Informacja

Drogi użytkowniku, aplikacja do prawidłowego działania wymaga obsługi JavaScript. Proszę włącz obsługę JavaScript w Twojej przeglądarce.

English (EN)·Polski (PL)·Yкраїнський (UK)
Przejdź do strony domowej biblioteki Centralna Biblioteka Wojskowa Link otwiera się w nowym oknie Logo biblioteki Prolib Integro - strona głównaCentralna Biblioteka Wojskowa

Wyszukujesz frazę "wire drawing" wg kryterium: Temat

  Lista filtrów
Wyrównaj
    Wyświetlanie 1-7 z 7
    Tytuł:
    The Effect of the Length of the Drawing Die Sizing Portion on the Energy and Force Parameters of the Medium-Carbon Steel Wire Drawing Process
    Autorzy:
    Suliga, M.
    Jabłońska, M.
    Hawryluk, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/356682.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    conical die
    wire drawing
    temperature
    drawing stress
    Opis:
    The paper discusses a theoretical and an experimental analyses of steel wire drawing in conical drawing dies with a varying length of the die sizing portion. The theoretical analysis was performed in the Drawing 2D, where the wire temperature and drawing stress were determined. The theoretical study was verified by the measurement of drawing force under laboratory conditions and by industrial multi-stage drawing tests carried out under commercial conditions. A relationship has been shown to exist between die sizing portion length and wire temperature and drawing stress.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 4; 1353-1359
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Estimation of the Level of Residual Stress in Wires with a Magnetic Method
    Ocena poziomu naprężeń własnych w drutach metodą magnetyczną
    Autorzy:
    Suliga, M.
    Borowik, L.
    Chwastek, K.
    Powiązania:
    https://bibliotekanauki.pl/articles/352809.pdf
    Data publikacji:
    2015
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    residual stress
    wire drawing
    hysteresis loop
    effective field
    naprężenia własne
    druty ciągnione
    pętla histerezy
    Opis:
    Residual stress present in wires after drawing process affects their magnetic properties. The paper presents a concept to estimate the level of residual stress on the basis of measurements of hysteresis loops. In order to describe the effect qualitatively the Jiles-Atherton-Sablik description is adapted. On the basis of variations in hysteresis loop shapes the average values of residual stress in wires for different single draft values are determined. It was found that the estimated average values by magnetic stresses are comparable with the results of numerical modeling and experimental studies.
    Naprężenia własne istniejące w drutach po procesie ciągnienia mają wpływ na ich właściwości magnetyczne. W pracy przedstawiono koncepcję oszacowania poziomu naprężeń własnych drutów na podstawie pomiarów pętli histerezy. W celu jakościowego opisu zjawiska zaadaptowano model Jilesa-Athertona-Sablika. Na podstawie zmian kształtu pętli histerezy oszacowano średnie wartości naprężeń własnych dla drutów ciągnionych z różnymi wartościami gniotu pojedynczego. Stwierdzono, że oszacowane metodą magnetyczną średnie wartości naprężeń własnych są porównywalne z wynikami z modelowania numerycznego i badań eksperymentalnych.
    Źródło:
    Archives of Metallurgy and Materials; 2015, 60, 1; 409-413
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The influence of the multipass drawing process in clasical and hydrodynamic dies on residual stresses of high carbon steel wires
    Wpływ wielostopniowego procesu ciągnienia w ciągadłach klasycznych i hydrodynamicznych na naprężenia własne w drutach ze stali wysokowęglowej
    Autorzy:
    Suliga, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/352653.pdf
    Data publikacji:
    2011
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    naprężenie
    stal wysokowęglowa
    ciągadła klasyczne
    ciągadła hydrodynamiczne
    temperatura
    residual stresses
    high carbon steel
    multipass wire drawing
    classical and hydrodynamic dies
    temperature
    redundant strain
    Opis:
    n the paper the influence of the multipass drawing process on residual stresses of high carbon steel wires has been assessed. The drawing process of φ5.5 mm wires to the final wire of φ1.6 mm was conducted in 11 passes, in industrial conditions, by means of a modern Koch multi-die drawing machine. The drawing speed in the last passes was 10 m/s. The experimental measure of residual stresses in wires drawn in classical and hydrodynamic dies by Sachs-Linicus method has been done. On the basis of numerical analyses of the wire drawing process, the distributions of longitudinal residual stresses on the cross section of wires, temperatures and redundant strain have been determined. The investigations have shown the essential influence of the multipass drawing process in hydrodynamic dies on residual stresses of high carbon steel wires. In the case of the wires drawn with hydrodynamic dies, in comparison to the wires drawn in classical dies, the 30% decrease of longitudinal residual stresses have been noted. It has been shown that the decrease of residual stresses in wires drawn in hydrodynamic dies is connected with a lower redundant strain by 14.7%. In addition, the application of hydrodynamic dies in the multipass drawing process leads to significant decreasing of temperature of the wire surface (in the last pass above 500 °C). Undoubtedly, the large increase of temperature in the sub-layer of wires drawn in classical die caused the rise of internal stresses related to the thermal expansion of steel. In consequence, it caused the increase of residual stresses.
    W pracy określono wpływ wielostopniowego procesu ciągnienia na naprężenia własne w drutach ze stali wysokowęglowej. Proces ciągnienia drutów o średnicy 5,5 mm na średnicę końcową 1,60 mm zrealizowano w 11 ciągach, w warunkach przemysłowych, na nowoczesnej ciągarce wielostopniowej Kocha. Prędkość ciągnienia na ostatnim ciągu wynosiła 10 m/s. Naprężenia własne w drutach po procesie ciągnienia w ciągadłach klasycznych i hydrodynamicznych wyznaczono w oparciu o badania doświadczalne wykorzystując metodę Sachsa-Linicusa. Natomiast w oparciu o analizę teoretyczną procesu ciągnienia określono rozkłady wzdłużnych naprężeń własnych na przekroju drutów, temperaturę, odkształcenia postaciowe i intensywność odkształcenia. Wykazano, że stosowanie w procesie wielostopniowego ciągnienia drutów wysokowęglowych ciągadeł hydrodynamicznych przyczynią się do znaczącego spadku wzdłużnych naprężeń własnych. Dla drutów ciągnionych w ciągadłach hydrodynamicznych, w stosunku do drutów ciągnionych w ciągadłach klasycznych, odnotowano spadek o około 30% wzdłużnych naprężeń własnych I rodzaju. Spadek naprężeń własnych w drutach ciągnionych w ciągadłach hydrodynamicznych należy wiązać z występowaniem dla tego wariantu mniejszych o 14,7% odkształceń postaciowych. Ponadto zastosowanie ciągadeł hydrodynamicznych w procesie wielostopniowego ciągnienia prowadzi do zasadniczego spadku temperatury drutu na jego powierzchni (w ostatnim ciągu o ponad 500 C). Znaczący wzrost temperatury w warstwie przypowierzchniowej drutów ciągnionych klasycznie przyczynił się do powstania naprężeń wewnętrznych związanych z rozszerzalnoącią cieplna\ą stali, co w konsekwencji spowodowało wzrost naprężeń własnych.
    Źródło:
    Archives of Metallurgy and Materials; 2011, 56, 4; 939-944
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    Research of Zinc Coatings in Thin Medium Carbon Steel Wires
    Autorzy:
    Suliga, M.
    Wartacz, R.
    Kania, H.
    Powiązania:
    https://bibliotekanauki.pl/articles/356515.pdf
    Data publikacji:
    2019
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    wire
    zinc coating
    drawing speed
    mechanical properties
    Opis:
    An analysis of the effect of drawing speed on the formation of a zinc coating in the multi-stage fine steel wire drawing process has been carried out in the article. Pre-hardened 2.2 mm-diameter material was drawn into 1.00 mm-diameter wire in 6 draws on a multi-stage drawing machine. The drawing process was carried out at a drawing speed of 5, 10, 15, 20 and 20 m/s, respectively. Mechanical tests were tests were performed for the final wires to determine their yield strength, ultimate tensile strength, uniform and total elongation and reduction in area. The thickness of the zinc coating on the wire surface was determined by the gravimetric method and based on metallographic examination. The use of electron scanning microscopy, on the other hand, enabled the identification of individual phases in the zinc coating. The above investigations were supplemented with corrosion testing of 1.00 mm-diameter wires. It has been demonstrated that drawing speed significantly influences not only the thickness of the zinc coating on the drawn wire surface, buts also its morphology and corrosion resistance.
    Źródło:
    Archives of Metallurgy and Materials; 2019, 64, 1; 413-420
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Effect of Drawing Speed on the Ageing of High-Carbon Steel Wire
    Autorzy:
    Suliga, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/351513.pdf
    Data publikacji:
    2018
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    steel
    wire
    drawing speed
    strain ageing
    mechanical properties
    Opis:
    The paper analyzes the effect of ageing on the variations in the mechanical and technological properties of steel wire. The process of drawing 5.5 mm-diameter wire rod into 1.70 mm wire was carried out in 12 draws on a Koch KGT multi-stage drawing machine in the drawing velocity range of 5-25 m/s. Finished 1.7 mm-diameter wires after, respectively, 1, 24, 720 and 8760 hours of the completion of the drawing process were subjected to testing to determine their mechanical and technological properties. The yield strength, YS; tensile strength, UTS; uniform elongation, Ar; total elongation, Ac; reduction of area, Z; number of twists, Nt; and the number of bends, Nb, have been determined. It has been demonstrated that variations in mechanical properties occur after the multi-stage drawing process due to ageing, with their degree and mode being dependent on the drawing speed.
    Źródło:
    Archives of Metallurgy and Materials; 2018, 63, 4; 1931-1935
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Influence of the High Speed Multipass Drawing Process on the Fatigue Strength of High Carbon Steel Wires
    Wpływ wielostopniowego procesu ciągnienia z dużymi prędkościami na wytrzymałość zmęczeniową drutów ze stali wysokowęglowej
    Autorzy:
    Suliga, M.
    Powiązania:
    https://bibliotekanauki.pl/articles/356211.pdf
    Data publikacji:
    2012
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    drawing speed
    fatigue strength
    rope wires
    wire roughness
    Opis:
    In this work the influence of the drawing speed on fatigue strength of high carbon steel wires has been assessed. The drawing process of φ5.5 mm wires to the final wire of φ1.6 mm was conducted in 11 passes, in industrial conditions, by means of a modern Koch multi-die drawing machine. The drawing speeds in the last passes were: 5, 10, 15 and 20 m/s. For φ1.6 mm wires the investigation of fatigue strength has been carried out. In order to explain the effect of drawing speed on fatigue strength of rope wires, the roughness of drawn wires have been also determined. In addition, the numerical analysis of the drawing process on the base of Drawing 2D in which distribution of redundant strain, has been shown. The data of investigations prove the favourable effect of high drawing speed on fatigue strength of drawn wires. It was found that the better fatigue strength of wires drawn at the speed of 20 m/s compared to the wires drawn at the speeds of 5-15 m/s is associated with a better geometric structure of the surface of those wires. In addition to the high fatigue strength of the wires drawn with high speed is related to theirs higher redundant strain. The obtained data investigation can be applied in wire industry while implementing the new technologies of high speed drawing process of high carbon steel wires.
    W pracy określono wpływ dużej prędkości ciągnienia na wytrzymałość zmęczeniowa drutów ze stali wysokowęglowej. Proces ciągnienia drutów o średnicy 5,5 mm na średnice końcowa 1,60 mm zrealizowano w 11 ciągach, w warunkach przemysłowych, na nowoczesnej ciągarce wielostopniowej Kocha. Prędkości ciągnienia na ostatnim ciągu wynosiły odpowiednio: 5, 10, 15 i 20 m/s. Badania wytrzymałości zmęczeniowej przeprowadzono dla drutów końcowych φ1,60 mm. Dla pełniejszej oceny wpływu wielkości prędkości ciągnienia na wytrzymałość zmęczeniowa drutów liniarskich przeprowadzono także badania chropowatości powierzchni. Dodatkowo w pracy, w oparciu o program Drawing 2d, przeprowadzono analizę numeryczną procesu ciągnienia, w której określono odkształcenia postaciowe w drutach po procesie ciągnienia. Uzyskane wyniki badan świadczą o korzystnym wpływie dużej prędkości ciągnienia na wytrzymałość zmęczeniowa drutów. Stwierdzono, ze lepsza wytrzymałość zmęczeniowa drutów ciągnionych z prędkością 20 m/s, w stosunku do drutów ciągnionych z prędkościami 5-15 m/s, związana jest z ich lepsza struktura geometryczna powierzchni oraz większymi odkształceniami postaciowymi. Uzyskane wyniki badan mogą być wykorzystane w przemyśle ciągarskim przy wdrażaniu nowych technologii szybkościowego ciągnienia drutów ze stali wysokowęglowych.
    Źródło:
    Archives of Metallurgy and Materials; 2012, 57, 4; 1172-1178
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
    Tytuł:
    The Influence of the Angle of the Working Part of the Die on the High Speed Drawing Process of Low Carbon Steel Wires
    Autorzy:
    Suliga, M.
    Wartacz, R.
    Michalczyk, J.
    Powiązania:
    https://bibliotekanauki.pl/articles/354396.pdf
    Data publikacji:
    2017
    Wydawca:
    Polska Akademia Nauk. Czytelnia Czasopism PAN
    Tematy:
    wire
    drawing angle
    high speed
    temperature
    lubrication
    mechanical properties
    Opis:
    The paper contains the theoretical and experimental analysis of the impact of the drawing angle on the drawing process and the properties of low carbon steel wires. A multi-stage drawing wire rod with a diameter of 5.5 mm on a wire with a diameter of 1.0 mm has been carried out in two stages. The first one consisted of preliminary drawing wire rod for the wire with a diameter of 2.2 mm which was next subjected to the drawing process at a speed of 25 m/sec at the final wire with a diameter of 1.0 mm. The wires were drawn in conventional dies with drawing angle α = 3, 4, 5, 6, 7 degrees. For the wires drawn in respective variants, the investigation of the mechanical properties was performed and the amount of lubricant on the surface of steel wires was determined. Numerical analysis of the process of drawing in the Drawing 2D complemented the experimental studies. It has been shown that when drawing at high speeds, properly chosen the value of the angle of the working part of the die can improve the lubrication conditions and mechanical properties of steel wires.
    Źródło:
    Archives of Metallurgy and Materials; 2017, 62, 2A; 483-487
    1733-3490
    Pojawia się w:
    Archives of Metallurgy and Materials
    Dostawca treści:
    Biblioteka Nauki
    Artykuł
      Wyświetlanie 1-7 z 7

      Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies