Tytuł:: The Effect of Grain-refinement on Zn-10Al Alloy Damping Properties
Autorzy:: Piwowarski, G.
Krajewski, P. K.
Buraś, J.
Krajewski, W. K.
Powiązania:: https://bibliotekanauki.pl/articles/381530.pdf
Data publikacji:: 2014
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: zinc-aluminium cast alloys
inoculation
grain refinement
damping
attenuation coefficient
stopy cynk-aluminium
uszlachetnianie stopów
współczynnik tłumienia
Opis:: The paper is devoted to grain-refinement of the medium-aluminium zinc based alloys (MAl-Zn). The system examined was sand cast Zn-10 wt. %. Al binary alloy (Zn-10Al) doped with commercial Al-3 wt. % Ti – 0.15 wt. % C grain refiner (Al-3Ti-0.15C GR). Basing on the measured attenuation coefficient of ultrasonic wave it was stated that together with significantly increased structure fineness damping decreases only by about 10 – 20%. The following examinations should establish the influence of the mentioned grain-refinement on strength and ductility of MAl-Zn cast alloys.
Źródło:: Archives of Foundry Engineering; 2014, 14, 4; 91-94
1897-3310
2299-2944
Pojawia się w:: Archives of Foundry Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Skocz do pozycji: 2.

Tytuł:: Damping properties vs. structure fineness of the high-zinc aluminum alloys
Autorzy:: Krajewski, W. K.
Haberl-Faerber, K.
Buras, J.
Krajewski, P. K.
Powiązania:: https://bibliotekanauki.pl/articles/380214.pdf
Data publikacji:: 2012
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: wysokocynkowy stop aluminium
rozdrobnienie ziarna
właściwości tłumiące
współczynnik tłumienia
high zinc aluminum alloys
grain refinement
damping properties
damping coefficient
Opis:: The subject of this study is the presentation of relation between the degree of structure fineness and ultrasonic wave damping coefficient for the high-zinc aluminium alloys represented in this study by the sand mould cast alloy Al - 20 wt% Zn (AlZn20). The studied alloy was refined with a modifying (Al,Zn)-Ti3 ternary master alloy, introducing Ti in the amount of 400 pm into metal. Based on the analysis of the initial and modified alloy macrostructure images and ultrasonic testing, it was found that the addition of (Al,Zn)-Ti3 master alloy, along side a significant fragmentation of grains, does not reduce the coefficient of ultrasonic waves with a frequency of 1MHz.