Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "aluminium content" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-8 z 8
    Tytuł:
    Influence of fertilization on the content of some aluminium fractions in acidic soils
    Autorzy:
    Filipek, T.
    Badora, A.
    Dechnik, I.
    Powiązania:
    https://bibliotekanauki.pl/articles/796966.pdf
    Data publikacji:
    1998
    Wydawca:
    Szkoła Główna Gospodarstwa Wiejskiego w Warszawie. Wydawnictwo Szkoły Głównej Gospodarstwa Wiejskiego w Warszawie
    Tematy:
    fertilization
    aluminium content
    aluminium fraction
    acid soil
    soil
    atmospheric pollutant
    potassium fertilization
    nitrogen fertilization
    Opis:
    The present studies were carried out on the basis of field experiment on the strongly acidic soil (pH 3.9). The following treatments were applied: liming, fertilization with manure and nitrogen in the form of ammonium (NH₄)₂SO₄ and nitrate Ca(NO₃)₂ forms of nitrogen, as well as sulphate K₂SO₄ and chloride KCl potassium fertilizers. Liming (CaCO₃) eliminated the effect of aluminium mobilization by (NH₄)₂SO₄. Calcium nitrate Ca(NO₃)₂ and potassium salt KCl limited the content of aluminium strongly bound to the soil organic matter.
    Źródło:
    Zeszyty Problemowe Postępów Nauk Rolniczych; 1998, 456
    0084-5477
    Pojawia się w:
    Zeszyty Problemowe Postępów Nauk Rolniczych
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Formation and Thermodynamic Analyses of Inclusions in Ti-Containing Steel Weld Metals with Different Al Contents
    Autorzy:
    Wang, Bingxin
    Jiang, Yingtian
    Powiązania:
    https://bibliotekanauki.pl/articles/2049426.pdf
    Data publikacji:
    2021
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    thermodynamic calculation
    electron probe micro-analyzer
    oxide inclusion
    aluminium content
    phase diagram
    Opis:
    Ti-containing steel weld metals with Al contents of 0.01-0.085% were prepared. The effects of Al contents on the inclusions evolution were investigated by means of thermodynamic calculations coupled with electron probe micro-analyses and transmission electron microscopy. The results show that the inclusions in the 0.01% Al weld metal are mainly composed of ilmenite withsome amounts of (Mn-Si-Al)-oxide and titanial_spinel. When Al content is increased up to 0.035%, a more amount of corundum and a small amount of pseudobrookite are formed. In 0.085% Al weld metal, the (Mn-Si-Al)-oxide disappears completely, and the inclusions contain a substantial amount of corundum, in addition to a minimal amount of pseudobrookite. Ti3O5, MnTi2O4 and MnTiO3 are the primary constituents of pseudobrookite, titanial_spinel and ilmenite, respectively. Titanial_spinel and ilmenite have higher amounts of Mn, but lower Ti levels compared with pseudobrookite. In the case of presence of a considerable amountsof titanial_spinel and ilmenite, Mn-depleted zone is formed in matrix around the inclusions.
    Źródło:
    Archives of Metallurgy and Materials; 2021, 66, 1; 171-180
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Effect of infection of Virginia mallow shoots by fungus Sclerotinia sclerotiorum on the contents and distribution of aluminium, manganese and iron
    Wpływ porażenia pędów ślazowca pensylwańskiego grzybem Sclerotinia sclerotiorum na zawartość i rozmieszczenie glinu, manganu i żelaza
    Autorzy:
    Kalembasa, D.
    Jaremko, D.
    Bik, B.
    Kaczmarek, J.
    Jedryczka, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/47241.pdf
    Data publikacji:
    2016
    Wydawca:
    Politechnika Bydgoska im. Jana i Jędrzeja Śniadeckich. Wydawnictwo PB
    Tematy:
    plant infection
    Sida hermaphrodita
    Virginia fanpetal
    shoot
    fungi
    Sclerotinia sclerotiorum
    aluminium distribution
    aluminium content
    manganese content
    iron content
    manganese distribution
    iron distribution
    Opis:
    The aim of the study was to determine the effect of inoculation of Virginia mallow (Sida hermaphrodita [L.] Rusby) with fungus Sclerotinia sclerotiorum [Lib.] de Bary, which causes stem rot, on the contents and distribution of aluminium, manganese and iron in the shoots of this plant. Field study was carried out during three years (2011-2013) in the soil and weather conditions of central-west Poland. Inoculation was carried out with isolates obtained from rapeseed and mallow. It consisted in a slight damage of stem epidermis and inserting wheat grain overgrown with mycelium of a given isolate. During plant growth, strong infection of mallow shoots was observed, which caused inhibition in the growth and development of the plant. At the stage of technological maturity, shoots were harvested from both the control and inoculated plots for chemical analyses. Contents of the studied elements were determinated in analytical solutions obtained from biomass ash after its “dry combustion” method, using ICP-OES spectrometer. Contents and distribution of aluminium, manganese and iron in mallow shoots depended upon plant parts and placement of pathogens on the stem. The highest amount of aluminium was found in the inoculated part, and the lowest in the apices part, regardless of isolate origin. In the case of iron and manganese distribution, statistically significant effect of the applied pathogen was found. Isolate from the mallow caused greater manganese accumulation and lower iron accumulation. The conducted study demonstrates a significant effect of infection with fungus S. sclerotiorum on the physiological processes that occur in Virginia mallow plants.
    Celem badań było oznaczenie wpływu inokulacji ślazowca pensylwań-skiego (Sida hermaphrodita [L.] Rusby) grzybem Sclerotinia sclerotiorum [Lib.] de Bary, wywołującym zgniliznę twardzikową, na zawartość i rozmieszczenie glinu, manganu i żelaza w pędach tej rośliny. Badania polowe prowadzono przez trzy lata (2011-2013) w warunkach glebowo-klimatycznych środkowozachodniej Polski. Inokulację przeprowadzono izolatami uzyskanymi z rzepaku i ślazowca; polegała ona na lekkim uszkodzeniu epidermy na łodydze i umieszczeniu w tym miejscu ziarna pszenicy przerośniętego grzybnią danego izolatu. W trakcie wegetacji roślin stwierdzano silne porażenie pędów ślazowca, powodujące zahamowanie wzrostu i rozwoju roślin. W fazie dojrzałości tech-nologicznej z obiektów kontrolnych i inokulowanych pobrano pędy do analiz chemi-cznych. Zawartość badanych pierwiastków oznaczono w roztworach analitycznych uzyskanych z popiołu biomasy po jej mineralizacji „na sucho”, na spektrometrze ICP- -OES. Zawartość i rozmieszczenie glinu, manganu i żelaza w pędach ślazowca była uzależniona od zdrowotności roślin oraz miejsca na łodydze. Najwięcej glinu stwierdzano w części inokulowanej, a najmniej w części wierzchołkowej, niezależnie od pochodzenia izolatu. W przypadku rozmieszczenia żelaza i manganu stwierdzono statystycznie istotny wpływ zastosowanego patogena; izolat ze ślazowca spowodował większe nagromadzenie manganu, ale mniejsze – żelaza. Wykonane badania wskazują na znaczny wpływ porażenia grzybem S. sclerotiorum na procesy fizjologiczne przebiegające w roślinach ślazowca pensylwańskiego. Osobniki z objawami zgnilizny twardzikowej tworzą biomasę o innych parametrach jakościowych.
    Źródło:
    Acta Scientiarum Polonorum. Agricultura; 2016, 15, 4
    1644-0625
    Pojawia się w:
    Acta Scientiarum Polonorum. Agricultura
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Preparation of Nano Aluminium Powder (NAP) using a Thermal Plasma: Process Development and Characterization
    Autorzy:
    Pant, A.
    Seth, T.
    Raut, V. B.
    Gajbhiye, V. P.
    Newale, S. P.
    Nandi, A. K.
    Prasanth, H.
    Pandey, R. K.
    Powiązania:
    https://bibliotekanauki.pl/articles/358835.pdf
    Data publikacji:
    2016
    Wydawca:
    Sieć Badawcza Łukasiewicz - Instytut Przemysłu Organicznego
    Tematy:
    nano aluminium
    thermal plasma
    DC arc plasma
    RF induction plasma
    aluminium content
    BET surface area
    HR-TEM
    Opis:
    A bottom up approach for the preparation of Nano Aluminium Powder (NAP) using a Transferred Arc Thermal Plasma Reactor (TAPR) is described. The aluminium block is subjected to evaporation by the application of a thermal plasma. The aluminium vapour produced is rapidly quenched to room temperature resulting in crystallization of the aluminium vapour in nano-particulate form. Various process parameters, such as the plasma torch power, reactor pressure and plasma gas composition were optimized. This paper also describes the characterization of NAP by analytical methods, for the estimation of the Active Aluminium Content (AAC), Total Aluminium Content (TAC), XRD, bulk density, BET surface area, HR-TEM etc. The results are compared with those for samples prepared in other thermal plasma reactors, such as the DC Arc Plasma Reactor (DCAPR) and the RF Induction Thermal Plasma Reactor (RFITPR), and for commercially available NAP samples (ALEX, prepared by the EEW technique).
    Źródło:
    Central European Journal of Energetic Materials; 2016, 13, 1; 53-71
    1733-7178
    Pojawia się w:
    Central European Journal of Energetic Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Aluminium Concentration in Plants Depending on Soil Contamination with Cadmium
    Zawartość glinu w roślinach w zależności od zanieczyszczenia gleby kadmem
    Autorzy:
    Ciećko, Z.
    Wyszkowski, M.
    Rolka, E.
    Powiązania:
    https://bibliotekanauki.pl/articles/388935.pdf
    Data publikacji:
    2011
    Wydawca:
    Towarzystwo Chemii i Inżynierii Ekologicznej
    Tematy:
    zanieczyszczenie kadmem
    kompost
    węgiel brunatny
    wapno
    bentonit
    rośliny
    zawartość glinu
    cadmium contamination
    compost
    brown coal
    lime
    bentonite
    plants
    aluminium content
    Opis:
    The aim of the study has been to determine the effect of soil contamination with cadmium (10, 20, 30 and 40 mg Cd ha–1 soil) on the concentration of aluminium in aboveground parts and roots of oats, maize, yellow lupine and radish. In order to neutralise cadmium, the following neutralising agents were introduced to soil: compost, brown coal, lime and bentonite. Apart from the plant species and type of organs, other factors which largely affected the concentration of aluminium were a rate of cadmium and type of a neutralising substance. Roots contained much more aluminium than aboveground parts of plants. The highest levels of aluminium were found in roots of yellow lupine and maize whereas the smallest concentrations of this metal were determined in grain and roots of oats. Soil contamination with cadmium caused bigger changes in the concentration of aluminium in aboveground parts of plants than in their roots, especially in the case of maize and yellow lupine. Cadmium applied at 20 mg (maize and yellow lupine roots) or 40 mg Cd ha–1 soil (aboveground parts of maize and yellow lupine) caused increased levels of cadmium in plant tissues. Any further increase in the rates of the pollutant caused depression in the content of aluminium in roots of the above crops. In the case of aboveground parts and roots of radish and grain of oats, less aluminium was observed in all cadmium contaminated objects. The range of effects produced by the test neutralising substances on the concentration of aluminium was varied. The neutralising agents tended to depress the content of aluminium in plant tissues. Brown coal, bentonite and lime caused larger changes in the content of aluminium than compost. The concentration of aluminium was correlated with yields of the crops. For most of the plants, these correlations were negative in the case of aboveground parts (except radish) and positive in roots (except yellow lupine). The concentration of aluminium in particular plant organs was correlated with a number of macro- and microelements, with the correlations being usually positive for manganese, iron, cobalt, lithium, copper and zinc but negative for sulphur and boron.
    Celem badań było określenie wpływu zanieczyszczenia gleby kadmem (10, 20, 30 i 40 mg Cd kg-1 gleby) na zawartość glinu w częściach nadziemnych i korzeniach owsa, kukurydzy, łubinu żółtego i rzodkiewki. Do neutralizacji kadmu wprowadzonego do gleby zastosowano: kompost, węgiel brunatny, wapno i bentonit. Na zawartość glinu w roślinach, oprócz gatunku i organu roślin, duży wpływ miała dawka kadmu, jak również rodzaj zaaplikowanej substancji neutralizującej. Korzenie zawierały zdecydowanie więcej glinu niż części nadziemne roślin. Najwięcej glinu stwierdzono w korzeniach łubinu żółtego i kukurydzy, a najmniej w ziarnie i słomie owsa. Zanieczyszczenie gleby kadmem spowodowało większe zmiany w zawartości glinu w częściach nadziemnych niż w korzeniach roślin, szczególnie w przypadku kukurydzy i łubinu żółtego. Dawki kadmu w wysokości 20 mg (korzenie kukurydzy i łubinu żółtego) lub 40 mg Cd kg-1 gleby (części nadziemne kukurydzy i łubinu żółtego) powodowały zwiększenie zawartości glinu. Dalszy wzrost dawek kadmu wywoływał zmniejszenie zawartości glinu w korzeniach tych roślin. W przypadku części nadziemnych i korzeni rzodkiewki oraz ziarna owsa odnotowano zmniejszenie zawartości glinu we wszystkich obiektach zanieczyszczonych kadmem. Zakres oddziaływania testowanych substancji neutralizujących na zawartość glinu był zróżnicowany. Dodatki neutralizujące na ogół obniżały zawartość glinu w roślinach. Węgiel brunatny, bentonit i wapno wywoływały większe zmiany w zawartości glinu w roślinach niż kompost. Zawartość glinu wykazywała skorelowanie z plonem roślin. U większości roślin wystąpiły relacje ujemne w częściach nadziemnych (oprócz rzodkiewki), a dodatnie w korzeniach (z wyjątkiem łubinu żółtego). Zawartość glinu w poszczególnych organach roślin była skorelowana z licznymi makro- i mikroelementami, w tym przeważnie dodatnio z zawartością manganu, żelaza, kobaltu, litu, kadmu, miedzi i cynku, a ujemnie z zawartością siarki i boru.
    Źródło:
    Ecological Chemistry and Engineering. A; 2011, 18, 12; 1641-1650
    1898-6188
    2084-4530
    Pojawia się w:
    Ecological Chemistry and Engineering. A
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Corrosion Behaviour Correlation of the Secondary Aluminium Casts in Natural Atmosphere and Laboratory Conditions
    Autorzy:
    Kuchariková, L.
    Liptáková, T.
    Tillová, E.
    Bonek, M.
    Medvecká, D.
    Powiązania:
    https://bibliotekanauki.pl/articles/352248.pdf
    Data publikacji:
    2020
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    secondary aluminium alloys
    high Fe content
    corrosion properties
    natural atmosphere
    Opis:
    The secondary aluminium alloys are very important material in actual industry from economic and ecological point of view. The secondary aluminium used for production of casts, however, contains some elements, i.e. iron, – affecting physical, chemical and mechanical behaviour. The subject of our investigation has been corrosion behaviour in natural atmosphere of the hypoeutectic AlSi7Mg0.3 cast alloys with various content of iron, because the Fe content affects not only mechanical properties but corrosion resistance, as well. Three types of the AlSi7Mg0.3 cast alloys were exposed for 9 months in natural atmosphere and the measure of their degradation by corrosion was found by determination of the weight loss and the light microscopy. In addition, a scanning electron microscopy (SEM) analyses and evaluation of surface changes were used. The corrosion behaviour in natural atmosphere was compared to results of the carried out electrochemical and exposure laboratory experiments in chloride solutions.
    Źródło:
    Archives of Metallurgy and Materials; 2020, 65, 4; 1455-1462
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Comparative assessment of Al-Si alloy gassing degree with the application of the „first bubble” and „solidification under decreased pressure” methods
    Porównawcza ocena stopnia zagazowania stopów Al-Si z zastosowaniem metody „pierwszego pęcherzyka” i metody „krzepnięcia pod obniżonym ciśnieniem”
    Autorzy:
    Zych, J.
    Piękoś, M.
    Kolczyk, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/263913.pdf
    Data publikacji:
    2016
    Wydawca:
    Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Wydawnictwo AGH
    Tematy:
    aluminum alloys
    gassing degree
    measuring the gas content
    stopy aluminium
    zagazowania
    badania zawartości gazów
    Opis:
    All aluminum alloys in a liquid state are characterised by easy oxidation and absorption of hydrogen from the surroundings (which are the main reasons for casting defects). The amount of hydrogen adsorbed by a liquid alloy depends mainly on temperature and melting time. The performed investigations were aimed at comparing two known methods of measuring a metal gassing degree; the first bubble method and sample solidification under decreased pressure. Liquid metal melting and holding processes were performed under different conditions that caused variability of its gassing degree, resulting in a variability of purity and quality of the liquid metal. The investigations were carried out with using the hypoeutectic aluminum-silica AK7 alloy.
    Wszystkie stopy aluminiowe w stanie ciekłym charakteryzują się łatwym utlenianiem i pochłanianiem wodoru z otaczającej atmosfery, co jest główną przyczyną wad odlewniczych. Ilość wodoru zaabsorbowanego przez ciekły stop zależy głównie od temperatury i czasu topienia. Przeprowadzone badania miały na celu porównanie dwóch znanych metod pomiaru stopnia zagazowania metalu, metodę pierwszego pęcherzyka oraz metodę krzepnięcia próbki pod obniżonym ciśnieniem. Proces topienia i przetrzymywania ciekłego metalu odbywał się w różnych warunkach, co powodowało zmienność stopnia zagazowania, a tym samym czystości i jakości ciekłego metalu. Wykonane badania zostały przeprowadzone z wykorzystaniem podeutektycznego stopu aluminium-krzem AK7.
    Źródło:
    Metallurgy and Foundry Engineering; 2016, 42, 1; 7-19
    1230-2325
    2300-8377
    Pojawia się w:
    Metallurgy and Foundry Engineering
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Quality of automotive sand casting with different wall thickness from progressive secondary alloy
    Autorzy:
    Pastierovičová, Lucia
    Kuchariková, Lenka
    Tillová, Eva
    Chalupová, Mária
    Pastirčák, Richard
    Powiązania:
    https://bibliotekanauki.pl/articles/26078793.pdf
    Data publikacji:
    2022
    Wydawca:
    Stowarzyszenie Menedżerów Jakości i Produkcji
    Tematy:
    jakość odlewów
    wtórny stop aluminium
    grubość ściany
    analiza ilościowa
    wyższa zawartość Fe
    quality of castings
    secondary aluminium alloy
    wall thickness
    quantitative analysis
    higher Fe content
    Opis:
    This paperwork is focused on the quality of AlSi6Cu4 casting with different wall thicknesses cast into the metal mold. Investigated are structural changes (the morphology, size, and distribution of structural components). The quantitative analysis is used to numerically evaluate the size and area fraction of structural parameters (α-phase, eutectic Si, intermetallic phases) between delivered experimental material and cast with different wall thicknesses. Additionally, the Brinell hardness is performed to obtain the mechanical property benefits of the thin-walled alloys. This research leads to the conclusion, that the AlSi6Cu4 alloy from metal mold has finer structural components, especially in small wall thicknesses, and thus has better mechanical properties (Brinell hardness). These secondary Al-castings have a high potential for use in the automotive industry, due to the thin thicknesses and thus lightweight of the construction.
    Źródło:
    Production Engineering Archives; 2022, 28, 2; 172--177
    2353-5156
    2353-7779
    Pojawia się w:
    Production Engineering Archives
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-8 z 8

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies