Magnesium aluminate spinel (MgAl2O4) is an important refractory material of magnesia origin. It is formed by the reaction of magnesium and aluminum oxides. In this study, TiO2 was added to magnesite waste and alumina (Al2O3) powders in different proportions and the mixtures were sintered at different temperatures after shaping. The aim of this study was to produce spinel economically by recycling waste materials. Therefore, titanium dioxide (TiO2) added magnesium aluminate spinel was produced and the products obtained were characterized by XRD and SEM-EDS analyses. In addition, bulk density, apparent porosity and microhardness values were measured and the effects of TiO2 additive on magnesium aluminate properties were examined. The better values were determined in samples doped 4 wt.% TiO2 at the sintering temperature of 1400°C.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00