Influence of the notch radius on changes of the [delta]J parameter under fatigue crack growth rate

In the paper, the influence of the notch radius on changes of the [delta]J parameter under low and high-cycle fatigue is discussed. The tests were carried out on plates made of FeP04-UNI 8092 deep-drawing steel. The specimens were characterised by double symmetric lateral notches with the notch root radius ranging from 0.2mm to 10mm. The MTS 809 servo-hydraulic device was used for tests performed at the Department of Management and Engineering in Vicenza (Padova University). All fa- tigue tests were performed under force control, by imposing a constant value of the nominal load ratio, R = 0, and a load amplitude Pa = 6 and 7 kN (which corresponded to the nominal amplitude of normal stresses a = 100, 117MPa before the crack initiation). The test frequency ranged from 13 and 15Hz.

W pracy przedstawiono wpływ promienia karbu na zmiany parametru [delta]J podczas badań wykonywanych w zakresie niskiej i wysokiej liczby cykli zmęczeniowych. Badaniom poddano próbki płaskie wykonane ze stali FeP04-UNI 8092. Próbki charakteryzowały się dwustronnymi symetrycznymi zewnętrznymi karbami z promieniami dna karbu w zakresie od 0,2 do 10mm. Wyniki badań prezentowane w pracy wykonywano na maszynie hydraulicznej MTS 809 w Department of Management and Engineering w Vicenzy (Universytet w Padwie).Wszystkie badanie zmęczeniowe były wykonywane przy obciążeniu z kontrolowaną siłą przy stałej wartości współczynnika asymetrii cyklu R = 0 i amplitudzie obciążenia Pa = 6 i 7 kN (która korespondowała z nominalną amplitudą naprężenia normalnego a = 100, 117MPa przed inicjacją pęknięcia). Badania wykonywano w zakresie częstotliwości obciążenia 13 i 15Hz.