Wyszukujesz frazę "equal-channel angular" wg kryterium: Wszystkie pola

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-18 z 18
    Tytuł:
    Thermal Stability of AA1050 Aluminum Alloy after Equal Channel Angular Pressing
    Autorzy:
    Koprowski, P.
    Bogucki, R.
    Bieda, M.
    Kawałko, J.
    Sztwiertnia, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/356187.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    ECAP
    hardness
    EBSD
    texture
    recrystallization
    Opis:
    The annealing behavior of AA1050 aluminum alloy deformed by equal-channel angular pressing (ECAP) was studied experimentally. The material was subjected to extrusion through die with channels intersecting at an 90° angle. Samples were pressed for up to 8 passes using route BC, then cut into slices and subsequently annealed for 1 hour at temperatures from 100°C to 350°C. Hardness measurements were performed on each slice. Microstructure of material was analyzed in the longitudinal section by means of Electron Backscatter Diffraction system in a scanning electron microscope (EBSD/SEM). From the obtained sets of Kikuchi diffraction patterns orientation maps and Image Quality maps were determined. Grain size, disorientation distributions and crystallographic texture were also estimated. ECAP caused significant improvement of hardness, with stabilization after 4 passes. Refinement of microstructure was obtained with the increasing amount of passes. Material properties were stable during annealing at temperatures lower than 150°C. Annealing at higher temperatures caused a decrease in hardness corresponding to an increase of the grain size.
    Źródło:
    Archives of Metallurgy and Materials; 2017, 62, 2A; 777-786
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Creep Behavior of a Zirconium Alloy Processed by Equal-Channel Angular Pressing
    Autorzy:
    Sklenicka, V.
    Dvorak, J.
    Kral, P.
    Svoboda, M.
    Kvapilova, M.
    Kopylov, V.
    Nikulin, S.
    Dobatkin, S.
    Powiązania:
    https://bibliotekanauki.pl/articles/1418491.pdf
    Data publikacji:
    2012-09
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    81.40.Lm
    62.20.Hg
    81.05.-t
    81.07.Bc
    81.70.Bt
    Opis:
    A Zr-2.5 wt%Nb alloy was processed by equal-channel angular pressing and then tested under creep conditions at 623 K using a tensile stress within the range from 120 to 300 MPa. The results show conventional power-law creep with a stress exponent of n > 3 which is consistent with an intragranular dislocation process involving the glide and climb of dislocations. It is demonstrated that diffusion creep is not important in these tests. For comparison purposes, the experiments were conducted using both the unprocessed alloy and after processing by equal-channel angular pressing. It was found that under same testing conditions the measured minimum creep rates in the pressed alloy with ultrafine grain sizes were faster than in the same alloy in a coarse-grained unprocessed condition.
    Źródło:
    Acta Physica Polonica A; 2012, 122, 3; 485-489
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of Temperature on Grain Refinement of Mg-3Al-1Zn Alloy Processed by Equal Channel Angular Pressing
    Autorzy:
    Molnár, P.
    Jäger, A.
    Lejček, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/1418440.pdf
    Data publikacji:
    2012-09
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    62.20.F-
    81.70.Bt
    81.20.Hy
    87.64.Ee
    Opis:
    In this work the effect of temperature on grain refinement of Mg-3Al-1Zn alloy (AZ31B) processed by equal channel angular pressing using route A is described. The deformation sequences consisted of equal channel angular pressing passes at 200C followed by passes at 150°C. Nonhomogeneous grain size distribution promotes shear band formation at 150°C. Shear bands with microcracks inside were analyzed by electron backscatter diffraction technique.
    Źródło:
    Acta Physica Polonica A; 2012, 122, 3; 461-464
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The equal channel angular extrusion process of multiphase high strength aluminium bronze
    Proces równokanałowego wyciskania kątowego wysokowytrzymałych wielofazowych brązów aluminiowych
    Autorzy:
    Gronostajski, Z.
    Hawryluk, M.
    Kuziak, R.
    Radwański, K.
    Skubiszewski, T.
    Zwierzchowski, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/355856.pdf
    Data publikacji:
    2012
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    aluminium bronzes
    ECAP
    strain
    microstructure
    grain size
    Opis:
    The aim of the research was to determine the deformation condition of ECAP process of multiphase high strength aluminium bronze BA1032. The studies have indicated that it is possible to deform multiphase aluminium bronze BA1032 in the ECAP process at a temperature of 400°C and die angle Φ=110°. The deformation of the bronzes at lower temperatures encounters some difficulties - cracks appear which make repeated ECAP impossible. The cracks appear on the top surface of the samples where it contacts the surface of the outlet channel. FEM simulations show that the largest plastic strains occur in this area. The proposed ECAP method of large plastic deformations as applied to the investigated aluminium bronzes makes it possible to obtain very strong refinement especially of eutectoid α+ γ2.
    Celem pracy było określenie warunków odkształcania w procesie ECAP wysokowytrzymałych wielofazowych brązów aluminiowych. Przeprowadzone badania wskazują na możliwość odkształcania wielofazowych brazów aluminiowych w tym procesie w temperaturze 400 °C dla kąta matrycy Φ=110°. Pewne trudności sprawia odkształcanie brązu w niższych temperaturach, gdyż pojawiają się wówczas pęknięcia, które uniemożliwiają prowadzenie procesu wielokrotnego przeciskania próbek przez kanał katowy. Pęknięcia pojawiaja sie na górnej powierzchni próbek w miejscu kontaktu z powierzchnią kanału wyjsciowego. Jak wykazuje symulacje MES w miejscu tym występują największe odkształcenia plastyczne. Zastosowana metoda dużych odkształceń plastycznych ECAP w przypadku badanych brazów aluminiowych pozwala uzyskać bardzo silne rozdrobnienie głównie eutektoidu α+ γ 2.
    Źródło:
    Archives of Metallurgy and Materials; 2012, 57, 4; 897-909
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Characterization Of An Equal Channel Angular Pressed Al-Zn-In Alloy
    Charakterytyka stopu Al-Zn-In otrzymanego metodą przeciskania w kanale kątowym
    Autorzy:
    Banjongprasert, C.
    Jak-Ra, A.
    Domrong, C.
    Patakham, U.
    Pongsaksawad, W.
    Chairuangsri, T.
    Powiązania:
    https://bibliotekanauki.pl/articles/352220.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    aluminum alloys
    equal channel angular pressing
    severe plastic deformation
    electron backscatter diffraction
    stopy aluminium
    przeciskanie przez kanał kątowy
    odkształcenie plastyczne duże
    dyfrakcja elektronów wstecznie rozproszonych
    Opis:
    Equal channel angular pressing (ECAP) is a technique that creates a high accumulated strain in metals and results in ultrafine-grained structure. In this study, Al-5Zn-0.02In was processed by ECAP at a room temperature using route Bc through an ECAP die (press angle of Φ = 100° and Ψ = 20°). The samples were subjected to ECAP with 1, 2, 3 and 4 passes. The processed specimens were characterized using electron backscatter diffraction (EBSD). The results confirmed the grain refinement of the alloy after ECAP to an average grain size less than 5 μm after 4-pass ECAP. The microhardness test shows that the hardness increased with the number of passes. The hardness of the cross-sectional area of the sample was similar to that tested along the pressing direction.
    Metoda przeciskania w kanale kątowym (ang. Equal channel angular pressing; ECAP) prowadzi do powstania bardzo wysokich naprężeń, w wyniku czego otrzymuje się ziarna o bardzo drobnej strukturze. W niniejszej pracy, stop Al-5Zn-0,02In wytwarzano metodą ECAP w temperaturze pokojowej, wykorzystując ścieżkę Bc przez matrycę ECAP (kąty krzywizny: Φ = 100° i Ψ = 20°). Próbki poddano ECAP z 1, 2, 3 i 4 przejściami. Otrzymane próbki badano metodą dyfrakcji elektronów wstecznie rozproszonych (ang. electron back scatter diffraction; EBSD). W stopie otrzymanym metodą ECAP z 4 przejściami, średnia wielkość ziaren wynosiła mniej niż 5 μm. Badania mikrotwardości wykazały, że twardość zwiększała się wraz z liczbą przejść. Twardość zmierzona w poprzek próbki byłą porównywalna do tej mierzonej wzdłuż osi nacisku.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 2A; 887-890
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    FEM simulation of combined extrusion method (ECAE/Direct Extrusion)
    Autorzy:
    Ayer, Ö
    Powiązania:
    https://bibliotekanauki.pl/articles/118033.pdf
    Data publikacji:
    2015
    Wydawca:
    Polskie Towarzystwo Promocji Wiedzy
    Tematy:
    FEM
    Equal Channel Angular Extrusion
    Direct Extrusion
    DEFORM 3D
    Opis:
    Equal Channel Angular Extrusion (ECAE) is known as a severe plastic deformation process and material is deformed without any geometrical change. It is widely used for obtaining high mechanical properties from the product. Direct Extrusion is another plastic deformation process in which a workpiece is reduced in cross-section by forcing it through the die opening of a small cross-sectional area than that of the original billet. In this study, these two processes are combined together via using DEFORM 3D which is a very specialized software for metal forming operations. Lead is used as workpiece material to simulate hot forming conditions and also process parameters (die angle and die land length) were investigated. The forming load and strain components were calculated from the FEM results obtained from DEFORM 3D software.
    Źródło:
    Applied Computer Science; 2015, 11, 2; 50-59
    1895-3735
    Pojawia się w:
    Applied Computer Science
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Mechanical Spectroscopy of Equal-Channel Angular Pressed Fe-Cr Alloys and Tungsten
    Spektroskopia mechaniczna stopów Fe-Cr i wolframu wyciskanych przez kanał kątowy
    Autorzy:
    Hao, T.
    Tang, H.
    Jiang, W.
    Wang, X.
    Fang, Q.
    Powiązania:
    https://bibliotekanauki.pl/articles/352822.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    mechanical spectroscopy
    internal friction technique
    Fe-18wt.%Cr alloy and pure W
    equal-channel angular
    spektroskopia mechaniczna
    technika tarcia wewnętrznego
    stop Fe-18wt%Cr i czystego W
    kanał kątowy
    Opis:
    nternal friction technique was used to investigate the microstructural stability of equal-channel angular pressed (ECAP) 9Cr1Mo steel (T91), Fe-18wt.%Cr alloy, and pure W. Several non-relaxation internal friction peaks are observed in three ECAP-strained specimens, which are related to the microstructural transition from a severely deformed state to a static recovery state of dislocations, and to recrystallized state. Along with the disappearance of the P1 peak, another relaxation internal friction peak P2 is observed during the second heating run only in Fe-18wt.%Cr alloy, and it does not disappear even during subsequent third heating run. This peak is not observed in T91 steel and W. The P2 peak is likely associated with a process of grain boundary (GB) sliding. Unlike T91, no abundant carbide precipitates distribute on GBs to pin GB and repulse GB sliding, thus, the P2 peak only occurs in Fe-18wt.%Cr alloy. It is concluded that high-temperature internal friction measurements are required to detect the grain boundary peak in pure W.
    Technika tarcia wewnętrznego została użyta do zbadania stabilności mikrostruktury poddanych wyciskaniu przez kanał kątowy stali 9Cr1Mo (T91), stopu Fe-18wt%Cr, i czystego W. Zaobserwowano wiele nie-relaksacyjnych pików tarcia wewnętrznego w trzech próbkach odkształconych przez ECAP, które są związane z przejściem ze stanu silnie odkształconego do statycznego stanu zdrowienia dyslokacji, i do stanu zrekrystalizowanego. Wraz z zanikiem piku P1, tylko w przypadku stopu Fe-18wt%Cr obserwowany jest inny pik P2 relaksacji tarcia wewnętrznego podczas drugiego ogrzewania, i nie znika nawet w kolejnym trzecim etapie ogrzewania. Pik ten nie jest obserwowany w stali T91 i W. Pik P2 prawdopodobnie związany jest procesem poślizgu granicy ziaren. W przeciwieństwie do stali T91, brak bogatych w węglik wydzieleń na granicach ziaren, które by unieruchomiły granice i uniemożliwiły poślizg, stąd pik P2 występuje tylko w przypadku stopu Fe-18wt.%Cr. Stwierdzono, że pomiary tarcia wewnętrznego w wysokiej temperaturze są potrzebne, aby wykryć pik granicy ziarna w czystym W.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 3A; 2101-2106
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Activation Energy for Grain Growth of the Isochronally Annealed Ultrafine Grained Magnesium Alloy after Hot Extrusion and Equal-Channel Angular Pressing (EX-ECAP)
    Autorzy:
    Stráská, J.
    Stráský, J.
    Janeček, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/1402085.pdf
    Data publikacji:
    2015-10
    Wydawca:
    Polska Akademia Nauk. Instytut Fizyki PAN
    Tematy:
    62.20.fq
    81.05.Bx
    81.20.Hy
    81.40.Lm
    81.70.Bt
    Opis:
    Magnesium alloy AZ31 prepared by hot extrusion and 4 passes of equal-channel angular pressing (EX-ECAP) has ultra-fine grained microstructure with an average grain size of 900 nm. Grain growth is analysed using a general equation for the grain growth and an Arrhenius equation. The calculated value of the activation energy for grain growth differs with the annealing temperature. The fitted value of activation energy for grain growth in the intermediate temperature range (210-400°C) is in accordance with the results of other authors, but it is shown in this study that such value is abnormally low and physically meaningless. More real values of apparent activation energy in this temperature range were calculated from the model assuming a linear increase of activation energy with increasing annealing temperature. Result of this linear model of evolution of activation energy in the temperature range between 210-400°C is expressed by the interval estimation of apparent activation energy values. It is concluded that the evolution of apparent activation energy can be explained by a change in the mechanism underlying the grain boundary migration. In the low temperature range, the grain boundary diffusion is dominant since the material is ultra-fine grained, whereas at higher temperatures, the lattice self-diffusion is more important.
    Źródło:
    Acta Physica Polonica A; 2015, 128, 4; 578-581
    0587-4246
    1898-794X
    Pojawia się w:
    Acta Physica Polonica A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Temperature and Die Angular Effect on Tensile Strength, Hardness, Extrusion Load and Flow Stress in Aluminum 6063 Processed by Equal Channel Angular Extrusion Method
    Autorzy:
    Azeez, Temitayo M.
    Mudashiru, Lateef O.
    Asafa, Tesleem B.
    Akande, Saheed
    Ikumapayi, Omolayo M.
    Kayode, Joseph F.
    Uchegbu, Ikenna D.
    Afolalu, Sunday A.
    Powiązania:
    https://bibliotekanauki.pl/articles/2201882.pdf
    Data publikacji:
    2023
    Wydawca:
    Stowarzyszenie Inżynierów i Techników Mechaników Polskich
    Tematy:
    die angle
    simulation
    aluminum
    temperature
    tensile strength
    Opis:
    Developing aluminum with good mechanical properties like hardness, tensile strength, and normal flow stress, Equal Channel Angular Extrusion (ECAE) method has been suggested as a suitable metal forming process. The load applied and extrusion temperature normally infl uences the flow stress behavior in extruded products and de- termine their mechanical properties. Consequently, how these factors affect mechanical behavior and flow stress of Al 6063 processed by ECAE was examined in this study. Extrusion temperatures were 350°C, 425°C, and 500°C with die angles of 130°, 140°, and 150°. 5 mm/s of ram speed was applied. Each extrudate’s tensile strength and hardness were measured using a Universal Testing Machine and a Rockwell hardness tester. Samples with equal dimensions and properties were also modeled using the Qform software at the extended die angle and temperature for proper analysis of flow stress in the extrudates. According to experimental results, the temperature had a greater effect on the tensile strength and hardness of the billet than the die angle. The extrudates’ grains also became finer as the billet temperature rose. Simulation findings showed that higher billet temperature led to a decrease in the extrudates’ flow stress. The simulation also demonstrated that billet temperature had a greater impact on extrusion load than die angle, with a maximum extrusion load of 5.5 MN being attained at 350 °C.
    Źródło:
    Advances in Science and Technology. Research Journal; 2023, 17, 1; 346--353
    2299-8624
    Pojawia się w:
    Advances in Science and Technology. Research Journal
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Investigation of the Ultrafine-Grained Structure Formation Under Different Strain Rates
    Autorzy:
    Kováčová, A.
    Kvačkaj, T.
    Bidulský, R.
    Bidulská, J.
    Kočiško, R.
    Dutkiewicz, J.
    Lityńska-Dobrzyńska, L.
    Powiązania:
    https://bibliotekanauki.pl/articles/353994.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    electron microscopy
    EBSD
    nanostructured materials
    equal channel angular processing
    grain refinement
    Opis:
    The present paper deals with a study on formation of specific substructural features in OFHC copper processed by equalchannel angular pressing (ECAP) considering different strain rate conditions. Since two mechanical tensile testing equipments were being used, strain rate response could be studied in a wide range (both in static and dynamic regimes). Moreover, the copper before tensile testing was subjected to drawing and ECAP, separately, which allows to study the influence of both structural and substructural features (CG vs. UFG structure). Considering the static regime, it was found that UFG materials have advanced properties, showing higher strength and ductility in comparison to their CG counterparts. However, this is valid only to the critical value of the strain rate. In the dynamic regime, mathematical linearized results imply that ultimate tensile strength in samples processed by ECAP increases twice every 10 s-1 rising, however, they lost approximately the same plastic properties than samples after drawing. Differences in the progress of mechanical properties are related to specific structural and substructural features evolved in the material during ECAP processing. Above mentioned features were studied in detail by methods of transmission and scanning electron microscopy (TEM, SEM).
    Źródło:
    Archives of Metallurgy and Materials; 2017, 62, 2A; 851-856
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Research of fatigue and mechanical properties AlMg1SiCu aluminium alloys
    Autorzy:
    Mihaliková, M
    Lišková, A
    Vojtko, M.
    Kvačkaj, T.
    Powiązania:
    https://bibliotekanauki.pl/articles/957961.pdf
    Data publikacji:
    2015
    Wydawca:
    Stowarzyszenie Inżynierów i Techników Mechaników Polskich
    Tematy:
    aluminum alloys
    mechanical properties
    fractography
    hardness
    equal channel angular pressing (ECAP)
    fatigue testing
    Opis:
    The paper is concerned with an analysis of utility and fatigue properties of industrially produced aluminium alloy, specifically EN AW 6061 (AlMg1SiCu), reinforced with the particles of SiC. The following properties were subject to evaluation: microstructure and sub-structure, mechanical characteristics. All of these mechanical properties in pre- and post- equal channel angular pressed (ECAP) state have been studied. The hardness was evaluated by Vickers hardness test at the load of HV10. The significant part the thesis was devoted to the fatigue properties at cyclic load in torsion. The presented results demonstrate well that the combination of fractography and microscopy can give a significant contribution to the knowledge of initiation and propagation crack in the aluminium alloy.
    Źródło:
    Advances in Science and Technology. Research Journal; 2015, 9, 28; 56-60
    2299-8624
    Pojawia się w:
    Advances in Science and Technology. Research Journal
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Grain refinement, microhardness distribution, strain hardening behaviour and mechanical proprieties of RD-ECAPed AA 1050
    Autorzy:
    Halimi, A.
    Hemmouche, L.
    Chettah, I. E.
    Louchene, Z. A.
    Powiązania:
    https://bibliotekanauki.pl/articles/38697115.pdf
    Data publikacji:
    2023
    Wydawca:
    Instytut Podstawowych Problemów Techniki PAN
    Tematy:
    aluminium alloys
    Rotary Die Equal Channel Angular Pressing
    microstructure
    longitudinal microhardness
    compression test
    Opis:
    This study aims to investigate the evolution of mechanical and microstructural characteristics of the 1050 aluminium alloy processed by Rotary Die Equal Channel Angular Pressing (RD-ECAP). The RD-ECAPed specimens were analysed after each pass using optical microscopy, quasi-static compression test and microhardness measurements. The results revealed a reduction in grain size from 29 _m before the RD-ECAP process to a minimum value of 2 _m at the second pass, corresponding to the maximum value of compressive yield strength, reaching 184MPa. Furthermore, there was an increase in hardness from 30 Hv to 63 Hv with a homogeneous distribution along the longitudinal surface, especially in the initial four RD-ECAP passes. Additionally, the appearance of a 45_ shear plane was observed at the last fifth pass, coinciding with the region of maximum microhardness.
    Źródło:
    Archives of Mechanics; 2023, 75, 6; 647-672
    0373-2029
    Pojawia się w:
    Archives of Mechanics
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Microhardness Evolution in Relation to the Crystalline Microstructure of Aluminum Alloy AA3004
    Autorzy:
    Izairi, N.
    Ajredini, F.
    Vevecka-Pfiftaj, A.
    Makreski, P.
    Ristova, M. M.
    Powiązania:
    https://bibliotekanauki.pl/articles/353733.pdf
    Data publikacji:
    2018
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    Al alloy
    AA3004
    equal-channel angular pressing
    ECAP
    microhardness
    SEM
    grain size
    XRD
    Opis:
    Equal-channel angular pressing (ECAP) was used as a technique for severe plastic deformation (SPD) on Al alloy AA3004. This technique produced fully dense materials of refined grain structure to sub-micrometer dimensions and advanced mechanical properties. The ECAP processing of samples was conducted as 1 to 4 passes through the die at room temperature. We present the results of the studied homogeneity evolution with the ECAP treatment. Furthermore, a Scanning Electron Microscope (SEM) was used for examination of the microstructure changes in samples undergone from 1 to 4 passes. The microhardness-HV increased upon each ECAP pass. The resulting micro-hardness evolution was attributed to crystalline microstructure modifications, such as the d-spacing (studied by X-ray Diffraction-XRD) depending on the number of ECAP pressings. The microcrystalline changes (grain refining evaluated from the Scanning Electron Microscopy - SEM images) were found to be related to the HV, following the Hall-Petch equation.
    Źródło:
    Archives of Metallurgy and Materials; 2018, 63, 3; 1101-1108
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of Machining Process Parameters and Number of Pass on Compaction Behaviour of Commercially Pure Aluminium Chips Consolidated by Equal Channel Angular Pressing (ECAP) Using Response Surface Methodology
    Autorzy:
    Palanivel, Ramaswamy
    Vigneshwaran, S.
    Alshqirate, Abedalrzaq
    Madhavan, R.
    Venkatachalam, P.
    Laubscher, R. F.
    Powiązania:
    https://bibliotekanauki.pl/articles/2048762.pdf
    Data publikacji:
    2022
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    ECAP
    response surface methodology
    relative density
    machining
    hardness
    chip consolidation
    Opis:
    This work investigates the compaction behaviour of commercial pure aluminium chips (CP Al) produced during a machining operation and subsequently consolidated by Equal Channel Angular Pressing (ECAP). Empirical models were developed to describe the relative density and hardness of the compacted product of ECAP as functions of the initial machining input parameters including cutting edge angle (CA), depth of cut (DOC) and then the number of consolidation pass during ECAP. The models were developed utilizing response surface methodology (RSM) based on data from a central composite face centred factorial design of experiments approach. The models were then validated by using Analysis of Variance (ANOVA). The effect of input parameters on the relative density and hardness of the ECAP consolidated samples are presented and discussed including details as regards to the mechanical and microstructural properties. An optimum set of input parameters are identified and presented where the best relative density and hardness are demonstrated.
    Źródło:
    Archives of Metallurgy and Materials; 2022, 67, 1; 357-370
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Channel cross-section influence on effective strain distribution in ECAP process
    Wpływ przekroju kanału kątowego na rozkład intensywności odkształcenia w procesie ECAP
    Autorzy:
    Chyła, P.
    Bednarek, S.
    Łukaszek-Sołek, A.
    Powiązania:
    https://bibliotekanauki.pl/articles/263794.pdf
    Data publikacji:
    2017
    Wydawca:
    Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
    Tematy:
    effective strain
    homogeneity of strain
    equal-channel angular pressing
    intensywność odkształcenia
    jednorodność odkształcenia
    przeciskanie przez kanał kątowy
    Opis:
    This study compares the numerically determined strain distributions after the application of the method of equal-channel angular pressing. The calculations were performed for four variants of the channel cross-sectional shapes – square, circular, and two rectangular ones with the same transverse surface area. The calculation results have been demonstrated as maps of effective strain distribution in the stabilized process.
    W pracy porównano wyznaczone numerycznie rozkłady odkształceń po zastosowaniu procesu przeciskania przez kanał kątowy. Obliczenia wykonano dla czterech wariantów przekroju kanału – kwadratowego, kołowego i dwóch prostokątnych, o takim samym polu powierzchni poprzecznej. Wyniki obliczeń przedstawiono w postaci map rozkładu intensywności odkształcenia w procesie ustalonym.
    Źródło:
    Metallurgy and Foundry Engineering; 2017, 43, 1; 31-40
    1230-2325
    2300-8377
    Pojawia się w:
    Metallurgy and Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Influence of equal channel angular extrusion on the structure of aluminium alloy EN AW 6060 for application in automotive industry
    Wpływ wyciskania kątowego w kanale walcowym na strukturę stopu aluminium EN AW 6060 do zastosowań w przemyśle samochodowym
    Autorzy:
    Valiček, J.
    Harničárová, M.
    Hlaváček, P.
    Hloch, S.
    Zeleňák, M.
    Kacalak, W.
    Łukianowicz, C.
    Kukiełka, L.
    Powiązania:
    https://bibliotekanauki.pl/articles/314242.pdf
    Data publikacji:
    2011
    Wydawca:
    Instytut Naukowo-Wydawniczy "SPATIUM"
    Tematy:
    stop aluminium
    deformacja plastyczna
    aluminium alloy
    plastic deformation
    Opis:
    The paper deals with the age-hardening aluminium alloy EN AW 6060 that has been subjected to severe plastic deformation by equal channel angular extrusion (ECAE). The initial state of the alloy was produced by cold pressing. This paper reports the results of the microstructure evaluation by light microscopy. The effect of the number of ECAE passes through a 90° angle on the mechanical properties and structure produced by ECAE was assessed. Further it was studied a decrease in strength of material due to a severe plastic deformation based on the micro hardness measurement depending on time.
    Artykuł dotyczy umocnienia stopu aluminium EN AW 6060 poddanego plastycznej deformacji w procesie kątowego wyciskania w kanale walcowym o stałej średnicy (KWSK). Stan początkowy stopu został wytworzony w procesie prasowania na zimno. Artykuł przedstawia wyniki pomiaru zmian mikrostruktury pod mikroskopem świetlnym. Przedstawiono wpływ liczby wyciśnięć pod kątem 90° na własności mechaniczne stopu. Stwierdzono obniżenie wytrzymałości materiału w czasie w wyniku plastycznej deformacji.
    Źródło:
    Autobusy : technika, eksploatacja, systemy transportowe; 2011, 12, 5; 405-413
    1509-5878
    2450-7725
    Pojawia się w:
    Autobusy : technika, eksploatacja, systemy transportowe
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effects of HE and ECAP processes on changes in microstructure and mechanical properties in copper, iron and zinc
    Autorzy:
    Kulczyk, Mariusz
    Skorupska, Monika
    Skiba, Jacek
    Przybysz, Sylwia
    Smalc-Koziorowska, Julita
    Powiązania:
    https://bibliotekanauki.pl/articles/27311391.pdf
    Data publikacji:
    2023
    Wydawca:
    Polska Akademia Nauk. Czasopisma i Monografie PAN
    Tematy:
    hydrostatic extrusion
    equal channel angular pressing
    rate of plastic deformation
    copper
    iron
    zinc
    wytłaczanie hydrostatyczne
    prasowanie kątowe równokanałowe
    szybkość odkształcenia plastycznego
    miedź
    żelazo
    cynk
    Opis:
    The research presented in this paper concerns the influence of the rate of plastic deformation generated directly in the processes of severe plastic deformations on the microstructure and properties of three metals: copper, iron and zinc. The equal channel angular pressing (ECAP) method was used, and it was performed at a low plastic deformation rate of ∼ 0.04 s−1. The high plastic strain rate was obtained using the hydrostatic extrusion (HE) method with the deformation rate at the level of ∼ 170 s−1. For all three tested materials different characteristic effects were demonstrated at the applied deformation rates. The smallest differences in the mechanical properties were observed in copper, despite the dynamic recrystallization processes that occurred in the HE process. In Armco iron samples, dynamic recovery processes in the range of high plastic deformation rates resulted in lower mechanical properties. The most significant effects were obtained for pure zinc, where, regardless of the method used, the microstructure was clearly transformed into bimodal after the ECAP process, and homogenized and refined after the HE process. After the HE process, the material was transformed from a brittle state to a plastic state and the highest mechanical properties were obtained.
    Źródło:
    Bulletin of the Polish Academy of Sciences. Technical Sciences; 2023, 71, 3; art. no. e145563
    0239-7528
    Pojawia się w:
    Bulletin of the Polish Academy of Sciences. Technical Sciences
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Intensywne odkształcenie plastyczne metali nieżelaznych
    Autorzy:
    Tański, T.
    Snopiński, P.
    Powiązania:
    https://bibliotekanauki.pl/articles/273898.pdf
    Data publikacji:
    2017
    Wydawca:
    Roble
    Tematy:
    metale nieżelazne
    intensywne odkształcenia plastyczne
    SPD
    skręcanie pod wysokim ciśnieniem
    HPT
    przeciskanie przez kanał kątowy
    ECAP
    non-ferrous metals
    severe plastic deformation
    high pressure torsion
    equal-channel angular pressing
    Źródło:
    LAB Laboratoria, Aparatura, Badania; 2017, 22, 4; 30-34
    1427-5619
    Pojawia się w:
    LAB Laboratoria, Aparatura, Badania
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-18 z 18

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies