L.
Góral, A.
Wierzbicka-Miernik, A.
Powiązania:
https://bibliotekanauki.pl/articles/354244.pdf
Data publikacji:
2012
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
stopy Al-Mn-Fe
mikrostruktura stopu
taśmy stopów
Al-Mn-Fe
quasicrystals
melt-spinning
DSC
TEM
Opis:
Microstructure of conventionally cast and melt spun Al91Mn7Fe2 alloy was examined by X-ray diffraction, SEM and TEM techniques. Three different phases were found in a mould cast ingot: Al6(Mn, Fe), Al4(Mn, Fe) and aluminium solid solution. Rapidly quenched ribbons cast using melt spinning technique with different speed values of rotating wheel: 25, 30 and 36 m/s had average width in a range of 30-50 µ. It was found that ribbons contain quasicrystalline particles with different sizes and shapes including large dendrites in a range of micrometers and smaller spherical particles below 1 µ embedded in an aluminium matrix. Composition of these particles was similar to the Al4(Mn, Fe) phase. Also quasicrystals in the form of eutectic were observed with slightly different composition close to the Al6(Mn, Fe) phase. All observed particles revealed 2, 3 and 5- fold symmetry, typical for icosahedral quasicrystals. Increase in microhardness up to 274 HV for melt spun ribbon comparing to 141 HV for the as-cast ingot was observed due to a change in phase composition and refinement of the phases. Thermal stability of quasicrystalline phase in the ribbon was examined by annealing in different temperatures. Temperatures for thermal treatment were chosen based on DSC curve which contains the exothermic peak in the temperature range 300-500degrees Celsius. Analysis of ribbons annealed for 30 minutes at 400degrees Celsius showed that transformation of quasicrystals to stable crystalline phase starts at quasicrystal/Al-matrix interfaces. After annealing for 4 hours at 500degrees Celsius only the Al6(Mn, Fe) phase and aluminium solid solution were observed in the ribbon microstructure.
Mikrostrukturę stopu Al91Mn7Fe2 odlanego do kokili oraz przygotowanego metoda odlewania na wirujący walec (melt spinning) scharakteryzowano za pomocą dyfrakcji rentgenowskiej oraz transmisyjnej i skaningowej mikroskopii elektronowej. W strukturze wlewka zaobserwowano trzy fazy: Al6(Mn, Fe), Al4 (Mn, Fe) oraz roztwór stały aluminium. Szybko chłodzone taśmy odlano przy trzech różnych prędkościach obracającego się walca: 25, 30 i 36 m/s. Grubość wszystkich otrzymanych taśm wynosiła około 30-50 µm. Mikrostruktura taśm składała sie z cząstek kwazikrystalicznych o zróżnicowanych kształtach i rozmiarach (w tym dużych dendrytów rzędu kilku mikrometrów, oraz mniejszych kulistych cząstek poniżej 1µm). Skład chemiczny tych cząstek był zbliżony do składu fazy Al4(Mn, Fe). Zaobserwowano również kwazikryształy w postaci eutektyki o składzie zbliżonym do składu fazy Al6(Mn, Fe). Uzyskane dyfrakcje elektronowe z obserwowanych cząstek wykazywały symetrie 2, 3 i 5-krotna, typowa dla kwazikryształów ikozaedrycznych. Zmiany składu fazowego oraz rozdrobnienia faz spowodowały wzrost mikrotwardości z 140 HV dla stopu wyjściowego do wartości 270 HV dla taśm. Stabilność termiczna fazy kwazikrystalicznej badano poprzez wygrzewanie taśm w różnych temperaturach, które wybrano w oparciu o krzywa DSC zawierająca pik egzotermiczny w przedziale temperatur 300-500 stopni Celsjusza. Analiza mikrostruktury taśmy wygrzewanej przez 30 min w 400 stopniach Celsjusza wykazała, że przemiana fazy kwazikrystalicznej w stabilna fazę krystaliczna rozpoczyna sie na granicy kwazikryształ/osnowa. Po wygrzewaniu przez 4 godz. w 500 stopniach Celsjusza w strukturze taśmy występowała jedynie faza Al6(Mn, Fe) oraz roztwór stały aluminium.
Źródło:
Archives of Metallurgy and Materials; 2012, 57, 3; 651-656
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
The Effect of Transition Metals on Quasicrystalline Phase Formation in Mechanically Alloyed Al65Cu20Fe15 Powder
Autorzy:
Mitka, M.
Kalita, D.
Góral, A.
Lityńska-Dobrzyńska, L.
Powiązania:
https://bibliotekanauki.pl/articles/351525.pdf
Data publikacji:
2020
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
mechanical alloying
quasicrystal
Al-Cu-Fe
transition metals
Opis:
The effect of replacing iron with transition metals (M = Mn, Cr, Co) on the microstructure of mechanically alloyed Al65 Cu20 Fe15 quasicrystalline powder was examined by X-ray diffraction and transmission electron microscopy methods. Powders of various compositions were milled in a high-energy planetary ball mill up to 30 hours at a rotation speed 350 rpm using WC milling media. The amount of the fourth additions was constant in all powders and Fe atoms were replaced with Mn, Cr or Co in a 1:1 ratio, while the content of the Al and Cu was selected in two ways: they remained the same as in the initial ternary Al65 Cu20 Fe15 alloy or changed to obtain e/a ratio = 1.75 (optimal for icosahedral quasicrystalline phase). Quasicrystalline phase formed in the quaternary Al65 Cu20 Fe7.5 M7.5 powders, whereas in the second group of compositions only crystalline phases were identified.
Źródło:
Archives of Metallurgy and Materials; 2020, 65, 3; 1129-1133
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Effect of alloying elements on microstructure and properties of Al-Mn-Fe ribbon
Wpływ dodatków stopowych na mikrostrukturę i własności szybko chłodzących taśm stopu Al-Mn-Fe
Autorzy:
Stan, K.
Lityńska-Dobrzyńska, L.
Ochin, P.
Wierzbicka-Miernik, A.
Wojewoda-Budka, J.
Góral, A.
Powiązania:
https://bibliotekanauki.pl/articles/351706.pdf
Data publikacji:
2013
Wydawca:
Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:
quasicrystals
aluminium alloys
Al-Mn-Fe
rapid quenching
TEM
DSC
kwazikryształy
stopy aluminium
szybkie chłodzenie
Opis:
Influence of Ti, V, Cr, Zr, and Mo additions on microstructure and mechanical properties of the Al91Mn7Fe2 quasicrystalline alloy produced by the melt spinning technique has been studied. It was found that the microstructure of obtained all ribbons was similar and consists of spherical or dendritic icosahedral quasicrystalline particles embedded in an aluminium matrix coexisting with small fraction of intermetallic phase. Comporing DSC curves obtained for each sample it was observed that the alloy with Mo addition exhibits the best thermal stability among prepared alloys. Addition of molybdenum caused a significant shift of the main exothermic peak corresponding to temperature of quasicrystalline phase decomposition from 450ºC for ternary alloy to about 550ºC for quaternary composition. Microhardness measured for all prepared alloys were similar with the mean value of about 200 HV only alloy with Zr addition exhibited higher microhardness of about 270 HV caused by strengthening effect of Zr localized in the grains of aluminium matrix.
W niniejszej pracy badano wpływ dodatków stopowych: Ti, V, Cr, Zr i Mo na mikrostrukturę oraz własności mechaniczne kwazikrystalicznego stopu Al91Mn7Fe2 przygotowanego metoda odlewania na wirujący walec (melt spinning). Uzyskane wyniki pokazały, ze mikrostruktura wszystkich otrzymanych taśm była zbliżona i zawierała sferyczne lub dendrytyczne cząstki kwazikrystaliczne umieszczone w osnowie aluminiowej wraz z niewielka ilością fazy międzymetalicznej. Porównując krzywe DSC dla każdej z próbek zaobserwowano, ze stop z dodatkiem molibdenu wykazuje najlepsza stabilność termiczna posród odlanych stopów. Dodatek tego pierwiastka spowodował znaczące przesuniecie głównego piku egzotermicznego związanego z rozpadem fazy kwazikrystalicznej o około 100ºC, to jest od temperatury 450ºC dla stopu trójskładnikowego do temperatury 550ºC dla stopu czteroskładnikowego. Wartości mikrotwardości zmierzone dla każdego ze stopów były zbliżone a ich średnia wartość wynosiła 200 HV. Wyjątek stanowił stop z dodatkiem Zr dla którego średnia wartość mikrotwardości wynosiła 270 HV ze względu na efekt umacniający, związany z obecnością cyrkonu w ziarnach osnowy.
Źródło:
Archives of Metallurgy and Materials; 2013, 58, 2; 341-346
1733-3490
Pojawia się w:
Archives of Metallurgy and Materials
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-3 z 3

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies