Tytuł:
Microstructure Mechanisms Governing the Creep Life of Ultrafine-Grained Cu-0.2 wt%Zr Alloy
Autorzy:
Kral, P.
Svoboda, M.
Dvorak, J.
Kvapilova, M.
Sklenicka, V.
Powiązania:
https://bibliotekanauki.pl/articles/1418438.pdf
Data publikacji:
2012-09
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
81.05.-t
61.66.Dk
62.20.Hg
68.37.Lp
Opis:
Equal-channel angular pressing was conducted at room temperature and extrusion was performed up to 12 passes using route where the billets were rotated by 90° in the same sense between consecutive passes. Tensile creep tests were performed at 473, 573 and 673 K at different constant applied stresses. It was observed that the original coarse grain size of unprocessed alloy was reduced to 0.3 μm after 8 equal-channel angular pressing passes and the grain growth during creep was restricted by precipitates with the mean diameter ≈ 4.0 nm. No significant effect on creep resistance was found after one equal-channel angular pressing pass at 473 and 573 K. However, the longest time to fracture was exhibited by alloy after 2 equal-channel angular pressing passes at 573 and 673 K but with further increasing number of equal-channel angular pressing passes a decrease in the time to fracture was observed. Nevertheless, the beneficial effect of equal-channel angular pressing on creep resistance was still documented after 8 passes for temperatures of 473 and 573 K. By contrast, creep tests performed at 673 K showed that the time to fracture of ultrafine-grained material is shorter as compared with that for as-received state. The 3D laser measurement of surface showed that the creep fracture process is accelerated by formation of vertical surface step relief and cavitation at the intersection of the shear bands during creep.
Źródło:
Acta Physica Polonica A; 2012, 122, 3; 457-460
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Creep Behavior of a Zirconium Alloy Processed by Equal-Channel Angular Pressing
Autorzy:
Sklenicka, V.
Dvorak, J.
Kral, P.
Svoboda, M.
Kvapilova, M.
Kopylov, V.
Nikulin, S.
Dobatkin, S.
Powiązania:
https://bibliotekanauki.pl/articles/1418491.pdf
Data publikacji:
2012-09
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
81.40.Lm
62.20.Hg
81.05.-t
81.07.Bc
81.70.Bt
Opis:
A Zr-2.5 wt%Nb alloy was processed by equal-channel angular pressing and then tested under creep conditions at 623 K using a tensile stress within the range from 120 to 300 MPa. The results show conventional power-law creep with a stress exponent of n > 3 which is consistent with an intragranular dislocation process involving the glide and climb of dislocations. It is demonstrated that diffusion creep is not important in these tests. For comparison purposes, the experiments were conducted using both the unprocessed alloy and after processing by equal-channel angular pressing. It was found that under same testing conditions the measured minimum creep rates in the pressed alloy with ultrafine grain sizes were faster than in the same alloy in a coarse-grained unprocessed condition.
Źródło:
Acta Physica Polonica A; 2012, 122, 3; 485-489
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
Tytuł:
Effect of Si Substitution and Annealing on Magnetocaloric Properties in $TbCo_2$
Autorzy:
Janatova, M.
Poltierova Vejpravova, J.
Javorsky, P.
Prokleska, J.
Svoboda, P.
Danis, S.
Powiązania:
https://bibliotekanauki.pl/articles/1813663.pdf
Data publikacji:
2008-01
Wydawca:
Polska Akademia Nauk. Instytut Fizyki PAN
Tematy:
65.40.Gd
75.30.Sg
Opis:
We report on magnetocaloric properties of the as-cast and annealed $TbCo_2$ with partial substitution of cobalt by silicon. The samples were characterized by powder X-ray diffraction and investigated by heat capacity measurements (8-300 K, in fields 0 T and 1 T). $TbCo_2$ undergoes a second-order type phase transition at $T_C$ = 240 K, from paramagnetic to ferrimagnetic state;similar behavior was revealed in the Si-doped compounds. The temperature dependence of magnetic entropy and the corresponding magnetocaloric effect were derived for all studied samples. The influence of the heat treatment and Si doping on magnetocaloric properties will be discussed in context of the analogue case $Er(Co_{1-x}Si_x)_2$.
Źródło:
Acta Physica Polonica A; 2008, 113, 1; 311-314
0587-4246
1898-794X
Pojawia się w:
Acta Physica Polonica A
Dostawca treści:
Biblioteka Nauki
Artykuł
    Wyświetlanie 1-3 z 3

    Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies