Tytuł:: Influence of the notch radius on changes of the [delta]J parameter under fatigue crack growth rate
Wpływ promienia karbu na zmiany parametru [delta]J przy prędkości wzrostu pęknięć zmęczeniowych
Autorzy:: Rozumek, D.
Powiązania:: https://bibliotekanauki.pl/articles/279739.pdf
Data publikacji:: 2009
Wydawca:: Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
Tematy:: fatigue crack growth
number of cycles
delta J parameter
load ratio
Opis:: In the paper, the influence of the notch radius on changes of the [delta]J parameter under low and high-cycle fatigue is discussed. The tests were carried out on plates made of FeP04-UNI 8092 deep-drawing steel. The specimens were characterised by double symmetric lateral notches with the notch root radius ranging from 0.2mm to 10mm. The MTS 809 servo-hydraulic device was used for tests performed at the Department of Management and Engineering in Vicenza (Padova University). All fa- tigue tests were performed under force control, by imposing a constant value of the nominal load ratio, R = 0, and a load amplitude Pa = 6 and 7 kN (which corresponded to the nominal amplitude of normal stresses a = 100, 117MPa before the crack initiation). The test frequency ranged from 13 and 15Hz.
W pracy przedstawiono wpływ promienia karbu na zmiany parametru [delta]J podczas badań wykonywanych w zakresie niskiej i wysokiej liczby cykli zmęczeniowych. Badaniom poddano próbki płaskie wykonane ze stali FeP04-UNI 8092. Próbki charakteryzowały się dwustronnymi symetrycznymi zewnętrznymi karbami z promieniami dna karbu w zakresie od 0,2 do 10mm. Wyniki badań prezentowane w pracy wykonywano na maszynie hydraulicznej MTS 809 w Department of Management and Engineering w Vicenzy (Universytet w Padwie).Wszystkie badanie zmęczeniowe były wykonywane przy obciążeniu z kontrolowaną siłą przy stałej wartości współczynnika asymetrii cyklu R = 0 i amplitudzie obciążenia Pa = 6 i 7 kN (która korespondowała z nominalną amplitudą naprężenia normalnego a = 100, 117MPa przed inicjacją pęknięcia). Badania wykonywano w zakresie częstotliwości obciążenia 13 i 15Hz.
Źródło:: Journal of Theoretical and Applied Mechanics; 2009, 47, 4; 751-759
1429-2955
Pojawia się w:: Journal of Theoretical and Applied Mechanics
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Influence of the mean loading on fatigue crack growth rate and life under bending
Wpływ obciążenia średniego na prędkość wzrostu pękania zmęczeniowego i trwałość przy zginaniu
Autorzy:: Rozumek, D.
Powiązania:: https://bibliotekanauki.pl/articles/280651.pdf
Data publikacji:: 2004
Wydawca:: Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
Tematy:: fatigue crack growth
integral range
number of cycles
load ratio
Opis:: The paper contains the results of experimental tests of the fatigue crack growth rate of steels 10HNAP and 18G2A under bending for different load ratios. In the tests, plane specimens with external unilateral sharp notches as stress concentrators were used. The results of the experimental tests are described by a nonlinear formula based on the ...J-integral range. The proposed formula for description of the fatigue crack growth rate, including the ...J-integral range, satisfactorily describes the results obtained experimentally.
W pracy przedstawiono wyniki badań doświadczalnych wzrostu prędkości pęknięć zmęczeniowych przy zginaniu w stalach 10HNAP i 18G2A dla różnych wartości współczynnika asymetrii cyklu R. Do badań użyto próbek płaskich z koncentratorem naprężeń w postaci zewnętrznego jednostronnego karbu ostrego. Wyniki badań doświadczalnych opisano nieliniowym związkiem zawierającym zakres całki ...J. Zaproponowany związek do opisu prędkości rozwoju pęknięcia zmęczeniowego, zawierający zakres całki ...J, w sposób zadowalający opisuje wyniki uzyskane doświadczalnie.
Źródło:: Journal of Theoretical and Applied Mechanics; 2004, 42, 1; 83-93
1429-2955
Pojawia się w:: Journal of Theoretical and Applied Mechanics
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 3.

Tytuł:: Influence of the material sensitivity factor on the stress ratio for different specimens geometries and materials under bending
Autorzy:: Pawliczek, R.
Rozumek, D.
Powiązania:: https://bibliotekanauki.pl/articles/282049.pdf
Data publikacji:: 2004
Wydawca:: Polskie Towarzystwo Mechaniki Teoretycznej i Stosowanej
Tematy:: stress ratio
number of cycles
bending
Opis:: In the paper, the influence of mean loads on the low cycle fatigue for notched specimens of different shapes of the cross section is analysed. The specimens are characterized by a similar value of the stress concentration factor (Kt = 2.46 for round specimens and Kt = 3.27 for specimens of the rectangular cross-section). A mathematical model describing the limiting stress plane under fatigue bending is applied, taking into account the influence of mean stresses. The model has been verified by 18G2A steel and PA6 aluminium alloy specimens via experimental test results under cyclic bending for stress ratios R = -1, -0.5, 0. The relationship between the stress amplitude and the stress mean value taking into account the number of cycles N before failure is described by a linear model, for which good agreement of the calculations with the experimental test results is achieved.
W pracy przeanalizowano wpływ obciążeń średnich przy niskocyklowym zmęczeniu dla próbek z karbem o różnych kształtach przekroju poprzecznego. Próbki cechowały się zbliżoną wartością współczynnika kształtu (Kt = 2.46 dla próbek okrągłych i Kt = 3.27 dla próbek o przekroju prostokątnym). Zastosowano model matematyczny opisujący płaszczyznę naprężeń granicznych przy cyklicznie zmiennym zginaniu z uwzględnieniem wpływu naprężeń średnich. Model zweryfikowano wynikami badań eksperymentalnych próbek ze stali 18G2A i stopu aluminium PA6 w warunkach cyklicznego zginania dla przebiegów o współczynniku asymetrii cyklu R = -1; -0.5; 0. Zależność amplitudy naprężeń od wartości średniej naprężeń z uwzględnieniem liczby cykli N do zniszczenia opisano liniowym modelem, dla którego uzyskano dobrą zgodność obliczeń z wynikami badań eksperymentalnych.
Źródło:: Journal of Theoretical and Applied Mechanics; 2004, 42, 2; 285-294
1429-2955
Pojawia się w:: Journal of Theoretical and Applied Mechanics
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 4.

Tytuł:: Badanie wzrostu pęknięć zmęczeniowych w spawanych próbkach poddanych zginaniu
Test of fatigue crack growth in welded specimens subjected to bending
Autorzy:: Lewandowski, J.
Rozumek, D.
Hepner, M.
Powiązania:: https://bibliotekanauki.pl/articles/211286.pdf
Data publikacji:: 2018
Wydawca:: Wojskowa Akademia Techniczna im. Jarosława Dąbrowskiego
Tematy:: złącza spawane
długości pęknięć zmęczeniowych
liczba cykli
zginanie
mikrostruktura
welded joints
fatigue cracks length
number of cycles
bending
microstructure
Opis:: W pracy przedstawiono wyniki badań wzrostu pęknięć zmęczeniowych próbek poddanych cyklicznemu zginaniu przy stałej amplitudzie momentu, wykonanych ze stali S355 z pachwinowymi spoinami. Badane próbki posiadały koncentratory naprężenia w postaci zewnętrznych, dwustronnych łagodnych karbów. Badania przeprowadzono przy stałej wartości współczynnika asymetrii cyklu R = -1 bez obróbki cieplnej i po takiej obróbce. W artykule zaprezentowano również wyniki badań mikrostruktury złączy spawanych z uwzględnieniem zmian zachodzących w materiale po obróbce cieplnej oraz wpływ tych zmian na trwałości zmęczeniowe próbek.
The paper presents the test results on the fatigue crack growth under cyclic bending specimens at constant moment amplitude made of S355 steel with fillet welds. Plane specimens with stress concentrators in form of the external two-sided blunt notches were tested. The tests were performed under constant value of the stress ratio R = -1 without and after heat treatment. The article also presents the test results of the microstructure of welded joints taking into account changes in the material after heat treatment and the impact of these changes on the fatigue life of specimens.
Źródło:: Biuletyn Wojskowej Akademii Technicznej; 2018, 67, 1; 185-195
1234-5865
Pojawia się w:: Biuletyn Wojskowej Akademii Technicznej
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "Rozumek, D." wg kryterium: Autor

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język