Tytuł:: Study of Bending Fatigue Properties of Al-Si Cast Alloy
Autorzy:: Tillová, E.
Závodská, D.
Kuchariková, L.
Chalupová, M.
Belan, J.
Powiązania:: https://bibliotekanauki.pl/articles/355910.pdf
Data publikacji:: 2017
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: secondary Al-Si cast alloy
fatigue properties
fracture
cast defects
Opis:: Fatigue properties of casting Al-alloys are very sensitive to the microstructural features of the alloy (e.g. size and morphology of the eutectic Si, secondary dendrite arm spacing – SDAS, intermetallics, grain size) and casting defects (porosity and oxides). Experimental study of bending fatigue properties of secondary cast alloys have shown that: fatigue tests up to 10⁶-10⁷cycles show mean fatigue limits of approx. 30-49 MPa (AlSi9Cu3 alloy – as cast state), approx. 65-76 MPa (AlSi9Cu3 alloy after solution treatment) and 60-70 MPa (self-hardened AlZn10Si8Mg alloy) in the tested casting condition; whenever large pore is present at or near the specimen’s surface, it will be the dominant cause of fatigue crack initiation; in the absence of large casting defects, the influence of microstructural features (Si morphology; Fe-rich phases) on the fatigue performance becomes more pronounced.
Źródło:: Archives of Metallurgy and Materials; 2017, 62, 3; 1591-1596
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Skocz do pozycji: 2.

Tytuł:: Study of the precipitation hardening process in recycled Al-Si-Cu cast alloys
Autorzy:: Kuchariková, L.
Tillová, E.
Matvija, M.
Belan, J.
Chalupová, M.
Powiązania:: https://bibliotekanauki.pl/articles/354012.pdf
Data publikacji:: 2017
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: precipitation hardening
recycled Al-Si-Cu cast alloys
Cu precipitate
mechanical properties
transmission electron microscopy
Opis:: The formation of extremely small uniformly dispersed particles of a second phase within the original phase matrix during heat treatment changed material properties. Therefore the characterization of precipitation had been investigated using high resolution transmission electron microscopy (TEM) and electron diffraction of thin foils for an AlSi9Cu3 cast alloy. For investigation the hardening effect onto mechanical properties of aluminium cast was used heat treatment, which consisted from solution treatment at 515°C / 4 hours (h), followed by quenching into water with temperature 50°C and artificial aging using different temperatures 170°C and 190°C with different holding time 2, 4, 8, 16, and 32 hours. The observations of microstructure and substructure reveals that precipitation hardening has caused great changes in size, morphology and distributions of structural components, the formation of precipitates of Cu phases, and the change of mechanical properties as well.
Źródło:: Archives of Metallurgy and Materials; 2017, 62, 1; 397-403
1733-3490
Pojawia się w:: Archives of Metallurgy and Materials
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce
odwiedzone

Skocz do pozycji: 3.

Tytuł:: Identification and Analysis of Intermetallic Phases in Age-Hardened Recycled AlSi9Cu3 Cast Alloy
Identyfikacja i analiza faz międzymetalicznych w utwardzanych przez starzenie stopach odlewniczych AlSi9Cu3 z recyklingu
Autorzy:: Hurtalová, L.
Tillová, E.
Chalupová, M.
Powiązania:: https://bibliotekanauki.pl/articles/139970.pdf
Data publikacji:: 2012
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Tematy:: Al-Si-Cu
cast alloy
age hardening
Fe-rich intermetallic phase
Cu-rich intermetallic phase
mechanical properties
stop odlewniczy
utwardzanie przez starzenie
faza międzymetaliczna wzbogacana żelazem
faza międzymetaliczna wzbogacana miedzią
właściwości mechaniczne
Opis:: Purpose: The influence of age-hardening solution treatment at temperature 515 degrees centigrade with holding time 4 hours, water quenching at 40 degrees centigrade and artificial aging by different temperature 130, 150, 170 and 210 degrees centigrade with different holding time 2, 4, 8, 16 and 32 hours on changes in morphology of Fe-rich Al₁₅(FeMn)₃Si₂ and Cu-rich (Al₂Cu, Al-Al₂Cu-Si) intermetallic phases in recycled AlSi9Cu3 cast alloy. Material/Methods: Recycled (secondary) AlSi9Cu3 cast alloy is used especially in automotive industry (dynamic exposed cast, engine parts, cylinder heads, pistons and so on). Microstructure was observed using a combination of different analytical techniques (scanning electron microscopy upon standard and deep etching and energy dispersive X-ray analysis – EDX) which have been used for the identification of the various phases. Quantitative study of changes in morphology of phases was carried out using Image Analyzer software NIS-Elements. The mechanical properties (Brinell hardness and tensile strength) were measured in line with STN EN ISO. Results/Conclusion: Age-hardening led to changes in microstructure include the spheroidization of eutectic silicon, gradual disintegration, shortening and thinning of Fe-rich intermetallic phases and Al-Al₂Cu-Si phases were fragmented, dissolved and redistributed within alpha-matrix. These changes led to increase in the hardness and tensile strength in the alloy.
Cel: Badanie wpływu utwardzania przez starzenie przesycanie w temperaturze 515 stopni Celsjusza z czasem przetrzymywania 4 godz., hartowanie wodne w 40 stopniach Celsjusza, starzenie przyspieszone w różnych temperaturach: 130, 150, 170 i 210 stopni Celsjusza, przy czasach przetrzymywania: 2, 4, 8, 16 i 32 godziny na zmiany w morfologii stopów odlewniczych AlSi9Cu3 z recyklingu wzbogaconych żelazem (Al₁₅(FeMn)₃Si₂) lub miedzią (Al₂Cu, Al-Al₂Cu-Si). Materiał i metody: Pochodzący z recyklingu (wtórny) stop odlewniczy aluminium AlSi9Cu3 jest powszechnie używany, zwłaszcza w przemyśle motoryzacyjnym (dynamiczne, odkryte odlewy, części silnika, głowice cylindrów, tłoki itp.). Mikrostrukturę odlewów badano stosując kombinację różnych technik analitycznych (elektronowa mikroskopia skaningowa w połączeniu z analizą rentgenowską z dyspersją energii (EDX), standardową i z głebokim wytrawianiem), co pozwoliło identyfikować różne fazy międzymetaliczne. Ocena ilościowa zmian w morfologii tych faz została przeprowadzona przy wykorzystaniu oprogramowania analizatora obrazów (Image Analyzer NIS-Elements). Właściwości mechaniczne (twardość w skali Brinella i wytrzymałość na rozciaganie) były mierzone zgodnie z normą STN EN ISO. Wyniki i wnioski: Utwardzanie przez starzenie prowadzi do zmian w mikrostrukturze, które polegają na sferoidyzacji krzemu eutektycznego, stopniowej dezintegracji, skracaniu i ścienianiu faz międzymetalicznych wzbogaconych żelazem. Fazy Al-Al₂Cu-Si podlegały fragmentacji, zostały rozpuszczone i redystrybuowane w osnowie stopu. Zmiany te prowadzą do wzrostu twardości stopu i jego wytrzymałości na rozciąganie.
Źródło:: Archive of Mechanical Engineering; 2012, LIX, 4; 385-396
0004-0738
Pojawia się w:: Archive of Mechanical Engineering
Dostawca treści:: Biblioteka Nauki

Artykuł

Zmień widok

na półce

Informacja

Wyszukujesz frazę "cast Al-Si" wg kryterium: Temat

Źródło danych

Dostawca treści

Kolekcja

Rok wydania

Wydawca

Temat

Autor

Typ dokumentu

Język