    Microstructure of Al2O3-13TiO2 coatings deposited from nanoparticles by plasma spraying
    Mikrostruktura powłok Al2O3-13TiO2 natryskanych plazmowo z nanocząstek
    Autorzy:
    Góral, A.
    Lityńska-Dobrzyńska, L.
    Żórawski, W.
    Berent, K.
    Wojewoda-Budka, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/355112.pdf
    Data publikacji:
    2013
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Al2O3-13TiO2 coating
    microstructura
    plasma spraying process
    powłoka Al2O3-13TiO2
    mikrostruktura
    proces natryskiwania plazmowego
    Opis:
    The aim of the study was to characterize nanostructured Al2O3-13TiO2 coatings deposited by plasma spraying on a grit blasted steel substrate. The Al2O3-13TiO2 coatings were characterized using scanning and transmission electron microscopy and X-ray diffraction techniques. Obtained coatings possessed a unique microstructure consisting of fully melted regions with the microstructure similar to a typical plasma sprayed lamellar morphology as the conventional coatings and areas comprising unmelted or partially melted nanosized particles. The analysis showed that most of the α-Al2O3 phase from the nanostructured powders transformed into γ-Al2O3 phase after plasma spraying process. Moreover, the presence of amorphous phase was also observed.
    W pracy przedstawiono charakterystykę nanostrukturalnych powłok Al2O3-13TiO2 natryskiwanych plazmowo na podłożu stalowym. Powłoki scharakteryzowano za pomocą skaningowej i transmisyjnej mikroskopii elektronowej oraz technik dyfrakcji rentgenowskiej. Mikrostruktura uzyskanych powłok składała się z obszarów powstałych z całkowicie stopionych proszków, podobnych do mikrostruktury powłok wytworzonych z proszków o rozmiarach konwencjonalnych, jak również z obszarów zawierających niestopione lub częściowo stopione nanocząstki. Wykazano, ze większość fazy α-Al2O3 występującej w materiale proszkowym uległa przemianie w faze γ-Al2O3 w trakcie procesu natryskiwania plazmowego. Zidentyfikowano również obecność fazy amorficznej.
    Źródło:
    Archives of Metallurgy and Materials; 2013, 58, 2; 335-339
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of Powder Grain Size and Titania Content on Mechanical and Tribological Properties of Plasma Sprayed AL2O3-TiO2 Ceramic Coatings
    Autorzy:
    Góral, A.
    Żórawski, W.
    Powiązania:
    https://bibliotekanauki.pl/articles/355219.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Al2O3-TiO2 coating
    nanostructures
    mechanical properties
    wear resistance
    Opis:
    In this work, three ceramic composite coatings Al2O3-3TiO2 C, Al2O3-13TiO2 C, and Al2O3-13TiO2 N were plasma sprayed on steel substrates. They were deposited with two conventional powders differing the volume fraction of TiO2 and nanostructured powder. The mechanical and tribological properties of the coatings were investigated and compared. The increase in TiO2 content from 3 wt.% to 13 wt.% in the conventional feedstock improved the mechanical properties and abrasion resistance of coatings. However, the size of the used powder grains had a much stronger influence on the properties of deposited coatings than the content of the titania phase. The Al2O3-13TiO2 coating obtained from nanostructured powder revealed significantly better properties than that plasma sprayed using conventional powder, i.e. 22% higher microhardness, 19% lower friction coefficient, and over twice as good abrasive wear resistance. In turn, the Al2O3-13TiO2 conventional coating showed an increase in microhardness and abrasive wear resistance, 36% and 43%, respectively, and 6% higher coefficient of friction compared to the Al2O3-3TiO2 conventional coating.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 1; 45-53
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Synthesis of magnesium aluminate spinel doped TiO2 from magnesite waste
    Autorzy:
    Canikoğlu, Nuray
    Powiązania:
    https://bibliotekanauki.pl/articles/2048865.pdf
    Data publikacji:
    2022
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    magnesium aluminate spinel
    MgAl2O4
    titanium dioxide
    TiO2
    magnesite waste
    alumina
    Al2O3
    Opis:
    Magnesium aluminate spinel (MgAl2O4) is an important refractory material of magnesia origin. It is formed by the reaction of magnesium and aluminum oxides. In this study, TiO2 was added to magnesite waste and alumina (Al2O3) powders in different proportions and the mixtures were sintered at different temperatures after shaping. The aim of this study was to produce spinel economically by recycling waste materials. Therefore, titanium dioxide (TiO2) added magnesium aluminate spinel was produced and the products obtained were characterized by XRD and SEM-EDS analyses. In addition, bulk density, apparent porosity and microhardness values were measured and the effects of TiO2 additive on magnesium aluminate properties were examined. The better values were determined in samples doped 4 wt.% TiO2 at the sintering temperature of 1400°C.
    Źródło:
    Archives of Metallurgy and Materials; 2022, 67, 1; 311-316
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-3 z 3

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies